CN105440466A - CPE-based degradable plastic - Google Patents
CPE-based degradable plastic Download PDFInfo
- Publication number
- CN105440466A CN105440466A CN201510977892.5A CN201510977892A CN105440466A CN 105440466 A CN105440466 A CN 105440466A CN 201510977892 A CN201510977892 A CN 201510977892A CN 105440466 A CN105440466 A CN 105440466A
- Authority
- CN
- China
- Prior art keywords
- parts
- cpe
- degradable plastic
- plastic
- lubricant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses CPE-based degradable plastic, and is characterized in that: the plastic comprises the following components in parts by weight: 50-80 parts of a master batch, 40-80 parts of modified starch, 1-3 parts of a pigment, and 2-4 parts of an auxiliary agent. The master batch is CPE plastic. The auxiliary agent comprises the following components: 10-15 parts of lubricant; 20-40 parts of a plasticizer, and 5-10 parts of an anti-oxidant. The lubricant is selected from one of barium stearate, fatty acid amide and glyceryl monostearate. The plasticizer is one of DEHP, DOP and DBP. The anti-oxidant is anti-oxidant 1010 or anti-oxidant TNP. The CPE-based degradable plastic has better mechanical properties and good stability, harmful substances are not easy to emit in usage process, and the plastic can be widely applied to the fields of food package and life.
Description
Technical field
The present invention relates to a kind of CPE base degradable plastic.
Background technology
Degradable plastics refers to and adds some auxiliary agents promoting it to degrade in the plastic or adopt reproducible natural matter to manufacture, application performance requirement can be met in use and preservation period, and after using under certain environmental conditions, within a short period of time can there is considerable change in its chemical structure, and cause some character to lose, or during synthesis, just there are class plastics of degradation property.Degradable plastics has very important effect in the white pollution problems solving globalization.
Degradable plastics is as multifunctional novel technologic material, and range of application is wide, and market potential is very big.According to pertinent data display, the consumption of biological degradation polyalcohol in 2000 accounts for about 2% of plastics total amount consumed, and consumption reaches about 4,000,000 ~ 5,000,000 t.The U.S. reaches 900,000 t in 2000, and Novon company of the U.S. has established the starch base polymeric material factory of 4.5 ten thousand t/a; Japan's degradative plastics actual market scale in 2000 reaches 200,000 t, and Japanese Showa Polymer Company has established the saturated alkyl system in polyester production of 500t/a.
Domestic also have tens of enterprises to plan to build or built starch base or natural fiber base (comprising paper pulp) production line, as: Changchun establishes sino-america joint-venture enterprise, produces 6000t starch-based material per year; Wuhan, Hubei " green " group plans to build joint venture, produces the mess-tin (tool) of sweet potato starch base; Shanghai Shi Run industrial corporation invests millions of unit and is building fiber base mess-tin factory based on bagasse; Granary, Jiangsu is big to be reached (in newly joint) corporate investment 1,000 ten thousand yuan, built fiber base production line; It is the production line of main raw material that spark development area, Shanghai spark papermaking company builds with paper pulp, produces 20,000 disposable tablewares daily; Shanghai Li Jun composite table-ware factory invests 3,000,000 yuan, the production equipment that to build with flour product factory pin material be raw material production disposable tableware.
Current degradable plastics Problems existing is mainly expensive, and be difficult to utilization and extention, starch-filled plastic falls and do not understand, and biodegradable plastic aftertreatment needs comprehensive compost construction; In addition, degradable plastics self-technique as more reasonably technical recipe, accurately controlled degradation, need to improve further with rear fast degradation, the thoroughly recovery and utilization technology etc. of degradation property and scrap stock and perfect.The definition that degraded by environment polymer is still ununified so far in the world and set up unified Test model synthetic techniques, identifier and Product checking standard completely, causes its technical market, produce market more chaotic.In addition, the current research of degradable plastics is degraded to master still with fluoropolymer resin, and majority fails the factor of auxiliary agent to take into account; Except complete biodegradable plastics, the middle degraded product impact on animal, plant of all the other various degradable plasticss in degradation process not yet can be evaluated etc.
