CN105440688A - Low temperature-resistant inlet manifold resonant cavity - Google Patents
Low temperature-resistant inlet manifold resonant cavity Download PDFInfo
- Publication number
- CN105440688A CN105440688A CN201510931091.5A CN201510931091A CN105440688A CN 105440688 A CN105440688 A CN 105440688A CN 201510931091 A CN201510931091 A CN 201510931091A CN 105440688 A CN105440688 A CN 105440688A
- Authority
- CN
- China
- Prior art keywords
- intake manifold
- low temperature
- parts
- rubber
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a low temperature-resistant inlet manifold resonant cavity. The low temperature-resistant inlet manifold resonant cavity is prepared from low temperature-resistant rubber. The low temperature-resistant rubber comprises, by weight, 100 parts of silicone rubber, 50 parts of white carbon black, 4 parts of diphenylsilanediol, 2 parts of ferric oxide and 0.5-2 parts of dicumyl peroxide. The low temperature-resistant inlet manifold resonant cavity is prepared from low temperature-resistant rubber, has good physical and chemical performances and further improves equipment integral reliability and prolongs a service life.
Description
Technical field
The present invention relates to auto parts machinery field, particularly a kind of motor intake manifold.
Background technology
In China, the development of automobile industry and plastic manufacturing process is advanced by leaps and bounds, the engine fittings that metal makes are replaced by the engine fittings of the plastic production taking intake manifold as representative gradually, as one of the parts of engine most critical, intake manifold achieves in automobile industry and applies widely, its Core Feature is for each cylinder of engine provides full and uniform gas mixture, is the key factor affecting engine forces and oil consumption.
When automobile travels at the environment that temperature is very low, special picture waits very cold region northeastward, and rubber accessory flexibility decrease at low ambient temperatures brittle failure occurs, causes gas leak of the oil leakage etc., directly affect the safety traffic of automobile.
Therefore, how to replace existing metal to make motor intake manifold with suitable plastic material, improve the quality of rubber accessory in cold environment, have great importance.
Summary of the invention
For solving above-mentioned the deficiencies in the prior art, the present invention proposes a kind of low temperature resistant intake manifold resonator cavity.
Technical scheme of the present invention is achieved in that
A kind of low temperature resistant intake manifold resonator cavity, each intake manifold arm 3 upper end air throttle 1 is communicated with intake manifold resonator cavity 2, each air outlet, intake manifold arm 3 bottom is connected with each cylinder head respectively by joint flange 4, also comprise gas rail 5 and multiple gas rail connecting branch 6, gas rail connecting branch 6 and intake manifold arm 3 one_to_one corresponding, gas rail 5 is communicated with the lower end of each intake manifold arm 3 by gas rail connecting branch 6;
Described intake manifold resonator cavity 2 is made up of cold resistant rubber, and this cold resistant rubber contains following component and weight part: 100 parts, silicon rubber, white carbon black 50 parts, Diphenylsilanediol 4 parts, ferric oxide 2 parts, dicumyl peroxide 0.5-2 part.
The invention has the beneficial effects as follows:
(1) can be used in inside motor car engine, reduce the loss that low temperature environment causes rubber brittle rupture;
(2) improve reliability and the work-ing life of Whole Equipment further, automobile is driven safely.
Accompanying drawing explanation
In order to be illustrated more clearly in the embodiment of the present invention or technical scheme of the prior art, be briefly described to the accompanying drawing used required in embodiment or description of the prior art below, apparently, accompanying drawing in the following describes is only some embodiments of the present invention, for those of ordinary skill in the art, under the prerequisite not paying creative work, other accompanying drawing can also be obtained according to these accompanying drawings.
