CN105499186A - Cleaning method of aluminum alloy hub mold - Google Patents
Cleaning method of aluminum alloy hub mold Download PDFInfo
- Publication number
- CN105499186A CN105499186A CN201510955831.9A CN201510955831A CN105499186A CN 105499186 A CN105499186 A CN 105499186A CN 201510955831 A CN201510955831 A CN 201510955831A CN 105499186 A CN105499186 A CN 105499186A
- Authority
- CN
- China
- Prior art keywords
- mould
- aluminium alloy
- wheel hub
- alloy wheel
- clear water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cleaning method of an aluminum alloy hub mold. The cleaning method comprises such five steps as clear water flushing,special cleaning agent scrubbing, clear water flushing, laser cleaning and clear water flushing, can makeboth impurities and oil stains on the surface of the aluminum alloy hub mold totally removed, greatly improves the cleanness of the aluminum alloy hub mold, guarantees the quality of a prepared aluminum alloy hub, reduces the loss of the surface of the mold from cleaning work when the hub mold is cleaned to the greatest extent, and prolongs the service lifetime of the mold; in addition, a related safe cleaning agent can be recycled by multiple times; and the whole operation process is harmless to human bodies, safe and environment-friendly.
Description
Technical field
The present invention relates to the technical field of aluminum-alloy wheel production and processing, is a kind of clean method of aluminium alloy wheel hub mould specifically.
Background technology
Aluminium alloy wheel hub mould is in the process preparing aluminium alloy wheel hub, often need to touch a lot of impurity, not only comprise granule foreign, also comprise the impurity such as some greasy dirts, thus bring certain impact to aluminium alloy wheel hub mould, not only affect its result of use, but also the quality of obtained aluminium alloy wheel hub can be affected, thus bring certain impact to production.
At present, for aluminium alloy wheel hub mould in production, the main mode adopting wet cloth wiping or clear water to rinse, period may use the cleaning agent of some wipe oils, and there are the following problems for such cleaning mode:
1, general cleaning agent can produce corrosion to die surface, and the residual of cleaning agent has more increased the weight of this impact;
2, partial impurities or spot are difficult to by common wiping or rinse removal, and cleaning effect is not fully up to expectations.
Summary of the invention
The present invention is intended to solve the relevant issues existed in prior art, proposes a kind of clean method of aluminium alloy wheel hub mould.
Technical scheme of the present invention is as follows:
A clean method for aluminium alloy wheel hub mould, comprises following process:
Step one, clear water is utilized to rinse die surface, after having rinsed, mould is dry;
Step 2, select hub mold cleaner special add clear water dilution 20-30 doubly obtain cleaning solution, there is spot to die surface to clean, described cleaner special is made up of the component of following mass percent: sodium trideceth sulfate 8%-10%, disodium ethylene diamine tetraacetate 8%-10%, surfactant 10%-15%, natrium carbonicum calcinatum 10%-14%, natrium citricum 10%-14%, sodium metasilicate 6%-8%, defoamer 1%, ethanol 30%-45%.
Step 3, employing clear water rinse the mould after step 2 process, after having rinsed, mould is dry;
Step 4, the mould after step 3 process to be placed on laser work platform, to utilize laser aid to carry out fixed point cleaning to the spot that mould still exists;
Step 5, employing clear water rinse the mould after step 4 process, after having rinsed, mould is dry.
Preferably, following technical scheme can also be selected:
The time of rinsing in step one is 3min-5min.
In step 2, cleaner special is made up of the component of following mass percent: sodium trideceth sulfate 9%, disodium ethylene diamine tetraacetate 9%, surfactant 12%, natrium carbonicum calcinatum 12%, natrium citricum 12%, sodium metasilicate 7%, defoamer 1%, ethanol 38%.
The time of rinsing in step 3 is 10min-15min.
The time of rinsing in step 5 is 1min-2min.
The mode that natural drying or machine are dried is adopted to carry out drying to mould in step one and step 5.
The mode adopting machine to dry in step 3 carries out drying to mould.
