CN105441764A - 一种钨基高密度合金 - Google Patents

一种钨基高密度合金 Download PDF

Info

Publication number
CN105441764A
CN105441764A CN201511003850.8A CN201511003850A CN105441764A CN 105441764 A CN105441764 A CN 105441764A CN 201511003850 A CN201511003850 A CN 201511003850A CN 105441764 A CN105441764 A CN 105441764A
Authority
CN
China
Prior art keywords
tungsten
parts
raw material
weight part
compound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201511003850.8A
Other languages
English (en)
Inventor
陈保云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU LIONY METALS Co Ltd
Original Assignee
CHANGSHU LIONY METALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU LIONY METALS Co Ltd filed Critical CHANGSHU LIONY METALS Co Ltd
Priority to CN201511003850.8A priority Critical patent/CN105441764A/zh
Publication of CN105441764A publication Critical patent/CN105441764A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种钨基高密度合金，包括钨化合物、锡料和铜化合物，所述钨化合物为正钨酸铵或钨酸中的任意一种，所述锡料为锡粉。该发明提供的钨基高密度合金，烧结温度低，烧结致密性好，烧结飞块成品密度高，硬度高。

Description

一种钨基高密度合金
技术领域
本发明涉及合金技术领域，具体涉及一种钨基高密度合金。
背景技术
钨基高密度合金也被称作“高密度合金”或“钨基重合金”，它是一种以钨为硬质相，以镍、铜或镍、铁等为黏结相构成的复合材料。钨基高密度合金具有密度高、强度高、延性好、韧性好、热膨胀系数小等一系列优异特性，被广泛的应用在信息、能源、冶金、航空航天、国防军工和核工业等领域。
飞块是工程机械发动机分配泵调速控制器中的一个关键零件。在工作时，四只飞块同时由飞块座带动作高速旋转，在不同转速下飞块张开角度不同，改变油量调节杆的位置，从而调节油量以控制发动机速度，保证柴油发动机：稳定在怠速转动时的最低转速，使发动机不熄火，限制柴油机的最高转速，防止飞车。飞块是发动机中一个致关重要的部件。
发明内容
本发明克服了上述的缺点，而提供一种钨基高密度合金。
为了实现上述目的，本发明是通过如下的技术方案来实现：该钨基高密度合金包括钨化合物、锡料和铜化合物。
优选的，所述钨化合物为正钨酸铵或钨酸中的任意一种。
优选的，所述锡料为锡粉。
优选的，所述铜化合物为乙二酸铜或碱式碳酸铜中的任意一种。
优选的，所述各原料的重量份分别为：钨化合物20~35份、锡料10~15份和铜化合物20~28份。
优选的，所述各原料的重量份分别为：所述各原料的重量份分别为：钨酸20份、锡粉10份和乙二酸铜20份。
优选的，所述各原料的重量份分别为：所述各原料的重量份分别为：正钨酸铵25份、锡粉12份和碱式碳酸铜25份。
优选的，所述各原料的重量份分别为：所述各原料的重量份分别为：正钨酸铵35份、锡粉15份和碱式碳酸铜28份。
本发明的有益效果是：烧结温度低，烧结致密性好，烧结飞块成品密度高，硬度高。
具体实施方式
实施例1
所述各原料的重量分别为：钨酸20kg、锡粉10kg和乙二酸铜20kg。
实施例2
所述各原料的重量分别为：正钨酸铵25kg、锡粉12kg和碱式碳酸铜25kg。
实施例3
所述各原料的重量分别为：正钨酸铵35kg、锡粉15kg和碱式碳酸铜28kg。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (8)

1.一种钨基高密度合金，其特征在于，包括钨化合物、锡料和铜化合物。
2.根据权利要求1所述的钨基高密度合金，其特征在于，所述钨化合物为正钨酸铵或钨酸中的任意一种。
3.根据权利要求1所述的钨基高密度合金，其特征在于，所述锡料为锡粉。
4.根据权利要求1所述的钨基高密度合金，其特征在于，所述铜化合物为乙二酸铜或碱式碳酸铜中的任意一种。
5.根据权利要求1所述的钨基高密度合金，其特征在于，所述各原料的重量份分别为：钨化合物20~35份、锡料10~15份和铜化合物20~28份。
6.根据权利要求1所述的钨基高密度合金，其特征在于，所述各原料的重量份分别为：所述各原料的重量份分别为：钨酸20份、锡粉10份和乙二酸铜20份。
7.根据权利要求1所述的钨基高密度合金，其特征在于，所述各原料的重量份分别为：所述各原料的重量份分别为：正钨酸铵25份、锡粉12份和碱式碳酸铜25份。
8.根据权利要求1所述的钨基高密度合金，其特征在于，所述各原料的重量份分别为：所述各原料的重量份分别为：正钨酸铵35份、锡粉15份和碱式碳酸铜28份。
CN201511003850.8A 2015-12-29 2015-12-29 一种钨基高密度合金 Pending CN105441764A (zh)