CN105367946A - Environment-friendly plastic - Google Patents
Environment-friendly plastic Download PDFInfo
- Publication number
- CN105367946A CN105367946A CN201510782232.1A CN201510782232A CN105367946A CN 105367946 A CN105367946 A CN 105367946A CN 201510782232 A CN201510782232 A CN 201510782232A CN 105367946 A CN105367946 A CN 105367946A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- friendly type
- polycarbonate
- type plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses an environment-friendly plastic, which comprises the following raw materials by weight: 12-19 parts of polycaprolactone, 6-13 parts of maleic anhydride modified polyethylene, 15-32 parts of polycarbonate, 10-25 parts of sodium oleoyl amino fatty acid, 3-4 parts of vinyl triethoxy silane, 25-40 parts of polyvinyl chloride and 18-25 parts of titanium magnesium alloy powder. The manufacture process of the environment-friendly plastic provided by the invention is environmentally friendly, and does not cause pollution; and the manufactured plastic has good strength, toughness and heat resistance.
Description
Technical field
The present invention relates to plastic cement technical field, especially, relate to a kind of environment-friendly type plastic.
Background technology
Along with the development of science and technology, field of plastic products focused on plastics product in appearance, higher requirement be it is also proposed to the various performances of plastics, existing plastics pollute larger in making processes, and many disadvantageous effects are brought to plastics, the plastics intensity made, toughness, resistance toheat are poor.
Therefore the plastics developing a kind of environment-friendly type become the necessary trend in market.
Summary of the invention
The object of the invention is to provide a kind of environment-friendly type plastic, pollutes larger problem to solve plastics in prior art in making processes.
For achieving the above object, the invention provides a kind of environment-friendly type plastic, wherein, be made up of the raw material of following weight part: pla-pcl 12 ~ 19 parts; Maleic anhydride modified polyethylene 6 ~ 13 parts; Polycarbonate 15 parts ~ 32 parts; Oleoyl amino acid sodium 10 ~ 25 parts; Vinyltriethoxysilane 3 ~ 4 parts; Polyvinyl chloride 25 ~ 40 parts; And 18 ~ 25 parts, titanium magnesium alloy powder.
Further, the invention provides a kind of environment-friendly type plastic, wherein, be made up of the raw material of following weight part:
Pla-pcl 15 parts; Maleic anhydride modified polyethylene 7 parts; Polycarbonate 20 parts; Oleoyl amino acid sodium 15 parts; Vinyltriethoxysilane 3 parts; Polyvinyl chloride 25 parts; And 18 parts, titanium magnesium alloy powder.
Further, the invention provides a kind of environment-friendly type plastic, wherein, be made up of the raw material of following weight part:
Pla-pcl 19 parts; Maleic anhydride modified polyethylene 13 parts; Polycarbonate 30 parts; Oleoyl amino acid sodium 25 parts; Vinyltriethoxysilane 4 parts; Polyvinyl chloride 35 parts; And 20 parts, titanium magnesium alloy powder.
The present invention has following beneficial effect: the invention provides a kind of environment-friendly type plastic, and environmental protection in making processes can not pollute, and the plastics intensity made, toughness, resistance toheat are fine.
Embodiment
A kind of environment-friendly type plastic that this preferred embodiment provides, its specific implementation process is as follows:
The invention provides a kind of environment-friendly type plastic, wherein, be made up of the raw material of following weight part: pla-pcl 12 ~ 19 parts; Maleic anhydride modified polyethylene 6 ~ 13 parts; Polycarbonate 15 parts ~ 32 parts; Oleoyl amino acid sodium 10 ~ 25 parts; Vinyltriethoxysilane 3 ~ 4 parts; Polyvinyl chloride 25 ~ 40 parts; And 18 ~ 25 parts, titanium magnesium alloy powder.
Embodiment 1:
The invention provides a kind of environment-friendly type plastic, wherein, be made up of the raw material of following weight part:
Pla-pcl 15 parts; Maleic anhydride modified polyethylene 7 parts; Polycarbonate 20 parts; Oleoyl amino acid sodium 15 parts; Vinyltriethoxysilane 3 parts; Polyvinyl chloride 25 parts; And 18 parts, titanium magnesium alloy powder.
Embodiment 2:
The invention provides a kind of environment-friendly type plastic, wherein, be made up of the raw material of following weight part:
Pla-pcl 19 parts; Maleic anhydride modified polyethylene 13 parts; Polycarbonate 30 parts; Oleoyl amino acid sodium 25 parts; Vinyltriethoxysilane 4 parts; Polyvinyl chloride 35 parts; And 20 parts, titanium magnesium alloy powder.
The present invention has following beneficial effect: the invention provides a kind of environment-friendly type plastic, and environmental protection in making processes can not pollute, and the plastics intensity made, toughness, resistance toheat are fine.
As can be seen from the above description, the above embodiments of the present invention achieve following technique effect:
The invention provides a kind of environment-friendly type plastic, environmental protection in making processes, can not pollute, and the plastics intensity made, toughness, resistance toheat are fine.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention; For a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. an environment-friendly type plastic, is characterized in that, is made up of the raw material of following weight part:
Pla-pcl 12 ~ 19 parts;
Maleic anhydride modified polyethylene 6 ~ 13 parts;
Polycarbonate 15 parts ~ 32 parts;
Oleoyl amino acid sodium 10 ~ 25 parts;
Vinyltriethoxysilane 3 ~ 4 parts;
Polyvinyl chloride 25 ~ 40 parts; And
18 ~ 25 parts, titanium magnesium alloy powder.
2. environment-friendly type plastic according to claim 1, is characterized in that: be made up of the raw material of following weight part:
Pla-pcl 15 parts; Maleic anhydride modified polyethylene 7 parts; Polycarbonate 20 parts; Oleoyl amino acid sodium 15 parts; Vinyltriethoxysilane 3 parts; Polyvinyl chloride 25 parts; And 18 parts, titanium magnesium alloy powder.
3. environment-friendly type plastic according to claim 1, is characterized in that: be made up of the raw material of following weight part:
Pla-pcl 19 parts; Maleic anhydride modified polyethylene 13 parts; Polycarbonate 30 parts; Oleoyl amino acid sodium 25 parts; Vinyltriethoxysilane 4 parts; Polyvinyl chloride 35 parts; And 20 parts, titanium magnesium alloy powder.