The beneficial effect of patent of invention:
The impurity of aluminium alloy wheel hub die surface and greasy dirt, by three kinds of multiple cleanings of mode, can be removed totally, substantially increase the cleannes of aluminium alloy wheel hub mould, ensure that the quality of obtained aluminium alloy wheel hub by the present invention in the lump; While to greatest extent hub mold being cleaned, reduce the loss of cleaning work to die surface, extend the mold use life-span; In addition, safely cleaning agent involved in the present invention can repeatedly recycle, and whole operating process is harmless, safety, environmental protection.
Detailed description of the invention
Below in conjunction with detailed description of the invention, embodiments of the present invention are described.
A clean method for aluminium alloy wheel hub mould, comprises following process:
Step one, utilize clear water to rinse die surface, the time of flushing is naturally dried by mould after 3min-5min has rinsed;
Step 2, select hub mold cleaner special add clear water dilution 20-30 doubly obtain cleaning solution, there is spot to die surface to clean, described cleaner special is made up of the component of following mass percent: sodium trideceth sulfate 9%, disodium ethylene diamine tetraacetate 9%, surfactant 12%, natrium carbonicum calcinatum 12%, natrium citricum 12%, sodium metasilicate 7%, defoamer 1%, ethanol 38%.
Step 3, employing clear water rinse the mould after step 2 process, and the time of flushing is 10min-15min, has rinsed rear use dryer and has been dried by mould;
Step 4, the mould after step 3 process to be placed on laser work platform, to utilize laser aid to carry out fixed point cleaning to the spot that mould still exists;
Step 5, employing clear water rinse the mould after step 4 process, and the time of flushing is 1min-2min, has rinsed rear use dryer and has been dried by mould.
The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, although the present invention with preferred embodiment openly as above, but, and be not used to limit the present invention, any those skilled in the art, do not departing within the scope of technical solution of the present invention, certainly the technology contents of announcement can be utilized to make a little change or modification, become the Equivalent embodiments of equivalent variations, in every case be the content not departing from technical solution of the present invention, according to any simple modification that technical spirit of the present invention is done above embodiment, equivalent variations and modification, all belong in the scope of technical solution of the present invention.
Claims (7)
1. a clean method for aluminium alloy wheel hub mould, is characterized in that: comprise following process:
Step one, clear water is utilized to rinse die surface, after having rinsed, mould is dry;
Step 2, select hub mold cleaner special add clear water dilution 20-30 doubly obtain cleaning solution, there is spot to die surface to clean, described cleaner special is made up of the component of following mass percent: sodium trideceth sulfate 8%-10%, disodium ethylene diamine tetraacetate 8%-10%, surfactant 10%-15%, natrium carbonicum calcinatum 10%-14%, natrium citricum 10%-14%, sodium metasilicate 6%-8%, defoamer 1%, ethanol 30%-45%.
Step 3, employing clear water rinse the mould after step 2 process, after having rinsed, mould is dry;
Step 4, the mould after step 3 process to be placed on laser work platform, to utilize laser aid to carry out fixed point cleaning to the spot that mould still exists;
Step 5, employing clear water rinse the mould after step 4 process, after having rinsed, mould is dry.
2. the clean method of aluminium alloy wheel hub mould according to claim 1, is characterized in that: the time of rinsing in step one is 3min-5min.
3. the clean method of aluminium alloy wheel hub mould according to claim 1, it is characterized in that: in step 2, cleaner special is made up of the component of following mass percent: sodium trideceth sulfate 9%, disodium ethylene diamine tetraacetate 9%, surfactant 12%, natrium carbonicum calcinatum 12%, natrium citricum 12%, sodium metasilicate 7%, defoamer 1%, ethanol 38%.
4. the clean method of aluminium alloy wheel hub mould according to claim 1, is characterized in that: the time of rinsing in step 3 is 10min-15min.
5. the clean method of aluminium alloy wheel hub mould according to claim 1, is characterized in that: the time of rinsing in step 5 is 1min-2min.
6. the clean method of the aluminium alloy wheel hub mould according to claim 1,2 or 5, is characterized in that: adopt the mode that natural drying or machine are dried to carry out drying to mould in step one and step 5.
7. the clean method of the aluminium alloy wheel hub mould according to claim 1 or 4, is characterized in that: the mode adopting machine to dry in step 3 carries out drying to mould.