Fig. 1 is the Facad structure schematic diagram of the intake manifold adopting a kind of low temperature resistant intake manifold resonator cavity of the present invention.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
As shown in Figure 1, adopt the intake manifold of a kind of low temperature resistant intake manifold resonator cavity of the present invention, comprise motor intake manifold resonator cavity 1, intake manifold resonator cavity 2, multiple intake manifold arm 3 and joint flange 4, each intake manifold arm 3 upper end air throttle 1 is communicated with intake manifold resonator cavity 2, each air outlet, intake manifold arm 3 bottom is connected with each cylinder head respectively by joint flange 4, also comprise gas rail 5 and multiple gas rail connecting branch 6, gas rail connecting branch 6 and intake manifold arm 3 one_to_one corresponding, gas rail 5 is communicated with the lower end of each intake manifold arm 3 by gas rail connecting branch 6.
Described intake manifold resonator cavity 2 is made up of cold resistant rubber, and this cold resistant rubber contains following component and weight part: 100 parts, silicon rubber, white carbon black 50 parts, Diphenylsilanediol 4 parts, ferric oxide 2 parts, dicumyl peroxide 0.5-2 part.
Raw-silastic continuously
Silicon rubber has the performances such as excellent thermotolerance, winter hardiness, dielectricity, resistance to ozone and resistance to atmospheric aging, the outstanding performance of silicon rubber is that use temperature is broad, can at-60 DEG C (or lower temperature) to+250 DEG C (or higher temperature) life-time service.Silicon rubber can be divided into heat vulcanized silicone rubber and room temperature vulcanized sili cone rubber two class by its vulcanization characteristics.Universal, super low-temperature resistant type, thermostable type, high-tenacity type, oil-resisting type, medical type etc. can be divided into by the difference of character and utilization.By the difference of monomer used, methyl vinyl silicone rubber can be divided into, methyl phenyl vinyl silicone rubber, fluorine silicon, nitrile silicone rubber etc.
In order to reach cold tolerance of the present invention, present invention employs phenyl siloxane rubber rubber.
White carbon black
White carbon black is the general name of white powder X-ray amorphous silicic acid and silicate product, mainly refers to precipitated silica, aerosil, superfine silicon dioxide gel and aerogel, also comprises Powdered synthetic aluminium silicate and Calucium Silicate powder etc.White carbon black is porous material, and it forms available SiO
2nH
2o represents, wherein nH
2o exists with the form of surface hydroxyl.Caustic alkali and hydrofluoric acid can be dissolved in, water insoluble, solvent and acid (except hydrofluoric acid).High temperature resistant, do not fire, tasteless, odorless, there is good electrical insulating property.
Preferably, described white carbon black belongs to precipitated silica, and building-up process is as follows:
Adopt water glass solution and acid-respons, obtain white carbon black through precipitation, filtration, washing, drying and calcining.Reaction formula is: Na
2siO
3+ 2H+-> white carbon black+2Na++H
20
Cold-resistant component
Cold-resistant component of the present invention comprises:
Diphenylsilanediol 4
Ferric oxide 2
Low temperature resistant intake manifold resonator cavity of the present invention adopts cold resistant rubber to make, and has good physics, chemical property, improves the reliability of overall equipment further.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. a low temperature resistant intake manifold resonator cavity, each intake manifold arm (3) upper end air throttle (1) is communicated with intake manifold resonator cavity (2), each intake manifold arm (3) air outlet, bottom is connected with each cylinder head respectively by joint flange (4), also comprise gas rail (5) and multiple gas rail connecting branch (6), gas rail connecting branch (6) and intake manifold arm (3) one_to_one corresponding, gas rail (5) is communicated with by the lower end of gas rail connecting branch (6) with each intake manifold arm (3); It is characterized in that,
Described intake manifold resonator cavity (2) is made up of cold resistant rubber, and this cold resistant rubber contains following component and weight part: 100 parts, silicon rubber, white carbon black 50 parts, Diphenylsilanediol 4 parts, ferric oxide 2 parts, dicumyl peroxide 0.5-2 part.
2. low temperature resistant intake manifold resonator cavity according to claim 1, is characterized in that, described silicon rubber is phenyl siloxane rubber.
3. low temperature resistant intake manifold resonator cavity according to claim 1, is characterized in that, described white carbon black is precipitated silica.