CN105462456A - 一种泵阀用抗静电粉末涂料 - Google Patents
一种泵阀用抗静电粉末涂料 Download PDFInfo
- Publication number
- CN105462456A CN105462456A CN201510865434.2A CN201510865434A CN105462456A CN 105462456 A CN105462456 A CN 105462456A CN 201510865434 A CN201510865434 A CN 201510865434A CN 105462456 A CN105462456 A CN 105462456A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- nano
- powder coating
- pump valve
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种泵阀用抗静电粉末涂料,由下列重量份的原料制成:羟基聚酯树脂52-54、氟碳树脂7-8、异氰尿酸三缩水甘油酯4-5、纳米三氧化二铝13-15、全氟辛基三乙氧基硅烷0.8-0.9、浓度为75wt%的乙醇溶液25-30、硅烷偶联剂kh5600.5-0.6、安息香0.2-0.3、PV99高效流平剂1.2-1.5、纳米ATO粉7-8、六偏磷酸钠0.4-0.5、水适量、聚乙烯吡咯烷酮0.8-1、乙氧基化烷基酸胺1.6-2、硫酸钡13-15。本发明制成的粉末涂料涂层表面平整光滑,还具有抗静电功能,用于泵阀等器件表面,能够大大降低灰尘的吸附力,同时工艺简单,防污性能优,防腐耐用。
Description
技术领域
本发明涉及涂料技术领域,尤其涉及一种泵阀用抗静电粉末涂料。
背景技术
近年来,粉末涂料的应用已超越了涂料工业中的水性涂料和高固体涂料等,成为工业界使用较多的涂料品种之一。粉末涂装工艺解决了传统油漆涂装工艺所存在的易燃、易爆和污染环境等问题,而且其涂层具备优越的性能,原料可回收再用,涂装工艺简单。可广泛应用于泵、阀门壳体涂装上。由于泵阀是铸件或锻件,因此其表面粗糙,目前现有技术针对阀门表面处理的功能性粉末涂料技术还存在一定缺陷,致使涂层出现缩孔、针眼和严重桔皮状等缺陷,进而导致泵阀在食品、生物、制药、化工、航天和电子等特殊领域应用受到限制。而且大部分泵阀都会用在高含水、高含砂、强腐蚀的介质环境等因素影响,加重了泵阀的腐蚀,更易在泵阀上结垢,从而造成泵阀使用寿命短,检验周期短、工作量大的问题,给使用带来不便,一般的表面强化工艺主要有金属镀层、陶瓷涂层、其他一些涂层,虽然在一定程度上减缓了磨损,提高了耐腐蚀性,但是都存在着不足之处:金属镀层容易分层导致脱落;陶瓷抗冲击性能差,容易发生碎裂现象;一些聚合物涂层力学和热性能差等。因而研究开发具有耐候、防水防腐等功能的粉末涂料,具有技术促进与产业提高的意义。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种泵阀用抗静电粉末涂料。
本发明是通过以下技术方案实现的:
一种泵阀用抗静电粉末涂料,由下列重量份的原料制成:羟基聚酯树脂52-54、氟碳树脂7-8、异氰尿酸三缩水甘油酯4-5、纳米三氧化二铝13-15、全氟辛基三乙氧基硅烷0.8-0.9、浓度为75wt%的乙醇溶液25-30、硅烷偶联剂kh5600.5-0.6、安息香0.2-0.3、PV99高效流平剂1.2-1.5、纳米ATO粉7-8、六偏磷酸钠0.4-0.5、水适量、聚乙烯吡咯烷酮0.8-1、乙氧基化烷基酸胺1.6-2、硫酸钡13-15。
所述一种泵阀用抗静电粉末涂料,由以下具体步骤制备而成:
(1)将纳米三氧化二铝放入浓度为75wt%的乙醇溶液中,搅拌分散均匀,然后加入全氟辛基三乙氧基硅烷,加热回流2-2.5小时,冷却后加入硅烷偶联剂kh560,继续搅拌反应2-3小时,最后减压蒸馏,脱去体系中的溶剂,在真空干燥箱中以80-85℃的温度干燥60-80分钟,得到活性纳米三氧化二铝;
(2)将纳米ATO粉加入5-7倍量的水中,以300转/分的速度分散30-50分钟,然后加入六偏磷酸钠、聚乙烯吡咯烷酮,加热至45-55℃,继续搅拌15-20分钟后转入超声振荡器中,超声分散40-50分钟后喷雾干燥,然后与硫酸钡混合,放入球磨机中球磨30-40分钟,得到改性填料;
