CN105522102A - 一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料及其制备方法 - Google Patents

一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料及其制备方法 Download PDF

Info

Publication number
CN105522102A
CN105522102A CN201610021229.2A CN201610021229A CN105522102A CN 105522102 A CN105522102 A CN 105522102A CN 201610021229 A CN201610021229 A CN 201610021229A CN 105522102 A CN105522102 A CN 105522102A
Authority
CN
China
Prior art keywords
nano
lost foam
preparation
foam casting
paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610021229.2A
Other languages
English (en)
Inventor
刘和明
刘和兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MINGGUANG CITY LIUXIANG PUMP INDUSTRY Co Ltd
Original Assignee
MINGGUANG CITY LIUXIANG PUMP INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MINGGUANG CITY LIUXIANG PUMP INDUSTRY Co Ltd filed Critical MINGGUANG CITY LIUXIANG PUMP INDUSTRY Co Ltd
Priority to CN201610021229.2A priority Critical patent/CN105522102A/zh
Publication of CN105522102A publication Critical patent/CN105522102A/zh
Pending legal-status Critical Current

Abstract

本发明涉及消失模铸造技术领域，具体涉及一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料及其制备方法，该涂料以粒径存在差异的铝矾土、纳米氧化锆、白刚玉粉混合作为耐火骨料，具有良好的透气性和高温稳定性，在高温金属液的冲击下不易开裂，而以气相二氧化硅、羧甲基纤维素钠等材料制备的混合悬浮剂有良好的增稠、防沉、补强等效果，加入的纳米二氧化铈有储氧能力，在浇注过程中能释放氧气，提高塑料的氧化燃烧效率，降低残炭；该发明制备的涂料涂层干燥后光洁度高，防砂粘性好，对热稳定，不污染金属液，制备的铸件表面缺陷少，质量更佳。

Description

一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料及其制备方法
技术领域
本发明涉及消失模铸造技术领域，具体涉及一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料及其制备方法。
背景技术
消失模用涂料是指在消失模铸造过程中涂覆在模样外表面的一层特制涂料，它在铸造过程中起着关键性的作用，由于模样是由泡沫塑料制成的，涂料的透气性、涂层强度、流变性等性质都将会对铸造产品产生至关重要的影响，性能优良的消失模涂料应当满足：(1)能够辅助提高泡沫塑料模样的强度和刚性，防止模样破坏和变形；(2)有隔离作用，将金属液与模型分开，防止金属液渗入干砂中，防止铸件表面形成缺陷；(3)透气作用，及时排除模样分解产生的气体或液体，防止铸件出现气孔、碳黑缺陷等；(4)要有良好的烧结剥离性、抗砂粘性、抗金属液侵蚀性等；(5)要有良好的润湿性、涂挂性、环保性、热稳定性、防潮等特性。
消失模涂料组成主要包括耐火骨料、粘接剂、溶剂、悬浮剂以及各类添加剂等成分，按其使用的粘结剂性质来分主要分为水基涂料、醇基涂料、树脂涂料等几类，其中水基涂料因为成本较低在实际生产中应用较为广泛，然而水基涂料存在涂层清理时容易溃散，容易粘砂，且大部分产品的使用性能仍存在缺陷，达不到前面所述的效果。
发明内容
本发明的目的在于，制备一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料，以获得具有高强度、高透气性、低残炭的模样涂层，从而改善铸件质量，为了实现上述目的，本发明采用的技术方案如下：
一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料，其特征在于，该涂料由以下重量份的原料制成：气相二氧化硅1-2、180-250目铝矾土45-55、纳米氧化锆6-8、氟化钙0.5-0.8、200-325目白刚玉粉15-20、白乳胶1-2、水性丙烯酸树脂1-1.5、木质素磺酸钠0.01-0.02、平平加0.01-0.02、纳米二氧化铈0.01-0.02、羧甲基纤维素钠0.1-0.2、防腐剂0.001-0.002、消泡剂0.01-0.02、软水30-40。
所述的一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料的制备方法，其特征在于，所述的制备方法为：
(1)先将木质素磺酸钠、平平加、羧甲基纤维素钠投入软水中，搅拌至完全溶解后，投入气相二氧化硅、纳米二氧化铈，超声高速搅拌使其在溶液中均匀分散，制备的混合浆料备用；
(2)将铝矾土、纳米氧化锆、白刚玉粉与16-20重量份的步骤(1)制备的浆料一起投入搅拌桶中，高速搅拌分散30-40min后，再加入所有其它剩余物料，并根据所需浆料密度添加软水，再继续搅拌分散40-50min，即得。
本发明涂料以粒径存在差异的铝矾土、纳米氧化锆、白刚玉粉混合作为耐火骨料，具有良好的透气性和高温稳定性，在高温金属液的冲击下不易开裂，而以气相二氧化硅、羧甲基纤维素钠等材料制备的混合悬浮剂有良好的增稠、防沉、补强等效果，加入的纳米二氧化铈有储氧能力，在浇注过程中能释放氧气，提高塑料的氧化燃烧效率，降低残炭；该发明制备的涂料涂层干燥后光洁度高，防砂粘性好，对热稳定，不污染金属液，制备的铸件表面缺陷少，质量更佳。
具体实施方式
实施例
本实施例的涂料由以下重量份的原料制成：气相二氧化硅1.5、200目铝矾土50、纳米氧化锆6、氟化钙0.6、325目白刚玉粉18、白乳胶1.5、水性丙烯酸树脂1.2、木质素磺酸钠0.01、平平加0.01、纳米二氧化铈0.01、羧甲基纤维素钠0.1、防腐剂0.001、消泡剂0.01、软水35。
该涂料的制备方法为：
(1)先将木质素磺酸钠、平平加、羧甲基纤维素钠投入软水中，搅拌至完全溶解后，投入气相二氧化硅、纳米二氧化铈，超声高速搅拌使其在溶液中均匀分散，制备的混合浆料备用；
(2)将铝矾土、纳米氧化锆、白刚玉粉与18重量份的步骤(1)制备的浆料一起投入搅拌桶中，高速搅拌分散35min后，再加入所有其它剩余物料，并添加适量的软水，继续搅拌分散45min，调节涂料密度为60波美度，即得。
本实施例所制得的涂料性能测试结果为：

Claims (2)

1.一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料，其特征在于，该涂料由以下重量份的原料制成：气相二氧化硅1-2、180-250目铝矾土45-55、纳米氧化锆6-8、氟化钙0.5-0.8、200-325目白刚玉粉15-20、白乳胶1-2、水性丙烯酸树脂1-1.5、木质素磺酸钠0.01-0.02、平平加0.01-0.02、纳米二氧化铈0.01-0.02、羧甲基纤维素钠0.1-0.2、防腐剂0.001-0.002、消泡剂0.01-0.02、软水30-40。
2.如权利要求1所述的一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料的制备方法，其特征在于，所述的制备方法为：
（1）先将木质素磺酸钠、平平加、羧甲基纤维素钠投入软水中，搅拌至完全溶解后，投入气相二氧化硅、纳米二氧化铈，超声高速搅拌使其在溶液中均匀分散，制备的混合浆料备用；
（2）将铝矾土、纳米氧化锆、白刚玉粉与16-20重量份的步骤（1）制备的浆料一起投入搅拌桶中，高速搅拌分散30-40min后，再加入所有其它剩余物料，并根据所需浆料密度添加软水，再继续搅拌分散40-50min，即得。
CN201610021229.2A 2016-01-11 2016-01-11 一种含纳米氧化锆增强的低残炭防粘砂消失模铸造用水基涂料及其制备方法 Pending CN105522102A (zh)