CN105461228B - A kind of sustainable thin plate glaze for generating anion and the thin plate being prepared by it - Google Patents
A kind of sustainable thin plate glaze for generating anion and the thin plate being prepared by it Download PDFInfo
- Publication number
- CN105461228B CN105461228B CN201510476049.9A CN201510476049A CN105461228B CN 105461228 B CN105461228 B CN 105461228B CN 201510476049 A CN201510476049 A CN 201510476049A CN 105461228 B CN105461228 B CN 105461228B
- Authority
- CN
- China
- Prior art keywords
- parts
- thin plate
- glaze
- sustainable
- anion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of sustainable thin plate glaze for generating anion and the thin plates being prepared by it.The thin plate glaze of the sustainable generation anion of the present invention is mainly made of the raw material of following weight ratio:10~40 parts of kaolin, 5~30 parts of albite, 10~60 parts of silica flour, 5~40 parts of lime stone, 5~40 parts of talcum, 2~20 parts of nano titanium dioxide powder, 2~20 parts of zinc oxide, 0.1~1.5 part of wood-fibred, 0.3~1.5 part of dispersant, 2~20 parts of hydroxypropyl methyl cellulose, 1~20 part of inorganic pigment.The ceramic thin plate that the present invention is prepared can release anion, and effectively adsorbs, eliminates the pernicious gases such as formaldehyde, ammonia, benzene, TVOC, and purification air eliminates peculiar smell, fire protection flame retarding.It can be widely applied to office block, indoor wall, the ground of family etc..By thin plate glaze layer outwardly sustained release anion, it is effectively improved indoor air quality, prodigious help is played to health.
Description
Technical field
The invention belongs to building material technical fields, and in particular to a kind of sustainable ceramic thin plate glaze for generating anion
And the thin plate being prepared by it.
Background technology
Since in fitment process, finishing material and new furniture generate many toxic and harmful gas, such as benzene, formaldehyde, ketone, ammonia
Deng in addition the harmful peculiar smell generated in people's daily life, then consumer increasingly payes attention to the ring of finishing material
Effect is protected, not only finishing material is required not discharge toxic and harmful gas, it is also desirable to which finishing material can decompose toxic and harmful gas.
But traditional thin plate does not have the function of eliminating and be harmful to poison gas, self can purify.
Invention content
It is an object of the invention to a kind of sustainable thin plate glaze for generating anion and the thin plates being prepared by it.
The technical solution used in the present invention is:
A kind of sustainable thin plate glaze for generating anion, is mainly made of the raw material of following weight ratio:Kaolin
10~40 parts, 5~30 parts of albite, 10~60 parts of silica flour, 5~40 parts of lime stone, talcum 5~40
Part, 2~20 parts of nano titanium dioxide powder, 2~20 parts of zinc oxide, 0.1~1.5 part of wood-fibred, dispersant 0.3~
1.5 parts, 2~20 parts of hydroxypropyl methyl cellulose, 1~20 part of inorganic pigment.
Preferably, the sustainable thin plate glaze for generating anion is mainly by the raw material group of following weight ratio
At:15~30 parts of kaolin, 10~25 parts of albite, 20~50 parts of silica flour, 10~30 parts of lime stone are sliding
10~30 parts of stone, 5~15 parts of nano titanium dioxide powder, 5~15 parts of zinc oxide, 0.3~1.2 part of wood-fibred,
0.5~1.2 part of dispersant, 3~15 parts of hydroxypropyl methyl cellulose, 5~18 parts of inorganic pigment.
The thin plate being prepared by the above-mentioned sustainable thin plate glaze for generating anion, preparation method are as follows:
1)Each glaze raw material is weighed, the glaze slip that granularity is 200-300 mesh is milled to after adding water;
2)By step 1)The glaze slip of preparation carries out glazing on green body, and glazed body is burnt at a temperature of 1200~1230 DEG C.
The beneficial effects of the invention are as follows:
The thin plate that the present invention is prepared can be adsorbed effectively, eliminate the pernicious gases such as formaldehyde, ammonia, benzene, TVOC, can purify sky
Gas eliminates peculiar smell, fire protection flame retarding, and releasing negative oxygen ion.
