CN105419165A - Cable filling material with water resistant effect - Google Patents
Cable filling material with water resistant effect Download PDFInfo
- Publication number
- CN105419165A CN105419165A CN201511006569.XA CN201511006569A CN105419165A CN 105419165 A CN105419165 A CN 105419165A CN 201511006569 A CN201511006569 A CN 201511006569A CN 105419165 A CN105419165 A CN 105419165A
- Authority
- CN
- China
- Prior art keywords
- parts
- filling material
- water resistant
- resistant effect
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Provided is a cable filling material with a water resistant effect. The cable filling material is prepared from the following raw materials, by weight, 35-42 parts of PVC resin powder, 1.6-3.2 parts of dioctyl phthalate, 0.6-0.9 part of anti-oxidant 300, 12-20 parts of composite filling material, 4-8 parts of antimonous oxide, 10-15 parts of vulcanizing auxiliary agent, 13-17 parts of magnesium hydroxide, 2-4 parts of carbon black, 12-16 parts of zinc oxide, 2-4 parts of nano zeolite molecular sieves, 6-10 parts of cupric nitrate, 5-9 parts of sodium aluminate, 6-8 parts of high-density polypropylene, 3-6 parts of water resistant agent, 16-24 parts of paraffin, 7-13 parts of hollow glass beads, 3-4 parts of urotropine, 2-6 parts of molybdena and 14-17 parts of tributyl citrate. The beneficial effects are that the cable filling material with a water resistant effect has high intensity, high fatigue resistance and corrosion resistance, the water resistant effect is improved, a good flame retardant performance is achieved, and the cost is lowered.
Description
Technical field
The present invention relates to a kind of cable filler with block-water effect.
Background technology
Must possess can not cause detrimentally affect to insulated core as cable filler, material itself does not possess water absorbability, the feature such as not easily to shrink, do not corrode.Because the cable core of cable forms by many insulated wire cores are stranded, will inevitably produce gap in cabling process, if these gaps are filled closely knit without material, the cable core of cable not quietly, reduces the cable life-span in use.Along with the development of science and technology, cable is filled material water-proof material and is constantly carried out renewal and improve, but cable filler cost domestic is at present high, and block-water effect is not good, requires further improvement.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of cable filler with block-water effect, has high strength, high resistance to fatigue, erosion resistance, improves block-water effect, good flame retardant properties, and reduce cost.
For solving prior art problem, technical scheme provided by the invention is, a kind of cable filler with block-water effect, and it is made up of the raw material of following parts by weight:
PVC resin powder 35-42 part, dioctyl phthalate (DOP) 1.6-3.2 part, antioxidant 300 0.6-0.9 part, compounded mix 12-20 part, antimonous oxide 4-8 part, vulcanization aid 10-15 part, magnesium hydroxide 13-17 part, carbon black 2-4 part, zinc oxide 12-16 part, molecular sieve of Nano zeolite 2-4 part, cupric nitrate 6-10 part, sodium aluminate 5-9 part, high density poly propylene 6-8 part, waterproofing agent 3-6 part, paraffin 16-24 part, hollow glass microbead 7-13 part, urotropine 3-4 part, molybdenum oxide 2-6 part, tributyl citrate 14-17 part.
Further, a kind of cable filler with block-water effect, it is made up of the raw material of following parts by weight:
PVC resin powder 38 parts, dioctyl phthalate (DOP) 2.5 parts, antioxidant 300 0.75 part, compounded mix 15 parts, antimonous oxide 6 parts, vulcanization aid 13 parts, magnesium hydroxide 15 parts, carbon black 3 parts, 14 parts, zinc oxide, molecular sieve of Nano zeolite 3 parts, cupric nitrate 8 parts, sodium aluminate 7 parts, high density poly propylene 7 parts, waterproofing agent 4.5 parts, 20 parts, paraffin, hollow glass microbead 10 parts, urotropine 3.5 parts, molybdenum oxide 4 parts, tributyl citrate 15 parts.
