CN105441513A - Method for preparing corn-based porous starch - Google Patents
Method for preparing corn-based porous starch Download PDFInfo
- Publication number
- CN105441513A CN105441513A CN201510877236.8A CN201510877236A CN105441513A CN 105441513 A CN105441513 A CN 105441513A CN 201510877236 A CN201510877236 A CN 201510877236A CN 105441513 A CN105441513 A CN 105441513A
- Authority
- CN
- China
- Prior art keywords
- corn
- preparation
- based porous
- starch
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a method for preparing corn-based porous starch. Corn is adopted as a raw material. The method comprises the steps that a certain amount of corn starch is firstly taken, a proper amount of distilled water is added, and the mixture is placed in a water bath to be heated and constantly stirred through a stirrer; when the solution is transparent, the system is cooled to room temperature, then a proper amount of lauryl sodium sulfate is added and stirred to be dissolved evenly, then the system is heated, glucamylase and alpha-amylase are added when certain temperature is achieved, and a certain amount of glutaric acid is added after full reacting; acetone washing, water washing and filtering are sequentially carried out, vacuum drying is carried out finally, and the finished product is obtained. The prepared porous starch is large in specific surface area, good in stability, simple in preparation process, rich in raw material and low in price, and industrialization can be achieved easily.
Description
Technical field
The present invention relates to a kind of modified starch, particularly a kind of Corn Porous Starch and preparation method thereof, belong to chemical industry synthesis field.
Background technology
Starch is a kind of natural macromolecule carbohydrate synthesized by photosynthesis in plant tissue by carbonic acid gas and water, the poly glucose sugar be made up of α-D-six ring glucose.It is extensively present in plant cell tissue, is green plants fruit, seed, stem tuber, block root main component, exists next in number only to Mierocrystalline cellulose and have the carbohydrate of recyclability at nature.Usually as a kind of green chemical industry raw material, when starch is as sorbent material, native starch grain relies on grain surface atom or the faint valency of atomic group to produce adsorptive power adsorbent, when adsorbate is subject to larger magnetism, adsorptive will disintegrate, and porous-starch is because having shrinkage pool, adsorbate can be sucked empty inwall, absorption is comparatively firm, and adsorptive is not easily departed from.
Porous-starch is exactly a kind of treated starch, also known as micropore starch, it be there is uncooked amylum enzyme activity enzyme at the porousness cellular products formed lower than acting on uncooked amylum under gelatinization point.Micropore starch surface is covered with the aperture that diameter is about 1 μm, and by surface to center deeply, the volume in hole accounts for about 50% of particle volume to aperture.By natural uncooked amylum after the outer reason of hydrolysis, forming aperture on its material surface, and extend to granule interior, is a kind of hollow particle of similar hornet's nest shape, can the various material of splendid attire in wherein, there is good adsorptivity.
Porous-starch is main compared with native starch following characteristics: (1) larger specific pore volume and specific surface area; (2) tap density, pellet density are lower; (3) good water suction, oil absorption; (4) course of processing does not use chemical reagent, and safe, nontoxic, using dosage is unrestricted, and cost is low, can natural degradation.Therefore can be used as a kind of efficient, nontoxic, safe sorbent material, be widely used in the industries such as food, medical and health, agricultural, papermaking, printing, makeup, washing composition, tackiness agent.
At present, prepare porous-starch and mainly contain following several method: one is physical method, such as, by ultrasonic irradiation or spray art; Two is adopt mechanical means, such as, by mechanical impacts such as ball-milling technologies; 3rd is biochemical method, such as alcohol sex change or acid hydrolysis, and in above-mentioned several method, the production cost of the mechanical impact such as ultrasonic irradiation, ball-milling technology method is higher, not easily realizes industrialization; And spray method and alcohol sex change are formed is a kind of solid popcorn polymer spheroid, adsorption only occurs in the gully of surface irregularity, and adsorptive capacity is limited, and application prospect is pessimistic; Acid-hydrolysis method speed of reaction under gelatinization point is comparatively slow, and degraded differs, and randomness is strong, is not easily formed poroid, limits the application of acid system; The present invention is using corn as raw material, adopt enzyme liberating processing method, spherex particle diameter and microvoid structure is controlled by regulating preparation process condition and adding suitable adjuvants, thus prepare a kind of corn-based porous-starch, the porous-starch specific surface area of preparation is large, have adsorption to many kinds of substance, production cost is low, easily realizes industrialization.
Summary of the invention
The object of this invention is to provide a kind of preparation method of the preparation corn-based porous-starch using corn as raw material, its main method steps is as follows:
(1) get a certain amount of W-Gum, add appropriate distilled water, be placed in water-bath and heat, Heating temperature is no more than 80 DEG C, and constantly stirs with agitator, until solution is transparent;
(2) be then cooled to room temperature, then add appropriate sodium lauryl sulphate, and stirring makes it be uniformly dissolved;
(3) again system is passed through heating in water bath, Heating temperature is no more than 50 DEG C, then adds a certain amount of glucoamylase and α-amylase successively, and stirring makes abundant reaction;
(4) add a certain amount of pentanedioic acid, and stirring makes abundant reaction;
(5), more successively with acetone cleaning, washing, filter;
(6) last vacuum-drying, gets product.
