CN105505176A - Liquid state wallpaper and imposing process - Google Patents

Liquid state wallpaper and imposing process Download PDF

Info

Publication number
CN105505176A
CN105505176A CN201610066111.1A CN201610066111A CN105505176A CN 105505176 A CN105505176 A CN 105505176A CN 201610066111 A CN201610066111 A CN 201610066111A CN 105505176 A CN105505176 A CN 105505176A
Authority
CN
China
Prior art keywords
wallpaper
film
liquid wallpaper
tight
screen frame
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610066111.1A
Other languages
Chinese (zh)
Other versions
CN105505176B (en
Inventor
张雪
张达
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Harbin Green-Coatings Science & Technology Co Ltd
Original Assignee
Harbin Green-Coatings Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Harbin Green-Coatings Science & Technology Co Ltd filed Critical Harbin Green-Coatings Science & Technology Co Ltd
Priority to CN201610066111.1A priority Critical patent/CN105505176B/en
Publication of CN105505176A publication Critical patent/CN105505176A/en
Application granted granted Critical
Publication of CN105505176B publication Critical patent/CN105505176B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to liquid state wallpaper and an imposing process. The liquid state wallpaper comprises the following components in percentage by weight: 50 to 60 percent of deionized water, 4.0 to 8.0 percent of pigment slurry, 32 to 42 percent of a film forming component, 1.0 to 3.0 percent of a flame retardant, 0.1 to 0.5 percent of a defoaming agent, 0.5 to 2.0 percent of a leveling agent, 1.0 to 3.0 percent of a film forming auxiliary, 0.2 to 1.0 percent of a bactericide and 0.5 to 5.0 percent of a thickening agent, wherein the film forming component comprises polyurethane resin and acrylic resin. According to the liquid state wallpaper, the specific film forming component is adopted, so that the problems of complex components and poor environmental friendliness of the liquid state wallpaper can be effectively solved. According to the imposing process provided by the invention, through the use of a silk screen and photosensitive resist, the complexity of an imposing preparation process is reduced, and the imposing cost is reduced.

Description

A kind of liquid wallpaper and layout technique
Technical field
The invention belongs to the technical field of wallpaper in material of construction, refer to a kind of liquid wallpaper and layout technique especially.
Background technology
Wallpaper is simple because of its use procedure at furnishing fields, can reduce the time of fitting up, and finishing flexibly, ought to account for the market share that tool is larger, but the price of wallpaper remains high always, has influence on wallpaper occupying in furnishing fields share.
Can find by analysis, having influence on reason that wallpaper holds at high price is that the production cost of wallpaper is too high, has directly had influence on the selling price of wallpaper.Existing traditional wallpaper need of production is through following operation: body paper sends, coating, dry-softening-embossing-cooling-cutting edge-buildup between dry (gel)-cooling-printing-version, and check-batch-packaging-vanning-process of complexity such as to put in storage.The complicacy of wallpaper technique directly causes market value high, and traditional wallpaper is very high for splicing gap construction requirement, splices badly directly to cause figure deviations, and seam edge time length can tilt.
On the other hand, owing to considering Environmental Factors, wallpaper material and layout glue material require also very high, and this just needs producer's input high cost to go to make new wallpaper material or layout glue material, thus result also in holding at high price of traditional wallpaper.
The price of tradition wallpaper is not only higher, and traditional wallpaper also exist non-moistureproof, the problem such as be not durable, easily crack, easily turn yellow and fade.In order to overcome the above-mentioned defect of traditional wallpaper, prior art uses liquid wallpaper to replace traditional wallpaper, and liquid wallpaper is exactly with emulsion paint printing metope or the metope with brush emulsion paint after putty moulding.
Liquid wallpaper, compared with traditional wallpaper, uses simple, economy and durability, environmental protection, without seam, is easy to clear up letter and facilitates secondary decoration, and can according to the random layout of the demand of client.But still there is the complicated and feature of environmental protection difference of composition and its layout operation is many afterwards problem in the existing liquid wallpaper used.
Summary of the invention
Order of the present invention be to provide a kind of liquid wallpaper and, the complicated and problem of feature of environmental protection difference with the component overcoming existing liquid wallpaper.
Another object of the present invention is to provide a kind of layout technique, to overcome the problem of existing layout complex procedures.
The present invention is achieved by the following technical solutions:
A kind of liquid wallpaper, comprises by weight percentage:
Described film-forming components is urethane resin and acrylic resin; Described urethane resin accounts for 97.2% of described film-forming components by weight percentage; Described acrylic resin accounts for 2.8% of described film-forming components.
