CN105524570B - Adhesive tape assembly, bonded product - Google Patents
Adhesive tape assembly, bonded product Download PDFInfo
- Publication number
- CN105524570B CN105524570B CN201610031217.8A CN201610031217A CN105524570B CN 105524570 B CN105524570 B CN 105524570B CN 201610031217 A CN201610031217 A CN 201610031217A CN 105524570 B CN105524570 B CN 105524570B
- Authority
- CN
- China
- Prior art keywords
- adhesive tape
- stretchable
- face
- bonded
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of Adhesive tape assembly of present invention offer, bonded product, belong to stretchable removal tape technology field, can solve the problems, such as that existing stretchable removal adhesive tape is easily broken off when being removed with big draw angle.The Adhesive tape assembly of the present invention is for being bonded at least one substrate, and it includes:Stretchable removal adhesive tape, with adhesive surface;Intermediary layer covers the stretchable at least partly adhesive surface for removing adhesive tape, and has opposite the first face and the second face;Wherein, first face is used to bond with the substrate;Second face is bonded on adhesive surface, and has at least partly described second face directly to be contacted with the adhesive surface;Second face has the Ra values between 0.1 μm to 7 μm.
Description
Technical field
The invention belongs to stretchable removal tape technology fields, and in particular to a kind of Adhesive tape assembly, bonded product.
Background technology
For considerations such as portability, aesthetics, in many mobile terminals (such as mobile phone, tablet computer, laptop)
Battery be to be bonded on shell by double faced adhesive tape.When battery is removed due to positioning inaccurate, repair etc., because
It can not be taken off between battery and shell for double faced adhesive tape, therefore battery can only be operated to pull down it from double faced adhesive tape
Come.But lithium battery is used in mobile terminal, lithium battery soft pliable directly operates on it and easily causes cell damage, very more
Wherein hypertoxic electrolyte leakage may extremely be caused and cause danger.For this purpose, stretchable removal adhesive tape fixed cellular terminal can be used
In battery.
As shown in Figure 1, stretchable removal adhesive tape 1 can be shunk when being stretched, to which its adhesive surface is hung down by with 9 surface of substrate
Straight power is simultaneously detached with substrate 9.As long as the stretchable one end for removing adhesive tape 1 is made to stay in substrate 9 (such as battery and shell) as a result,
Except, so that it may stretchable removal adhesive tape 1 is extracted out between two substrates 9 by stretching the end, and two substrates 9 is made to detach.
As shown in Fig. 2, after stretchable removal adhesive tape 1 is shunk and is detached with substrate 9, opposed substrate 9 is also wanted to move one
Segment distance could be deviate between substrate 9.Due to the difference of 9 structure of substrate, therefore stretchable removal adhesive tape 1 can only be in many cases
Specific draw angle (i.e. draw direction and the stretchable angle removed between adhesive tape 1 and 9 contact surface of substrate) is stretched.This
In the case of, an edge part (right part of the lower surface of upside substrate 9 in Fig. 2) meeting between stretchable removal adhesive tape 1 of substrate 9
Contacted because of the effect of drawing force and there are certain pressure, so when stretchable removal adhesive tape 1 can in substrate 9 sliding and by
To resistance to sliding (including frictional force and cohesive force etc.), and the resistance to sliding increases with the increase of draw angle.Therefore work as
When draw angle excessive (such as at 45 ° to 90 °), it is easy to cause stretchable removal adhesive tape 1 and is pulled off and can not normally remove.
Invention content
It is an object of the present invention to provide a kind of Adhesive tape assemblies, and stretchable removal adhesive tape is avoided that using the Adhesive tape assembly
It is pulled off (even removal of big draw angle) during removing, improves its reliability.
The Adhesive tape assembly is for being bonded at least one substrate, and it includes:
Stretchable removal adhesive tape, with adhesive surface;
Intermediary layer, covers the stretchable at least partly adhesive surface for removing adhesive tape, and with the first opposite face and
Second face;Wherein,
First face is used to bond with the substrate;
Second face is bonded on the adhesive surface, and has at least partly described second face directly to be connect with the adhesive surface
It touches;
Second face has the Ra values between 0.1 μm to 7 μm.
A kind of specific implementation mode according to the present invention, second face have the Ra values between 0.15 μm to 6 μm.
A kind of specific implementation mode according to the present invention, the Adhesive tape assembly further include low-viscous layer, be located at it is described in
Between one end of interlayer and the stretchable removal adhesive tape;And between the low-viscous layer and the stretchable removal adhesive tape
Adhesion strength and the low-viscous layer in the adhesion strength of intermediary's interlayer, at least one be less than the intermediary layer with
Adhesion strength between the substrate.
It is a further object to provide a kind of bonded products, wherein having stretchable removal adhesive tape, this is stretchable
It removes adhesive tape and is not susceptible to fracture (even removal of big draw angle) when being stretched and removing, reliability is high.
The bonded product includes:
First substrate has the first face to be bonded;
Stretchable removal adhesive tape, with adhesive surface, the stretchable part for removing adhesive tape is bonded in described first
On face to be bonded, another part extends to outside the described first face to be bonded;
Intermediary layer is at least set between the edge part and the stretchable removal adhesive tape in the described first face to be bonded, and
With opposite the first face and the second face;First face is at least partly bonded on the edge part in the described first face to be bonded,
Second face have 0.1 μm to 7 μm between Ra values, and wherein with the edge part for being bonded in the first face to be bonded first
The second opposite face of face is in direct contact the adhesive surface.
A kind of specific implementation mode according to the present invention, the bonded product further include the second substrate, have with it is described
The second face to be bonded that first face to be bonded is oppositely arranged;And the stretchable both sides for removing adhesive tape all have the bonding
Face, the stretchable part for removing adhesive tape are bonded between the described first face to be bonded and the second face to be bonded.
A kind of specific implementation mode according to the present invention, the bonded product are mobile terminal;First substrate is electricity
Pond;Second substrate is the shell of the mobile terminal.
