CN105401337A - Alginate fiber spunlace non-woven fabric and manufacturing method thereof - Google Patents
Alginate fiber spunlace non-woven fabric and manufacturing method thereof Download PDFInfo
- Publication number
- CN105401337A CN105401337A CN201510686846.XA CN201510686846A CN105401337A CN 105401337 A CN105401337 A CN 105401337A CN 201510686846 A CN201510686846 A CN 201510686846A CN 105401337 A CN105401337 A CN 105401337A
- Authority
- CN
- China
- Prior art keywords
- alginate
- fiber
- alginate fibre
- blended fiber
- nonwoven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an alginate fiber spunlace non-woven fabric with an efficacy of absorbing heavy metals and a manufacturing method thereof. The non-woven fabric is made of alginate fibers and plant mixed fibers in a blending manner. Weight ratio of the alginate fibers and the plant mixed fibers is x: y, wherein 10<=x<100, 0<y<=90, and dimension of the fiber is 1.5 D, 38 mm. The alginate fibers are made of raw materials of calcium alginate which is extracted from brown seaweeds. The method is simple in production process, convenient in material drawing, and low in cost, and mixing proportion of the alginate fibers and other plant mixed fibers can be adjusted in a targeted manner in a processing process. The alginate fiber non-woven fabric can be used as a material base cloth of a mask. In a use process, through soaking the fabric in essences in different efficacies, the fabric becomes a good functional component carrier. The materials are safe and do not contain toxic and harmful substances, a mask cloth can stand long-time immersion of an essence, and the fabric can be naturally degraded after use, so the fabric is more friendly to environment.
Description
Technical field
The invention belongs in field of textiles, particularly a kind of alginate fibre spunlace non-woven cloth and preparation method thereof of adsorbable heavy-metal residual thing, is mainly used in mask substrate.
Background technology
By recognizing the analysis of facial mask Industry, along with 80, after 90sly gradually grow up as consumption main flow, current mask product has developed into female consumer skin type product used in everyday, and along with pulling of brand business advertisement and popularizing further of Sales Channel, especially along with facial mask brand is in the extensive popularization of ecommerce channel, the consumption sense of purchasing of Chinese women consumer to mask becomes more strong, and the consumption straight line of mask substrate improves.
In the cosmetics such as present widely used skin care products, suncream, whitening spot-removing, the cosmetics (comprising the brand that some are internationally famous) of quite a few are had to contain the compositions such as heavy metal, hormone or violated antibiotic in varying degrees.These harmful components that can be detected or not be detected, easily pile up on human body skin top layer, may become the hidden danger of hiding in human body, at any time may to healthy generation harm.
Main flow mask substrate does not possess effect of Adsorption of Heavy Metals residue substantially on the market, common facial mask is all realize adsorbing the heavy-metal residual in cosmetics by adding marine algae extract (Zostera marina extract or trehalose) in Essence, and effect is undesirable.
Containing a large amount of carboxyls and hydroxyl on the alginic acid strand be rich in alginate fibre, there is stronger complexing power with heavy metal ion, stable chelate can be formed by the modes such as complexing and metal ion.Take sodium alginate as raw material, not only adsorption capacity is large, adsorption rate fast to sting by water the alginate fibre prepared without spinning process, is a kind of desirable green bio matter sorbing material.Therefore alginate fibre becomes the splendid raw material making mask substrate, and colleague's alginate fibre mask substrate also has good Whitening, spot, antibacterial mite-inhibiting, potent lock water effect.
Summary of the invention
The object of this invention is to provide a kind of alginate fibre spunlace non-woven cloth with Adsorption of Heavy Metals effect and preparation method thereof.
In order to realize foregoing invention object, the present invention by the following technical solutions: a kind of alginate fibre spunlace non-woven cloth, described nonwoven fabric adopts and is mixed with alginate fibre and plant blended fiber.
Described alginate fibre and plant blended fiber weight ratio are x:y, wherein 10≤x < 100,0 < y≤90; Fiber is of a size of 1.5D, 38mm.
The calcium alginate that described alginate fibre adopts brown seaweed to extract is that raw material is prepared from.
Described plant blended fiber adopts cotton fiber, xylon, bamboo fibre, camphorwood sky silk, beech sky silk to be mixed.
Described nonwoven fabric intersects or semidecussation spunlace non-woven cloth entirely.
A preparation method for alginate fibre spunlace non-woven cloth, comprises the following steps:
(1) take alginate fibre and plant blended fiber raw material in proportion, carry out pre-opener separately, fibrous raw material is become relaxed state by original impaction state shredding;
(2) mix through the alginate fibre of shredding and plant blended fiber fully, and by further for mixed blended fiber shredding;
(3) blended fiber after smart shredding is divided into two parts, and a part carries out combing lapping drawing-off combing together with remaining another part blended fiber again, is excised in place not neat for the cloth two ends Bian Kou after combing;
(4) spun-laced machine water thorn, by fine for high pressure water flow jet on fiber web, makes fiber mutually entangled, thus fibre web is reinforced and possesses certain brute force, entirely intersected or semidecussation spunlace non-woven cloth, and water thorn pressure is 500 ~ 650N;
(5) dried by cloth, drying and processing, temperature is 95 ~ 135 DEG C.