Described deionization electrical conductivity of water is less than 5.0 μ S/cm.
The number-average molecular weight of described film-forming components is 5500-8500.
Described defoamer is not containing organosilyl defoamer.
Described film coalescence aid is alcohols and ethers modified material ethylene glycol monomethyl ether.
Described thickening material is nonionic polyurethane thickening material; Described thickening material is about 20000mPa.s 20 DEG C time, and nonvolatile component is 60%.
A kind of layout technique, for liquid wallpaper according to any one of brushing the claims 1 to 6, comprises the following steps:
Prepare the screen frame that stretches tight, with stretching tight, network folder clamps silk screen, is fixed on base frame by described silk screen; To stretch tight net glue at described silk screen lower surface and the brushing of described base frame contact part; After the described net glue that stretches tight parches, remove described silk screen namely complete described in stretch tight screen frame preparation;
Stretch tight described in use sense optical cement is evenly coated on screen frame tow sides after, drying and processing;
The described screen frame that stretches tight is fitted with design sheet original text, in setting-up time, carries out exposure-processed; The screen frame that stretches tight described in after exposure is through rinsing and drying.
Further, the time shutter is 7.5 minutes.
Described layout technique also comprises scrapes sample, and the described screen frame that stretches tight is compressed article to be undertaken the printing of, and uses described liquid wallpaper to carry out blade coating, make described liquid wallpaper through after the described screen frame that stretches tight to described in article to be undertaken the printing of, stretch tight described in removing screen frame, scrapes sample described in completing.
The invention has the beneficial effects as follows:
The present invention by adopting specific film-forming components, the complicated and problem of feature of environmental protection difference of the component that effectively can overcome existing liquid wallpaper.
Layout technique of the present invention, by the use of silk screen and photoresists, reduces the complicacy of layout preparation technology, reduces layout cost.
Embodiment
Describe technical scheme of the present invention in detail by the following examples, following embodiment is only exemplary, only can be used for explaining and technical scheme of the present invention being described, and can not be interpreted as being the restriction to technical solution of the present invention.
The invention provides a kind of liquid wallpaper, its composition comprises by weight percentage:
In this application, described film-forming components is urethane resin and acrylic resin; Described urethane resin accounts for 97.2% of described film-forming components by weight percentage; Described acrylic resin accounts for 2.8% of described film-forming components.
Polyurethane resin component is adopted to be utilize the high strength of this resin, anti tear and antiwear characteristic in the application, the one-tenth film strength, anti tear and the wear resisting property that make wallpaper last are high, in film-forming components, add acrylic resin simultaneously, utilize the film forming properties of acrylic resin, make last wallpaper rete smooth, and have certain toughness, not only increase the outward appearance sensation of wallpaper, and improve the feel of wallpaper.
In this application, the number-average molecular weight of the film-forming components selected is 5500-8500, and the application selects the number-average molecular weight of this scope, and can ensure that the film forming of wallpaper is even, the mobility of the liquid wallpaper when brushing is applicable to; If the number-average molecular weight selected is less than 5500, then the film-formation result of liquid wallpaper is poor, and mobility is high, in use can cause into lepthymenia and uneven; If the number-average molecular weight selected is greater than 8500, then the film forming properties of liquid wallpaper is poor, and the fragility after film forming becomes large, and rete is uneven.
In this application, the pH value of film-forming components is between 8.3-9.0, and the second-order transition temperature of film-forming components is at 110-125 DEG C; The pH value of liquid wallpaper is between 8.3-9.0, and this pH value has influence on the pH value of liquid wallpaper; The too high or too low quality of forming film all affecting liquid wallpaper of pH value, if pH value is too low, has influence on the film formation time of liquid wallpaper; If pH value is too high, the time of drying of liquid wallpaper is long, is vulnerable to the pollution of environment for use and the problem of water resistance difference.
Described deionization electrical conductivity of water is less than 5.0 μ S/cm.
In this application, fire retardant is inorganic combustion inhibitor, selects magnesium hydroxide or aluminium hydroxide, the use of fire retardant, is conducive to the security improving liquid wallpaper, and by using inorganic combustion inhibitor, meets environmental requirement.
Described defoamer is not containing organosilyl defoamer, in this application, the model that the defoamer used is produced for German enlightening high (tego) is 830 defoamers, and the application does not specially require defoamer, can select the defoamer of other model as required.