Specific implementation mode
With reference to embodiment, the present invention is further illustrated, and however, it is not limited to this.
Embodiment 1
A kind of sustainable thin plate glaze for generating anion, is made of the raw material of following weight ratio:15 parts of kaolin, sodium
25 parts of feldspar, 50 parts of silica flour, 30 parts of lime stone, 30 parts of talcum, 5 parts of nano titanium dioxide powder, 15 parts of zinc oxide, wood
1.2 parts of fiber, 0.5 part of dispersant, 15 parts of hydroxypropyl methyl cellulose, 5 parts of inorganic pigment.
Embodiment 2
A kind of sustainable thin plate glaze for generating anion, is made of the raw material of following weight ratio:20 parts of kaolin, sodium
20 parts of feldspar, 40 parts of silica flour, 20 parts of lime stone, 25 parts of talcum, 8 parts of nano titanium dioxide powder, 12 parts of zinc oxide, wood
0.1~1.5 part of fiber, 0.7 part of dispersant, 12 parts of hydroxypropyl methyl cellulose, 10 parts of inorganic pigment.
Embodiment 3
A kind of sustainable thin plate glaze for generating anion, is made of the raw material of following weight ratio:25 parts of kaolin, sodium
15 parts of feldspar, 30 parts of silica flour, 15 parts of lime stone, 20 parts of talcum, 12 parts of nano titanium dioxide powder, 8 parts of zinc oxide, wood
0.5 part of fiber, 0.9 part of dispersant, 8 parts of hydroxypropyl methyl cellulose, 15 parts of inorganic pigment.
Embodiment 4
A kind of sustainable thin plate glaze for generating anion, is made of the raw material of following weight ratio:30 parts of kaolin, sodium
10 parts of feldspar, 20 parts of silica flour, 10 parts of lime stone, 15 parts of talcum, 15 parts of nano titanium dioxide powder, 5 parts of zinc oxide, wood
0.3 part of fiber, 1.2 parts of dispersant, 5 parts of hydroxypropyl methyl cellulose, 18 parts of inorganic pigment.
The thin plate glaze of embodiment 1-4 is prepared into thin plate, steps are as follows:
1)Each glaze raw material is weighed, the glaze slip that granularity is 200-300 mesh is milled to after adding water;
2)By step 1)The glaze slip of preparation carries out glazing on green body, and glazed body is burnt at a temperature of 1200~1230 DEG C.
According to JC/T 1074-2008《Function of purifying indoor air coating material purifying property》Standard, detector detection are real
72 hours purifying properties of thin plate that the glaze of a 1-4 is prepared are applied, testing result is as shown in the table:
As seen from the above table, light sheet products performance of the invention far more than《Function of purifying indoor air coating material》Purification property
It can standard.
According to JC/T 1016-2006《The test method of material anion-generating capacity》Standard, to use anion thin plate with
The negative ion amount that common thin plate generates is detected, as a result as follows:
Inspection project | Inspection result |
Anion-generating capacity, a/cm3 | 3310 |
Claims (3)
1. a kind of sustainable thin plate glaze for generating anion, is mainly made of the raw material of following weight ratio:Kaolin 15
~30 parts, 10~25 parts of albite, 20~50 parts of silica flour, 10~30 parts of lime stone, 10~30 parts of talcum, nano-titanium dioxide
5~15 parts of powder, 5~15 parts of zinc oxide, 0.3~1.2 part of wood-fibred, 0.5~1.2 part of dispersant, hydroxypropyl methyl cellulose 3
~15 parts, 5~18 parts of inorganic pigment.
2. the thin plate being prepared by the sustainable thin plate glaze for generating anion described in claim 1.
3. thin plate according to claim 2, preparation method are as follows:
1) each glaze raw material is weighed, the glaze slip that granularity is 200-300 mesh is milled to after adding water;
2) glaze slip for preparing step 1) carries out glazing to green body, and glazed body is burnt at a temperature of 1200~1230 DEG C.