CN105386195A - Fabric capable of resisting static electricity - Google Patents
Fabric capable of resisting static electricity Download PDFInfo
- Publication number
- CN105386195A CN105386195A CN201510680237.3A CN201510680237A CN105386195A CN 105386195 A CN105386195 A CN 105386195A CN 201510680237 A CN201510680237 A CN 201510680237A CN 105386195 A CN105386195 A CN 105386195A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fiber
- wool
- layer
- per square
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fabric capable of resisting static electricity. The fabric capable of resisting the static electricity is characterized in that the fabric comprises a fabric body (1), the surface of the fabric body (1) is provided with a fine-striped fabric layer (2) which is connected with the fabric body (1) through threads, multiple pieces of bold-striped rectangular short stripe cloth (3) are distributed on the fine-striped fabric layer (2), the multiple pieces of the short stripe cloth (3) are arranged in the horizontal direction in a staggered mode and fixed on the fine-striped fabric layer (2) through threads, the bottom face of the fabric body (1) is provided with a fluff layer (4), and the bottom face of the fluff layer (4) is provided with an anti-static layer (5). According to the fabric capable of resisting the static electricity, the short stripe cloth protrudes the plane where the fine-striped fabric layer is located, so that the layering feeling of the striped fabric is enhanced; by means of the fluff layer, the heat retention property of the striped fabric is enhanced; meanwhile, by means of the anti-static layer, the anti-static property is improved.
Description
Technical field
The present invention relates to one can anlistatig fabric, belongs to fabric technical field.
Background technology
Traditional fabric is generally single layer structure, and function is comparatively single.In recent years along with the development of textile industry, occurred double-layer fabric, double-layer fabric is three-dimensional structure, has solid layer feeling, and abundant degree and intensity are all relatively good, but do not possess electrostatic-proof function.
Summary of the invention
The object of the invention is to overcome above-mentioned deficiency, provide the good one of solid layer feeling can anlistatig fabric.
The object of the present invention is achieved like this:
One can anlistatig fabric, comprise fabric body, described fabric body surface is provided with microgroove precoat, microgroove precoat is connected with fabric body line, coarse groove rectangle that described microgroove precoat distributes billet cloth, described billet cloth alternate in the horizontal direction, and be fixed on microgroove precoat with line, the bottom surface of described fabric body is provided with tapetum, and tapetum bottom surface is provided with antistatic backing.
Make and a kind ofly can the process of anlistatig fabric be:
1), yarn variety design:
Select wool fibre, poly butylene succinate silk thread and polyolefin elastic fiber, to wool fibre, poly butylene succinate silk thread and polyolefin elastic fiber carry out ANTIPILLING process, ferment treatment and soft treatment, ANTIPILLING process selects phosphate antimonous oxide mixture as ANTIPILLING agent, phosphate antimonous oxide amount of mixture is wool fibre weight 1.5-4%, ferment treatment system uses protease to process, protease consumption is the 0.1-0.2% of wool fibre weight, the softener that soft treatment is selected is water-soluble organic silicon softener, water-soluble organic silicon softener consumption is the 6-8% of wool fibre weight,
2), spinning process:
By the super-fine wool fiber of dyeing rear 70%, the polyester fiber of 30% passes through and hair → hacking → shredding → carding (slivering) → drafting (in the lump, two also) → open-end spinning → automatic winding, wherein control relative humidity 50% ~ 55% in spinning technological process, temperature 25 DEG C ~ 30 DEG C.
In combing oil, select NimateCF-5 wool lubricant, NimateC602 cationic antistatic agent, with spray-on process, add and account for the wool lubricant of gross weight 10% and account for the antistatic additive of gross weight 10%, make fiber have excellent lubricity, increase coherent, the antistatic behaviour of fiber, what improve fiber can cardability, contributes to the full and uniform mixing of different performance fiber.
In carding process, feed the hair cycle and grasp 50s ~ 60s, sliver exporting speed is no more than 100m/min, shaping grammes per square metre 5g/m, and irregular coefficient controls within 2%.
In drawing process, the height that spinning 25/1 is public props up slubbing yarn, and parameter 8.2, two in the lump also rear wool top grammes per square metre controls at 4g/m.Select import autoleveller draw frame (D45 type), the even coefficient of variation of lower machine wool top grammes per square metre is no more than 0.5% ~ 1%.In this process, must control drafting multiple well, total draft controls 7.8 times, wherein dominant draft 4.58 times, follow-up drawing-off 1.7 times.
3), weaving process:
Warping → gait, plug in reed, inserted sheet → arrow shaft are weaved, and the height of 25/1 public is propped up slubbing yarn by Rapier looms, organizes based on the twill of 2/2, adopt the mode looming weaving of single-warp single-abb, upper machine fabric width is 178cm, upper machine through close be 225/10cm, filling density is 216/10cm.
