CN105368331A - Multifunctional bamboo wood processing adhesive and manufacturing method thereof - Google Patents
Multifunctional bamboo wood processing adhesive and manufacturing method thereof Download PDFInfo
- Publication number
- CN105368331A CN105368331A CN201510801222.8A CN201510801222A CN105368331A CN 105368331 A CN105368331 A CN 105368331A CN 201510801222 A CN201510801222 A CN 201510801222A CN 105368331 A CN105368331 A CN 105368331A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- bamboo wood
- wood processing
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a multifunctional bamboo wood processing adhesive and a manufacturing method thereof, and relates to the technical field of bamboo wood processing. The multifunctional bamboo wood processing adhesive comprises the following raw materials: epoxy resin, a thixotropic agent, a flame retardant, an UV absorber, an emulsifier, titania, silica, organic silane coupling agent, butyl acrylate, vinyl acetate, a filler and a pigment, the multifunctional bamboo wood processing adhesive is applicable to bonding of different plastic, paper, wood and bamboo, has good adhesion effect, is non-pollution, non-mildew and non-deguming after long-term bonding, and can be widely used in packaging adhesion and bamboo wood processing bonding fields.
Description
Technical field
The present invention relates to bamboo wood processing technique field, be specifically related to a kind of multifunction bamboo wood processing sizing agent and manufacture method thereof.
Background technology
Existing bamboo wood section is processed with three kinds of methods, and one is that bamboo wood is processed into fiber or powder, stick with glue agent mixing, through mold pressing, extrude, hot-forming; The second is that bamboo wood is processed into bulk or sheet, is pressed into sheet material and section bar through gummed, and as multi-ply wood, finger-jointed plate, unstressed plate etc., the product that this kind of method is produced, has continued the woody body performance deficiency of bamboo, as moisture absorption cracking, corrosion-deformation, damage by worms, inflammable etc.; The third first to be rived well-thought-out plan silk by machinery by former bamboo, the bamboo basket basket body of different shape is formed again after manual assembly, glue are adhesively fixed, then through polishing, boring, mounting handle, bamboo basket needed for final formation, this bamboo basket can also mix the lid made through overmolding with same material, form the bamboo basket gift box of a similar bamboo box.
The starting material of bamboo basket are that growth cycle is short, fast growth, adaptable bamboo is along with China's expanding economy, the prosperity of tourism, golden week economy emergence, the demand of people to ready-to-eat is increasing, bamboo basket have the advantage of low-carbon environment-friendly, for the packaging of numerous food, as: the outer packaging of the various consumer's goods of steamed crab bamboo basket packaging, red bayberry bamboo basket packaging, strawberry bamboo basket packaging, soft-shelled turtle bamboo basket packaging, rice wine bamboo basket etc., and Application Areas is expanded rapidly.As food product pack, and then higher requirement be it is also proposed to bamboo basket processing, this just requires that the sizing agent used in the bamboo basket course of processing will have the performances such as high barrier, high impact properties, thermophilic digestion resistance, resistance to medium, ensure the fresh and nutrition of ready-to-eat, the quality guaranteed period extending food is the most important thing.
Summary of the invention
(1) technical problem solved
Not enough for prior art, the invention provides multifunction bamboo wood processing sizing agent and manufacture method thereof, multifunction bamboo wood processing sizing agent of the present invention is pollution-free, do not go mouldy, can not come unstuck by prolonged adhesion, there is high barrier, high impact properties, thermophilic digestion resistance, resistance to medium, packaging bonding can be widely used in, bamboo wood processing bonding field, ensure that the fresh of ready-to-eat and nutrition, extends the quality guaranteed period of food.
(2) technical scheme
For realizing above object, the present invention is achieved by the following technical programs:
A kind of multifunction bamboo wood processing sizing agent, is made up of the raw material of following weight part: epoxy resin 15-27 part, thixotropic agent 0.5-1 part, fire retardant 0.2-0.8 part, UV absorption agent 3-9 part, emulsifying agent 0.8-2.2 part, titanium dioxide 5-15 part, silicon-dioxide 6-17 part, organo silane coupling agent 4-10 part, butyl acrylate 17-22 part, vinyl acetate 20-25 part, filler 1-4 part, pigment 1-3 part.
Preferably, described multifunction bamboo wood processing sizing agent is made up of the raw material of following weight part: epoxy resin 16-26 part, thixotropic agent 0.6-1 part, fire retardant 0.3-0.7 part, UV absorption agent 3-8 part, emulsifying agent 1.2-2.2 part, titanium dioxide 6-14 part, silicon-dioxide 7-16 part, organo silane coupling agent 5-10 part, butyl acrylate 18-22 part, vinyl acetate 21-25 part, filler 1-3 part, pigment 1-2 part.
