CN105369170A - 一种铝锂合金型材黑白斑点控制方法 - Google Patents

一种铝锂合金型材黑白斑点控制方法 Download PDF

Info

Publication number
CN105369170A
CN105369170A CN201510958298.1A CN201510958298A CN105369170A CN 105369170 A CN105369170 A CN 105369170A CN 201510958298 A CN201510958298 A CN 201510958298A CN 105369170 A CN105369170 A CN 105369170A
Authority
CN
China
Prior art keywords
black
quenching
white spots
minutes
lithium alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510958298.1A
Other languages
English (en)
Inventor
王艳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Southwest Aluminum Group Co Ltd
Original Assignee
Southwest Aluminum Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Southwest Aluminum Group Co Ltd filed Critical Southwest Aluminum Group Co Ltd
Priority to CN201510958298.1A priority Critical patent/CN105369170A/zh
Publication of CN105369170A publication Critical patent/CN105369170A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铝锂合金型材黑白斑点控制方法，在淬火时减少淬火升温时间，其淬火升温时间为20分钟至30分钟。在实际生产中，经小批量投料生产发现1420CZ铝锂合金型材表面黑白斑点现象主要产生在淬火加热保温过程中，经多次取样进行相关检测和对比分析，结果均表明黑白斑点处于铝锂合金脱锂层表层，黑斑区域未见组织差异，也未深入金属基体，黑白斑点形成的密集度主要跟淬火升温时间有关，通过对淬火制度的调整，型材表面黑白斑点基本上得到了有效的控制，黑白斑点也能明显减轻，即在淬火时减少淬火升温时间，其淬火升温时间为20分钟至30分钟，能够有效的减少黑白斑点。

Description

一种铝锂合金型材黑白斑点控制方法
技术领域
本发明涉及铝锂合金型材生产方法技术领域，特别涉及一种铝锂合金型材黑白斑点控制方法。
背景技术
请参考图1，图1为现有技术中黑白斑点的金相结构示意图。1420CZ铝锂合金作为一种中高强度，轻质的功能材料，其附加值相当高。在实际生产过程中该铝锂合金型材表面一直存在黑白斑点现象，有些呈点状，有些呈无规则块状。用户在使用过程中需对制品进行阳极氧化，以增强该合金的耐蚀性以及其它性能，而该型材的黑白斑点影响到后部工序的开展。
因此，如何提供一种铝锂合金型材黑白斑点控制方法，以减少黑白斑点，是本领域技术人员目前需要解决的技术问题。
发明内容
本发明的目的是提供一种铝锂合金型材黑白斑点控制方法，以减少黑白斑点。
为解决上述技术问题，本发明提供如下方案：
一种铝锂合金型材黑白斑点控制方法，在淬火时减少淬火升温时间，其淬火升温时间为20分钟至30分钟。
优选的，上述淬火升温时间为30分钟。
优选的，上述淬火升温时间为25分钟。
优选的，铝锂合金型材的装炉量为100公斤-900公斤。
优选的，铝锂合金型材为1420CZ铝锂合金。
上述本发明所提供的铝锂合金型材黑白斑点控制方法，在淬火时减少淬火升温时间，其淬火升温时间为20分钟至30分钟。在实际生产中，经小批量投料生产发现1420CZ铝锂合金型材表面黑白斑点现象主要产生在淬火加热保温过程中，经多次取样进行相关检测和对比分析，结果均表明黑白斑点处于铝锂合金脱锂层表层，黑斑区域未见组织差异，也未深入金属基体，能谱微区分析黑斑部位含O、C、Mg等元素，分析结论认定为是由于型材在空气炉高温淬火过程中表面脱锂和镁元素氧化而形成的表面色差现象，是高镁、高锂含量的1420合金所独有的一种特性。黑白斑点形成的密集度主要跟淬火升温时间有关，通过对淬火制度的调整，型材表面黑白斑点基本上得到了有效的控制，黑白斑点也能明显减轻，即在淬火时减少淬火升温时间，其淬火升温时间为20分钟至30分钟，能够有效的减少黑白斑点。
附图说明
图1为现有技术中黑白斑点的金相结构示意图；
图2为采用铝锂合金型材黑白斑点控制方法后正常的黑白斑点的金相结构示意图。
具体实施方式
为了使本技术领域的技术人员更好地理解本发明方案，下面结合附图和具体实施方式对本发明作进一步的详细说明。
请参考图2，图2为采用铝锂合金型材黑白斑点控制方法后正常的黑白斑点的金相结构示意图。
本发明实施例所提供的铝锂合金型材黑白斑点控制方法，在淬火时减少淬火升温时间，其淬火升温时间为20分钟至30分钟。在实际生产中，经小批量投料生产发现1420CZ铝锂合金型材表面黑白斑点现象主要产生在淬火加热保温过程中，经多次取样进行相关检测和对比分析，结果均表明黑白斑点处于铝锂合金脱锂层表层，黑斑区域未见组织差异，也未深入金属基体，能谱微区分析黑斑部位含O、C、Mg等元素，分析结论认定为是由于型材在空气炉高温淬火过程中表面脱锂和镁元素氧化而形成的表面色差现象，是高镁、高锂含量的1420合金所独有的一种特性。黑白斑点形成的密集度主要跟淬火升温时间有关，通过对淬火制度的调整，型材表面黑白斑点基本上得到了有效的控制，黑白斑点也能明显减轻，即在淬火时减少淬火升温时间，其淬火升温时间为20分钟至30分钟，能够有效的减少黑白斑点。
为了进一步优化上述方案，淬火升温时间为30分钟，黑白斑点控制效果最好，当然，淬火升温时间也可以为25分钟。淬火升温时间主要与装炉量有关，一般，铝锂合金型材的装炉量为100公斤-900公斤，采用淬火升温时间为20分钟至30分钟时间最佳。其中，铝锂合金型材可以为1420CZ铝锂合金。
本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以对本发明进行若干改进和修饰，这些改进和修饰也落入本发明权利要求的保护范围内。

Claims (5)

1.一种铝锂合金型材黑白斑点控制方法，其特征在于，在淬火时减少淬火升温时间，其淬火升温时间为20分钟至30分钟。
2.根据权利要求1所述的铝锂合金型材黑白斑点控制方法，其特征在于，所述淬火升温时间为30分钟。
3.根据权利要求1所述的铝锂合金型材黑白斑点控制方法，其特征在于，所述淬火升温时间为25分钟。
4.根据权利要求1所述的铝锂合金型材黑白斑点控制方法，其特征在于，铝锂合金型材的装炉量为100公斤-900公斤。
5.根据权利要求1所述的铝锂合金型材黑白斑点控制方法，其特征在于，铝锂合金型材为1420CZ铝锂合金。
CN201510958298.1A 2015-12-18 2015-12-18 一种铝锂合金型材黑白斑点控制方法 Pending CN105369170A (zh)