CN105419401A - Modified production method for titanium dioxide pigment of composite high-molecular polymers - Google Patents
Modified production method for titanium dioxide pigment of composite high-molecular polymers Download PDFInfo
- Publication number
- CN105419401A CN105419401A CN201510787729.2A CN201510787729A CN105419401A CN 105419401 A CN105419401 A CN 105419401A CN 201510787729 A CN201510787729 A CN 201510787729A CN 105419401 A CN105419401 A CN 105419401A
- Authority
- CN
- China
- Prior art keywords
- parts
- titanium dioxide
- dioxide pigment
- wetting agent
- producing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a modified production method for titanium dioxide pigment of composite high-molecular polymers. The method includes the steps of adding 10-50 parts of water to 100 parts of rutile type titanium dioxide to be evenly stirred into a sizing agent, sequentially adding 5-12 parts of bentonite SD-2, 5-15 parts of polyester polymers and 2-7 parts of aluminium oxide powder to be evenly stirred, sequentially adding 1-5 parts of methyl alcohol, 1-3 parts of wetting agent and 1-3 parts of chloridized propylene epoxide to be stirred and react for 0.5-2 h, and conducting filtering, stoving, drying and grinding. The titanium dioxide pigment is applied to paint, the rheology state of titanium dioxide pigment in a paint solution can be obviously improved, and the dispersion performance of titanium dioxide pigment can be improved; meanwhile, the light stability of titanium dioxide pigment is higher, and titanium dioxide pigment has higher weather resistance.
Description
Technical field
The invention belongs to technical field of chemistry and chemical engineering, particularly relate to the modified formula technology of titanium dioxide white pigment.
Background technology
Pigment, as the coloring matter decorated and protect, can be applied in each fields such as ink, plastics, rubber, coating, papermaking with dispersion state.White opaque pigment is based on titanium pigment, and excellent is important selection with R type titanium dioxide.But titanium dioxide light stability difference common is at present easy to change, disperse bad in solvent dispersion simultaneously, and pulverize easily caking, tinting strength and opacifying power need to improve.
Summary of the invention
Goal of the invention: for above-mentioned existing Problems existing and deficiency, the object of this invention is to provide a kind of titanium white powder pigment modified producing method of compound macromolecular polymer, be applied in coating and obviously can improve its rheology in coating solution and improve its dispersing property, its light stability is stronger simultaneously, has higher weathering resistance.
Technical scheme: for achieving the above object, the present invention is by the following technical solutions: a kind of titanium white powder pigment modified producing method of compound macromolecular polymer, the water of 10 ~ 50 parts is added and the formation slurry that stirs in 100 parts of Rutile type Titanium Dioxides, then the wilkinite SD-2 of 5 ~ 12 parts is added successively, the polyester polymers of 5 ~ 15 parts, the aluminium sesquioxide powder of 2 ~ 7 parts also stirs, then the methyl alcohol of 1 ~ 5 part is added successively, the chlorination propylene oxide of the wetting agent of 1 ~ 3 part and 1 ~ 3 part, and stirring reaction 0.5 ~ 2h, eventually pass filtration, dry, drying and grinding, .
As preferably, described polyester polymers is polyethylene, polyvinyl chloride, or the multipolymer of polyethylene and vinyl acetate between to for plastic.
As preferably, described wetting agent is naphthenic acid zinc salt, sodium laurylsulfonate or dodecyl stearate.
Beneficial effect: compared with prior art, the present invention has the following advantages: methyl alcohol carries out trace as polar solvent and introduces the formation that can impel wilkinite and titanium dioxide colloidal dispersion, simultaneously aluminium sesquioxide carries out to titanium dioxide the light stability that adsorption type surface treatment is conducive to pigment, the introducing of acid or alkali formula polyester polymers surface of pigments can form the charge adsorption thicker coating layer of formation thus the stronger dispersion agent of conduct and anti-flocculation agent again, amide compound and wetting agent and titanium dioxide surface generation organic adsorption can prevent pigment from again luming, be beneficial to dispersion, thus improve dispersiveness and the tinting strength of titanium dioxide.
Embodiment
Below in conjunction with specific embodiment, illustrate the present invention further, these embodiments should be understood only be not used in for illustration of the present invention and limit the scope of the invention, after having read the present invention, the amendment of those skilled in the art to the various equivalent form of value of the present invention has all fallen within the application's claims limited range.
Embodiment 1
First in the Rutile type Titanium Dioxide of 100 weight parts, the water of 25 parts is added and high-speed stirring dispersion forms slurry, then drop into 10 parts of wilkinite SD-2 and 5 part aluminium sesquioxides and stir, finally drop into the methyl alcohol of the naphthenic acid zinc salt wetting agent of 2 parts, 5 polyethylene, 5 parts of acrylamides and 2 parts, after stirring reaction 2h, through filter pulp, and naturally dry or dry at 40 ~ 60 DEG C, final drying abrasive dust.
Embodiment 2
First in the Rutile type Titanium Dioxide of 100 weight parts, the water of 25 parts is added and high-speed stirring dispersion forms slurry, then drop into 10 parts of wilkinite SD-2 and 5 part aluminium sesquioxides and stir, finally drop into the methyl alcohol of the naphthenic acid zinc salt wetting agent of 1 part, 5 polyvinyl chloride, 5 parts of acrylamides and 2 parts, after stirring reaction 2h, through filter pulp, and naturally dry or dry at 40 ~ 60 DEG C, final drying abrasive dust.
Claims (3)
1. the titanium white powder pigment modified producing method of a compound macromolecular polymer, it is characterized in that: in 100 parts of Rutile type Titanium Dioxides, add the water of 10 ~ 50 parts and the formation slurry that stirs, then the wilkinite SD-2 of 5 ~ 12 parts, the polyester polymers of 5 ~ 15 parts, the aluminium sesquioxide powder of 2 ~ 7 parts stirring is added successively, then the chlorination propylene oxide of the methyl alcohol of 1 ~ 5 part, the wetting agent of 1 ~ 3 part and 1 ~ 3 part is added successively, and stirring reaction 0.5 ~ 2h, eventually pass filtration, oven dry, dry and grinding.
2. the titanium white powder pigment modified producing method of compound macromolecular polymer according to claim 1, is characterized in that: described polyester polymers is polyethylene, polyvinyl chloride, or the multipolymer of polyethylene and vinyl acetate between to for plastic.
3. the titanium white powder pigment modified producing method of compound macromolecular polymer according to claim 1, is characterized in that: described wetting agent is naphthenic acid zinc salt, sodium laurylsulfonate or dodecyl stearate.