(3)将羟基聚酯树脂、氟碳树脂、异氰尿酸三缩水甘油酯放入高速搅拌机中以1000转/分的速度搅拌20-30分钟后加入活性纳米三氧化二铝以及改性填料,继续搅拌10-15分钟后出料,将混合料送入双螺杆熔融挤出机,继续加入其余剩余成分,熔融挤出,压片,经粉碎过180目筛得到微细粉即得。
本发明的优点是:本发明添加少量的氟碳树脂替代部分羟基聚酯树脂,在粉末涂料固化的过程中,氟碳树脂中的氟碳链段发生了表面富集,所以少量的氟就可以明显提高涂层的疏水疏油性,同时可以提高涂层的耐热水、耐酸碱性能以及柔韧性;配合添加经过特殊工艺处理制得的活性纳米三氧化二铝,很容易与F-C键形成化学键接,使涂层结构更牢固,而且涂层表面对水的接触角急剧增大,进一步提高了涂层的疏水性,制成的粉末涂料有远比一般粉末涂料优异的抗腐蚀、耐酸碱、耐候性、憎水憎油性等。
本发明通过添加纳米ATO粉、硫酸钡等成分通过改性制成改性填料,具备良好的导电性,从而提高抗静电功效,配合添加具备防腐功效的安息香等成分,本发明制成的粉末涂料涂层表面平整光滑,还具有抗静电功能,用于泵阀等器件表面,能够大大降低灰尘的吸附力,同时工艺简单,防污性能优,防腐耐用。
具体实施方式
一种泵阀用抗静电粉末涂料,由下列重量份(公斤)的原料制成:羟基聚酯树脂52、氟碳树脂7、异氰尿酸三缩水甘油酯4、纳米三氧化二铝13、全氟辛基三乙氧基硅烷0.8、浓度为75wt%的乙醇溶液25、硅烷偶联剂kh5600.5、安息香0.2、PV99高效流平剂1.2、纳米ATO粉7、六偏磷酸钠0.4、水适量、聚乙烯吡咯烷酮0.8、乙氧基化烷基酸胺1.6、硫酸钡13。
所述一种泵阀用抗静电粉末涂料,由以下具体步骤制备而成:
(1)将纳米三氧化二铝放入浓度为75wt%的乙醇溶液中,搅拌分散均匀,然后加入全氟辛基三乙氧基硅烷,加热回流2小时,冷却后加入硅烷偶联剂kh560,继续搅拌反应2小时,最后减压蒸馏,脱去体系中的溶剂,在真空干燥箱中以80℃的温度干燥60分钟,得到活性纳米三氧化二铝;
(2)将纳米ATO粉加入5倍量的水中,以300转/分的速度分散30分钟,然后加入六偏磷酸钠、聚乙烯吡咯烷酮,加热至45℃,继续搅拌15分钟后转入超声振荡器中,超声分散40分钟后喷雾干燥,然后与硫酸钡混合,放入球磨机中球磨40分钟,得到改性填料;
(3)将羟基聚酯树脂、氟碳树脂、异氰尿酸三缩水甘油酯放入高速搅拌机中以1000转/分的速度搅拌20分钟后加入活性纳米三氧化二铝以及改性填料,继续搅拌10分钟后出料,将混合料送入双螺杆熔融挤出机,继续加入其余剩余成分,熔融挤出,压片,经粉碎过180目筛得到微细粉即得。
将本发明粉末涂料采用静电喷涂施工方法作用于泵、阀门等器件表面上,经过180℃的充分固化,自然冷却至室温,放置24小时后,测定涂层性能:漆膜外观平整光滑,表面色调一致,无颗粒、针孔、气泡、皱纹;附着力达到1级,耐中性盐雾性2000小时无异常,抗冲击强度大于60cm。
Claims (2)
1.一种泵阀用抗静电粉末涂料,其特征在于,由下列重量份的原料制成:羟基聚酯树脂52-54、氟碳树脂7-8、异氰尿酸三缩水甘油酯4-5、纳米三氧化二铝13-15、全氟辛基三乙氧基硅烷0.8-0.9、浓度为75wt%的乙醇溶液25-30、硅烷偶联剂kh5600.5-0.6、安息香0.2-0.3、PV99高效流平剂1.2-1.5、纳米ATO粉7-8、六偏磷酸钠0.4-0.5、水适量、聚乙烯吡咯烷酮0.8-1、乙氧基化烷基酸胺1.6-2、硫酸钡13-15。
2.根据权利要求1所述一种泵阀用抗静电粉末涂料,其特征在于,由以下具体步骤制备而成:
(1)将纳米三氧化二铝放入浓度为75wt%的乙醇溶液中,搅拌分散均匀,然后加入全氟辛基三乙氧基硅烷,加热回流2-2.5小时,冷却后加入硅烷偶联剂kh560,继续搅拌反应2-3小时,最后减压蒸馏,脱去体系中的溶剂,在真空干燥箱中以80-85℃的温度干燥60-80分钟,得到活性纳米三氧化二铝;
(2)将纳米ATO粉加入5-7倍量的水中,以300转/分的速度分散30-50分钟,然后加入六偏磷酸钠、聚乙烯吡咯烷酮,加热至45-55℃,继续搅拌15-20分钟后转入超声振荡器中,超声分散40-50分钟后喷雾干燥,然后与硫酸钡混合,放入球磨机中球磨30-40分钟,得到改性填料;
(3)将羟基聚酯树脂、氟碳树脂、异氰尿酸三缩水甘油酯放入高速搅拌机中以1000转/分的速度搅拌20-30分钟后加入活性纳米三氧化二铝以及改性填料,继续搅拌10-15分钟后出料,将混合料送入双螺杆熔融挤出机,继续加入其余剩余成分,熔融挤出,压片,经粉碎过180目筛得到微细粉即得。