CN105440777A - 一种新型环保油墨的制备方法 - Google Patents
一种新型环保油墨的制备方法 Download PDFInfo
- Publication number
- CN105440777A CN105440777A CN201510952496.7A CN201510952496A CN105440777A CN 105440777 A CN105440777 A CN 105440777A CN 201510952496 A CN201510952496 A CN 201510952496A CN 105440777 A CN105440777 A CN 105440777A
- Authority
- CN
- China
- Prior art keywords
- parts
- printing ink
- novel environment
- preparation
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种新型环保油墨的制备方法,由以下重量份数比配置而成,包括;15~20份大豆油,5~10份氢氧化铝,4~8份玉米淀粉,10~15份颜料,10~20份卡诺巴蜡,15~30份硫酸钡,8~14份醇酸树脂,3~6份甘油松香酯,6~15份桐油。本发明使用玉米淀粉作为防反印剂,它的作用是防止印刷油墨层反印到纸张背面,以保证印刷质量。本发明将甘油松香酯引入油墨体系,这是由于单独由干性油制成的油型连结料分子量小,固着速度慢,光泽不好,乳化易严重,所以,将甘油松香酯引入油墨的连结料中,连结料的各项性能得到了重大改善。
Description
技术领域
本发明涉及一种新型环保油墨的制备方法。
背景技术
油墨是用于包装材料印刷的重要材料,它通过印刷将图案、文字表现在承印物上油墨中包括主要成分和辅助成分,它们均匀地混合并经反复轧制而成一种粘性胶状流体。由颜料、连结料和助剂等组成。用于书刊、包装装潢、建筑装饰等各种印刷。随着社会需求增大,油墨品种和产量也相应扩展和增长。
但是传统油墨易退色,掉色不易清洗,含有矿物油、化学助剂等与人体不适合的成分,在日前人们对环保型产品的需求与日俱增的趋势下,在儿童书籍、学校、医院等很多场合下都需要使用环保型油墨。
发明内容
本发明的目的在于:针对现有技术中存在的上述技术问题,提供一种无毒,不污染环境,对人体无害,掉色容易清洗的环保油墨及其制备方法。
本发明是通过以下技术方案实现的:
一种新型环保油墨的制备方法,其具体步骤如下:
(1)将15~20份大豆油,5~10份氢氧化铝,4~8份玉米淀粉在常温下混合搅拌均匀;
(2)将10~15份颜料,10~20份卡诺巴蜡,15~30份硫酸钡,8~14份醇酸树脂在常温下混合搅拌均匀;
(3)将步骤(1)和步骤(2)得出的产品倒入搅拌桶中,加入3~6份甘油松香酯和6~15份桐油后慢慢搅拌,逐渐从0℃升到20℃即可制得所述的环保油墨。
进一步,所述的步骤(2)中加入包括3~5份TX-10,5~7份亚麻油混合搅拌均匀。
综上所述,由于采用了上述技术方案,本发明的有益效果是:本发明使用玉米淀粉作为防反印剂,它的作用是防止印刷油墨层反印到纸张背面,以保证印刷质量。本发明将甘油松香酯引入油墨体系,这是由于单独由干性油制成的油型连结料分子量小,固着速度慢,光泽不好,乳化易严重,所以,将甘油松香酯引入油墨的连结料中,连结料的各项性能得到了重大改善。
具体实施方式
本说明书中公开的所有特征,或公开的所有方法或过程中的步骤,除了互相排斥的特征和/或步骤以外,均可以以任何方式组合。
本说明书(包括任何附加权利要求和摘要)中公开的任一特征,除非特别叙述,均可被其他等效或具有类似目的的替代特征加以替换。即,除非特别叙述,每个特征只是一系列等效或类似特征中的一个例子而已。
一种新型环保油墨,由以下重量份数比配置而成,包括;15~20份大豆油,5~10份氢氧化铝,4~8份玉米淀粉,10~15份颜料,10~20份卡诺巴蜡,15~30份硫酸钡,8~14份醇酸树脂,3~6份甘油松香酯,6~15份桐油。
进一步,还包括3~5份TX-10,5~7份亚麻油。
进一步,所述的颜料为无机颜料。
进一步,所述的颜料为浅色颜料,所述的浅色颜料包括颜料黄、颜料蓝、颜料白、颜料橘黄。
进一步,所述的大豆油18份,氢氧化铝8份,玉米淀粉5份,颜料11份,卡诺巴蜡15份,硫酸钡20,醇酸树脂10,甘油松香酯5,桐油10份。
进一步,所述的TX-10为4份,亚麻油6份。
一种新型环保油墨的制备方法,其具体步骤如下:
(1)将15~20份大豆油,5~10份氢氧化铝,4~8份玉米淀粉在常温下混合搅拌均匀;
(2)将10~15份颜料,10~20份卡诺巴蜡,15~30份硫酸钡,8~14份醇酸树脂在常温下混合搅拌均匀;
(3)将步骤(1)和步骤(2)得出的产品倒入搅拌桶中,加入3~6份甘油松香酯和6~15份桐油后慢慢搅拌,逐渐从0℃升到20℃即可制得所述的环保油墨。
进一步,所述的步骤(2)中加入包括3~5份TX-10,5~7份亚麻油混合搅拌均匀。
以上所述的具体实施例,对本发明的目的、技术方案和有益效果进行了进一步详细说明,所应理解的是,以上所述仅为本发明的具体实施例而已,并不用于限制本发明。本发明扩展到任何在本说明书中披露的新特征或任何新的组合,以及披露的任一新的方法或过程的步骤或任何新的组合。
Claims (2)
1.一种新型环保油墨的制备方法,其特征在于,其具体步骤如下:
(1)将15~20份大豆油,5~10份氢氧化铝,4~8份玉米淀粉在常温下混合搅拌均匀;
(2)将10~15份颜料,10~20份卡诺巴蜡,15~30份硫酸钡,8~14份醇酸树脂在常温下混合搅拌均匀;
(3)将步骤(1)和步骤(2)得出的产品倒入搅拌桶中,加入3~6份甘油松香酯和6~15份桐油后慢慢搅拌,逐渐从0℃升到20℃即可制得所述的环保油墨。
2.根据权利要求1所述的新型环保油墨的制备方法,其特征在于,所述的步骤(2)中加入包括3~5份TX-10,5~7份亚麻油混合搅拌均匀。