CN105566934A - Reinforced wood-plastic plate - Google Patents
Reinforced wood-plastic plate Download PDFInfo
- Publication number
- CN105566934A CN105566934A CN201610073527.6A CN201610073527A CN105566934A CN 105566934 A CN105566934 A CN 105566934A CN 201610073527 A CN201610073527 A CN 201610073527A CN 105566934 A CN105566934 A CN 105566934A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood
- raw material
- plastic plate
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A reinforced wood-plastic plate is manufactured from, by weight, 50-58 parts of wood powder, 18-24 parts of rice hull, 7-11 parts of sodium stearate, 17-26 parts of butyl p-hydroxybenzoate, 9-19 parts of light calcium carbonate, 17-21 parts of butyral resin, 17-25 parts of polypropylene, 17-25 parts of linear low-density polyethylene, 0.3-0.8 part of walnut shells, 0.3-0.8 part of chestnut shells, 0.3-0.8 part of grape seeds, 1-3 parts of calcium hydroxide, 6-12 parts of kaolin, 6-12 parts of nano bauxite, 1-2 parts of magnets, 2-4 parts of aminopropyltriethoxysilane, 1-2 parts of dicumyl peroxide, 6-13 parts of ethyl methacrylate, 13-23 parts of 5-type polyvinyl chloride polyester, 3-7 parts of oxidized polyethlene wax, 0.1-0.2 part of wheat germ oil, 0.1-0.2 part of olive oil and 0.1-0.2 part of beer with the alcohol content of 8%. The wood-plastic plate is low in price, the manufacturing process is simple and convenient, toxins and pungent smells are avoided, high strength and high wear resistance are achieved, the plate is good in binding performance, free of cracks and bubbles and excellent in waterproof and mould preventing performance, and the wood-plastic plate has good radiation absorbing capacity, can protect the human body against radiation well, and is long in service life.
Description
Technical field
The present invention relates to Wood-plastic material field, be specifically related to a kind of strengthening wood and mould plate.
Background technology
Wood-plastic material is the material that a kind of wood powder, xylon or vegetable fibre filling thermoplastic polymer is made through high temperature high pressure process, have the advantage of timber and plastics concurrently, its main raw material is agriculture and forestry organic waste material (as waste wood, farm crop rice straw etc.) and thermoplastics.Agricultural crop straw is as the by product of agriculture production, and output is large, distribution is wide, according to statistics annual about 8 ~ 1,000,000,000 tons of current China agricultural crop straw generation.For a long time, both at home and abroad the comprehensive utilization of agricultural crop straw is conducted extensive research, obtain some available approach, wherein important one is exactly by wood fibre and plastic blend, prepare matrix material, as by cotton field waste and the mixing of discarded mulch film, add suitable additive and make wood-plastic floor board; Stalk or Pericarppium arachidis hypogaeae are mixed with PVC, PP or PE, High Temperature High Pressure prepares Wood-plastic material.The Application and Development of Wood-plastic material is conducive to protecting forest resources, and slows down waste wood and plastics to the pollution of environment, makes full use of the natural resources.
Summary of the invention
Technical problem to be solved by this invention is to provide one to have high-strength, high-anti-friction; sheet material binding property is good; do not ftracture non-foaming; have the mould proof performance of superior waterproof; and wood of the present invention is moulded plate and is had and well inhale radiation capacity; can human body be protected very well from radiation, plate be moulded by the strengthening wood of long service life.
Technical problem to be solved by this invention realizes by the following technical solutions:
Plate moulded by a kind of strengthening wood, the raw material of following weight part is adopted to make: wood powder 50-58 part, rice husk 18-24 part, sodium stearate 7-11 part, butyl p-hydroxybenzoate 17-26 part, light calcium carbonate 9-19 part, butyral resin 17-21 part, polypropylene 17-25 part, linear low density polyethylene 17-25 part, nut-shell 0.3-0.8 part, chestnut shell 0.3-0.8 part, Semen Vitis viniferae 0.3-0.8 part, calcium hydroxide 1-3 part, kaolin 6-12 part, nano aluminum alumina 6-12 part, magnetite 1-2 part, aminopropyltriethoxywerene werene 2-4 part, oxidation diisopropylbenzene(DIPB) 1-2 part, β-dimethyl-aminoethylmethacrylate 6-13 part, polyvinyl chloride polyester 5 type 13-23 part, oxidized polyethlene wax 3-7 part, Wheat germ oils 0.1-0.2 part, sweet oil 0.1-0.2 part, 8 ° of beer 0.1-0.2 parts.
Strengthen the preparation method that plate moulded by wood, comprise the following steps,
Above-mentioned each raw material is dropped into drying machine drying, bake out temperature is 120-150 DEG C, taking-up puts into-50 DEG C of freezers freezing 48 hours, take out, then drop into drying machine drying, bake out temperature is 65-75 DEG C, water ratio is made to be not more than 1.2%, then each raw material powder is broken into fine powder, after entering stirrer stirring, sends into extruder for shaping.