Preferentially, step (1) in, water bath heating temperature is 70-80 DEG C.
Preferentially, step (2) in, the amount of the sodium lauryl sulphate of interpolation and the ratio of W-Gum are 1mL:5g.
Preferentially, step (3) in, the glucoamylase of interpolation and the mass ratio of α-amylase are 1:1.
Preferentially, step (3) in, system Heating temperature is 35-45 DEG C, and the reaction times is 5-10h.
Preferentially, step (4) in, the amount of the pentanedioic acid of interpolation and the ratio of W-Gum are 1mL:100g.
Preferentially, step (6) in, vacuum-drying temperature is no more than 70 DEG C.
The present invention has following advantages and characteristic:
(1) the porous-starch specific surface area prepared is large, good stability;
(2) preparation technology is simple;
(3) abundant raw material, cheap.
Embodiment
Embodiment one:
Get 5g W-Gum and put into beaker, add 100ml distilled water, being positioned over one is equipped with in machine mixer water bath heating device, heating and temperature control is at 70 DEG C, start agitator, until solution becomes transparent rear stopping heating, when system is cooled to room temperature, 1mL sodium lauryl sulphate is added again in container, and stirring makes it be uniformly dissolved, system is heated, when temperature reaches 45 DEG C, add 0.05 glucoamylase and 0.05 α-amylase, and stirring makes fully, after reaction 5h, add the pentanedioic acid of 0.05g again, after stirring makes it fully, then pour in acetone, precipitation washes with water, be placed on vacuum-drying in 70 DEG C of environment, get product.
Embodiment two:
Get 10g W-Gum and put into beaker, add 200ml distilled water, being positioned over one is equipped with in machine mixer water bath heating device, heating and temperature control is at 75 DEG C, start agitator, until solution becomes transparent rear stopping heating, when system is cooled to room temperature, 2mL sodium lauryl sulphate is added again in container, and stirring makes it be uniformly dissolved, system is heated, when temperature reaches 40 DEG C, add 0.1 glucoamylase and 0.1 α-amylase, and stirring makes fully, after reaction 5h, add the pentanedioic acid of 0.1g again, after stirring makes it fully, then pour in acetone, precipitation washes with water, be placed on vacuum-drying in 65 DEG C of environment, get product.
Embodiment three:
Get 20g W-Gum and put into beaker, add 300ml distilled water, being positioned over one is equipped with in machine mixer water bath heating device, heating and temperature control is at 80 DEG C, start agitator, until solution becomes transparent rear stopping heating, when system is cooled to room temperature, 4mL sodium lauryl sulphate is added again in container, and stirring makes it be uniformly dissolved, system is heated, when temperature reaches 35 DEG C, add 0.05 glucoamylase and 0.05 α-amylase, and stirring makes fully, after reaction 10h, add the pentanedioic acid of 0.2g again, after stirring makes it fully, then pour in acetone, precipitation washes with water, be placed on vacuum-drying in 60 DEG C of environment, get product.
Claims (7)
1. a preparation method for corn-based porous-starch, is characterized in that, this preparation method comprises the steps:
(1) get a certain amount of W-Gum, add appropriate distilled water, be placed in water-bath and heat, Heating temperature is no more than 80 DEG C, and constantly stirs with agitator, until solution is transparent;
(2) be then cooled to room temperature, then add appropriate sodium lauryl sulphate, and stirring makes it be uniformly dissolved;
(3) again system is passed through heating in water bath, Heating temperature is no more than 50 DEG C, then adds a certain amount of glucoamylase and α-amylase successively, and stirring makes abundant reaction;
(4) add a certain amount of pentanedioic acid, and stirring makes abundant reaction;
(5), more successively with acetone cleaning, washing, filter;
(6) last vacuum-drying, gets product.
2. the preparation method of a kind of corn-based porous-starch according to claim 1, is characterized in that, step (1) in, water bath heating temperature is 70-80 DEG C.
3. the preparation method of a kind of corn-based porous-starch according to claim 1, is characterized in that, step (2) in, the amount of the sodium lauryl sulphate of interpolation and the ratio of W-Gum are 1mL:5g.
4. the preparation method of a kind of corn-based porous-starch according to claim 1, is characterized in that, step (3) in, the glucoamylase of interpolation and the mass ratio of α-amylase are 1:1.
5. the preparation method of a kind of corn-based porous-starch according to claim 1, is characterized in that, step (3) in, system Heating temperature is 35-45 DEG C, and the reaction times is 5-10h.
6. the preparation method of a kind of corn-based porous-starch according to claim 1, is characterized in that, step (4) in, the amount of the pentanedioic acid of interpolation and the ratio of W-Gum are 1mL:100g.
7. the preparation method of a kind of corn-based porous-starch according to claim 1, is characterized in that, step (6) in, vacuum-drying temperature is no more than 70 DEG C.