CN105482072A - Sponge for automobile glove box - Google Patents
Sponge for automobile glove box Download PDFInfo
- Publication number
- CN105482072A CN105482072A CN201511023626.5A CN201511023626A CN105482072A CN 105482072 A CN105482072 A CN 105482072A CN 201511023626 A CN201511023626 A CN 201511023626A CN 105482072 A CN105482072 A CN 105482072A
- Authority
- CN
- China
- Prior art keywords
- parts
- glove box
- sponge
- automobile glove
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to sponge for an automobile glove box, and belongs to the technical field of automobile accessories. The sponge for the automobile glove box is prepared from, by weight, 150-180 parts of polyether polyol, 100-120 parts of toluene diisocynate, 8-30 parts of a foaming agent, 5-10 parts of a foam stabilizer, 2-4 parts of a catalyst, 1-3 parts of a chain extender, 1-3 parts of a cross-linking agent and 20-50 parts of a fire retardant. The sponge for the automobile glove box has the good elastic resilience and buffering effect. If the body touches the glove box, the buffering effect can be achieved, injuries are reduced, the good dust isolation and fire retardant performance is achieved, and objects inside the glove box can be better protected; if the glove box has the refrigeration performance, the effects of heat isolation and energy loss reduction can be achieved.
Description
Technical field
The present invention relates to a kind of automobile glove box with sponge, belong to Automobile Products technical field.
Background technology
Glove box is one of important parts of automotive interior, its Main Function is storing, but now along with the development of automotive industry, the effect of glove box is also not only confined to storing, for example present a lot of cars have started the air channel connecting air-conditioning with glove box, be used as the storage tank of cold storage function, and the position of glove box is in copilot front, therefore its structural sponge is just very important, not only want high resilience, resiliency, and good sealing will be had, thermal insulation etc., but current most of glove boxes are just added with one deck imitation leather outside structure, or easy sponge is housed below imitation leather, do not reach required effect.
Summary of the invention
The object of the invention is to solve the weak point that above-mentioned prior art exists, provide that a kind of rebound resilience, resiliency are good, heat insulation, dust-separation, fire-retardant automobile glove box use sponge.
The present invention is achieved by the following technical solutions:
A kind of automobile glove box is with sponge, and its special character is to be made up of following raw material by weight ratio: polyether glycol 150-180 part, tolylene diisocyanate 100-120 part, whipping agent 8-30 part, foam stabilizer 5-10 part, catalyzer 2-4 part, chainextender 1-3 part, linking agent 1-3 part, fire retardant 20-50 part;
Described whipping agent is the mixture of fluoro trichloromethane, water, carbonic acid gas;
Described foam stabilizer is silicone oil;
Described catalyzer is the mixture of dibutyl tin laurate, stannous octoate, triethylene diamine, two (dimethylaminoethyl) ether;
Described chainextender is the mixture of neopentyl glycol, sorbyl alcohol, glycerine;
Described linking agent is the mixture of cyanacrylate and dicumyl peroxide;
Described fire retardant is the mixture of melamine cyanurate and clorafin;
Described a kind of automobile glove box, with sponge, is made up of the raw material of following optimum proportioning by weight: polyether glycol 175 parts, tolylene diisocyanate 110 parts, whipping agent 20 parts, foam stabilizer 7 parts, catalyzer 3 parts, chainextender 2 parts, linking agent 2 parts, fire retardant 35 parts.
A kind of automobile glove box of the present invention is with sponge; not only there is good rebound resilience and resiliency; if health encounters glove box can play shock absorption; reduce injury; and possess good dust-separation, flame retardant properties; can better article in hand saver case, if glove box have refrigeration more can, heat insulation, to reduce energy waste effect can also be played.
Embodiment
Below provide the specific embodiment of the present invention, be used for being described in further detail formation of the present invention.
Embodiment 1
A kind of automobile glove box of the present embodiment, with sponge, is made up of following raw material by weight ratio: polyether glycol 150 parts, tolylene diisocyanate 100 parts, whipping agent 8 parts, foam stabilizer 5 parts, catalyzer 2 parts, chainextender 1 part, linking agent 1 part, fire retardant 20 parts;
Described whipping agent is the mixture of fluoro trichloromethane, water, carbonic acid gas;
Described foam stabilizer is silicone oil;
Described catalyzer is the mixture of dibutyl tin laurate, stannous octoate, triethylene diamine, two (dimethylaminoethyl) ether;
Described chainextender is the mixture of neopentyl glycol, sorbyl alcohol, glycerine;
Described linking agent is the mixture of cyanacrylate and dicumyl peroxide;
Described fire retardant is the mixture of melamine cyanurate and clorafin.
Embodiment 2
A kind of automobile glove box of the present embodiment, with sponge, is made up of following raw material by weight ratio: polyether glycol 180 parts, tolylene diisocyanate 120 parts, whipping agent 30 parts, foam stabilizer 10 parts, catalyzer 4 parts, chainextender 3 parts, linking agent 3 parts, fire retardant 50 parts.
Embodiment 3
Described a kind of automobile glove box of the present embodiment, with sponge, is made up of the raw material of following optimum proportioning by weight: polyether glycol 175 parts, tolylene diisocyanate 110 parts, whipping agent 20 parts, foam stabilizer 7 parts, catalyzer 3 parts, chainextender 2 parts, linking agent 2 parts, fire retardant 35 parts.
A kind of automobile glove box of above embodiment is with sponge; not only there is good rebound resilience and resiliency; if health encounters glove box can play shock absorption; reduce injury; and possess good dust-separation, flame retardant properties; can better article in hand saver case, if glove box have refrigeration more can, heat insulation, to reduce energy waste effect can also be played.
Claims (8)
1. automobile glove box is with a sponge, it is characterized in that being made up of following raw material by weight ratio: polyether glycol 150-180 part, tolylene diisocyanate 100-120 part, whipping agent 8-30 part, foam stabilizer 5-10 part, catalyzer 2-4 part, chainextender 1-3 part, linking agent 1-3 part, fire retardant 20-50 part.
2. a kind of automobile glove box, with sponge, is characterized in that described whipping agent is the mixture of fluoro trichloromethane, water, carbonic acid gas according to claim 1.
3. a kind of automobile glove box, with sponge, is characterized in that described foam stabilizer is silicone oil according to claim 1.
4. a kind of automobile glove box, with sponge, is characterized in that described catalyzer is the mixture of dibutyl tin laurate, stannous octoate, triethylene diamine, two (dimethylaminoethyl) ether according to claim 1.
5. a kind of automobile glove box, with sponge, is characterized in that described chainextender is the mixture of neopentyl glycol, sorbyl alcohol, glycerine according to claim 1.
6. a kind of automobile glove box, with sponge, is characterized in that described linking agent is the mixture of cyanacrylate and dicumyl peroxide according to claim 1.
7. a kind of automobile glove box, with sponge, is characterized in that described fire retardant is the mixture of melamine cyanurate and clorafin according to claim 1.
8. a kind of automobile glove box, with sponge, is characterized in that being made up of the raw material of following optimum proportioning by weight: polyether glycol 175 parts, tolylene diisocyanate 110 parts, whipping agent 20 parts, foam stabilizer 7 parts, catalyzer 3 parts, chainextender 2 parts, linking agent 2 parts, fire retardant 35 parts according to claim 1.