Summary of the invention
The object of this invention is to provide a kind of mechanical property good, the strong and plastic material of easily degraded of stability.
The present invention is achieved through the following technical solutions:
A kind of CPE base degradable plastic, is characterized in that, comprise following component by weight: masterbatch 50-80 part; Treated starch 40-80 part; Pigment 1-3 part; Auxiliary agent 2-4 part.
Described masterbatch is CPE plastics.
Described auxiliary agent comprises following component by weight: lubricant 10-15 part; Softening agent 20-40 part; Oxidation inhibitor 5-10 part.
Described lubricant is the one in barium stearate, fatty acid amide, glyceryl monostearate.
Described softening agent is the one in DEHP, DOP, DBP.
Described oxidation inhibitor is antioxidant 1010 or antioxidant TNP.
The invention has the beneficial effects as follows: the present invention has stronger mechanical property and satisfactory stability, in use not easily distributes objectionable impurities, food product pack and sphere of life can be widely used in.
Embodiment
Embodiment 1
A kind of CPE base degradable plastic, is characterized in that, comprise following component by weight: masterbatch 80 parts; Treated starch 80 parts; Pigment 3 parts; Auxiliary agent 4 parts.
Masterbatch is CPE plastics.
Auxiliary agent comprises following component by weight: lubricant 10 parts; 20 parts, softening agent; 5 parts, oxidation inhibitor.
Lubricant is barium stearate.
Softening agent is DEHP.
Oxidation inhibitor is antioxidant 1010.
Embodiment 2
A kind of CPE base degradable plastic, is characterized in that, comprise following component by weight: masterbatch 50 parts; Treated starch 40 parts; Pigment 1 part; Auxiliary agent 2 parts.
Masterbatch is CPE plastics.
Auxiliary agent comprises following component by weight: lubricant 15 parts; 40 parts, softening agent; 10 parts, oxidation inhibitor.
Lubricant is fatty acid amide.
Softening agent is DBP.
Oxidation inhibitor is antioxidant 1010.
Embodiment 3
A kind of CPE base degradable plastic, is characterized in that, comprise following component by weight: masterbatch 60 parts; Treated starch 60 parts; Pigment 2 parts; Auxiliary agent 3 parts.
Masterbatch is CPE plastics.
Auxiliary agent comprises following component by weight: lubricant 12 parts; 30 parts, softening agent; 8 parts, oxidation inhibitor.
Lubricant is glyceryl monostearate.
Softening agent is DOP.
Oxidation inhibitor is antioxidant TNP.
The present invention has stronger mechanical property and satisfactory stability, in use not easily distributes objectionable impurities, can be widely used in food product pack and sphere of life.
Although above-mentioned, the specific embodiment of the present invention is described; but not limiting the scope of the invention; on the basis of technical scheme of the present invention, those skilled in the art do not need to pay various amendment or distortion that creative work can make still within protection scope of the present invention.
Claims (6)
1. a CPE base degradable plastic, is characterized in that, comprises following component by weight: masterbatch 50-80 part; Treated starch 40-80 part; Pigment 1-3 part; Auxiliary agent 2-4 part.
2. a kind of CPE base degradable plastic according to claim 1, is characterized in that: described masterbatch is CPE plastics.
3. a kind of CPE base degradable plastic according to claim 1, is characterized in that: described auxiliary agent comprises following component by weight: lubricant 10-15 part; Softening agent 20-40 part; Oxidation inhibitor 5-10 part.
4. a kind of CPE base degradable plastic according to claim 3, is characterized in that: described lubricant is the one in barium stearate, fatty acid amide, glyceryl monostearate.
5. a kind of CPE base degradable plastic according to claim 3, is characterized in that: described softening agent is the one in DEHP, DOP, DBP.
6. a kind of CPE base degradable plastic according to claim 3, is characterized in that: described oxidation inhibitor is antioxidant 1010 or antioxidant TNP.