Described film coalescence aid is alcohols and ethers modified material ethylene glycol monomethyl ether, reaches emulsion film forming speed moderate, and hardness increases.
Described thickening material is nonionic polyurethane thickening material; Described thickening material is about 20000mPa.s 20 DEG C time, and nonvolatile component is 60%.
In this application, flow agent and sterilant are now conventional flow agent and sterilant, do not illustrate in this application.
Embodiment 1
A kind of liquid wallpaper, its composition comprises by weight percentage:
In this application, described film-forming components is urethane resin and acrylic resin; Described urethane resin accounts for 97.2% of described film-forming components by weight percentage; Described acrylic resin accounts for 2.8% of described film-forming components.
Add deionized water in a kettle., start homogenizer slowly adds corresponding amount while stirring successively by formula order each component with 200 revs/min, after reinforced, homogenizer is regulated to stir 2 hours with 700 revs/min, pack after using 200 order filter-cloth filterings, without the need to Pressurized-heated in whole preparation process.
Embodiment 2
A kind of liquid wallpaper, its composition comprises by weight percentage:
In this application, described film-forming components is urethane resin and acrylic resin; Described urethane resin accounts for 97.2% of described film-forming components by weight percentage; Described acrylic resin accounts for 2.8% of described film-forming components.
Add deionized water in a kettle., start homogenizer slowly adds corresponding amount while stirring successively by formula order each component with 200 revs/min, after reinforced, homogenizer is regulated to stir 2 hours with 700 revs/min, pack after using 200 order filter-cloth filterings, without the need to Pressurized-heated in whole preparation process.
Embodiment 3
A kind of liquid wallpaper, its composition comprises by weight percentage:
In this application, described film-forming components is urethane resin and acrylic resin; Described urethane resin accounts for 97.2% of described film-forming components by weight percentage; Described acrylic resin accounts for 2.8% of described film-forming components.
Add deionized water in a kettle., start homogenizer slowly adds corresponding amount while stirring successively by formula order each component with 200 revs/min, after reinforced, homogenizer is regulated to stir 2 hours with 700 revs/min, pack after using 200 order filter-cloth filterings, without the need to Pressurized-heated in whole preparation process.
Embodiment 4
A kind of liquid wallpaper, its composition comprises by weight percentage:
In this application, described film-forming components is urethane resin and acrylic resin; Described urethane resin accounts for 97.2% of described film-forming components by weight percentage; Described acrylic resin accounts for 2.8% of described film-forming components.
Add deionized water in a kettle., start homogenizer slowly adds corresponding amount while stirring successively by formula order each component with 200 revs/min, after reinforced, homogenizer is regulated to stir 2 hours with 700 revs/min, pack after using 200 order filter-cloth filterings, without the need to Pressurized-heated in whole preparation process.
Embodiment 5
A kind of liquid wallpaper, its composition comprises by weight percentage:
In this application, described film-forming components is urethane resin and acrylic resin; Described urethane resin accounts for 97.2% of described film-forming components by weight percentage; Described acrylic resin accounts for 2.8% of described film-forming components.
Add deionized water in a kettle., start homogenizer slowly adds corresponding amount while stirring successively by formula order each component with 200 revs/min, after reinforced, homogenizer is regulated to stir 2 hours with 700 revs/min, pack after using 200 order filter-cloth filterings, without the need to Pressurized-heated in whole preparation process.
Embodiment 6
A kind of liquid wallpaper, its composition comprises by weight percentage:
In this application, described film-forming components is urethane resin and acrylic resin; Described urethane resin accounts for 97.2% of described film-forming components by weight percentage; Described acrylic resin accounts for 2.8% of described film-forming components.
Add deionized water in a kettle., start homogenizer slowly adds corresponding amount while stirring successively by formula order each component with 200 revs/min, after reinforced, homogenizer is regulated to stir 2 hours with 700 revs/min, pack after using 200 order filter-cloth filterings, without the need to Pressurized-heated in whole preparation process.
The present invention also provides a kind of layout technique, and for brushing above-mentioned liquid wallpaper, this layout technique comprises the following steps:
Prepare the screen frame that stretches tight, with stretching tight, network folder clamps silk screen, is fixed on base frame by described silk screen, and the shape of base frame can be determined as required, does not carry out certain illustrated in this application; To stretch tight net glue at described silk screen lower surface and the brushing of described base frame contact part, in this application, the net glue that stretches tight is the glue now commonly using bonding, and the kind of glue can change as required, not within the technical scope that this application claims protection; After the described net glue that stretches tight parches, remove described silk screen namely complete described in stretch tight screen frame preparation.