4), postfinishing process:
Final finishing comprises: singe-singly to boil-braying-bis-ly boil-dry-photocatalyst working fluid pads-dry-TEFLON three-prevention finishing-bake-ripe to be repaiied-bristle-cropping-bristle-dewing-tank steams, in addition, consumption 30g/l-the 50g/l of photocatalyst working fluid, pick-up rate 75%-85%, car 25m/min-30m/min is kept when the use of photocatalyst working fluid, temperature 120 DEG C-135 DEG C, the mangle 75-85% of TEFLON three-prevention finishing processing, the speed of a motor vehicle keeps 18-22m/min, temperature 160-180 DEG C, finally obtained fabric specification is: yarn count 96/2-100/2Nm, total tightness degree 145-165, through close 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, grammes per square metre 340-390 gram/meter.
Compared with prior art, the invention has the beneficial effects as follows:
The present invention is a kind of can protrude the place plane of microgroove precoat by billet cloth in anlistatig fabric, and enhance the stereovision of strip fabric, tapetum enhances the warmth retention property of strip fabric, and antistatic backing improves static electricity resistance simultaneously.
Accompanying drawing explanation
Fig. 1 is that the present invention is a kind of can the structural representation of anlistatig fabric.
Fig. 2 is the A-A sectional view of Fig. 1.
In figure: fabric body 1, microgroove precoat 2, billet cloth 3, tapetum 4, antistatic backing 5.
Detailed description of the invention
See Fig. 1 and Fig. 2, the present invention relates to one can anlistatig fabric, comprise fabric body 1, described fabric body 1 surface is provided with microgroove precoat 2, and microgroove precoat 2 is connected with line with fabric body 1, coarse groove rectangle that described microgroove precoat 2 distributes billet cloth 3, described billet cloth 3 alternate in the horizontal direction, and being fixed on microgroove precoat 2 with line, the bottom surface of described fabric body 1 is provided with tapetum 4, and tapetum 4 bottom surface is provided with antistatic backing 5.
Make and a kind ofly can the process of anlistatig fabric be:
1), yarn variety design:
Select wool fibre, poly butylene succinate silk thread and polyolefin elastic fiber, to wool fibre, poly butylene succinate silk thread and polyolefin elastic fiber carry out ANTIPILLING process, ferment treatment and soft treatment, ANTIPILLING process selects phosphate antimonous oxide mixture as ANTIPILLING agent, phosphate antimonous oxide amount of mixture is wool fibre weight 1.5-4%, ferment treatment system uses protease to process, protease consumption is the 0.1-0.2% of wool fibre weight, the softener that soft treatment is selected is water-soluble organic silicon softener, water-soluble organic silicon softener consumption is the 6-8% of wool fibre weight,
2), spinning process:
By the super-fine wool fiber of dyeing rear 70%, the polyester fiber of 30% passes through and hair → hacking → shredding → carding (slivering) → drafting (in the lump, two also) → open-end spinning → automatic winding, wherein control relative humidity 50% ~ 55% in spinning technological process, temperature 25 DEG C ~ 30 DEG C.
In combing oil, select NimateCF-5 wool lubricant, NimateC602 cationic antistatic agent, with spray-on process, add and account for the wool lubricant of gross weight 10% and account for the antistatic additive of gross weight 10%, make fiber have excellent lubricity, increase coherent, the antistatic behaviour of fiber, what improve fiber can cardability, contributes to the full and uniform mixing of different performance fiber.
In carding process, feed the hair cycle and grasp 50s ~ 60s, sliver exporting speed is no more than 100m/min, shaping grammes per square metre 5g/m, and irregular coefficient controls within 2%.
In drawing process, the height that spinning 25/1 is public props up slubbing yarn, and parameter 8.2, two in the lump also rear wool top grammes per square metre controls at 4g/m.Select import autoleveller draw frame (D45 type), the even coefficient of variation of lower machine wool top grammes per square metre is no more than 0.5% ~ 1%.In this process, must control drafting multiple well, total draft controls 7.8 times, wherein dominant draft 4.58 times, follow-up drawing-off 1.7 times.
3), weaving process:
Warping → gait, plug in reed, inserted sheet → arrow shaft are weaved, and the height of 25/1 public is propped up slubbing yarn by Rapier looms, organizes based on the twill of 2/2, adopt the mode looming weaving of single-warp single-abb, upper machine fabric width is 178cm, upper machine through close be 225/10cm, filling density is 216/10cm.
