CN105541265A - Cement particle board and preparation method thereof - Google Patents
Cement particle board and preparation method thereof Download PDFInfo
- Publication number
- CN105541265A CN105541265A CN201610037843.8A CN201610037843A CN105541265A CN 105541265 A CN105541265 A CN 105541265A CN 201610037843 A CN201610037843 A CN 201610037843A CN 105541265 A CN105541265 A CN 105541265A
- Authority
- CN
- China
- Prior art keywords
- cement
- wood chipboard
- bonded wood
- calcium
- bonded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of building materials, and in particular relates to a cement particle board and a preparation method thereof. The cement particle board is characterized by comprising the following components in parts by weight: 10-40 parts of wood shavings, 15-50 parts of high-calcium coal ash, 30-55 parts of sulfate aluminum cement, 2-5 parts of sodium silicate and 0.2-2.2 parts of calcium chloride. The cement particle board provided by the invention is light in weight, high in strength and low in manufacturing cost; as sulfate aluminum cement is adopted to replace ordinary Portland cement of the prior art, the cement particle board provided by the invention is short in production period, and the production efficiency is greatly improved.
Description
Technical field
The invention belongs to building material technical field, relate to a kind of cement-bonded wood chipboard and preparation method thereof specifically.
Background technology
Cement-bonded wood chipboard is used as the acoustic barrier material etc. of inside and outside wall board, partition plate, floor, railway or highway both sides abroad in a large number, and application at home at present is also progressively expanding.This sheet material is generally prepared from by cement, wooden shavings, flyash and various additive, and timber intensity is high, and fire protection flame retarding is good, water tolerance and sound-insulating performance all better.But in order to physical and mechanical properties such as the intensity that ensures cement-bonded wood chipboard, usually require that the calcium content of flyash is lower, general calcium oxide content is lower than 8%.
As Chinese patent CN200310106131.X discloses a kind of wooden refinforced cement moulding plate and production technique thereof, described sheet material is prepared from following ratio by following starting material: wood wool: 10-35%, cement: 30-50%, flyash: 15-50%, water glass: 0.1-5%, water: 1-10%.Its production technique comprises the following steps: 1) be mixed in proportion by each raw material and stir into mixture through mating formation into slab and compression molding; 2) slab is sent into curing kilns temperature 60-95 DEG C, humidity at 60-100%, maintenance 4-16 hour, then enters steam-cured still naturally cooling after 1-3 the steam-cured 6-12 of normal atmosphere hour; 3) cooled sheet material carries out drying at the temperature of 88-100 DEG C; 4) cuts sheet material; 5) plate surface is sprayed.Cost of the present invention is low, and timber intensity is high, and product can have multiple outer shape, pattern, improves labour productivity, reduces the labour intensity of personnel.
Disclosed in above-mentioned patent, wooden refinforced cement moulding plate does not relate to high-calcium fly ass and activator thereof.The calcium oxide content of the flyash wherein used is lower, according to during containing the high-calcium fly ass of more than 15% calcium oxide in this patent formulation, slab early strength may be caused lower, slab frangibility when unloading plate.High-calcium fly ass, because it contains more than 15% calcium oxide, the comparatively slow and volumetric expansion after aquation of its hydration rate, shrinking percentage is high at normal temperatures easily to cause sheet material, reduces the intensity of sheet material, has thus had a strong impact on the utilization of high-calcium fly ass in cement-bonded wood chipboard.
The information being disclosed in this background technology part is only intended to increase the understanding to general background of the present invention, and should not be regarded as admitting or imply in any form that this information structure has been prior art that persons skilled in the art are known.
Summary of the invention
High for light weight cement plate cost in prior art, the defects such as the production cycle is long, and operation is loaded down with trivial details, the object of the invention is to provide a kind of light weight, the environment protecting cement plate that with short production cycle, cost is low.
Technical scheme provided by the invention is:
A kind of cement-bonded wood chipboard, comprises following component: wood wool 10-40 part, high-calcium fly ass 15-50 part, aluminosulfate cement 30-55 part, water glass 2-5 part and calcium chloride 0.2-2.2 part by weight.
As preferably, described cement-bonded wood chipboard, also comprises following component by weight: auxiliary agent 0.1-2 part.
As preferably, described auxiliary agent is at least one in sodium-chlor, plaster stone, calcium hydroxide, sodium sulfate, Sulfite lignin and trolamine.
As preferably, described wood wool is prepared from by fast growing wood, brush wood or shrub, and the size of described wood wool is: long 10-80 millimeter, wide 2-8 millimeter, thick 0.2-0.5 millimeter.
Preferably, the length of described wood wool is 10-30 millimeter.