Description of the drawings
Fig. 1 is that the existing stretchable adhesive tape that removes is stretched the principle schematic of removal;
Fig. 2 is the existing stretchable principle schematic for removing adhesive tape and being stretched when removing with big draw angle;
Fig. 3 is a kind of stretchable cross-sectional view for removing adhesive tape of the embodiment of the present invention;
Fig. 4 is the overlooking structure diagram of the stretchable removal adhesive tape of Fig. 3;
Fig. 5 is the cross-sectional view that the stretchable removal adhesive tape of Fig. 3 is stretched when removing;
Fig. 6 is the stretchable cross-sectional view for removing adhesive tape of another kind of the embodiment of the present invention;
Fig. 7 is another stretchable cross-sectional view for removing adhesive tape of the embodiment of the present invention;
Fig. 8 is a kind of cross-section structure of bonded product of the stretchable removal adhesive tape using Fig. 7 of the embodiment of the present invention
Schematic diagram;
Fig. 9 is the cross-sectional view that the stretchable removal adhesive tape in the bonded product of Fig. 8 is stretched when removing;
Figure 10 is another cross-section structure signal that the stretchable removal adhesive tape in the bonded product of Fig. 8 is stretched when removing
Figure;
Wherein, reference numeral is:1, stretchable removal adhesive tape;11, adhesive surface;2, intermediary layer;21, the first face;22, second
Face;219, pressure sensitive adhesives;3, low-viscous layer;4, non-adhesive layer;9, substrate;91, the first substrate;92, the second substrate.
Specific implementation mode
To make those skilled in the art more fully understand technical scheme of the present invention, below in conjunction with the accompanying drawings and specific embodiment party
Present invention is further described in detail for formula.
Term is explained
In the present invention, following term or the meaning of describing mode are as follows:
" stretchable removal adhesive tape " refer to after it is bonded in substrate, can be by applying drawing along its length to it
Power and realize the adhesive tape detached with substrate.
" draw angle " refers to, to the practical direction of motion stretched of stretchable removal adhesive tape, with stretchable removal glue
Angle between band and substrate between contact surface.
" contact adhesive " refers to the substance that can be bonded in substrate, and it is at least under environment temperature (5 DEG C to 40 DEG C)
Meet the following conditions:(1) there is lasting viscosity;(2) it can be achieved with bonding under the pressure pressed with finger;(3) can change
Shape is to be attached in substrate;(4) its cohesive strength is enough the removal for keeping it substantially clean from substrate.
The nouns of locality are waited up and down for the statement of each attached drawing, are only the relative bearing for concrete condition in figure, and
The restriction to the specific direction of actual product of the present invention is not constituted.
" mobile terminal " refers to the equipment with calculation processing ability that can be carried by user and be used on the move, packet
Include but be not limited to mobile phone, tablet computer (such as iPad), laptop.
Adhesive tape assembly
As shown in Figures 3 to 10, the embodiment of the present invention provides a kind of Adhesive tape assembly, is used to be bonded at least one base
On bottom 9, and Adhesive tape assembly includes:
Stretchable removal adhesive tape 1, with adhesive surface 11;
Intermediary layer 2 covers the stretchable at least partly adhesive surface 11 for removing adhesive tape 1, and has the first opposite face 21
With the second face 22;Wherein,
First face 21 is used to bond with substrate 9;
Second face 22 is bonded on adhesive surface 11, and has at least partly the second face 22 directly to be contacted with adhesive surface 11;
Second face 22 has the Ra values between 0.1 μm to 7 μm.
That is, as shown in Figure 3, Figure 4, the Adhesive tape assembly of the embodiment of the present invention includes conventional stretchable removal adhesive tape
1, which is equipped with the adhesive surface 11 (having sticking face) for being bonded with substrate 9.
At least part of adhesive surface 11 is covered with intermediary layer 2, intermediary layer 2 towards the side of adhesive surface 11 be the second face 22, the second face
22 have specific roughness, i.e. its Ra value (profile arithmetic mean deviation, arithmetical mean deviation of the
Profile) between 0.1 μm to 7 μm, and at least the second face of part 22 is directly to be contacted with adhesive surface 11;And intermediary layer 2
The other side be the first face 21, first face 21 is for being bonded in substrate 9.
When Adhesive tape assembly is bonded in substrate 9, intermediary layer 2 can between stretchable removal adhesive tape 1 and substrate 9,
As " intermediary " of the two, and the second face 22 with specific roughness can connect with stretchable removal adhesive tape 1 (adhesive surface 11)
It touches.Thus as shown in figure 5, when being stretched to stretchable removal adhesive tape 1, stretchable removal adhesive tape 1 can be detached with intermediary layer 2
And slided on second face 22, i.e., the originally stretchable sliding for removing adhesive tape 1 in substrate 9 becomes on the second face 22
Sliding.The present invention has now surprisingly been found that, if the face (the second face 22) contacted with stretchable removal adhesive tape 1 is with specific coarse
Degree, then its resistance to sliding between stretchable removal adhesive tape 1 is with regard to relatively low.Therefore, the above intermediary layer 2 can reduce stretchable removal glue
Band 1 be stretched remove when (when especially draw angle is larger) suffered by resistance to sliding, to avoid stretchable 1 quilt of removal adhesive tape
It breaks, improves the reliability of Adhesive tape assembly.
Why have face and the stretchable resistance to sliding removed between adhesive tape 1 of specific roughness relatively low, it may be possible to due to
Following reason (restriction set forth below not to action principle of the present invention):When stretchable removal adhesive tape 1 is stretched, surface
Molecule occurs height-oriented and surface undulation and is largely eliminated, you can stretching 1 surface of removal adhesive tape can become coarse
The very low shiny surface of degree, the contact area if the face being in contact with it is also very smooth between the two is very big at this time, leads to still have one
The stretchable removal adhesive tape 1 of fixed viscosity can be well-bonded with the face, and resistance to sliding increases.If correspondingly, with stretchable removal glue
Face with 1 contact is excessively coarse, then the stretchable adhesive tape 1 that removes is easy to be scratched by the spike of coarse structure in sliding process, from
And causes resistance to sliding to increase and stretchable removal adhesive tape 1 is made to be easily broken off.And when roughness is located at particular range, can make with
Upper both sides influence reaches balance, resistance to sliding is preferably minimized, best avoids stretchable removal adhesive tape 1 from being pulled off.
