CN105400992A - Novel storage cage - Google Patents
Novel storage cage Download PDFInfo
- Publication number
- CN105400992A CN105400992A CN201510963380.3A CN201510963380A CN105400992A CN 105400992 A CN105400992 A CN 105400992A CN 201510963380 A CN201510963380 A CN 201510963380A CN 105400992 A CN105400992 A CN 105400992A
- Authority
- CN
- China
- Prior art keywords
- alloy
- alloy material
- rotating shaft
- melt
- underframe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel storage cage comprising a rotating shaft made of an alloy material. The alloy material comprises the following components: 1-2% of P, 2.7% of Cu, 1.8% of Y, 0.7% of Zr, 1.2% of Ir, 0.8% of Pt and the balance of Ti and unavoidable impurities; and the alloy material is prepared through the following steps of (1) melting Ti, P, Ti-Cu alloy and Ti-Y alloy at the protective atmosphere; (2) regulating the temperature to 900 DEG C, adding Ti-Zr alloy, Ti-Ir alloy and Ti-Pt alloy into a melt, uniformly stirring, preserving the heat and standing for 39 minutes; and (3) introducing argon, standing to cool the melt to 690 DEG C, and carrying out pressure casting to obtain the alloy material. The rotating shaft of the novel storage cage is high in strength, light in weight, good in wear resistance, corrosion resistance, cold resistance and oxidation resistance and capable of stably working for a long term.
Description
Technical field
The present invention relates to Novel storage cage.
Background technology
Novel storage cage is suitable for mobile, and the rotating shaft under comprising underframe and being located at underframe and roller, the performance requriements of countershaft is higher.
Summary of the invention
The object of the present invention is to provide a kind of Novel storage cage, its rotating shaft is made up of alloy material, and shaft strength is high, lightweight, abrasion-resistant, corrosion-resistant, cold-resistant, anti-oxidant, weather resistance is good, can long-term stable operation.
For achieving the above object, technical scheme of the present invention is a kind of Novel storage cage of design, the rotating shaft under comprising underframe and being located at underframe and roller, and described rotating shaft is made up of alloy material, and by weight percentage, the composition of this alloy material is:
P:1~2%,
Cu:2.7%,
Y:1.8%,
Zr:0.7%,
Ir:1.2%,
Pt:0.8%,
Surplus is Ti and inevitable impurity;
Described alloy material is prepared as follows:
1) by Ti, P and Ti-Cu alloy, the melting under protective atmosphere of Ti-Y alloy;
2) temperature is adjusted to 900 DEG C, adds Ti-Zr alloy, Ti-Ir alloy and Ti-Pt alloy, stir in melt, and insulation leaves standstill 39 minutes;
3) pass into argon gas, left standstill by melt and be cooled to 690 DEG C, die casting obtains alloy material.
Preferably, Novel storage cage, the rotating shaft under comprising underframe and being located at underframe and roller, described rotating shaft is made up of alloy material, and by weight percentage, the composition of this alloy material is:
P:1%,
Cu:2.7%,
Y:1.8%,
Zr:0.7%,
Ir:1.2%,
Pt:0.8%,
Surplus is Ti and inevitable impurity;
Described alloy material is prepared as follows:
1) by Ti, P and Ti-Cu alloy, the melting under protective atmosphere of Ti-Y alloy;
2) temperature is adjusted to 900 DEG C, adds Ti-Zr alloy, Ti-Ir alloy and Ti-Pt alloy, stir in melt, and insulation leaves standstill 39 minutes;
3) pass into argon gas, left standstill by melt and be cooled to 690 DEG C, die casting obtains alloy material.
Preferably, Novel storage cage, the rotating shaft under comprising underframe and being located at underframe and roller, described rotating shaft is made up of alloy material, and by weight percentage, the composition of this alloy material is:
P:2%,
Cu:2.7%,
Y:1.8%,
Zr:0.7%,
Ir:1.2%,
Pt:0.8%,
Surplus is Ti and inevitable impurity;
Described alloy material is prepared as follows:
1) by Ti, P and Ti-Cu alloy, the melting under protective atmosphere of Ti-Y alloy;
2) temperature is adjusted to 900 DEG C, adds Ti-Zr alloy, Ti-Ir alloy and Ti-Pt alloy, stir in melt, and insulation leaves standstill 39 minutes;
3) pass into argon gas, left standstill by melt and be cooled to 690 DEG C, die casting obtains alloy material.