As preferably, in described high-calcium fly ass, the content of calcium oxide is 15-40%; The mass percentage concentration of described water glass is 35%; The mass percentage concentration of described calcium chloride is 30%.
As preferably, described aluminosulfate cement is fast hard special cement, and after 3d, intensity can reach 42.5MPa.
The present invention also provides a kind of preparation method of cement-bonded wood chipboard, comprises the following steps:
(1) wood wool, high-calcium fly ass, aluminosulfate cement, water glass, calcium chloride, water and auxiliary agent are mixed, stir, then mat formation into slab, slab buttress fork truck is placed in chilling press, pressurizes.
(2), after the dwell time terminates, slab is carried out maintenance;
(3) sheet material being sent into steam-cured still carries out steam-cured, then cools;
(4) drying is carried out to sheet material, obtain described cement-bonded wood chipboard.
Wherein, step adds water when mixing raw material in (1), and the ratio controlling the gross weight of water and the weight sum of high-calcium fly ass and cement in mixture is 1:2.
Wherein, in step (1), when colding pressing to described slab, described pressure is 4-6MPa, and the dwell time is 4-8 hour.
Wherein, in step (2), control curing temperature is 30-40 DEG C, relative humidity 70-90%, curing time 8-12 hour;
Wherein, a steam-cured pressure 1.8-4 normal atmosphere of sheet material in step (3), steam-cured time 8-16 hour;
Wherein, the temperature controlling described drying in step (4) is 60-75 DEG C, makes the water ratio of sheet material reach 6-12%.
Compared with prior art, the present invention has following beneficial effect:
1. cement-bonded wood chipboard light weight of the present invention is high-strength, and low cost of manufacture is with short production cycle; Cement-bonded wood chipboard of the present invention adopts aluminosulfate cement to substitute prior art ordinary portland cement, substantially increases production efficiency.
2. cement-bonded wood chipboard of the present invention utilizes usually discarded high-calcium fly ass as tackiness agent, not only ensure that the use properties of cement-bonded wood chipboard meets " cement sawdust plate (JC/T411-1991) " standard-required, and greatly reduce the cost of cement-bonded wood chipboard.
3. the raw material high-calcium fly ass of cement-bonded wood chipboard of the present invention belongs to trade waste, power station needs the fund of at substantial to process high-calcium fly ass, the present invention utilizes the waste in power station manufacture cement-bonded wood chipboard both to save production cost and additionally reduces environmental pollution, also creates higher economic worth simultaneously; Another important source material of the present invention is shrub or brush wood wood shavings, because these wood wools are tiny, usually be all difficult to for the manufacture of cement-bonded wood chipboard, adopt the cement-bonded wood chipboard of method manufacture of the present invention not only can use these wood shavings, and " cement sawdust plate (JC/T411-1991) " standard can also be reached, meet the use properties of cement-bonded wood chipboard, therefore the present invention has also expanded manufacture shaving board wood raw material scope.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is described in detail, but is to be understood that protection scope of the present invention not by the restriction of embodiment.
Clearly represent unless otherwise other, otherwise in whole specification sheets and claims, term " comprise " or its conversion as " comprising " or " including " etc. by be understood to include the element of stating or integral part, and do not get rid of other element or other integral part.
embodiment 1:
A kind of cement-bonded wood chipboard, comprises following component: wood wool 10 parts, high-calcium fly ass 15 parts, aluminosulfate cement 30 parts, water glass 2 parts and 0.2 part, calcium chloride by weight; Described cement-bonded wood chipboard, also comprises following component by weight: auxiliary agent 0.1 part; Described auxiliary agent is sodium-chlor; Described wood wool is prepared from by fast growing wood, and the size of described wood wool is: long 10 millimeters, wide 2 millimeters, thick 0.2 millimeter; In described high-calcium fly ass, the content of calcium oxide is 15%; The mass percentage concentration of described water glass is 35%, and solvent is water; The mass percentage concentration of described calcium chloride is 30%, and solvent is water; Described aluminosulfate cement is fast hard special cement, and after 3d, intensity can reach 42.5MPa.
The preparation method of described cement-bonded wood chipboard, comprises the following steps:
(1) wood wool, high-calcium fly ass, aluminosulfate cement, water glass, calcium chloride, water and auxiliary agent are mixed, stir, then mat formation into slab, slab buttress fork truck is placed in chilling press, pressurizes; Add water when mixing raw material, the ratio controlling the gross weight of water and the weight sum of high-calcium fly ass and cement in mixture is 1:2; When colding pressing to described slab, described pressure is 4MPa, and the dwell time is 4 hours;
(2), after the dwell time terminates, slab is carried out maintenance; Controlling curing temperature is 30 DEG C, relative humidity 70%, curing time 8 hours;
(3) sheet material being sent into steam-cured still carries out steam-cured, then cools; Steam-cured pressure 1.8 normal atmosphere of sheet material, 8 hours steam-cured time;
(4) drying is carried out to sheet material, obtain described cement-bonded wood chipboard; The temperature controlling described drying is 60 DEG C, makes the water ratio of sheet material reach 6%.