A kind of specific implementation mode according to the present invention, the second face 22 have the Ra values between 0.15 μm to 6 μm.
That is, second face 22 more preferably has between 0.2 μm to 5 μm preferably with the Ra values between 0.15 μm to 6 μm
Ra values, further preferably with the Ra values between 0.5 μm to 4 μm.
Wherein, any of stretchable removal adhesive tape product, such as 3M wounds can be used in above stretchable removal adhesive tape 1
The stretchable removal adhesive tape of 6701-150 types of new company (U.S., the Minnesota State, Sao Paulo), is not described in detail herein.
Wherein, although in the drawings with it is stretchable remove adhesive tape 1 every side be entirely adhesive surface 11 as an example,
It should be appreciated that if only portion is adhesive surface 11 in the stretchable side for removing adhesive tape 1, and remaining position is without viscous
Property and feasible.For example, the stretchable one end for removing adhesive tape 1 can be without viscosity, using as drawing when being stretched
Hand.
Wherein, any of film layer can be used in above intermediary layer 2, another as long as one side can be bonded in substrate 9
Side has the above specific roughness.Preferably, which can be made of polymer material, such as polyimides, poly-
Ethylene glycol terephthalate, makrolon etc., are not described in detail herein.
And the thickness of intermediary layer 2 generally can be at a few micrometers between hundreds of microns, such as between 5 μm to 800 μm, preferably
Between 10 μm to 500 μm, more preferably between 20 μm to 200 μm, further preferably between 25 μm to 100 μm.
A kind of specific implementation mode according to the present invention, the first face 21 are equipped with pressure sensitive adhesives 219 or double faced adhesive tape.
That is, being the first face 21 of intermediary layer 2 since Adhesive tape assembly has part surface, therefore to realize Adhesive tape assembly
With the bonding of substrate 9, then first face 21 will be bonded in substrate 9;Therefore, it is preferably provided with pressure-sensitive adhesive on the first face 21
Agent 219 or double faced adhesive tape.The pressure sensitive adhesives 219 can be conventional Acrylate pressure sensitive binder, polyurethane pressure sensitive binder,
Polyvinyl chloride pressure sensitive adhesives etc., is not described in detail herein.
Certainly, if the first face 21 does not have binder, but to be carried out in substrate 9 cohesive position setting binder or
Double faced adhesive tape and feasible.
A kind of specific implementation mode according to the present invention, the stretchable both sides for removing adhesive tape 1 all have adhesive surface 11, wherein
Only there are one be bonded with intermediary layer 2 on adhesive surface 11.
That is, as shown in Fig. 3, Fig. 6, stretchable removal adhesive tape 1 can both sides have adhesive surface 11, this is because can draw
It stretches and removes adhesive tape 1 commonly used in the inconvenient occasion that directly adhesive tape is torn from substrate 9, and general adhesive tape is all in this occasion
It is bonded between two substrates 9, therefore the preferably stretchable both sides for removing adhesive tape 1 can be bonded.And due in reality
In the application of border, can generally determine in advance when to remove stretchable removals adhesive tape 1 should (can only in such as Figure 10 to which direction stretching
Stretch upward), and stretchable removal adhesive tape 1 is only in (the first substrate in such as Figure 10 of substrate 9 close to draw direction side
91) it is slided on, as long as therefore stretchable removal adhesive tape 1 is equipped with intermediary layer 2 in the side.
A kind of specific implementation mode according to the present invention, the stretchable at least one end for removing adhesive tape 1 do not have intermediary layer
2。
That is, as shown in Fig. 3, Fig. 7, the stretchable at least one end for removing adhesive tape 1 be arranged more than in
Interlayer 2.This is because when removing stretchable removal adhesive tape 1, stretchable removal adhesive tape 1 first to be made to be detached with intermediary layer 2, to protect
Demonstrate,proving stretchable removal adhesive tape 1 can slide on intermediary layer 2 to reduce resistance to sliding.And if the stretchable end for removing adhesive tape 1
Also there is intermediary layer 2, then the end of the two flushes as shown in Figure 6, therefore is at this moment difficult the two to be separated in end.
A kind of specific implementation mode according to the present invention, on the stretchable length direction for removing adhesive tape 1, the second face 22 with
The size for the part that adhesive surface 11 is in direct contact is at least 5 millimeters.
That is, stretchable remove in the intermediary layer 2 being arranged on adhesive tape 1, the second face directly contacted with adhesive surface 11
22 will be to the youthful and the elderly 5 millimeters (can also have and be equipped with other structures between the second face of part 22 and adhesive surface 11).This is because being drawn
It is practical to only have 9 edge part of substrate and the stretchable resistance to sliding removed between adhesive tape 1 larger when stretching, thus it is at least necessary in the position
Equipped with the intermediary layer 2 (the second face 22) directly contacted with adhesive surface 11.And the it is a discovery of the invention that larger part of the above resistance to sliding
General length is within 5 millimeters, therefore the second face 22 directly contacted with adhesive surface 11 should be 5 millimeters to the youthful and the elderly.Certainly, if directly
22 length of the second face contacted with adhesive surface 11 is longer, to preferably play the role of reducing resistance to sliding and feasible.
A kind of specific implementation mode according to the present invention, on being bonded with the adhesive surface 11 of intermediary layer 2, along stretchable removal
The length direction of adhesive tape 1, intermediary layer 2 only cover a part for the adhesive surface 11;Or, in the adhesive surface 11 for being bonded with intermediary layer 2
On, along the stretchable length direction for removing adhesive tape 1, the adhesive surface 11 is completely covered in intermediary layer 2.
That is, on the adhesive surface 11 with intermediary layer 2, intermediary layer 2 can be as shown in figure 3, only cover the adhesive surface
11 part.This is because as previously mentioned, length is smaller in fact the higher part of resistance to sliding, as long as therefore the part adhesive face
11 are equipped with intermediary layer 2, and such other positions are still that the stretchable adhesive surface 11 for removing adhesive tape 1 is directly viscous with substrate 9
Knot can ensure that the stretchable adhesive property for removing 1 script of adhesive tape is constant as possible.
