CN105461277A - Environmentally friendly tire casting gypsum powder and preparation process thereof - Google Patents
Environmentally friendly tire casting gypsum powder and preparation process thereof Download PDFInfo
- Publication number
- CN105461277A CN105461277A CN201410400806.XA CN201410400806A CN105461277A CN 105461277 A CN105461277 A CN 105461277A CN 201410400806 A CN201410400806 A CN 201410400806A CN 105461277 A CN105461277 A CN 105461277A
- Authority
- CN
- China
- Prior art keywords
- parts
- gypsum powder
- preparation process
- environmentally friendly
- casting gypsum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An environmentally friendly tire casting gypsum powder and a preparation process thereof. The gypsum powder consists of the following raw materials by weight: 100 parts of alpha-gypsum powder, 15-25 parts of white portland cement, 0.1.5-5 parts of sulfonated melamine formaldehyde resin, 1-3 parts of peach gum and 5-15 parts of vegetable fibers. The present invention also includes a preparation process of the environmentally friendly tire casting gypsum powder. The environmentally friendly tire casting gypsum powder has longer effective stirring time and flow time, as well as appropriate initial setting time and final setting time. The prepared casting gypsum mold has the advantages of high strength, no environmental pollution, wide scope of adaptation and long service life. The preparation process is simple, easy to operate, and suitable for industrial production.
Description
Technical field
The present invention relates to a kind of environment-friendly type tire casting gypsum powder and preparation technology thereof.
Background technology
At present, most of tyre casting gypsum die production producer is when making tyre casting gypsum mould, high strength gypsum (α-gypsum) powder is all directly used to be starting material, Mold Making is carried out in mass ratio for 1:0.5 ~ 0.55 mixes with water, because the rare thick degree of gained calcium plaster is higher, its effective churning time only has 5min, flowing time 3 ~ 5min, presetting period 8min, final setting time 30min.In addition, utilize mould obtained by described α-terra alba, the coefficient of expansion is large, is about 0.5; Dry folding strength is low, is about 7MPa; Dry ultimate compression strength is also lower, about 22MPa.Due to starting material presetting period too short, effective churning time and flowing time also shorter, not only cause certain limitation to operation, nor be beneficial to the finishing to obtained mould, and due to undercapacity, greatly reduce the mold use life-span.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, a kind of existing longer effective churning time and flowing time are provided, there are again suitable presetting period and final setting time, environmentally safe, and by the high ceramic-reinforced tyre casting gypsum powder of its casting plaster mould strength made and preparation technology thereof.
The object of the invention is to be achieved through the following technical solutions:
The environment-friendly type tire casting gypsum powder of the present invention, is made up of the raw material of following parts by weight: α-terra alba 100 parts, white portland cement 15 ~ 25 parts, sulfonated melamine compound resin 0.5 ~ 1.5 part, peach gum 1 ~ 3 part, 5 ~ 15 parts, vegetable fibre.
Further, preferred version parts by weight: α-terra alba 100 parts, white portland cement 20 parts, sulfonated melamine compound resin 1 part, peach gum 2 parts, 10 parts, vegetable fibre.
The preparation technology of the environment-friendly type tire casting gypsum powder of the present invention, first takes each component raw material by described parts by weight, then each component raw material is placed in mixer mixing 20 ~ 30min.
Described raw material is nontoxic, free of contamination environment-friendly type raw material, α-terra alba is main raw, white portland cement is toughener, sulfonated melamine compound resin is water reducer, also toughener or sizing agent effect is played, peach gum is additive, and existing sizing agent effect has delayed coagulation again, and vegetable fibre is weighting agent.
Compared with existing α-terra alba, the environment-friendly type tire casting gypsum powder of the present invention, not only have clear improvement in effective churning time, flowing time, presetting period and final setting time, and environmentally safe, the intensity of especially obtained tire casting mould significantly improves, the every technical parameter requirement of current domestic tire enterprise to tire casting mould can be reached completely, wide accommodation, long service life; In addition, its raw material sources is extensive, cheap, low cost of manufacture; Its preparation technology is simple, and easy handling, is conducive to suitability for industrialized production.
The invention will be further described below in conjunction with embodiment for embodiment.
Embodiment 1
The environment-friendly type tire casting gypsum powder of the present embodiment, is made up of the raw material of following parts by weight: α-terra alba 100 parts, white portland cement 15 parts, sulfonated melamine compound resin 0.5 part, peach gum 1 part, 5 parts, vegetable fibre.
Preparation: first take each component raw material by described parts by weight, is then placed in mixer mixing 20 ~ 30min by each component raw material.
Embodiment 2
The environment-friendly type tire casting gypsum powder of the present embodiment, is made up of the raw material of following parts by weight: α-terra alba 100 parts, white portland cement 20 parts, sulfonated melamine compound resin 1 part, peach gum 2 parts, 10 parts, vegetable fibre.Its preparation technology is with embodiment 1.
Claims (3)
1. an environment-friendly type tire casting gypsum powder, is characterized in that, is made up of the raw material of following parts by weight: α-terra alba 100 parts, white portland cement 15 ~ 25 parts, sulfonated melamine compound resin 0.5 ~ 1.5 part, peach gum 1 ~ 3 part, 5 ~ 15 parts, vegetable fibre.
2. environment-friendly type tire casting gypsum powder according to claim 1, is characterized in that, is made up of the raw material of following parts by weight: α-terra alba 100 parts, white portland cement 20 parts, sulfonated melamine compound resin 1 part, peach gum 2 parts, 10 parts, vegetable fibre.
3. a preparation method for environment-friendly type tire casting gypsum powder as claimed in claim 1 or 2, is characterized in that: first take each component raw material by described parts by weight, then each component raw material is placed in mixer mixing 20 ~ 30min.