embodiment 2:
A kind of cement-bonded wood chipboard, comprises following component: wood wool 40 parts, high-calcium fly ass 50 parts, aluminosulfate cement 55 parts, water glass 5 parts and 2.2 parts, calcium chloride by weight; Described cement-bonded wood chipboard, also comprises following component by weight: auxiliary agent 2 parts; Described auxiliary agent is plaster stone; Described wood wool is prepared from by brush wood, and the size of described wood wool is: long 80 millimeters, wide 8 millimeters, thick 0.5 millimeter; In described high-calcium fly ass, the content of calcium oxide is 40%; The mass percentage concentration of described water glass is 35%, and solvent is water; The mass percentage concentration of described calcium chloride is 30%, and solvent is water; Described aluminosulfate cement is fast hard special cement, and after 3d, intensity can reach 42.5MPa.
The preparation method of described cement-bonded wood chipboard, comprises the following steps:
(1) wood wool, high-calcium fly ass, aluminosulfate cement, water glass, calcium chloride, water and auxiliary agent are mixed, stir, then mat formation into slab, slab buttress fork truck is placed in chilling press, pressurizes; Add water when mixing raw material, the ratio controlling the gross weight of water and the weight sum of high-calcium fly ass and cement in mixture is 1:2; When colding pressing to described slab, described pressure is 6MPa, and the dwell time is 8 hours;
(2), after the dwell time terminates, slab is carried out maintenance; Controlling curing temperature is 40 DEG C, relative humidity 90%, curing time 12 hours;
(3) sheet material being sent into steam-cured still carries out steam-cured, then cools; Steam-cured pressure 4 normal atmosphere of sheet material, 16 hours steam-cured time;
(4) drying is carried out to sheet material, obtain described cement-bonded wood chipboard; The temperature controlling described drying is 75 DEG C, makes the water ratio of sheet material reach 12%.
embodiment 3:
A kind of cement-bonded wood chipboard, comprises following component: wood wool 30 parts, high-calcium fly ass 30 parts, aluminosulfate cement 40 parts, water glass 3 parts and 1.5 parts, calcium chloride by weight; Described cement-bonded wood chipboard, also comprises following component by weight: auxiliary agent 1 part; Described auxiliary agent is calcium hydroxide; Described wood wool is prepared from by shrub, and the size of described wood wool is: long 40 millimeters, wide 4 millimeters, thick 0.4 millimeter; In described high-calcium fly ass, the content of calcium oxide is 30%; The mass percentage concentration of described water glass is 35%, and solvent is water; The mass percentage concentration of described calcium chloride is 30%, and solvent is water; Described aluminosulfate cement is fast hard special cement, and after 3d, intensity can reach 42.5MPa.
The preparation method of described cement-bonded wood chipboard, comprises the following steps:
(1) wood wool, high-calcium fly ass, aluminosulfate cement, water glass, calcium chloride, water and auxiliary agent are mixed, stir, then mat formation into slab, slab buttress fork truck is placed in chilling press, pressurizes; Add water when mixing raw material, the ratio controlling the gross weight of water and the weight sum of high-calcium fly ass and cement in mixture is 1:2; When colding pressing to described slab, described pressure is 5MPa, and the dwell time is 6 hours;
(2), after the dwell time terminates, slab is carried out maintenance; Controlling curing temperature is 35 DEG C, relative humidity 80%, curing time 10 hours;
(3) sheet material being sent into steam-cured still carries out steam-cured, then cools; Steam-cured pressure 3 normal atmosphere of sheet material, 12 hours steam-cured time;
(4) drying is carried out to sheet material, obtain described cement-bonded wood chipboard; The temperature controlling described drying is 70 DEG C, makes the water ratio of sheet material reach 8%.
comparative example 1:
A kind of wooden refinforced cement moulding plate and production technique thereof, described sheet material is prepared from mass ratio by following starting material: wood wool 10-35%, ordinary Portland cement 30-50%, flyash 15-50%, water glass 0.1-5% and water 1-10%.
Its production technique comprises the following steps:
(1) each raw material is mixed in proportion stirs into mixture through mating formation into slab and compression molding;
(2) slab is sent into curing kilns temperature 60-95 DEG C, humidity at 60-100%, maintenance 4-16 hour, then enters steam-cured still naturally cooling after 1-3 the steam-cured 6-12 of normal atmosphere hour;
(3) cooled sheet material carries out drying at the temperature of 88-100 DEG C;
(4) cuts sheet material;
(5) plate surface is sprayed.
embodiment 4: the performance measurement of cement-bonded wood chipboard of the present invention
In the cement-bonded wood chipboard prepared by embodiment 1-3, comparative example 1, the wooden refinforced cement moulding plate of preparation adopts 300KN (WE30) universal hydraulic testing machine (testing tool is AEC-201 type strength of cement trier) to measure its folding strength, and test result is in table 1.
