CN105504585A - Wood plastic material - Google Patents
Wood plastic material Download PDFInfo
- Publication number
- CN105504585A CN105504585A CN201511026590.6A CN201511026590A CN105504585A CN 105504585 A CN105504585 A CN 105504585A CN 201511026590 A CN201511026590 A CN 201511026590A CN 105504585 A CN105504585 A CN 105504585A
- Authority
- CN
- China
- Prior art keywords
- percent
- wood
- plastic material
- lubricant
- wood plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a wood plastic material. The material is prepared from the following raw materials in percentage by weight: 20-40 percent of waste polyvinyl chloride, 10-15 percent of plant fibers, 15-25 percent of calcium bicarbonate, 2-7 percent of adhesive, 3-6 percent of a lubricating agent, 2-30 percent of wood powder, 1-22 percent of straw powder, 2-10 percent of polyacrylate, 1-4 percent of zirconium oxide and 2-6 percent of ruthenium oxide. The wood plastic material can be formed by one-step processing, and has the advantages and positive effects of simple processing and low cost.
Description
Technical field
The invention relates to building materials, particularly relates to a kind of Wood-plastic material.
Background technology
Thermoplastic wood-plastic composite (WPC) adopts xylon or vegetable fibre to fill, strengthens, and through hot pressing compound, the modified thermoplastic material that different processing mode makes such as to melt extrude.In recent years increasingly exhausted with global resources, social environment consciousness is day by day surging, proposes requirements at the higher level to timber and petroleum chemicals application.In this context, this advantage that can play each component in material of wood plastic composite, the use limitation that overcome because strength of wood is low, the large and organic materials Young's modulus of variability is low etc. causes, can make full use of again discarded timber and plastics, reduce environmental pollution.At present, the product improving material added value is more and more subject to people's extensive concern.
Summary of the invention
The problem that the invention will solve is to provide a kind of Wood-plastic material, can a step process, and processing is simple.
For solving the problems of the technologies described above, the technical scheme that the invention adopts is: a kind of Wood-plastic material, is processed by the raw material production of following weight proportion: waste polyvinyl chloride 20 ~ 40%, vegetable fibre 10 ~ 15%, Calcium hydrogen carbonate 15 ~ 25%, cementing agent 2 ~ 7%, lubricant 3 ~ 6%, wood powder 2 ~ 30%, straw powder 1 ~ 22%, polypropylene ester 2 ~ 10%, zirconium white 1 ~ 4%, ruthenium oxide 2 ~ 6%.
Further, described lubricant is compounded lubricant P90/P130.
The advantage that the invention has and positively effect are: provide a kind of Wood-plastic material, can a step process, and processing is simple, and product cost is low.
Embodiment
Below the specific embodiment of the invention is elaborated.
A kind of Wood-plastic material, is processed by the raw material production of following weight proportion: waste polyvinyl chloride 20 ~ 40%, vegetable fibre 10 ~ 15%, Calcium hydrogen carbonate 15 ~ 25%, cementing agent 2 ~ 7%, lubricant 3 ~ 6%, wood powder 2 ~ 30%, straw powder 1 ~ 22%, polypropylene ester 2 ~ 10%, zirconium white 1 ~ 4%, ruthenium oxide 2 ~ 6%.
Further, described lubricant is compounded lubricant P90/P130.
Above the embodiment of the invention has been described in detail, but described content being only the preferred embodiment of the invention, can not being considered to for limiting practical range of the present invention.All equalizations done according to the invention scope change and improve, and all should still belong within this patent covering scope.
Claims (2)
1. a Wood-plastic material, is characterized in that: processed by the raw material production of following weight proportion: waste polyvinyl chloride 20 ~ 40%, vegetable fibre 10 ~ 15%, Calcium hydrogen carbonate 15 ~ 25%, cementing agent 2 ~ 7%, lubricant 3 ~ 6%, wood powder 2 ~ 30%, straw powder 1 ~ 22%, polypropylene ester 2 ~ 10%, zirconium white 1 ~ 4%, ruthenium oxide 2 ~ 6%.
2. a kind of Wood-plastic material according to claim 1, is characterized in that: described lubricant is compounded lubricant P90/P130.