Alternatively, also can be as shown in fig. 6, if certain adhesive surface 11 carries intermediary layer 2, the bonding be just completely covered in intermediary layer 2
Face 11.Obviously, if intermediary layer 2 is only located at the stretchable portion for removing adhesive tape 1, careful pair must be carried out when attaching
Position, with ensure intermediary layer 2 be located at substrate 9 edge part (otherwise intermediary layer 2 just do not have reduce resistance to sliding effect), grasp
It is difficult to make.And if intermediary layer 2 covers entire adhesive surface 11, operates just simpler.
A kind of specific implementation mode according to the present invention, in the stretchable width direction for removing adhesive tape 1, intermediary layer 2
Size is greater than or equal to the stretchable width for removing adhesive tape 1.
Obviously, from reduce resistance to sliding and it is easy to use from the point of view of, the second face 22 should cover the whole of adhesive surface 11
A width range, i.e., as shown in figure 4, intermediary layer 2 should be with stretchable removal adhesive tape 1 with wide or more wider than its.
Certainly, if the width of intermediary layer 2 is smaller than the stretchable width for removing adhesive tape 1, certain reduction can also be played
The effect of resistance to sliding.Typically, stretchable removal adhesive tape 1 is avoided to be pulled off to reliable, then 2 width of intermediary layer
It at least should be stretchable and remove the 30%, more preferably at least 50% of 1 width of adhesive tape, further preferably at least 80%.Obviously,
When 2 width of intermediary layer is less than stretchable removal 1 width of adhesive tape, it should preferably be set to stretchable removal 1 width direction of adhesive tape
Middle part.
A kind of specific implementation mode according to the present invention, Adhesive tape assembly further include low-viscous layer 3, are located at intermediary layer 2
Between one end and stretchable removal adhesive tape 1;And low-viscous layer 3 and the stretchable adhesion strength and low removed between adhesive tape 1
In adhesion strength between viscous layer 3 and intermediary layer 2, at least one is less than the adhesion strength between intermediary layer 2 and substrate 9.
That is, as shown in fig. 7, can be also equipped between an end of intermediary layer 2 and stretchable removal adhesive tape 1 low
Viscous layer 3 (obviously, in the position equipped with low-viscous layer 3, then the second face 22 is not in direct contact with adhesive surface 11), the low-viscous layer
3 have lower adhesion strength, to ensure its it is stretchable removal adhesive tape 1 between adhesion strength and/or its between intermediary layer 2
Adhesion strength it is lower than the adhesion strength between intermediary layer 2 and substrate 9.As a result, the effect of the low-viscous layer 3 be make intermediary layer 2 with
The stretchable separation stress removed between adhesive tape 1 is less than the cohesive force between intermediary layer 2 and substrate 9, thus during removal, energy
Ensure that necessarily stretchable removal adhesive tape 1 is detached with intermediary layer 2, without will produce intermediary layer 2 with stretchable removal adhesive tape 1 one
Play the case where being removed from substrate 9.
A kind of specific implementation mode according to the present invention, low-viscous layer 3 and the stretchable adhesion strength removed between adhesive tape 1 are big
Adhesion strength between low-viscous layer 3 and intermediary layer 2.
That is, mode more preferably, low-viscous layer 3 and the stretchable adhesion strength removed between adhesive tape 1 are larger,
And the adhesion strength between intermediary layer 2 is smaller.In this way when detaching stretchable removal adhesive tape 1 with intermediary layer 2, low-viscous layer 3
Will necessarily be bonded on stretchable removal adhesive tape 1 and be detached with intermediary layer 2, with it is stretchable remove adhesive tape 1 continue to stretch it is low
Viscous layer 3 will be pulled away (as shown in Figure 10), to not influence to influence cunning of the stretchable removal adhesive tape 1 on intermediary layer 2
It is dynamic.
Specifically, existing low adhesive film or low viscous coating can be used in the above low-viscous layer 3.Alternatively, due to intermediary layer 2
The face (the second face 22) contacted with low-viscous layer 3 is without viscosity, therefore one-faced tapes can also be used in low-viscous layer 3, viscous to have with it
The one side of property clings intermediary layer 2.Certainly, since the adhesion strength between preferred low-viscous layer 3 and stretchable removal adhesive tape 1 is more than
Its adhesion strength between intermediary layer 2, therefore when using one-faced tapes as low-viscous layer 3, the stripping between intermediary layer 2 is strong
Degree cannot be too big, usually can in 1 gram inch between 200 gram inch, more preferably in 1 gram inch between 100 gram inch,
Further preferably in 0.5 gram inch between 50 gram inch.
A kind of specific implementation mode according to the present invention, Adhesive tape assembly further include non-adhesive layer 4, are located at stretchable removal
At least side of at least one end of adhesive tape 1, non-adhesive layer 4 is far from the stretchable face for removing adhesive tape 1 without viscosity.
That is, as shown in fig. 7, can also be equipped with the inviscid layer in outside (its inside in 1 end of stretchable removal adhesive tape
Can toughness to be bonded on stretchable removal adhesive tape 1).As previously mentioned, stretchable removal adhesive tape 1 after bonding must there are one
End stays in except substrate 9, to carry out stretched operation.And before being stretched, to prevent the end from unexpected bonding occurs,
Therefore it can have disposed thereon non-adhesive layer 4 (effect is similar to release film).Position, length of the non-adhesive layer 4 etc. can be according to specific
Need to determine, if for example, as shown in Figure 8 it is stretchable remove adhesive tape 1 end can be folded over to come and be bonded in the first substrate 91,
As long as then it does not carry out cohesive side and is equipped with non-adhesive layer 4.Specifically, the non-adhesive layer 4 can be known inviscid
Film (such as release film), non-stick coating layer, one-faced tapes, are not described in detail herein.