The performance measurement of table 1 cement-bonded wood chipboard of the present invention
As can be seen from Table 1, the folding strength of cement-bonded wood chipboard of the present invention is far above comparative example 1, and apparent flawless, nothing cracking, its density is also far below comparative example 1.
embodiment 5: the water tolerance of cement-bonded wood chipboard of the present invention measures
5.1 test materialss and method
The cement-bonded wood chipboard that test materials uses embodiment of the present invention 1-3 to prepare and the wooden refinforced cement moulding plate obtained by comparative example 1.
Get 4 blocks of sheet materials, with paraffin and rosin blend (mass ratio 1:1), sheet material edge and the back side are closed.Then immerse 1/2 of sheet material area in the tap water of room temperature, observe, till surface appearance foaming, efflorescence, peeling off.
5.2 test results and analysis
The water tolerance of table 2 cement-bonded wood chipboard of the present invention measures
As can be seen from Table 2, the water tolerance of cement-bonded wood chipboard of the present invention is far above comparative example 1.
The aforementioned description to concrete exemplary of the present invention is to illustrate and the object of illustration.These descriptions not want the present invention to be defined as disclosed precise forms, and obviously, according to above-mentioned instruction, can much change and change.The object selected exemplary embodiment and describe is to explain certain principles of the present invention and practical application thereof, thus those skilled in the art can be realized and utilize various different exemplary of the present invention and various different selection and change.Scope of the present invention is intended to limited by claims and equivalents thereof.
Claims (10)
1. a cement-bonded wood chipboard, is characterized in that, comprises following component by weight: wood wool 10-40 part, high-calcium fly ass 15-50 part, aluminosulfate cement 30-55 part, water glass 2-5 part and calcium chloride 0.2-2.2 part.
2. cement-bonded wood chipboard according to claim 1, is characterized in that, described cement-bonded wood chipboard, also comprises following component by weight: auxiliary agent 0.1-2 part.
3. cement-bonded wood chipboard according to claim 2, is characterized in that, described auxiliary agent is at least one in sodium-chlor, plaster stone, calcium hydroxide, sodium sulfate, Sulfite lignin and trolamine.
4. cement-bonded wood chipboard according to claim 1, is characterized in that, described wood wool is prepared from by fast growing wood, brush wood or shrub, and the size of described wood wool is: long 10-80 millimeter, wide 2-8 millimeter, thick 0.2-0.5 millimeter.
5. cement-bonded wood chipboard according to claim 4, is characterized in that, the length of described wood wool is 10-30 millimeter.
6. cement-bonded wood chipboard according to claim 1, is characterized in that, in described high-calcium fly ass, the content of calcium oxide is 15-40%; The mass percentage concentration of described water glass is 35%; The mass percentage concentration of described calcium chloride is 30%.
7. cement-bonded wood chipboard according to claim 1, is characterized in that, described aluminosulfate cement is fast hard special cement, and after 3d, intensity can reach 42.5MPa.
8., according to the preparation method of the arbitrary described cement-bonded wood chipboard of claim 1-7, it is characterized in that, comprise the following steps:
(1) wood wool, high-calcium fly ass, aluminosulfate cement, water glass, calcium chloride, water and auxiliary agent are mixed, stir, then mat formation into slab, slab buttress fork truck is placed in chilling press, pressurizes.
(2), after the dwell time terminates, slab is carried out maintenance;
(3) sheet material being sent into steam-cured still carries out steam-cured, then cools;
(4) drying is carried out to sheet material, obtain described cement-bonded wood chipboard.
9. the preparation method of cement-bonded wood chipboard according to claim 8, is characterized in that, step adds water when mixing raw material in (1), and the ratio controlling the gross weight of water and the weight sum of high-calcium fly ass and cement in mixture is 1:2; In step (1), when colding pressing to described slab, described pressure is 4-6MPa, and the dwell time is 4-8 hour; In step (2), control curing temperature is 30-40 DEG C, relative humidity 70-90%, curing time 8-12 hour; A steam-cured pressure 1.8-4 normal atmosphere of sheet material in step (3), steam-cured time 8-16 hour.
10. the preparation method of cement-bonded wood chipboard according to claim 8, is characterized in that, the temperature controlling described drying in step (4) is 60-75 DEG C, makes the water ratio of sheet material reach 6-12%.