Containing a large amount of carboxyls and hydroxyl on the alginic acid strand be rich in alginate fibre, there is stronger complexing power with heavy metal ion, stable chelate can be formed by the modes such as complexing and metal ion.Take sodium alginate as raw material, not only adsorption capacity is large, adsorption rate fast to sting by water the alginate fibre prepared without spinning process, is a kind of desirable green bio matter sorbing material.Therefore alginate fibre becomes the splendid raw material making mask substrate, and colleague's alginate fibre mask substrate also has good Whitening, spot, antibacterial mite-inhibiting, potent lock water effect.
The present invention is main raw material with alginate fibre, utilizes its spinnability, water imbibition, lock water-based, Adsorption of Heavy Metals effect the plant blended fiber being aided with other pulling force characteristics outstanding makes alginate fibre nonwoven fabric, can be used as face-mask material base cloth.
The present invention has the following advantages: production technology of the present invention is simple, draw materials conveniently, cheap, can in process the mixed proportion of specific aim adjustment alginate fibre and other plant blended fiber, the Essence in use by soaking different efficacies comes thus becomes good functional component carrier.Material safety can not stand Essence long period of soaking containing poisonous and harmful substance composition, film cloth, using can natural degradation, more friendly to environment.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further illustrated.
embodiment 1
Parts by weight 20 parts of alginate fibre raw materials are mixed in cotton blender machine with 80 parts of plant blended fiber raw materials, enter two line fine openers after mixing, entirely intersected or semidecussation cloth to cotton, two line combings, drawing-off, water thorn, oven dry, trimming through two line cotton feeders.Pre-opener weight 350KG, water thorn pressure 500N; Bake out temperature 95 DEG C.
embodiment 2
Parts by weight 30 parts of alginate fibre raw materials are mixed in cotton blender machine with 70 parts of plant blended fiber raw materials, enter two line fine openers after mixing, entirely intersected or semidecussation cloth to cotton, two line combings, drawing-off, water thorn, oven dry, trimming through two line cotton feeders.Pre-opener weight 350KG, water thorn pressure 600N; Bake out temperature 110 DEG C.
embodiment 3
Parts by weight 40 parts of alginate fibre raw materials are mixed in cotton blender machine with 60 parts of plant blended fiber raw materials, enter two line fine openers after mixing, entirely intersected or semidecussation cloth to cotton, two line combings, drawing-off, water thorn, oven dry, trimming through two line cotton feeders.Pre-opener weight 350KG, water thorn pressure 650N; Bake out temperature 135 DEG C.
Although the present invention with preferred embodiment openly as above; but embodiment is not for limiting the present invention, being anyly familiar with this those skilled in the art, without departing from the spirit and scope of the invention; can make various changes or retouch from working as, but same within protection scope of the present invention.What therefore protection scope of the present invention should define with the claims of the application is as the criterion.
Claims (6)
1. an alginate fibre spunlace non-woven cloth, is characterized in that: described nonwoven fabric adopts and is mixed with alginate fibre and plant blended fiber.
2. nonwoven fabric according to claim 1, is characterized in that: described alginate fibre and plant blended fiber weight ratio are x:y, wherein 10≤x < 100,0 < y≤90; Fiber is of a size of 1.5D, 38mm.
3. nonwoven fabric according to claim 2, is characterized in that: the calcium alginate that described alginate fibre adopts brown seaweed to extract is that raw material is prepared from.
4. nonwoven fabric according to claim 3, is characterized in that: described plant blended fiber adopts cotton fiber, xylon, bamboo fibre, camphorwood sky silk, beech sky silk to be mixed.
5. nonwoven fabric according to claim 4, is characterized in that: described nonwoven fabric intersects or semidecussation spunlace non-woven cloth entirely.
6., according to a preparation method for the arbitrary described alginate fibre spunlace non-woven cloth of claim 1 to 5, it is characterized in that comprising the following steps:
(1) take alginate fibre and plant blended fiber raw material in proportion, carry out pre-opener separately, fibrous raw material is become relaxed state by original impaction state shredding;
(2) mix through the alginate fibre of shredding and plant blended fiber fully, and by further for mixed blended fiber shredding;
(3) blended fiber after smart shredding is divided into two parts, and a part carries out combing lapping drawing-off combing together with remaining another part blended fiber again, is excised in place not neat for the cloth two ends Bian Kou after combing;
(4) spun-laced machine water thorn, by fine for high pressure water flow jet on fiber web, makes fiber mutually entangled, thus fibre web is reinforced and possesses certain brute force, entirely intersected or semidecussation spunlace non-woven cloth, and water thorn pressure is 500 ~ 650N;
(5) dried by cloth, drying and processing, temperature is 95 ~ 135 DEG C.