Stretch tight described in use sense optical cement is evenly coated on screen frame tow sides after, in this application, apply twice altogether, make coating evenly and after ensureing all to cover silk screen, drying and processing; Be drying and processing in unglazed situation herein, in drying course, the drying mode with ray can not be used to dry, expose phenomenon in advance to prevent photoresists.
Fitted with design sheet original text by the described screen frame that stretches tight, design original text is that client waits the pattern original text needed, and carries out exposure-processed in 7.5 minutes; In this application, crucial technology is the time shutter, if the time shutter is short, then layout is because exposing insufficient and causing the disappearance of pattern, if the time shutter is long, not only has influence on the careful of pattern, and cause photoresists to rinse well, screen frame stretch tight described in after exposure through high pressure water washing, unexposed photoresists are rinsed out completely, then after drying, complete layout preparation.
Described layout technique also comprises scrapes sample, and the described screen frame that stretches tight is compressed article to be undertaken the printing of, and uses described liquid wallpaper to carry out blade coating, make described liquid wallpaper through after the described screen frame that stretches tight to described in article to be undertaken the printing of, stretch tight described in removing screen frame, scrapes sample described in completing.
After completing layout, construction brushing can be carried out:
First, first piece of layout is placed on the correct position of metope, compress layout, brush, after guaranteeing that liquid wallpaper evenly infiltrates layout, remove layout, first piece of layout decorative pattern is printed on metope.
Then rinse layout, this first piece of layout rinsed well, dry up stand-by, the metope simultaneously brushed first needs certain hour to dry, and is using the flash-off time about 30 minutes of liquid wallpaper of the application.
If continuous pattern splicing is constructed after needing half an hour again, if disconnected pattern or multiple patterns splicing, then can sequential production.
Can also with locating device in the layout of the application, if secondary brushing is carried out in the layout of splicing continuously, only need locating device and brushing justified margin first, or planning reserves corresponding gap and can carry out splicing and brush.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (9)

1. a liquid wallpaper, is characterized in that: comprise by weight percentage:
Described film-forming components is urethane resin and acrylic resin; Described urethane resin accounts for 97.2% of described film-forming components by weight percentage; Described acrylic resin accounts for 2.8% of described film-forming components.
2. liquid wallpaper according to claim 1, is characterized in that: described deionization electrical conductivity of water is less than 5.0 μ S/cm.
3. liquid wallpaper according to claim 1, is characterized in that: the number-average molecular weight of described film-forming components is 5500-8500.
4. liquid wallpaper according to claim 1, is characterized in that: described defoamer is not for containing organosilyl defoamer.
5. liquid wallpaper according to claim 1, is characterized in that: described film coalescence aid is alcohols and ethers modified material ethylene glycol monomethyl ether.
6. liquid wallpaper according to claim 1, is characterized in that: described thickening material is nonionic polyurethane thickening material; Described thickening material is about 20000mPa.s 20 DEG C time, and nonvolatile component is 60%.
7. a layout technique, for liquid wallpaper according to any one of brushing the claims 1 to 6, is characterized in that: comprise the following steps:
Prepare the screen frame that stretches tight, with stretching tight, network folder clamps silk screen, is fixed on base frame by described silk screen; To stretch tight net glue at described silk screen lower surface and the brushing of described base frame contact part; After the described net glue that stretches tight parches, remove described silk screen namely complete described in stretch tight screen frame preparation;
Stretch tight described in use sense optical cement is evenly coated on screen frame tow sides after, drying and processing;
The described screen frame that stretches tight is fitted with design sheet original text, in setting-up time, carries out exposure-processed; The screen frame that stretches tight described in after exposure is through rinsing and drying.
8. layout technique according to claim 7, is characterized in that: the time shutter is 7.5 minutes.
9. layout technique according to claim 7, it is characterized in that: described layout technique also comprises scrapes sample, the described screen frame that stretches tight is compressed article to be undertaken the printing of, described liquid wallpaper is used to carry out blade coating, make described liquid wallpaper through after the described screen frame that stretches tight to described in article to be undertaken the printing of, stretch tight described in removing screen frame, scrapes sample described in completing.
CN201610066111.1A 2016-01-29 2016-01-29 A kind of liquid wallpaper and layout technique Active CN105505176B (en)