CN105401415A - Flannel fabric - Google Patents
Flannel fabric Download PDFInfo
- Publication number
- CN105401415A CN105401415A CN201510980325.5A CN201510980325A CN105401415A CN 105401415 A CN105401415 A CN 105401415A CN 201510980325 A CN201510980325 A CN 201510980325A CN 105401415 A CN105401415 A CN 105401415A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- parts
- fabric
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses flannel fabric, which has undergone dyeing and finishing treatment. The dyeing and finishing treatment comprises the following steps: 1) pretreatment; 2) dyeing; and 3) finishing: successively pouring 1-2 parts by weight of sodium butyl ricinoleate sulfate, 1.2 parts by weight of hydroxypropyl methyl cellulose, 0.5 part by weight of calcium hydrate, 0.9 part by weight of sodium propyl paraben, and 1.3 parts by weight of 2-Pentanol, 1,1',1'',1'''-(1,2-ethandiyldinitrilo) tetrakis into 13.7 parts by weight of deionized water, and uniformly stirring; pouring 0.9 part by weight of melamine polyphosphate, 0.9 part by weight of chitosan and 0.2 part by weight of tea polyphenol, continuously stirring until all the materials are fully and uniformly mixed so as to prepare a finishing solution; and carrying out dip padding treatment on the fabric in the finishing solution, taking the fabric out and drying the fabric at constant temperature. The flannel fabric of the invention has excellent anti-moth, antimicrobial, mildew-resistant, flame-retardant and antistatic properties, has strong washability and feels soft.
Description
Technical field
The present invention relates to flannel fabric.
Background technology
Mothproof, antibacterial, the mildew-resistant of existing fabric, fire-retardant, antistatic, washing fastness all have much room for improvement, and feel is soft not.
Summary of the invention
The object of the present invention is to provide a kind of flannel fabric, there is excellent mothproof, antibacterial, mildew-resistant, fire-retardant, antistatic property, and washability is strong, soft.
For achieving the above object, technical scheme of the present invention is a kind of flannel fabric of design, and it is through dyeing and finishing process, and described dyeing and finishing process comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 weight portion sesame oil acid butyl ester sodium sulphate, 1.2 weight portion hydroxypropyl methylcelluloses, 0.5 weight portion calcium hydroxide, 0.9 weight portion propylben sodium salt, 1.3 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate are dropped in 13.7 parts by mass deionized waters successively, stirs; Drop into 0.9 parts by weight of phosphoric acid melamine, 0.9 weight portion shitosan, 0.2 weight portion Tea Polyphenols more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
Preferably, flannel fabric, it is through dyeing and finishing process, and described dyeing and finishing process comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 weight portion sesame oil acid butyl ester sodium sulphate, 1.2 weight portion hydroxypropyl methylcelluloses, 0.5 weight portion calcium hydroxide, 0.9 weight portion propylben sodium salt, 1.3 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate are dropped in 13.7 parts by mass deionized waters successively, stirs; Drop into 0.9 parts by weight of phosphoric acid melamine, 0.9 weight portion shitosan, 0.2 weight portion Tea Polyphenols more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
Preferably, flannel fabric, it is through dyeing and finishing process, and described dyeing and finishing process comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 weight portion sesame oil acid butyl ester sodium sulphate, 1.2 weight portion hydroxypropyl methylcelluloses, 0.5 weight portion calcium hydroxide, 0.9 weight portion propylben sodium salt, 1.3 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate are dropped in 13.7 parts by mass deionized waters successively, stirs; Drop into 0.9 parts by weight of phosphoric acid melamine, 0.9 weight portion shitosan, 0.2 weight portion Tea Polyphenols more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
Advantage of the present invention and beneficial effect are: provide a kind of flannel fabric, have excellent mothproof, antibacterial, mildew-resistant, fire-retardant, antistatic property, and washability are strong, soft.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of flannel fabric, it is through dyeing and finishing process, and described dyeing and finishing process comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 weight portion sesame oil acid butyl ester sodium sulphate, 1.2 weight portion hydroxypropyl methylcelluloses, 0.5 weight portion calcium hydroxide, 0.9 weight portion propylben sodium salt, 1.3 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate are dropped in 13.7 parts by mass deionized waters successively, stirs; Drop into 0.9 parts by weight of phosphoric acid melamine, 0.9 weight portion shitosan, 0.2 weight portion Tea Polyphenols more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
Embodiment 2
Flannel fabric, it is through dyeing and finishing process, and described dyeing and finishing process comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 weight portion sesame oil acid butyl ester sodium sulphate, 1.2 weight portion hydroxypropyl methylcelluloses, 0.5 weight portion calcium hydroxide, 0.9 weight portion propylben sodium salt, 1.3 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate are dropped in 13.7 parts by mass deionized waters successively, stirs; Drop into 0.9 parts by weight of phosphoric acid melamine, 0.9 weight portion shitosan, 0.2 weight portion Tea Polyphenols more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
Embodiment 3
Flannel fabric, it is through dyeing and finishing process, and described dyeing and finishing process comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 weight portion sesame oil acid butyl ester sodium sulphate, 1.2 weight portion hydroxypropyl methylcelluloses, 0.5 weight portion calcium hydroxide, 0.9 weight portion propylben sodium salt, 1.3 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate are dropped in 13.7 parts by mass deionized waters successively, stirs; Drop into 0.9 parts by weight of phosphoric acid melamine, 0.9 weight portion shitosan, 0.2 weight portion Tea Polyphenols more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. flannel fabric, is characterized in that, it is through dyeing and finishing process, and described dyeing and finishing process comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 weight portion sesame oil acid butyl ester sodium sulphate, 1.2 weight portion hydroxypropyl methylcelluloses, 0.5 weight portion calcium hydroxide, 0.9 weight portion propylben sodium salt, 1.3 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate are dropped in 13.7 parts by mass deionized waters successively, stirs; Drop into 0.9 parts by weight of phosphoric acid melamine, 0.9 weight portion shitosan, 0.2 weight portion Tea Polyphenols more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
2. flannel fabric according to claim 1, is characterized in that, it is through dyeing and finishing process, and described dyeing and finishing process comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 weight portion sesame oil acid butyl ester sodium sulphate, 1.2 weight portion hydroxypropyl methylcelluloses, 0.5 weight portion calcium hydroxide, 0.9 weight portion propylben sodium salt, 1.3 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate are dropped in 13.7 parts by mass deionized waters successively, stirs; Drop into 0.9 parts by weight of phosphoric acid melamine, 0.9 weight portion shitosan, 0.2 weight portion Tea Polyphenols more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
3. flannel fabric according to claim 1, is characterized in that, it is through dyeing and finishing process, and described dyeing and finishing process comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 weight portion sesame oil acid butyl ester sodium sulphate, 1.2 weight portion hydroxypropyl methylcelluloses, 0.5 weight portion calcium hydroxide, 0.9 weight portion propylben sodium salt, 1.3 weight portion octadecyldimethyl ethoxy quaternary ammonium nitrate are dropped in 13.7 parts by mass deionized waters successively, stirs; Drop into 0.9 parts by weight of phosphoric acid melamine, 0.9 weight portion shitosan, 0.2 weight portion Tea Polyphenols more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.