Preferably, described multifunction bamboo wood processing sizing agent is made up of the raw material of following weight part: epoxy resin 21 parts, thixotropic agent 0.8 part, fire retardant 0.5 part, 6 parts, UV absorption agent, emulsifying agent 1.6 parts, titanium dioxide 10 parts, silica 11 part, organo silane coupling agent 7 parts, butyl acrylate 20 parts, vinyl acetate 23 parts, filler 2 parts, pigment 2 parts.
Preferably, described multifunction bamboo wood processing sizing agent is made up of the raw material of following weight part: epoxy resin 20 parts, thixotropic agent .07 part, fire retardant 0.6 part, 7 parts, UV absorption agent, emulsifying agent 1.3 parts, titanium dioxide 9 parts, silica 13 parts, organo silane coupling agent 8 parts, butyl acrylate 21 parts, vinyl acetate 24 parts, filler 1 part, pigment 1 part.
Preferably, described emulsifying agent is the compound emulsifying agent that anionic emulsifier and nonionic emulsifying agent are formed.
Preferably, described anionic emulsifier is one or more in alkyl-sulphate, polyvinyl alcohol, Seconary Alkane Sulphonate Sodium compound; Described nonionic emulsifying agent is one or more in alkylaryl Soxylat A 25-7 compounds.
A manufacture method for multifunction bamboo wood processing sizing agent, comprises the following steps:
S1, configuration diluent: each raw material taking weight part, is added in vinyl acetate by selected titanium dioxide, silicon-dioxide, and the obtained diluent that stirs is for subsequent use;
S2, the epoxy resin of weight part is joined stirring and dissolving in butyl acrylate, and the diluent adding step S1 obtained stirs, then add UV absorption agent, emulsifying agent and organo silane coupling agent, stir, obtain mix emulsion fluid;
S3, thixotropic agent, fire retardant, filler, pigment to be added successively in mix emulsion fluid obtained in step S2, fully stirs 40-60min.
(3) beneficial effect
The invention provides a kind of multifunction bamboo wood processing sizing agent and manufacture method thereof, the present invention be applicable to that difference is moulded, paper, wood, bonding between bamboo, there is good bonding effect, pollution-free, do not go mouldy, can not come unstuck by prolonged adhesion, packaging bonding can be widely used in, bamboo wood processing bonding field; Multifunction bamboo wood processing sizing agent of the present invention has uvioresistant, radioprotective, resistant to elevated temperatures function, improves opacity and barrier, makes the quality guaranteed period of its store food of bamboo basket of bamboo wood processing longer.
Embodiment
For making the object of the embodiment of the present invention, technical scheme and advantage clearly, below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1:
The present embodiment multifunction bamboo wood processing sizing agent, is made up of the raw material of following weight part: epoxy resin 15 parts, thixotropic agent 0.5 part, fire retardant 0.2 part, 3 parts, UV absorption agent, emulsifying agent 0.8 part, titanium dioxide 5 parts, silicon-dioxide 6 parts, organo silane coupling agent 4 parts, butyl acrylate 17 parts, vinyl acetate 20 parts, filler 1 part, pigment 1 part.
According to the present embodiment parts by weight of raw materials, its manufacture method comprises the following steps:
S1, configuration diluent: each raw material taking weight part, is added in vinyl acetate by selected titanium dioxide, silicon-dioxide, and the obtained diluent that stirs is for subsequent use;
S2, the epoxy resin of weight part is joined stirring and dissolving in butyl acrylate, and the diluent adding step S1 obtained stirs, then add UV absorption agent, emulsifying agent and organo silane coupling agent, stir, obtain mix emulsion fluid;
S3, thixotropic agent, fire retardant, filler, pigment to be added successively in mix emulsion fluid obtained in step S2, fully stirs 40-60min.
Embodiment 2:
The present embodiment multifunction bamboo wood processing sizing agent, is made up of the raw material of following weight part: epoxy resin 21 parts, thixotropic agent 0.8 part, fire retardant 0.5 part, 6 parts, UV absorption agent, emulsifying agent 1.6 parts, titanium dioxide 10 parts, silica 11 part, organo silane coupling agent 7 parts, butyl acrylate 20 parts, vinyl acetate 23 parts, filler 2 parts, pigment 2 parts.
According to the present embodiment parts by weight of raw materials, its manufacture method is with embodiment 1.
Embodiment 3:
The present embodiment multifunction bamboo wood processing sizing agent, is made up of the raw material of following weight part: epoxy resin 20 parts, thixotropic agent .07 part, fire retardant 0.6 part, 7 parts, UV absorption agent, emulsifying agent 1.3 parts, titanium dioxide 9 parts, silica 13 parts, organo silane coupling agent 8 parts, butyl acrylate 21 parts, vinyl acetate 24 parts, filler 1 part, pigment 1 part.