Wherein, although the low-viscous layer 3 more than being depicted simultaneously in Fig. 7 to Figure 10 and non-adhesive layer 4, between the two
Have no positive connection.In one Adhesive tape assembly product, can have low-viscous layer 3 and non-adhesive layer 4 simultaneously, it also can be only therein
It is a kind of.
Wherein, on the outside of the stretchable removal adhesive tape 1 (intermediary layer 2, non-adhesive layer 4), can also be equipped with conventional release film or
Release paper prevents it from unexpected bond occurs for protecting adhesive surface 11 when not in use.
In the part attached drawing of the embodiment of the present invention, intermediary layer 2, low-viscous layer 3, non-adhesive layer 4 etc. are to be recessed to draw
Stretch remove adhesive tape 1 inside, but this merely to schematically indicate these structures should be located at it is stretchable removal adhesive tape 1 which
Side, and do not represent the recess being actually equipped in stretchable removal adhesive tape 1 for accommodating these structures.
Bonded product
The embodiment of the present invention also provides a kind of bonded product comprising:
First substrate 91 has the first face to be bonded;
Stretchable removal adhesive tape 1, with adhesive surface 11, the stretchable part for removing adhesive tape 1 is bonded in first and waits gluing
In junction, another part extends to outside the first face to be bonded;
Intermediary layer 2 is at least set between the edge part and stretchable removal adhesive tape 1 in the first face to be bonded, and has phase
To the first face 21 and the second face 22;First face 21 is at least partly bonded on the edge part in the first face to be bonded, the second face 22
With the Ra values between 0.1 μm to 7 μm, and wherein opposite with the first face 21 of edge part for being bonded in the first face to be bonded second
Face 22 is in direct contact adhesive surface 11.
That is, as shown in figure 8, it includes above-mentioned stretchable removal adhesive tape 1 and intermediary that the embodiment of the present invention, which provides a kind of,
The bonded product of layer 2.Wherein, stretchable removal adhesive tape 1 is equipped on the first face to be bonded of the first substrate 91, and at least the
Above-mentioned intermediary layer 2 is equipped between the edge part in one face to be bonded and stretchable removal adhesive tape 1, further, at least at the edge
The second face 22 at portion is in direct contact with adhesive surface 11, to ensure when stretchable removal adhesive tape 1 is stretched removal, intermediary layer 2
It can play the role of reducing resistance to sliding, stretchable removal adhesive tape 1 is avoided to be pulled off.
Specifically, the above bonded product can be obtained by the way that above-mentioned Adhesive tape assembly to be bonded in the first substrate 91.
But if first individually attaching intermediary layer 2 in the first substrate 91, stretchable removal adhesive tape 1 is attached to the intermediary again later
Layer 2 and first is in substrate 91, also can be obtained more than bonded product.
A kind of specific implementation mode according to the present invention, the first substrate 91 further include the side to connect with the first face to be bonded
Portion;Stretchable removal adhesive tape 1 is at least partly bonded on side;It also is provided with intermediary between side and stretchable removal adhesive tape 1
Layer 2.
That is, the side of the first substrate 91 can also be equipped with above stretchable removal adhesive tape 1 and intermediary layer 2.This is
Because as shown in figure 8, stretchable removal adhesive tape 1 will be also bonded on the side of the first substrate 91 in many cases, and working as and stretching
Angle very big (such as close to 90 °) when, 91 side of the first substrate and stretchable remove also will produce larger sliding resistance between adhesive tape 1
Power, therefore the position also preferably is provided with intermediary layer 2.
A kind of specific implementation mode according to the present invention, bonded product further include the second substrate 92, have and are waited for first
The second face to be bonded that adhesive surface is oppositely arranged;And the stretchable both sides for removing adhesive tape 1 all have adhesive surface 11, stretchable removal
A part for adhesive tape 1 is bonded between the first face to be bonded and the second face to be bonded.
That is, as shown in figure 8, the first substrate 91 and the second substrate 92 can be bonded together by the above Adhesive tape assembly,
Therefore the stretchable part for removing adhesive tape 1 should be located between two faces to be bonded, and as previously mentioned, to guarantee stretchable shifting
It is removed except adhesive tape 1 stretches, therefore stretchable removal adhesive tape 1 will also have at least one end to be located at except two faces to be bonded.
Certainly, in bonded product, may also comprise more than low-viscous layer 3, the structures such as non-adhesive layer 4, and these structures
Presence cannot influence stretchable removal adhesive tape 1 function of itself.If for example, with low-viscous layer 3 when, as long as in being located at
One end of interlayer 2, such as can only in the position of the upper surface (can also be with the presence of side) of corresponding first substrate 91, and
The position of 91 bottom surface of corresponding first substrate is then not present.For another example, if when with non-adhesive layer 4, should be located at except two substrates
In order to avoid influencing the bonding to substrate.
A kind of specific implementation mode according to the present invention, bonded product are mobile terminal;First substrate 91 is battery;Second
Substrate 92 is the shell of mobile terminal.
That is, the present invention is especially suitable for the electricity to mobile terminal (such as mobile phone, tablet computer, laptop)
Pond is fixed, and specially battery is bonded on the shell of mobile terminal.Certainly, example above, which is not constituted, protects the present invention
Protect the restriction of range.
It, can be as shown in figure 9, first by stretchable removal when removing the battery (such as lithium battery) of above mobile terminal
The end of adhesive tape 1 and low-viscous layer 3 are removed from substrate and intermediary layer 2.Later as shown in Figure 10, stretchable removal adhesive tape is stretched
1 end makes stretchable removal adhesive tape 1 be detached with two substrates and intermediary layer 2, and deviates from between two substrates, and in drawing process
In, it is that stretchable removal adhesive tape 1 slides on intermediary layer 2 in 9 edge part of substrate (91 lower surface right part of the first substrate in figure),
Therefore the resistance to sliding suffered by stretchable removal adhesive tape 1 is smaller, it is not easy to break.And after stretchable removal adhesive tape 1 is thoroughly removed,
Can by battery (the first substrate 91) take out and in turn, then by thereon remnants intermediary layer 2 tear, you can complete tearing open for battery
It unloads.