4), postfinishing process:
Final finishing comprises: singe-singly to boil-braying-bis-ly boil-dry-photocatalyst working fluid pads-dry-TEFLON three-prevention finishing-bake-ripe to be repaiied-bristle-cropping-bristle-dewing-tank steams, in addition, consumption 30g/l-the 50g/l of photocatalyst working fluid, pick-up rate 75%-85%, car 25m/min-30m/min is kept when the use of photocatalyst working fluid, temperature 120 DEG C-135 DEG C, the mangle 75-85% of TEFLON three-prevention finishing processing, the speed of a motor vehicle keeps 18-22m/min, temperature 160-180 DEG C, finally obtained fabric specification is: yarn count 96/2-100/2Nm, total tightness degree 145-165, through close 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, grammes per square metre 340-390 gram/meter.
Claims (2)
1. one kind can anlistatig fabric, it is characterized in that: comprise fabric body (1), described fabric body (1) surface is provided with microgroove precoat (2), microgroove precoat (2) is connected with line with fabric body (1), described microgroove precoat (2) upper distribution coarse groove rectangle billet cloth (3), described billet cloth (3) alternate in the horizontal direction, and be fixed on microgroove precoat (2) with line, the bottom surface of described fabric body (1) is provided with tapetum (4), and tapetum (4) bottom surface is provided with antistatic backing (5).
2. make according to claim 1 a kind of can the process of anlistatig fabric, it is characterized in that:
1), yarn variety design:
Select wool fibre, poly butylene succinate silk thread and polyolefin elastic fiber, to wool fibre, poly butylene succinate silk thread and polyolefin elastic fiber carry out ANTIPILLING process, ferment treatment and soft treatment, ANTIPILLING process selects phosphate antimonous oxide mixture as ANTIPILLING agent, phosphate antimonous oxide amount of mixture is wool fibre weight 1.5-4%, ferment treatment system uses protease to process, protease consumption is the 0.1-0.2% of wool fibre weight, the softener that soft treatment is selected is water-soluble organic silicon softener, water-soluble organic silicon softener consumption is the 6-8% of wool fibre weight,
2), spinning process:
By the super-fine wool fiber of dyeing rear 70%, the polyester fiber of 30% passes through and hair → hacking → shredding → carding (slivering) → drafting (in the lump, two also) → open-end spinning → automatic winding, wherein control relative humidity 50% ~ 55% in spinning technological process, temperature 25 DEG C ~ 30 DEG C.
In combing oil, select NimateCF-5 wool lubricant, NimateC602 cationic antistatic agent, with spray-on process, add and account for the wool lubricant of gross weight 10% and account for the antistatic additive of gross weight 10%, make fiber have excellent lubricity, increase coherent, the antistatic behaviour of fiber, what improve fiber can cardability, contributes to the full and uniform mixing of different performance fiber.
In carding process, feed the hair cycle and grasp 50s ~ 60s, sliver exporting speed is no more than 100m/min, shaping grammes per square metre 5g/m, and irregular coefficient controls within 2%.
In drawing process, the height that spinning 25/1 is public props up slubbing yarn, and parameter 8.2, two in the lump also rear wool top grammes per square metre controls at 4g/m.Select import autoleveller draw frame (D45 type), the even coefficient of variation of lower machine wool top grammes per square metre is no more than 0.5% ~ 1%.In this process, must control drafting multiple well, total draft controls 7.8 times, wherein dominant draft 4.58 times, follow-up drawing-off 1.7 times.
3), weaving process:
Warping → gait, plug in reed, inserted sheet → arrow shaft are weaved, and the height of 25/1 public is propped up slubbing yarn by Rapier looms, organizes based on the twill of 2/2, adopt the mode looming weaving of single-warp single-abb, upper machine fabric width is 178cm, upper machine through close be 225/10cm, filling density is 216/10cm.
4), postfinishing process:
Final finishing comprises: singe-singly to boil-braying-bis-ly boil-dry-photocatalyst working fluid pads-dry-TEFLON three-prevention finishing-bake-ripe to be repaiied-bristle-cropping-bristle-dewing-tank steams, in addition, consumption 30g/l-the 50g/l of photocatalyst working fluid, pick-up rate 75%-85%, car 25m/min-30m/min is kept when the use of photocatalyst working fluid, temperature 120 DEG C-135 DEG C, the mangle 75-85% of TEFLON three-prevention finishing processing, the speed of a motor vehicle keeps 18-22m/min, temperature 160-180 DEG C, finally obtained fabric specification is: yarn count 96/2-100/2Nm, total tightness degree 145-165, through close 615-796 root/10 centimetre, filling density 400-358 root/10 centimetre, grammes per square metre 340-390 gram/meter.