According to the present embodiment parts by weight of raw materials, its manufacture method is with embodiment 1.
Embodiment 4:
The present embodiment multifunction bamboo wood processing sizing agent, is made up of the raw material of following weight part: epoxy resin 27 parts, thixotropic agent 1 part, fire retardant 0.8 part, 9 parts, UV absorption agent, emulsifying agent 2.2 parts, titanium dioxide 15 parts, silica 17 parts, organo silane coupling agent 10 parts, butyl acrylate 22 parts, vinyl acetate 25 parts, filler 4 parts, pigment 3 parts.
According to the present embodiment parts by weight of raw materials, its manufacture method is with embodiment 1.
It should be noted that, in this article, the such as relational terms of first and second grades and so on is only used for an entity or operation to separate with another entity or operational zone, and not necessarily requires or imply the relation that there is any this reality between these entities or operation or sequentially.And, term " comprises ", " comprising " or its any other variant are intended to contain comprising of nonexcludability, thus make to comprise the process of a series of key element, method, article or equipment and not only comprise those key elements, but also comprise other key elements clearly do not listed, or also comprise by the intrinsic key element of this process, method, article or equipment.When not more restrictions, the key element limited by statement " comprising ... ", and be not precluded within process, method, article or the equipment comprising described key element and also there is other identical element.
Above embodiment is only in order to illustrate technical scheme of the present invention, be not intended to limit, although with reference to previous embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that: it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature; And these amendments or replacement, do not make the essence of appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (7)
1. a multifunction bamboo wood processing sizing agent, it is characterized in that, be made up of the raw material of following weight part: epoxy resin 15-27 part, thixotropic agent 0.5-1 part, fire retardant 0.2-0.8 part, UV absorption agent 3-9 part, emulsifying agent 0.8-2.2 part, titanium dioxide 5-15 part, silicon-dioxide 6-17 part, organo silane coupling agent 4-10 part, butyl acrylate 17-22 part, vinyl acetate 20-25 part, filler 1-4 part, pigment 1-3 part.
2. multifunction bamboo wood processing sizing agent as claimed in claim 1, it is characterized in that, be made up of the raw material of following weight part: epoxy resin 16-26 part, thixotropic agent 0.6-1 part, fire retardant 0.3-0.7 part, UV absorption agent 3-8 part, emulsifying agent 1.2-2.2 part, titanium dioxide 6-14 part, silicon-dioxide 7-16 part, organo silane coupling agent 5-10 part, butyl acrylate 18-22 part, vinyl acetate 21-25 part, filler 1-3 part, pigment 1-2 part.
3. multifunction bamboo wood processing sizing agent as claimed in claim 1, it is characterized in that, be made up of the raw material of following weight part: epoxy resin 21 parts, thixotropic agent 0.8 part, fire retardant 0.5 part, 6 parts, UV absorption agent, emulsifying agent 1.6 parts, titanium dioxide 10 parts, silica 11 part, organo silane coupling agent 7 parts, butyl acrylate 20 parts, vinyl acetate 23 parts, filler 2 parts, pigment 2 parts.
4. multifunction bamboo wood processing sizing agent as claimed in claim 1, it is characterized in that, be made up of the raw material of following weight part: epoxy resin 20 parts, thixotropic agent .07 part, fire retardant 0.6 part, 7 parts, UV absorption agent, emulsifying agent 1.3 parts, titanium dioxide 9 parts, silica 13 parts, organo silane coupling agent 8 parts, butyl acrylate 21 parts, vinyl acetate 24 parts, filler 1 part, pigment 1 part.
5. multifunction bamboo wood processing sizing agent as claimed in claim 1, it is characterized in that, described emulsifying agent is the compound emulsifying agent that anionic emulsifier and nonionic emulsifying agent are formed.
6. multifunction bamboo wood processing sizing agent as claimed in claim 4, is characterized in that, described anionic emulsifier is one or more in alkyl-sulphate, polyvinyl alcohol, Seconary Alkane Sulphonate Sodium compound; Described nonionic emulsifying agent is one or more in alkylaryl Soxylat A 25-7 compounds.
7. a manufacture method for the multifunction bamboo wood processing sizing agent as described in as arbitrary in claim 1-6, is characterized in that, comprise the following steps:
S1, configuration diluent: each raw material taking weight part, is added in vinyl acetate by selected titanium dioxide, silicon-dioxide, and the obtained diluent that stirs is for subsequent use;
S2, the epoxy resin of weight part is joined stirring and dissolving in butyl acrylate, and the diluent adding step S1 obtained stirs, then add UV absorption agent, emulsifying agent and organo silane coupling agent, stir, obtain mix emulsion fluid;
S3, thixotropic agent, fire retardant, filler, pigment to be added successively in mix emulsion fluid obtained in step S2, fully stirs 40-60min.