Test method
1) roughness test
The test method of the roughness of intermediary layer includes:It is laid in glass plate after intermediary layer to be cut into the piece of 10cm × 10cm
On, both sides are fixed with one-faced tapes, with instead of TR-200 type roughness testers of peak scientific & technical corporation (China, Beijing) when Beijing
Its roughness (Ra values) is tested, tests 4 millimeters of stroke every time, each intermediary layer surveys 5 data.
2) mechanical stretching
The stretchable removal adhesive tape in the above bonded product is stretched with mechanical equipment, tests its maximum tensile stress
Be that no fracture occurs, specifically include:
It is bonded intermediary layer in the 9495LE type double faced adhesive tapes side of 3M Creative Company (U.S., the Minnesota State, Sao Paulo),
And it is cut into the piece of 20mm × 120mm together, the double faced adhesive tape other side is fitted in the anodic oxygen of 20mm × 100mm × 2mm later
Change on aluminium block (side and the back side for being partially encased in anodic oxidation aluminium block grown).
By the stretchable removal adhesive tape (thickness of the 6701-150 types of 3M Creative Company (U.S., the Minnesota State, Sao Paulo)
150 μm, bilateral is adhesive surface) cut into the piece of 10mm × 80mm.
On the intermediary layer (being contacted with the second face of intermediary layer) that stretchable removal adhesive tape is attached on anodic oxidation aluminium block,
End exposes 10mm and is used as knob, and the PE films (polyethylene film) that are sticked on the stretchable removal adhesive tape in knob portion are used as non-adhesive layer.
Anodic oxidation aluminium block is fitted in the stretchable removal adhesive tape other side on stainless steel plate between two parties, to be equivalent to use
Anodic oxidation aluminium block is bonded together by the above Adhesive tape assembly with stainless steel plate.
Pressurize in 15 seconds is carried out with 6 kilograms of press, it is ensured that fully fitting.
Sample segment is 1 hour resident, sample segment aging 72 hours at 65 DEG C of temperature and 90% relative humidity.
Fixed stainless steel plate and anodic oxidation aluminium block, with Instron Corporation's (U.S., Massachusetts, promise Wood)
3365 type tensile testing machines of Instron are with the tensile speed of 90 ° of draw angle and 300mm/min to stretchable removal adhesive tape
It is stretched, record maximum tensile stress and whether is broken, each sample surveys 5 data.
3) it stretches by hand
The stretchable removal adhesive tape in the above bonded product is stretched by hand, tests whether it is broken,
It specifically includes:
Side is bonded intermediary on the 9495LE type double faced adhesive tapes of 3M Creative Company (U.S., the Minnesota State, Sao Paulo)
Layer, and is cut into the piece of 20mm × 20mm together, later by the double faced adhesive tape other side fit in Huawei Tech Co., Ltd (China,
Guangdong, Shenzhen) HuaWei HB417094EBC type batteries bottom edge portion and side, wherein lateral parts thickness be 6mm,
Therefore it is attached to the long 14mm of intermediary layer of battery bottom surface edge part.
By the stretchable removal adhesive tape (thickness of the 6701-150 types of 3M Creative Company (U.S., the Minnesota State, Sao Paulo)
150 μm, bilateral is adhesive surface) cut into the piece of 10mm × 80mm.
Stretchable removal adhesive tape is attached on the bottom surface and side of the above battery and is reserved the knob of 10mm, wherein in battery
The edge part and side of bottom surface, stretchable removal adhesive tape is set on intermediary layer and (is contacted with the second face of intermediary layer), in battery floor
The stretchable removal adhesive tape of other positions in face is then placed directly against on battery.
Pressurize in 15 seconds is carried out with 6 kilograms of press, it is ensured that fully fitting, sample are 1 hour resident.
Stretchable removal adhesive tape is stretched with the speed of about 90 ° of draw angle and about 2000mm/min with hand, is remembered
Whether record is broken, each sample surveys 5 data.
Specific embodiment
Embodiment 1
With the PI original film (polyimides of 25 μm of the thickness of Rui Huatai films Science and Technology Ltd. (China, Guangdong, Shenzhen)
Film), conduct after being polished with the 320 mesh sand paper of 3M Creative Company (U.S., the Minnesota State, Sao Paulo) one surface
Intermediary layer, with buffed surface for the second face.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Embodiment 2
With the PI original film (polyimides of 25 μm of the thickness of Rui Huatai films Science and Technology Ltd. (China, Guangdong, Shenzhen)
Film), conduct after being polished with the 500 mesh sand paper of 3M Creative Company (U.S., the Minnesota State, Sao Paulo) one surface
Intermediary layer, with buffed surface for the second face.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Comparative example 1
With the PI original film (polyimides of 25 μm of the thickness of Rui Huatai films Science and Technology Ltd. (China, Guangdong, Shenzhen)
Film), in the case where not polishing directly as intermediary layer.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Embodiment 3
With the TORAY L01 type PET film (polyethylene terephthalates in beautiful (TORAY) Co., Ltd. in east (Japan, Tokyo)
Ester film), make after being polished with the 320 mesh sand paper of 3M Creative Company (U.S., the Minnesota State, Sao Paulo) one surface
For intermediary layer, with buffed surface for the second face.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Embodiment 4
With the TORAY L01 type PET film (polyethylene terephthalates in beautiful (TORAY) Co., Ltd. in east (Japan, Tokyo)
Ester film), make after being polished with the 500 mesh sand paper of 3M Creative Company (U.S., the Minnesota State, Sao Paulo) one surface
For intermediary layer, with buffed surface for the second face.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Comparative example 2
With the TORAY L01 type PET film (polyethylene terephthalates in beautiful (TORAY) Co., Ltd. in east (Japan, Tokyo)
Ester film), in the case where not polishing directly as intermediary layer.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Embodiment 5
With the 7585 type label materials of 3M Creative Company (U.S., the Minnesota State, Sao Paulo), in the case where not polishing
Directly as intermediary layer.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Comparative example 3
With the 57817 type label materials of 3M Creative Company (U.S., the Minnesota State, Sao Paulo), the case where not polishing
Under directly as intermediary layer.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Embodiment 6
It is direct in the case where not polishing with the ATL battery membranes in Beijing Xiaomi Technology Co., Ltd. (China, Beijing)
As intermediary layer.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Comparative example 4
Without using intermediary layer, and with the HuaWei HB417094EBC of Huawei Tech Co., Ltd (China, Guangdong, Shenzhen)
The film layer on type battery surface itself is directly tested, for example following table of test result without polishing.