The invention has the beneficial effects as follows: the cable filler with block-water effect of the present invention, there is high strength, high resistance to fatigue, erosion resistance, improve block-water effect, good flame retardant properties, and reduce cost.
Embodiment
embodiment 1
Have a cable filler for block-water effect, it is made up of the raw material of following parts by weight:
PVC resin powder 35 parts, dioctyl phthalate (DOP) 1.6 parts, antioxidant 300 0.6 part, compounded mix 12 parts, antimonous oxide 4 parts, vulcanization aid 10 parts, magnesium hydroxide 13 parts, carbon black 2 parts, 12 parts, zinc oxide, molecular sieve of Nano zeolite 2 parts, cupric nitrate 6 parts, sodium aluminate 5 parts, high density poly propylene 6 parts, waterproofing agent 3 parts, 16 parts, paraffin, hollow glass microbead 7 parts, urotropine 3 parts, molybdenum oxide 2 parts, tributyl citrate 14 parts.
embodiment 2
Have a cable filler for block-water effect, it is made up of the raw material of following parts by weight:
PVC resin powder 42 parts, dioctyl phthalate (DOP) 3.2 parts, antioxidant 300 0.9 part, compounded mix 20 parts, antimonous oxide 8 parts, vulcanization aid 15 parts, magnesium hydroxide 17 parts, carbon black 4 parts, 16 parts, zinc oxide, molecular sieve of Nano zeolite 4 parts, cupric nitrate 10 parts, sodium aluminate 9 parts, high density poly propylene 8 parts, waterproofing agent 6 parts, 24 parts, paraffin, hollow glass microbead 13 parts, urotropine 4 parts, molybdenum oxide 6 parts, tributyl citrate 17 parts.
embodiment 3
Have a cable filler for block-water effect, it is made up of the raw material of following parts by weight:
PVC resin powder 38 parts, dioctyl phthalate (DOP) 2.5 parts, antioxidant 300 0.75 part, compounded mix 15 parts, antimonous oxide 6 parts, vulcanization aid 13 parts, magnesium hydroxide 15 parts, carbon black 3 parts, 14 parts, zinc oxide, molecular sieve of Nano zeolite 3 parts, cupric nitrate 8 parts, sodium aluminate 7 parts, high density poly propylene 7 parts, waterproofing agent 4.5 parts, 20 parts, paraffin, hollow glass microbead 10 parts, urotropine 3.5 parts, molybdenum oxide 4 parts, tributyl citrate 15 parts.
Claims (2)
1. there is a cable filler for block-water effect, it is characterized in that: it is made up of the raw material of following parts by weight:
PVC resin powder 35-42 part, dioctyl phthalate (DOP) 1.6-3.2 part, antioxidant 300 0.6-0.9 part, compounded mix 12-20 part, antimonous oxide 4-8 part, vulcanization aid 10-15 part, magnesium hydroxide 13-17 part, carbon black 2-4 part, zinc oxide 12-16 part, molecular sieve of Nano zeolite 2-4 part, cupric nitrate 6-10 part, sodium aluminate 5-9 part, high density poly propylene 6-8 part, waterproofing agent 3-6 part, paraffin 16-24 part, hollow glass microbead 7-13 part, urotropine 3-4 part, molybdenum oxide 2-6 part, tributyl citrate 14-17 part.
2. the cable filler with block-water effect according to claim 1, is characterized in that: it is made up of the raw material of following parts by weight:
PVC resin powder 38 parts, dioctyl phthalate (DOP) 2.5 parts, antioxidant 300 0.75 part, compounded mix 15 parts, antimonous oxide 6 parts, vulcanization aid 13 parts, magnesium hydroxide 15 parts, carbon black 3 parts, 14 parts, zinc oxide, molecular sieve of Nano zeolite 3 parts, cupric nitrate 8 parts, sodium aluminate 7 parts, high density poly propylene 7 parts, waterproofing agent 4.5 parts, 20 parts, paraffin, hollow glass microbead 10 parts, urotropine 3.5 parts, molybdenum oxide 4 parts, tributyl citrate 15 parts.