CN105506959A - Production technology of sandwich mesh cloth - Google Patents
Production technology of sandwich mesh cloth Download PDFInfo
- Publication number
- CN105506959A CN105506959A CN201510839068.3A CN201510839068A CN105506959A CN 105506959 A CN105506959 A CN 105506959A CN 201510839068 A CN201510839068 A CN 201510839068A CN 105506959 A CN105506959 A CN 105506959A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- finishing agent
- stir
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production technology of sandwich mesh cloth. The technology includes the steps of: 1) putting 3-4 parts by mass of aluminum sulfate, 1.2 parts by mass of calcium chloride and 2.4 parts by mass of thiourea into 10.4 parts by mass of deionized water, performing mixing, and stirring the materials evenly; 2) then slowly adding 2.8 parts by mass of tetrahydroxyethyl phosphorus chloride, 1.9 parts by mass of nano-zinc oxide and 2.6 parts by mass of polyethylene glycol at the same time, further performing stirring till complete and uniform mixing, thus obtaining a finishing agent; and 3) subjecting cloth to padding treatment in a finishing agent containing impregnation solution, and conducting constant temperature drying. According to the production technology of sandwich mesh cloth provided by the invention, the finished cloth has excellent flame retardant properties and antifouling properties and wash, and strong washability.
Description
Technical field
The present invention relates to the production technology of sandwich eyelet fabric.
Background technology
The fire resistance of existing cloth, antifouling property and washing fastness all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of production technology of sandwich eyelet fabric, the cloth after its arrangement has excellent fire resistance, antifouling property, and washability is strong.
For achieving the above object, technical scheme of the present invention designs a kind of production technology of sandwich eyelet fabric, comprises the steps:
1) in 10.4 parts by mass deionized waters, drop into 3 ~ 4 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Preferably, the production technology of sandwich eyelet fabric, comprises the steps:
1) in 10.4 parts by mass deionized waters, drop into 3 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Preferably, the production technology of sandwich eyelet fabric, comprises the steps:
1) in 10.4 parts by mass deionized waters, drop into 4 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Preferably, the production technology of sandwich eyelet fabric, comprises the steps:
1) in 10.4 parts by mass deionized waters, drop into 3.4 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Advantage of the present invention and beneficial effect are: a kind of production technology of sandwich eyelet fabric, and the cloth after its arrangement has excellent fire resistance, antifouling property, and washability is strong.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
The production technology of sandwich eyelet fabric, comprises the steps:
1) in 10.4 parts by mass deionized waters, drop into 3 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Embodiment 2
The production technology of sandwich eyelet fabric, comprises the steps:
1) in 10.4 parts by mass deionized waters, drop into 4 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Embodiment 3
The production technology of sandwich eyelet fabric, comprises the steps:
1) in 10.4 parts by mass deionized waters, drop into 3.4 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. the production technology of sandwich eyelet fabric, is characterized in that, comprises the steps:
1) in 10.4 parts by mass deionized waters, drop into 3 ~ 4 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
2. the production technology of sandwich eyelet fabric according to claim 1, is characterized in that, comprise the steps:
1) in 10.4 parts by mass deionized waters, drop into 3 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
3. the production technology of sandwich eyelet fabric according to claim 1, is characterized in that, comprise the steps:
1) in 10.4 parts by mass deionized waters, drop into 4 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
4. the production technology of sandwich eyelet fabric according to claim 1, is characterized in that, comprise the steps:
1) in 10.4 parts by mass deionized waters, drop into 3.4 parts by mass aluminum sulfate, 1.2 parts by mass calcium chloride, 2.4 parts by mass thiocarbamide mixing, stir;
2) slowly add 2.8 parts by mass four ethoxy phosphorus chloride, 1.9 parts by mass nano zine oxides, 2.6 parts by mass polyethylene glycol more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.