Wherein, the method for mechanical stretching is similar with above description, and difference lies in do not make double faced adhesive tape, intermediary layer and anodic oxygen
Change aluminium block, and directly stretchable removal adhesive tape is set between the above battery and stainless steel plate.The method stretched by hand also with
Upper description is similar, difference lies in without using intermediary layer, and stretchable removal adhesive tape is directly bonded in the surface of the above battery.When
So, other parameters and mode etc. are constant in test method at this time.
Embodiment 7
With the GHF860M2AB type PC films (polycarbonate membrane) in Sumitomo (Sumitomo) group (Japan, Tokyo), do not beating
Directly as intermediary layer in the case of mill.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Comparative example 5
It is direct in the case where not polishing with the 2SLKN type release films in Mitsubishi (Mitsubishi) group (Japan, Tokyo)
As intermediary layer.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Embodiment 8
With the 1002BO type automobile black films of 3M Creative Company (U.S., the Minnesota State, Sao Paulo), the case where not polishing
Under directly as intermediary layer.
The above test, for example following table of test result are carried out after bonded product is made with the intermediary layer.
Table 1, each embodiment and comparative example the second face of intermediary layer roughness
Project | Ra values 1 (μm) | Ra values 2 (μm) | Ra values 3 (μm) | Ra values 4 (μm) | Ra values 5 (μm) | Average Ra value |
Embodiment 1 | 1.069 | 1.907 | 1.791 | 1.085 | 1.174 | 1.405 |
Embodiment 2 | 0.384 | 0.283 | 0.299 | 0.541 | 0.528 | 0.407 |
Comparative example 1 | 0.068 | 0.090 | 0.075 | 0.098 | 0.098 | 0.086 |
Embodiment 3 | 1.66 | 1.60 | 1.50 | 2.16 | 1.86 | 1.76 |
Embodiment 4 | 0.420 | 0.588 | 0.512 | 0.509 | 0.692 | 0.544 |
Comparative example 2 | 0.056 | 0.029 | 0.035 | 0.051 | 0.050 | 0.044 |
Embodiment 5 | 0.657 | 0.664 | 0.645 | 0.671 | 0.663 | 0.660 |
Comparative example 3 | 0.094 | 0.069 | 0.096 | 0.076 | 0.067 | 0.077 |
Embodiment 6 | 0.221 | 0.255 | 0.166 | 0.197 | 0.324 | 0.233 |
Comparative example 4 | 0.076 | 0.065 | 0.059 | 0.064 | 0.079 | 0.069 |
Embodiment 7 | 2.223 | 2.102 | 2.452 | 2.302 | 3.536 | 2.523 |
Comparative example 5 | 0.092 | 0.052 | 0.049 | 0.104 | 0.072 | 0.080 |
Embodiment 8 | 5.48 | 6.896 | 6.166 | 5.94 | 6.867 | 6.270 |
Table 2, each embodiment and comparative example the maximum tensile stress of resident 1 hour mechanical stretching (do not mark, indicate
It is unbroken)
Table 3, each embodiment and comparative example the maximum tensile stress of mechanical stretching of aging 72 hours (do not mark, indicate
It is unbroken)
Protective layer | Data 1 (N) | Data 2 (N) | Data 3 (N) | Data 4 (N) | Data 5 (N) | Average (N) |
Embodiment 1 | 5.88 | 5.86 | 6.72 | 7.48 | 6.56 | 6.50 |
Embodiment 2 | 7.31 | 11.057 | 5.05 | 4.90 | 8.90 | 7.44 |
Embodiment 3 | 7.82 | 8.30 | 7.81 | 8.21 | 7.12 | 7.85 |
Embodiment 4 | 7.53 | 6.62 | 4.67 | 7.62 | 7.51 | 6.79 |
Embodiment 5 | 4.47 | 8.11 | 8.05 | 4.36 | 5.64 | 6.13 |
Embodiment 6 | 10.77 | 7.24 | 9.38 | 12.36 | 10.24 | 10.00 |
Embodiment 7 | 8.04 | 8.96 | 6.83 | 7.16 | 8.91 | 7.98 |
Embodiment 8 | 6.17 | 6.24 | 6.68 (fractures) | 5.42 | 5.44 | 5.99 |
The test result of table 4, each embodiment and comparative example stretched by hand
Protective layer | Data 1 | Data 2 | Data 3 | Data 4 | Data 5 | It is average |
Embodiment 1 | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken |
Embodiment 2 | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken |
Comparative example 1 | Fracture | Fracture | Fracture | Fracture | Fracture | Fracture |
Embodiment 3 | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken |
Embodiment 4 | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken |
Comparative example 2 | Fracture | Fracture | Fracture | Fracture | Fracture | Fracture |
Embodiment 5 | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken |
Comparative example 3 | Fracture | Fracture | Fracture | Fracture | Fracture | Fracture |
Embodiment 6 | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken |
Comparative example 4 | Fracture | Fracture | Fracture | Fracture | Fracture | Fracture |
Embodiment 7 | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken | It is unbroken |
Comparative example 5 | Fracture | Fracture | Fracture | Fracture | Fracture | Fracture |
Embodiment 8 | It is unbroken | Fracture | It is unbroken | It is unbroken | It is unbroken | It is unbroken |
From the above various embodiments as it can be seen that when the Ra values in the second face of intermediary layer are in the range of 0.1 μm to 7 μm, Ra is removed
Being worth maximum embodiment 8 has individual sample fracture outer, and other all stretchable removal adhesive tapes all can be smoothly removed without sending out
Raw fracture.This shows that the roughness in range above can effectively avoid stretchable removal adhesive tape and is pulled off really.If moreover, Ra values
It is unfavorable to avoiding the stretchable fracture for removing adhesive tape, therefore the Ra values in the second face of the above intermediary layer are preferably smaller than 6 μ when excessive
M, more preferably less than 5 μm.
