CN105419442A - Self-cleaning material - Google Patents
Self-cleaning material Download PDFInfo
- Publication number
- CN105419442A CN105419442A CN201510897311.7A CN201510897311A CN105419442A CN 105419442 A CN105419442 A CN 105419442A CN 201510897311 A CN201510897311 A CN 201510897311A CN 105419442 A CN105419442 A CN 105419442A
- Authority
- CN
- China
- Prior art keywords
- parts
- self
- cleaning material
- hydrochloric acid
- tensio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a self-cleaning material. The self-cleaning material consists of the following components in parts by weight: 30-50 parts of ethyl orthosilicate, 15-25 parts of anhydrous ethanol, 1-5 parts of a surfactant, 1-5 parts of essential oil, 1-5 parts of a curing agent and 1-5 parts of hydrochloric acid solution. The self-cleaning material provided by the invention has an effect of sterilization, and can purify the air at the same time; and therefore, a product prepared by using the self-cleaning material disclosed by the invention is excellent in performance and is an environment-friendly product.
Description
Technical field
The present invention relates to Material Field, particularly relate to a kind of self-cleaning material.
Background technology
In recent years, people get more and more for the concern of air-conditioning air intake Air quality, and general cystose and the aluminium foil compound of adopting makes sandwich board in ventilation duct of air conditioner, air in existing ventilating duct for air-conditioner is not owing to upgrading timely and effectively and sterilizing, can not automatically cleaning be carried out, IAQ (indoor air quality) can be caused to be deteriorated.
Therefore, prior art also needs to further develop and improve.
Summary of the invention
The object of the present invention is to provide a kind of self-cleaning material, be intended to solve the single problem of current self-cleaning material function.
Technical scheme of the present invention is as follows:
A kind of self-cleaning material, wherein, described self-cleaning material is composed of the following components according to parts by weight:
Tetraethoxy 30-50 part;
Dehydrated alcohol 15-25 part;
Tensio-active agent 1-5 part;
Essential oil 1-5 part;
Solidifying agent 1-5 part;
Hydrochloric acid soln 1-5 part.
Described self-cleaning material, wherein, described tensio-active agent is tween-80 and the silicone oil parts by weight proportioning according to 1:1.
Described self-cleaning material, wherein, described solidifying agent is toluenesulphonic acids.
Described self-cleaning material, wherein, the pH of described hydrochloric acid soln is 2.
Described self-cleaning phenolic foam material, wherein, described self-cleaning material is composed of the following components according to parts by weight:
Tetraethoxy 40 parts;
Dehydrated alcohol 20 parts;
5 parts, tensio-active agent;
Essential oil 1 part;
1 part, solidifying agent;
Hydrochloric acid soln 1 part.
Beneficial effect: the invention provides a kind of self-cleaning material, material of the present invention has effect of disinfection, can purify air simultaneously, and the product performance thus utilizing self-cleaning material of the present invention to prepare well are superior and be environmentally friendly product.
Embodiment
For making object of the present invention, technical scheme and advantage clearly, clearly, the present invention is described in more detail below.
The invention provides a kind of self-cleaning material, wherein, described self-cleaning material is composed of the following components according to parts by weight:
Tetraethoxy 30-50 part;
Dehydrated alcohol 15-25 part;
Tensio-active agent 1-5 part;
Essential oil 1-5 part;
Solidifying agent 1-5 part;
Hydrochloric acid soln 1-5 part.
Wherein, described tensio-active agent is tween-80 and the silicone oil parts by weight proportioning according to 1:1.In specific embodiment, described solidifying agent is toluenesulphonic acids.Preferably, the pH of described hydrochloric acid soln is 2.
Explanation technical solution of the present invention is explained further below by embodiment
Embodiment 1
Described self-cleaning phenolic foam material, wherein, described self-cleaning material is composed of the following components according to parts by weight:
Tetraethoxy 40 parts;
Dehydrated alcohol 20 parts;
5 parts, tensio-active agent;
Essential oil 1 part;
1 part, solidifying agent;
Hydrochloric acid soln 1 part.
Wherein, described tensio-active agent is tween-80 and the silicone oil parts by weight proportioning according to 1:1.In specific embodiment, described solidifying agent is toluenesulphonic acids.Preferably, the pH of described hydrochloric acid soln is 2.
Its preparation process is: according to described composition of raw materials consumption, fully stir under room temperature, foams 20 minutes in 80-95 DEG C of environment, obtained finished product.
Embodiment 2
Described self-cleaning material is composed of the following components according to parts by weight:
Tetraethoxy 30-50 part;
Dehydrated alcohol 15-25 part;
Tensio-active agent 1-5 part;
Essential oil 1-5 part;
Solidifying agent 1-5 part;
Hydrochloric acid soln 1-5 part.
Wherein, described tensio-active agent is tween-80 and the silicone oil parts by weight proportioning according to 1:1.In specific embodiment, described solidifying agent is toluenesulphonic acids.Preferably, the pH of described hydrochloric acid soln is 2.
Its preparation process is: according to described composition of raw materials consumption, fully stir under room temperature, foams 20 minutes in 80-95 DEG C of environment, obtained finished product.
The invention provides a kind of self-cleaning material, material of the present invention has effect of disinfection, can purify air simultaneously, and the product performance thus utilizing self-cleaning material of the present invention to prepare well are superior and be environmentally friendly product.
Should be understood that, application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can be improved according to the above description or convert, and all these improve and convert the protection domain that all should belong to claims of the present invention.
Claims (5)
1. a self-cleaning material, is characterized in that: described self-cleaning material is composed of the following components according to parts by weight:
Tetraethoxy 30-50 part;
Dehydrated alcohol 15-25 part;
Tensio-active agent 1-5 part;
Essential oil 1-5 part;
Solidifying agent 1-5 part;
Hydrochloric acid soln 1-5 part.
2. self-cleaning material according to claim 1, is characterized in that, described tensio-active agent is tween-80 and the silicone oil parts by weight proportioning according to 1:1.
3. self-cleaning material according to claim 1, is characterized in that, described solidifying agent is toluenesulphonic acids.
4. self-cleaning material according to claim 1, is characterized in that, the pH of described hydrochloric acid soln is 2.
5. self-cleaning material according to claim 1, is characterized in that, described self-cleaning material is composed of the following components according to parts by weight:
Tetraethoxy 40 parts;
Dehydrated alcohol 20 parts;
5 parts, tensio-active agent;
Essential oil 1 part;
1 part, solidifying agent;
Hydrochloric acid soln 1 part.