The invention has the beneficial effects as follows: it is cheap that plate material moulded by wood of the present invention; manufacture craft is easy; nontoxicly to have no irritating odor; have high-strength, high-anti-friction, sheet material binding property is good, does not ftracture non-foaming; have the mould proof performance of superior waterproof; and wood of the present invention is moulded plate and is had and well inhale radiation capacity, can human body be protected very well from radiation, long service life.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
Plate moulded by a kind of strengthening wood, the raw material of following weight part is adopted to make: wood powder 50 parts, 18 parts, rice husk, sodium stearate 7 parts, butyl p-hydroxybenzoate 17 parts, light calcium carbonate 9 parts, butyral resin 21 parts, polipropene 25 part, linear low density polyethylene 25 parts, nut-shell 0.8 part, chestnut shell 0.8 part, Semen Vitis viniferae 0.8 part, 3 parts, calcium hydroxide, kaolin 12 parts, 12 parts, nano aluminum alumina, magnetite 2 parts, aminopropyltriethoxywerene werene 4 parts, oxidation diisopropylbenzene(DIPB) 2 parts, β-dimethyl-aminoethylmethacrylate 13 parts, 23 parts, polyvinyl chloride polyester 5 type, oxidized polyethlene wax 7 parts, Wheat germ oils 0.2 part, 0.2 part, sweet oil, 8 ° of beer 0.2 part.
Strengthen the preparation method that plate moulded by wood, comprise the following steps,
Above-mentioned each raw material is dropped into drying machine drying, bake out temperature is 120 DEG C, taking-up puts into-50 DEG C of freezers freezing 48 hours, take out, then drop into drying machine drying, bake out temperature is 65 DEG C, water ratio is made to be not more than 1.2%, then each raw material powder is broken into fine powder, after entering stirrer stirring, sends into extruder for shaping.
Embodiment 2
Plate moulded by a kind of strengthening wood, the raw material of following weight part is adopted to make: wood powder 54 parts, 21 parts, rice husk, sodium stearate 9 parts, butyl p-hydroxybenzoate 22 parts, light calcium carbonate 14 parts, butyral resin 19 parts, polypropylene 21 parts, linear low density polyethylene 21 parts, nut-shell 0.5 part, chestnut shell 0.5 part, Semen Vitis viniferae 0.5 part, 2 parts, calcium hydroxide, kaolin 9 parts, 9 parts, nano aluminum alumina, magnetite 1.5 parts, aminopropyltriethoxywerene werene 3 parts, oxidation diisopropylbenzene(DIPB) 1.5 parts, β-dimethyl-aminoethylmethacrylate 9 parts, 18 parts, polyvinyl chloride polyester 5 type, oxidized polyethlene wax 5 parts, Wheat germ oils 0.15 part, 0.15 part, sweet oil, 8 ° of beer 0.15 part.
Strengthen the preparation method that plate moulded by wood, comprise the following steps,
Above-mentioned each raw material is dropped into drying machine drying, bake out temperature is 135 DEG C, taking-up puts into-50 DEG C of freezers freezing 48 hours, take out, then drop into drying machine drying, bake out temperature is 70 DEG C, water ratio is made to be not more than 1.2%, then each raw material powder is broken into fine powder, after entering stirrer stirring, sends into extruder for shaping.
Embodiment 3
Plate moulded by a kind of strengthening wood, the raw material of following weight part is adopted to make: wood powder 58 parts, 24 parts, rice husk, sodium stearate 11 parts, butyl p-hydroxybenzoate 26 parts, light calcium carbonate 19 parts, butyral resin 21 parts, polipropene 25 part, linear low density polyethylene 25 parts, nut-shell 0.8 part, chestnut shell 0.8 part, Semen Vitis viniferae 0.8 part, 3 parts, calcium hydroxide, kaolin 12 parts, 12 parts, nano aluminum alumina, magnetite 2 parts, aminopropyltriethoxywerene werene 4 parts, oxidation diisopropylbenzene(DIPB) 2 parts, β-dimethyl-aminoethylmethacrylate 13 parts, 23 parts, polyvinyl chloride polyester 5 type, oxidized polyethlene wax 7 parts, Wheat germ oils 0.2 part, 0.2 part, sweet oil, 8 ° of beer 0.2 part.
Strengthen the preparation method that plate moulded by wood, comprise the following steps,
Above-mentioned each raw material is dropped into drying machine drying, bake out temperature is 150 DEG C, taking-up puts into-50 DEG C of freezers freezing 48 hours, take out, then drop into drying machine drying, bake out temperature is 75 DEG C, water ratio is made to be not more than 1.2%, then each raw material powder is broken into fine powder, after entering stirrer stirring, sends into extruder for shaping.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (2)
1. plate moulded by a strengthening wood, it is characterized in that, the raw material of following weight part is adopted to make: wood powder 50-58 part, rice husk 18-24 part, sodium stearate 7-11 part, butyl p-hydroxybenzoate 17-26 part, light calcium carbonate 9-19 part, butyral resin 17-21 part, polypropylene 17-25 part, linear low density polyethylene 17-25 part, nut-shell 0.3-0.8 part, chestnut shell 0.3-0.8 part, Semen Vitis viniferae 0.3-0.8 part, calcium hydroxide 1-3 part, kaolin 6-12 part, nano aluminum alumina 6-12 part, magnetite 1-2 part, aminopropyltriethoxywerene werene 2-4 part, oxidation diisopropylbenzene(DIPB) 1-2 part, β-dimethyl-aminoethylmethacrylate 6-13 part, polyvinyl chloride polyester 5 type 13-23 part, oxidized polyethlene wax 3-7 part, Wheat germ oils 0.1-0.2 part, sweet oil 0.1-0.2 part, 8 ° of beer 0.1-0.2 parts.
2. a kind ofly strengthen the preparation method that plate moulded by wood as claimed in claim 1, it is characterized in that: comprise the following steps,
Above-mentioned each raw material is dropped into drying machine drying, bake out temperature is 120-150 DEG C, taking-up puts into-50 DEG C of freezers freezing 48 hours, take out, then drop into drying machine drying, bake out temperature is 65-75 DEG C, water ratio is made to be not more than 1.2%, then each raw material powder is broken into fine powder, after entering stirrer stirring, sends into extruder for shaping.