Correspondingly, from above each comparative example as it can be seen that respectively when the Ra values in the second face of intermediary layer are less than 0.1 μm, then machinery is drawn
Stretchable removal adhesive tape majority is all pulled off in stretching, and then all stretchable removal adhesive tape can be all pulled off in stretching by hand.And
In practical applications, it is not generally possible to the result ability that stretchable removal adhesive tape is removed, therefore is stretched by hand slowly using machinery
More there is referential.This shows to think that roughness is smaller in traditional concept, and the smaller idea of resistance to sliding is incorrect, if
Two surface roughness are too low, also result in stretchable removal adhesive tape and are pulled off.
It can be seen that whether it is what, by polishing that no matter intermediary layer is what material, intended use, but as long as its
The roughness in two faces be in more than particular range in, you can play and preferably avoid stretchable removal adhesive tape during removal
The effect being pulled off;As long as and its roughness exceed the range, it is whether excessive or too small, be easy to cause stretchable removal
Adhesive tape is pulled off.This shows mode only according to the invention, and the roughness in the second face of intermediary layer is controlled in the particular range
It is interior, it can be only achieved and avoid stretchable removal adhesive tape breaking, improve the effect of its reliability.
It is understood that the principle that embodiment of above is intended to be merely illustrative of the present and the exemplary implementation that uses
Mode, however the present invention is not limited thereto.For those skilled in the art, in the essence for not departing from the present invention
In the case of refreshing and essence, various changes and modifications can be made therein, these variations and modifications are also considered as protection scope of the present invention.
Claims (14)
1. a kind of Adhesive tape assembly is used to be bonded at least one substrate, wherein the Adhesive tape assembly includes:
Stretchable removal adhesive tape, with adhesive surface;
Intermediary layer covers the stretchable at least partly adhesive surface for removing adhesive tape, and has opposite the first face and second
Face;Wherein,
First face is used to bond with the substrate;
Second face is bonded on the adhesive surface, and has at least partly described second face directly to be contacted with the adhesive surface;
Second face has the Ra values between 0.1 μm to 7 μm;
Low-viscous layer is located between an end of the intermediary layer and the stretchable removal adhesive tape;And the low viscosity
In layer and the stretchable adhesion strength removed between adhesive tape and the adhesion strength of the low-viscous layer and intermediary's interlayer,
At least one is less than the adhesion strength between the intermediary layer and the substrate.
2. Adhesive tape assembly according to claim 1, wherein
Second face has the Ra values between 0.15 μm to 6 μm.
3. Adhesive tape assembly according to claim 1, wherein
First face is equipped with pressure sensitive adhesives or double faced adhesive tape.
4. Adhesive tape assembly according to claim 1, wherein
The stretchable both sides for removing adhesive tape all have the adhesive surface, are bonded on adhesive surface described in only one of which
State intermediary layer.
5. Adhesive tape assembly according to claim 1, wherein
The stretchable at least one end for removing adhesive tape does not have the intermediary layer.
6. Adhesive tape assembly according to claim 1, wherein
In the stretchable width direction for removing adhesive tape, the size of the intermediary layer is greater than or equal to the stretchable removal
The width of adhesive tape.
7. Adhesive tape assembly according to claim 1, wherein
On the stretchable length direction for removing adhesive tape, the ruler for the part that second face is in direct contact with the adhesive surface
It is very little to be at least 5 millimeters.
8. Adhesive tape assembly according to claim 1, wherein
On the adhesive surface for being bonded with the intermediary layer, along the stretchable length direction for removing adhesive tape, the intermediary layer only covers
A part for the adhesive surface;
Or
On the adhesive surface for being bonded with the intermediary layer, along the stretchable length direction for removing adhesive tape, the intermediary layer covers completely
Cover the adhesive surface.
9. Adhesive tape assembly according to claim 1, wherein
The low-viscous layer and the stretchable adhesion strength removed between adhesive tape are more than the low-viscous layer and the intermediary layer
Between adhesion strength.
10. Adhesive tape assembly according to claim 1, wherein further include:
Non-adhesive layer, is located at at least side of the stretchable at least one end for removing adhesive tape, and the non-adhesive layer is remote
From the stretchable face for removing adhesive tape without viscosity.
11. a kind of bonded product, wherein including:
First substrate has the first face to be bonded;
Stretchable removal adhesive tape, with adhesive surface, the stretchable part for removing adhesive tape is bonded in described first and waits gluing
In junction, another part extends to outside the described first face to be bonded;
Intermediary layer is at least set between the edge part and the stretchable removal adhesive tape in the described first face to be bonded, and has
Opposite the first face and the second face;First face is at least partly bonded on the edge part in the described first face to be bonded, described
Second face has the Ra values between 0.1 μm to 7 μm, and the first face phase wherein with the edge part for being bonded in the first face to be bonded
To the second face be in direct contact the adhesive surface;
Low-viscous layer is located between an end of the intermediary layer and the stretchable removal adhesive tape;And the low viscosity
In layer and the stretchable adhesion strength removed between adhesive tape and the adhesion strength of the low-viscous layer and intermediary's interlayer,
At least one is less than the adhesion strength between the intermediary layer and the substrate.
12. bonded product according to claim 11, wherein
First substrate further includes the side to connect with the described first face to be bonded;
The stretchable removal adhesive tape is at least partly bonded on the side;
It also is provided with the intermediary layer between the side and the stretchable removal adhesive tape.
13. bonded product according to claim 11, wherein further include the second substrate, have and wait gluing with described first
The second face to be bonded that junction is oppositely arranged;And
The stretchable both sides for removing adhesive tape all have the adhesive surface, and the stretchable part for removing adhesive tape is bonded in
Between first face to be bonded and the second face to be bonded.
14. bonded product according to claim 13, wherein
The bonded product is mobile terminal;
First substrate is battery;
Second substrate is the shell of the mobile terminal.