Advantage of the present invention and beneficial effect are: provide a kind of Novel storage cage, its rotating shaft is made up of alloy material, and shaft strength is high, lightweight, abrasion-resistant, corrosion-resistant, cold-resistant, anti-oxidant, weather resistance is good, can long-term stable operation.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of Novel storage cage, the rotating shaft under comprising underframe and being located at underframe and roller, described rotating shaft is made up of alloy material, and by weight percentage, the composition of this alloy material is:
P:1~2%,
Cu:2.7%,
Y:1.8%,
Zr:0.7%,
Ir:1.2%,
Pt:0.8%,
Surplus is Ti and inevitable impurity;
Described alloy material is prepared as follows:
1) by Ti, P and Ti-Cu alloy, the melting under protective atmosphere of Ti-Y alloy;
2) temperature is adjusted to 900 DEG C, adds Ti-Zr alloy, Ti-Ir alloy and Ti-Pt alloy, stir in melt, and insulation leaves standstill 39 minutes;
3) pass into argon gas, left standstill by melt and be cooled to 690 DEG C, die casting obtains alloy material.
Embodiment 2
Novel storage cage, the rotating shaft under comprising underframe and being located at underframe and roller, described rotating shaft is made up of alloy material, and by weight percentage, the composition of this alloy material is:
P:1%,
Cu:2.7%,
Y:1.8%,
Zr:0.7%,
Ir:1.2%,
Pt:0.8%,
Surplus is Ti and inevitable impurity;
Described alloy material is prepared as follows:
1) by Ti, P and Ti-Cu alloy, the melting under protective atmosphere of Ti-Y alloy;
2) temperature is adjusted to 900 DEG C, adds Ti-Zr alloy, Ti-Ir alloy and Ti-Pt alloy, stir in melt, and insulation leaves standstill 39 minutes;
3) pass into argon gas, left standstill by melt and be cooled to 690 DEG C, die casting obtains alloy material.
Embodiment 3
Novel storage cage, the rotating shaft under comprising underframe and being located at underframe and roller, described rotating shaft is made up of alloy material, and by weight percentage, the composition of this alloy material is:
P:2%,
Cu:2.7%,
Y:1.8%,
Zr:0.7%,
Ir:1.2%,
Pt:0.8%,
Surplus is Ti and inevitable impurity;
Described alloy material is prepared as follows:
1) by Ti, P and Ti-Cu alloy, the melting under protective atmosphere of Ti-Y alloy;
2) temperature is adjusted to 900 DEG C, adds Ti-Zr alloy, Ti-Ir alloy and Ti-Pt alloy, stir in melt, and insulation leaves standstill 39 minutes;
3) pass into argon gas, left standstill by melt and be cooled to 690 DEG C, die casting obtains alloy material.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. Novel storage cage, is characterized in that, the rotating shaft under comprising underframe and being located at underframe and roller, and described rotating shaft is made up of alloy material, and by weight percentage, the composition of this alloy material is:
P:1~2%,
Cu:2.7%,
Y:1.8%,
Zr:0.7%,
Ir:1.2%,
Pt:0.8%,
Surplus is Ti and inevitable impurity;
Described alloy material is prepared as follows:
1) by Ti, P and Ti-Cu alloy, the melting under protective atmosphere of Ti-Y alloy;
2) temperature is adjusted to 900 DEG C, adds Ti-Zr alloy, Ti-Ir alloy and Ti-Pt alloy, stir in melt, and insulation leaves standstill 39 minutes;
3) pass into argon gas, left standstill by melt and be cooled to 690 DEG C, die casting obtains alloy material.
2. Novel storage cage according to claim 1, is characterized in that, the rotating shaft under comprising underframe and being located at underframe and roller, and described rotating shaft is made up of alloy material, and by weight percentage, the composition of this alloy material is:
P:1%,
Cu:2.7%,
Y:1.8%,
Zr:0.7%,
Ir:1.2%,
Pt:0.8%,
Surplus is Ti and inevitable impurity;
Described alloy material is prepared as follows:
1) by Ti, P and Ti-Cu alloy, the melting under protective atmosphere of Ti-Y alloy;
2) temperature is adjusted to 900 DEG C, adds Ti-Zr alloy, Ti-Ir alloy and Ti-Pt alloy, stir in melt, and insulation leaves standstill 39 minutes;
3) pass into argon gas, left standstill by melt and be cooled to 690 DEG C, die casting obtains alloy material.
3. Novel storage cage according to claim 1, is characterized in that, the rotating shaft under comprising underframe and being located at underframe and roller, and described rotating shaft is made up of alloy material, and by weight percentage, the composition of this alloy material is:
P:2%,
Cu:2.7%,
Y:1.8%,
Zr:0.7%,
Ir:1.2%,
Pt:0.8%,
Surplus is Ti and inevitable impurity;
Described alloy material is prepared as follows:
1) by Ti, P and Ti-Cu alloy, the melting under protective atmosphere of Ti-Y alloy;
2) temperature is adjusted to 900 DEG C, adds Ti-Zr alloy, Ti-Ir alloy and Ti-Pt alloy, stir in melt, and insulation leaves standstill 39 minutes;
3) pass into argon gas, left standstill by melt and be cooled to 690 DEG C, die casting obtains alloy material.