CN105463516A - 一种铅合金阳极板生产方法 - Google Patents

一种铅合金阳极板生产方法 Download PDF

Info

Publication number
CN105463516A
CN105463516A CN201610030899.0A CN201610030899A CN105463516A CN 105463516 A CN105463516 A CN 105463516A CN 201610030899 A CN201610030899 A CN 201610030899A CN 105463516 A CN105463516 A CN 105463516A
Authority
CN
China
Prior art keywords
anode plate
rare earth
lead alloy
alloy anode
calloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610030899.0A
Other languages
English (en)
Inventor
丁元法
杜洪伍
黄健
苏向东
李鹏
李勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NEW-MATERIAL RESEARCH AND DEVELOPMENT BASE GUIZHOU PROV
Original Assignee
NEW-MATERIAL RESEARCH AND DEVELOPMENT BASE GUIZHOU PROV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NEW-MATERIAL RESEARCH AND DEVELOPMENT BASE GUIZHOU PROV filed Critical NEW-MATERIAL RESEARCH AND DEVELOPMENT BASE GUIZHOU PROV
Priority to CN201610030899.0A priority Critical patent/CN105463516A/zh
Publication of CN105463516A publication Critical patent/CN105463516A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铅合金阳极板生产方法，该方法是只在熔炼炉将铅升温至450～500℃，直接加入钙铝合金，待钙铝熔化后，然后直接加入稀土、金属银等金属；搅拌至稀土、金属银等金属完全熔化，将混合均匀的液体按常规工艺浇铸、扎制、剪切、焊接即得铅合金阳极板。本发明是对传统铅合金阳极板生产工艺的革命性改变，炉温无需再升温至700～800℃高温，具有环保、节能降耗、生产效率高、设备使用寿命长等特点，并简化了生产工序。

Description

一种铅合金阳极板生产方法
技术领域
本发明涉及一种铅合金阳极板生产方法，属于冶金技术领域。
背景技术
铅合金阳极板主要用于湿法电解锌、电解锰等工业。传统的铅合金阳极板生产方法是先在500～600℃下熔化铅，然后在铅液表面加入铝作保护剂，制造铅-钙中间合金，再用铅-钙中间合金生产出最终铅钙合金。由于铝的熔点较高，通常高达700多度，所以在熔铝时需要升温至700～800℃，人工搅拌一个半小时，等铝完全熔化后再降温至500～600℃，向铅熔液中加入钙、稀土、银等金属。这种工艺不但工人劳动强度大，耗时长，生产效率低，而且每一炉都要先升温再降温，能耗大，生产成本高，升温熔铝时还会导致铅蒸汽大量挥发，危害人体健康，对环境造成污染，频繁的升温和降温过程也会增加设备损耗，缩短设备使用寿命。
发明内容
本发明所要解决的技术问题在于提供一种节约能耗、工艺简便、操作简单、生产效率高的铅合金阳极板生产方法，以克服现有技术的不足。
为解决上述技术问题，本发明的技术方案如下：
一种铅合金阳极板生产方法，该方法是只在熔炼炉将铅升温至450～500℃，直接加入钙铝合金，待钙铝合金熔化后，然后直接加入稀土、金属银等金属；搅拌至稀土、金属银等金属完全熔化，将混合均匀的液体按照常规工艺进行浇铸、扎制、剪切、焊接即得铅合金阳极板。
上述的铅合金阳极板生产方法中，所述的钙铝合金可以是钙铝块、钙铝屑、钙铝粉或钙铝粒的形式；
上述的铅合金阳极板生产方法中，所述的金属银可以是银块、银屑、银粉或银粒的形式；稀土可以是稀土块、稀土屑、稀土粉或稀土粒的形式。
有益效果：与现有技术相比，本发明是对传统铅合金阳极板冶炼工艺的革命性改变，具有以下特点：
1、环保：全程低温熔炼，减少了铅蒸汽挥发，降低了环境污染。
2、节能降耗：由于无需每炉都升温至700～800度，大幅降低了电耗，节约了能源，降低了成本，每炼1吨至少能降低成本100元，经济效益明显。
3、生产效率高、耗时短：由于省去了每炉升温熔铝的工序，因此工艺得到简化，操作简单，无需搅拌，大大降低了劳动强度，缩短了冶炼时间，提高了生产效率。
4、保护设备：由于省去了每炉升温熔铝的工序，避免了冶炼炉的频繁升温和降温，降低了设备损耗，延长了使用寿命。
5、由于铝的比重比铅小很多，且在液态铅中的溶解度较小，因此，在加入铅液中时，铝往往浮在铅液表面，在高温下与氧气反应会产生大量的浮渣，吸附不少的液态铅，导致在捞走浮渣的过程带走大量的液态金属铅，造成浪费。而本发明将钙铝合金锭加入铅液时，不会浮在铅液表面，减少了铅的浪费。
下面结合具体实施方式对本发明作进一步的说明。
具体实施方式
实施例1：在冶炼时，先在熔炼炉中将铅升温至450～500℃，直接加入一定量的钙铝合金，待钙铝合金熔化后，然后直接加入稀土、金属银等金属；搅拌至稀土、金属银等金属完全熔化，将混合均匀的液体按照常规工艺进行浇铸、轧制、剪切、焊接即得铅合金阳极板。
本发明的实施方式不限于上述实施例，在不脱离本发明宗旨的前提下做出的各种变化均属于本发明的保护范围之内。

Claims (3)

1.一种铅合金阳极板生产方法，其特征在于：该方法是只在熔炼炉将铅升温至450～500℃，直接加入钙铝合金，待钙铝合金熔化后，然后直接加入稀土、金属银；搅拌至稀土、金属银完全熔化，将混合均匀的液体按照常规工艺进行浇铸、轧制、剪切、焊接即得铅合金阳极板。
2.根据权利要求1所述的铅合金阳极板生产方法，其特征在于：所述的钙铝合金是钙铝块、钙铝屑、钙铝粉或钙铝粒的形式。
3.根据权利要求1所述的铅合金阳极板生产方法，其特征在于：所述的金属银是银块、银屑、银粉或银粒的形式；稀土是稀土块、稀土屑、稀土粉或稀土粒的形式。
CN201610030899.0A 2016-01-19 2016-01-19 一种铅合金阳极板生产方法 Pending CN105463516A (zh)