CN105297423A - Fabric after-finishing process - Google Patents
Fabric after-finishing process Download PDFInfo
- Publication number
- CN105297423A CN105297423A CN201510886843.0A CN201510886843A CN105297423A CN 105297423 A CN105297423 A CN 105297423A CN 201510886843 A CN201510886843 A CN 201510886843A CN 105297423 A CN105297423 A CN 105297423A
- Authority
- CN
- China
- Prior art keywords
- mass
- parts
- fabric
- finishing agent
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fabric after-finishing process. The fabric after-finishing process comprises the following steps: 1) putting 1-2 parts by mass of melamine, 1.5 parts by mass of dichloromethane, 0.9 part by mass of honeysuckle flower and 1.4 parts by mass of maleic anhydride into 24 parts by mass of deionized water, mixing the materials and stirring the materials uniformly; 2) simultaneously adding 2.6 parts by mass of petroleum sulfonate, 1.5 parts by mass of hydroxyethyl cellulose, 0.8 part by mass of ammonium dodecyl trimethyl sulfate and 1.4 parts by mass of palmatine slowly and continuously stirring the materials until the materials are fully mixed uniformly, thus preparing a finishing agent; and 3) carrying out padding treatment on a fabric in an impregnation liquid containing the finishing agent and drying the fabric at a constant temperature. The fabric finished by the fabric after-finishing process has excellent antibacterial, flame retardant, anti-wrinkle and antistatic properties and strong washability.
Description
Technical field
The present invention relates to the postfinishing process of fabric.
Background technology
Antibacterial, fire-retardant, crease-resistant, antistatic performance and the washing fastness of existing fabric all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of postfinishing process of fabric, the fabric after its arrangement has excellent antibacterial, fire-retardant, crease-resistant, antistatic performance, and washability is strong.
For achieving the above object, technical scheme of the present invention designs a kind of postfinishing process of fabric, comprises the steps:
1) in 24 parts by mass deionized waters, drop into 1 ~ 2 parts by mass melamine, 1.5 parts by mass Methylene chloride, 0.9 parts by mass honeysuckle, 1.4 parts by mass maleic anhydride mixing, stir;
2) slowly add 2.6 parts by mass petroleum sulfonates, 1.5 parts by mass hydroxyethylcelluloses, 0.8 parts by mass trimethyl ammonium sulfate, 1.4 parts by mass fibrauretines more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Preferably, the postfinishing process of fabric, comprises the steps:
1) in 24 parts by mass deionized waters, drop into 1 parts by mass melamine, 1.5 parts by mass Methylene chloride, 0.9 parts by mass honeysuckle, 1.4 parts by mass maleic anhydride mixing, stir;
2) slowly add 2.6 parts by mass petroleum sulfonates, 1.5 parts by mass hydroxyethylcelluloses, 0.8 parts by mass trimethyl ammonium sulfate, 1.4 parts by mass fibrauretines more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Preferably, the postfinishing process of fabric, comprises the steps:
1) in 24 parts by mass deionized waters, drop into 2 parts by mass melamines, 1.5 parts by mass Methylene chloride, 0.9 parts by mass honeysuckle, 1.4 parts by mass maleic anhydride mixing, stir;
2) slowly add 2.6 parts by mass petroleum sulfonates, 1.5 parts by mass hydroxyethylcelluloses, 0.8 parts by mass trimethyl ammonium sulfate, 1.4 parts by mass fibrauretines more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Advantage of the present invention and beneficial effect are: the postfinishing process providing a kind of fabric, and the fabric after its arrangement has excellent antibacterial, fire-retardant, crease-resistant, antistatic performance, and washability is strong.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A postfinishing process for fabric, comprises the steps:
1) in 24 parts by mass deionized waters, drop into 1 ~ 2 parts by mass melamine, 1.5 parts by mass Methylene chloride, 0.9 parts by mass honeysuckle, 1.4 parts by mass maleic anhydride mixing, stir;
2) slowly add 2.6 parts by mass petroleum sulfonates, 1.5 parts by mass hydroxyethylcelluloses, 0.8 parts by mass trimethyl ammonium sulfate, 1.4 parts by mass fibrauretines more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Embodiment 2
The postfinishing process of fabric, comprises the steps:
1) in 24 parts by mass deionized waters, drop into 1 parts by mass melamine, 1.5 parts by mass Methylene chloride, 0.9 parts by mass honeysuckle, 1.4 parts by mass maleic anhydride mixing, stir;
2) slowly add 2.6 parts by mass petroleum sulfonates, 1.5 parts by mass hydroxyethylcelluloses, 0.8 parts by mass trimethyl ammonium sulfate, 1.4 parts by mass fibrauretines more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Embodiment 3
The postfinishing process of fabric, comprises the steps:
1) in 24 parts by mass deionized waters, drop into 2 parts by mass melamines, 1.5 parts by mass Methylene chloride, 0.9 parts by mass honeysuckle, 1.4 parts by mass maleic anhydride mixing, stir;
2) slowly add 2.6 parts by mass petroleum sulfonates, 1.5 parts by mass hydroxyethylcelluloses, 0.8 parts by mass trimethyl ammonium sulfate, 1.4 parts by mass fibrauretines more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. the postfinishing process of fabric, is characterized in that, comprises the steps:
1) in 24 parts by mass deionized waters, drop into 1 ~ 2 parts by mass melamine, 1.5 parts by mass Methylene chloride, 0.9 parts by mass honeysuckle, 1.4 parts by mass maleic anhydride mixing, stir;
2) slowly add 2.6 parts by mass petroleum sulfonates, 1.5 parts by mass hydroxyethylcelluloses, 0.8 parts by mass trimethyl ammonium sulfate, 1.4 parts by mass fibrauretines more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
2. the postfinishing process of fabric according to claim 1, is characterized in that, comprises the steps:
1) in 24 parts by mass deionized waters, drop into 1 parts by mass melamine, 1.5 parts by mass Methylene chloride, 0.9 parts by mass honeysuckle, 1.4 parts by mass maleic anhydride mixing, stir;
2) slowly add 2.6 parts by mass petroleum sulfonates, 1.5 parts by mass hydroxyethylcelluloses, 0.8 parts by mass trimethyl ammonium sulfate, 1.4 parts by mass fibrauretines more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
3. the postfinishing process of fabric according to claim 1, is characterized in that, comprises the steps:
1) in 24 parts by mass deionized waters, drop into 2 parts by mass melamines, 1.5 parts by mass Methylene chloride, 0.9 parts by mass honeysuckle, 1.4 parts by mass maleic anhydride mixing, stir;
2) slowly add 2.6 parts by mass petroleum sulfonates, 1.5 parts by mass hydroxyethylcelluloses, 0.8 parts by mass trimethyl ammonium sulfate, 1.4 parts by mass fibrauretines more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.