CN105504629A - Asbestos-free fiber compressing board and preparation method - Google Patents
Asbestos-free fiber compressing board and preparation method Download PDFInfo
- Publication number
- CN105504629A CN105504629A CN201511015516.4A CN201511015516A CN105504629A CN 105504629 A CN105504629 A CN 105504629A CN 201511015516 A CN201511015516 A CN 201511015516A CN 105504629 A CN105504629 A CN 105504629A
- Authority
- CN
- China
- Prior art keywords
- percent
- asbestos
- rubber
- magnesium silicate
- compressed panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an asbestos-free fiber compressing board and a preparation method. The asbestos-free fiber compressing board is characterized by comprising the following components in weight proportions: 65.0 percent of acrylic fiber or acrylic slurry, 3.0 percent of paper pulp, 7.0 percent of natural rubber, 5.6 percent of nitrile rubber or chloroprene rubber adhesive or butadiene-styrene rubber or ethylene propylene rubber, 0.3 percent of sulfur, 0.3 percent of rubber accelerator M, 0.3 percent of antiager D, 0.7 percent of zinc oxide, 2.0 percent of polyurethane varnish, 1.4 percent of bocour blue and 14.2 percent of barium sulfate. Compared with the prior art, the asbestos-free fiber compressing board provided by the invention has the advantages that a formula of the asbestos-free fiber compressing board is completely free of asbestos, does not contain sepiolite, and takes acrylic fibers as a main component; the prepared board is enough in strength, and meanwhile, is very low in leakage rate.
Description
Technical field
The present invention relates to a kind of without fibrous magnesium silicate compressed panel and preparation method.
Background technology
Asbestos rubber compressed panel is widely used for making gasket seal, but because asbestos have harm to human body, some developed countries forbid all, some external automobile brands also strictly prohibit the use the pad containing asbestos, so each producer has to set about developing the formula without asbestos compressed panel, domestic method the most conventional replaces asbestos with sepiolite, but sepiolite is general and asbestos are twin ore deposits, be difficult to thoroughly be separated, obtained sheet material is carried out with this formula, if have X-ray to detect, still can find the asbestos of 5 ~ 10%, finally reject by the client of more American-European developed countries, cause very large loss.。
Summary of the invention
Primary technical problem to be solved by this invention provides a kind of without fibrous magnesium silicate compressed panel for above-mentioned prior art.
The further technical problem to be solved of the present invention is to provide a kind of preparation method without fibrous magnesium silicate compressed panel.
The present invention solves the technical scheme that above-mentioned primary technical problem adopts: a kind of without fibrous magnesium silicate compressed panel, it is characterized in that: this comprises the component of following weight proportion without fibrous magnesium silicate compressed panel:
Acrylic fiber or acrylic fibers pulp: 65.0%
Paper pulp: 3.0%
Natural rubber: 7.0%
Paracril or neoprene latex or butadiene-styrene rubber or ethylene-propylene diene copolymer: 5.6%
Sulfur: 0.3%
Rubber accelerator M:0.3%
Antioxidant D: 0.3%
Zinc oxide: 0.7%
Polyurethane varnish: 2.0%
Titanium is blue or green blue: 1.4%
Barium sulfate: 14.2%.
Preferably, described natural rubber adopts 1# cigarette electricity glue.
Preferably, described paracril adopts 26# paracril.
The present invention solves the technical scheme that above-mentioned further technical problem adopts: a kind of preparation method without fibrous magnesium silicate compressed panel with above-mentioned formula, is characterized in that: comprise the steps:
Step 1, blue or green to acrylic fiber or acrylic fibers slurry, paper pulp, natural rubber, paracril or neoprene latex or butadiene-styrene rubber or ethylene-propylene diene copolymer, Sulfur, rubber accelerator M, antioxidant D, zinc oxide, Polyurethane varnish, titanium blue and these 11 kinds of materials of barium sulfate to be prepared according to weight proportion described in claim 1, pour in material pool, fully stir;
Step 2, compound step 1 obtained are poured special making in the Cheng Zhangji of compressed panel into and are made without fibrous magnesium silicate compressed panel.
Compared with prior art, the invention has the advantages that: provided by the invention without in fibrous magnesium silicate compressed panel formula 100% without asbestos, without sepiolite, based on acrylic fiber, obtained sheet material has enough intensity, while leakage rate very low.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
The component comprising following weight proportion without fibrous magnesium silicate compressed panel that the present embodiment provides:
Acrylic fiber or acrylic fibers pulp: 65.0%
Paper pulp: 3.0%
Natural rubber: 7.0%
Paracril: 5.6%
Sulfur: 0.3%
Rubber accelerator M:0.3%
Antioxidant D: 0.3%
Zinc oxide: 0.7%
Polyurethane varnish: 2.0%
Titanium is blue or green blue: 1.4%
Barium sulfate: 14.2%.
This formula 100% is without asbestos, and without sepiolite, based on acrylic fiber, obtained sheet material has enough intensity.For different use media, wherein paracril can use neoprene latex instead, the stupid glue of fourth, and ethylene-propylene diene copolymer etc. substitute, and as needed other color, can use other dyestuff instead.
In the present embodiment, natural rubber adopts 1# cigarette electricity glue, and paracril adopts 26# paracril.
The above-mentioned preparation method without fibrous magnesium silicate compressed panel comprises the steps:
Step 1, blue or green to acrylic fiber or acrylic fibers slurry, paper pulp, natural rubber, paracril, Sulfur, rubber accelerator M, antioxidant D, zinc oxide, Polyurethane varnish, titanium blue and these 11 kinds of materials of barium sulfate to be prepared according to weight proportion described in claim 1, pour in material pool, fully stir;
Step 2, compound step 1 obtained are poured special making in the Cheng Zhangji of compressed panel into and are made without fibrous magnesium silicate compressed panel.
Claims (4)
1. without a fibrous magnesium silicate compressed panel, it is characterized in that: this comprises the component of following weight proportion without fibrous magnesium silicate compressed panel:
Acrylic fiber or acrylic fibers pulp: 65.0%
Paper pulp: 3.0%
Natural rubber: 7.0%
Paracril: 5.6%
Sulfur: 0.3%
Rubber accelerator M:0.3%
Antioxidant D: 0.3%
Zinc oxide: 0.7%
Polyurethane varnish: 2.0%
Titanium is blue or green blue: 1.4%
Barium sulfate: 14.2%.
2. according to claim 1 without fibrous magnesium silicate compressed panel, it is characterized in that: described natural rubber adopts 1# cigarette electricity glue.
3. according to claim 1 without fibrous magnesium silicate compressed panel, it is characterized in that: described paracril adopts 26# paracril.
4., as claimed in claim 1 without a preparation method for fibrous magnesium silicate compressed panel, it is characterized in that: comprise the steps:
Step 1, blue or green to acrylic fiber or acrylic fibers slurry, paper pulp, natural rubber, paracril or neoprene latex or butadiene-styrene rubber or ethylene-propylene diene copolymer, Sulfur, rubber accelerator M, antioxidant D, zinc oxide, Polyurethane varnish, titanium blue and these 11 kinds of materials of barium sulfate to be prepared according to weight proportion described in claim 1, pour in material pool, fully stir;
Step 2, compound step 1 obtained are poured special making in the Cheng Zhangji of compressed panel into and are made without fibrous magnesium silicate compressed panel.