CN105418981A - Degradable environment-friendly material - Google Patents
Degradable environment-friendly material Download PDFInfo
- Publication number
- CN105418981A CN105418981A CN201510903792.8A CN201510903792A CN105418981A CN 105418981 A CN105418981 A CN 105418981A CN 201510903792 A CN201510903792 A CN 201510903792A CN 105418981 A CN105418981 A CN 105418981A
- Authority
- CN
- China
- Prior art keywords
- parts
- friendly material
- degradable environment
- coupling agent
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a degradable environment-friendly material which comprises, by weight parts, 20-50 parts of plant fiber starch, 15-30 parts of polypropylene glycol, 15-25 parts of polysorbate, 10-15 parts of glycerinum, 5-10 parts of poly-endoenzyme and polyhydroxybutyrate and 1-5 parts of coupling agent. The degradable environment-friendly material is good in mechanical intensity and plasticity and extensive in application, does not generate environment-damaging substances in the degrading process, meets the requirements of green degrading, and thus has extensive market prospects.
Description
Technical field
The present invention relates to degradation material field, particularly relate to a kind of degradable environment-friendly material.
Background technology
Although one time foam tableware brings convenience to the life of people, its difficult degradation, can cause serious white pollution to environment.Although there is the difficult degradation problem that some starch-based degrading materials solve expanded plastic and cause in recent years on the market, these degradable materials, due to bad mechanical strength, poor plasticity, thus can not be applied widely.
Therefore, prior art also needs to further develop and improve.
Summary of the invention
The object of the present invention is to provide a kind of degradable environment-friendly material, be intended to solve current degradable plastics poor plasticity, the problem of bad mechanical strength.
Technical scheme of the present invention is as follows:
A kind of degradable environment-friendly material, wherein, it is composed of the following components by weight:
Plant fiber starch 20-50 part;
POLYPROPYLENE GLYCOL 15-30 part;
Polysorbate 15-25 part;
Glycerine 10-15 part;
Poly-own endoenzyme and poly butyric ester 5-10 part;
Coupling agent 1-5 part.
Described degradable environment-friendly material, wherein, it is composed of the following components by weight:
Plant fiber starch 35 parts;
POLYPROPYLENE GLYCOL 25 parts;
Polysorbate 20 part;
Glycerine 12 parts;
Poly-own endoenzyme and poly butyric ester 10 parts;
Coupling agent 5 parts.
Described degradable environment-friendly material, wherein, described coupling agent is zirconium class coupling agent.
Beneficial effect: the invention provides a kind of degradable environment-friendly material, this mechanical strength is good, plasticity-strong, of many uses, and does not produce the material of welding in decomposition course, meets the requirement of green degraded, thus has wide market outlook.
Embodiment
For making object of the present invention, technical scheme and advantage clearly, clearly, the present invention is described in more detail below.
The invention provides a kind of degradable environment-friendly material, wherein, it is composed of the following components by weight:
Plant fiber starch 20-50 part;
POLYPROPYLENE GLYCOL 15-30 part;
Polysorbate 15-25 part;
Glycerine 10-15 part;
Poly-own endoenzyme and poly butyric ester 5-10 part;
Coupling agent 1-5 part.
Wherein, in preferred embodiment, described coupling agent is zirconium class coupling agent.
Technical scheme of the present invention is set forth further below by embodiment.
Embodiment 1
Described degradable environment-friendly material, wherein, it is composed of the following components by weight:
Plant fiber starch 35 parts;
POLYPROPYLENE GLYCOL 25 parts;
Polysorbate 20 part;
Glycerine 12 parts;
Poly-own endoenzyme and poly butyric ester 10 parts;
Coupling agent 5 parts.
Embodiment 2
Plant fiber starch 50 parts;
POLYPROPYLENE GLYCOL 30 parts;
Polysorbate 15 parts;
Glycerine 15 parts;
Poly-own endoenzyme and poly butyric ester 10 parts;
Coupling agent 1 part.
The invention provides a kind of degradable environment-friendly material, this mechanical strength is good, plasticity-is strong, of many uses, and in decomposition course, do not produce the material of welding, meet the requirement of green degraded, thus there are wide market outlook.
Should be understood that, application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can be improved according to the above description or convert, and all these improve and convert the protection domain that all should belong to claims of the present invention.
Claims (3)
1. a degradable environment-friendly material, is characterized in that, it is composed of the following components by weight:
Plant fiber starch 20-50 part;
POLYPROPYLENE GLYCOL 15-30 part;
Polysorbate 15-25 part;
Glycerine 10-15 part;
Poly-own endoenzyme and poly butyric ester 5-10 part;
Coupling agent 1-5 part.
2. degradable environment-friendly material according to claim 1, is characterized in that, it is composed of the following components by weight:
Plant fiber starch 35 parts;
POLYPROPYLENE GLYCOL 25 parts;
Polysorbate 20 part;
Glycerine 12 parts;
Poly-own endoenzyme and poly butyric ester 10 parts;
Coupling agent 5 parts.
3. degradable environment-friendly material according to claim 1, is characterized in that: described coupling agent is zirconium class coupling agent.