CN105367943A - Fireproof and flame-retardant PVC tube - Google Patents
Fireproof and flame-retardant PVC tube Download PDFInfo
- Publication number
- CN105367943A CN105367943A CN201510735695.2A CN201510735695A CN105367943A CN 105367943 A CN105367943 A CN 105367943A CN 201510735695 A CN201510735695 A CN 201510735695A CN 105367943 A CN105367943 A CN 105367943A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame retardant
- retardant pvc
- fire resistant
- pvc pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fireproof and flame-retardant PVC tube. The fireproof and flame-retardant PVC tube is prepared from, by weight, 60-80 parts of PVC resin, 1-3 parts of montmorillonite, 1-2 parts of lubricant, 3-5 parts of inorganic flame retardant, 1-3 parts of heat stabilizer, 2-4 parts of filler and 6-10 parts of impact modifier. The prepared PVC tube has the advantages of being high in strength, good in flame retardance and the like.
Description
Technical field
The present invention relates to PVC material technical field, be specifically related to a kind of fire resistant flame retardant pvc pipe.
Background technology
PVC pipeline is the maximum plastic conduit of the market share, accounts for the share of plastic conduit nearly 70%.In recent years, China's PVC development is very fast, and annual growth rate reaches 8%, and the annual growth rate of demand 2%.In plastic pipe, PVC consumption holds a safe lead always, is widely used in water supply and sewerage pipeline.
Polyvinyl chloride resin inherently has high flame retardant, and pure polyvinyl chloride resin oxygen index reaches 24.5, can think a kind of material of excellent flame retardancy.But often add a large amount of auxiliary agents in order to improve Drawing abillity and pliability in its course of processing, and auxiliary agent is generally inflammable substance, a large amount of interpolations then reduce the flame retardant resistance of flexible PVC greatly.In addition, during PVC burning, raw smoke which is large, and interpolation is organic fire retardant mostly, not only poisonous, and easily causes secondary pollution.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of fire resistant flame retardant pvc pipe, and intensity is high, good flame resistance.
A kind of fire resistant flame retardant pvc pipe, is made up of the raw material of following parts by weight: be made up of the raw material of following parts by weight: polyvinyl chloride resin 60-80 part, polynite 1-3 part, lubricant 1-2 part, inorganic combustion inhibitor 3-5 part, thermo-stabilizer 1-3 part, weighting agent 2-4 part, impact modifier 6-10 part.
As a further improvement on the present invention, described polynite is nano imvite.
As a further improvement on the present invention, described inorganic combustion inhibitor is one or both combinations in antimonous oxide, magnesium hydroxide and aluminium hydroxide.
As a further improvement on the present invention, described thermo-stabilizer is rare-earth stearate and hydrotalcite.
As a further improvement on the present invention, described lubricant is stearin.
As a further improvement on the present invention, described impact modifier is MBS auxiliary agent.
Compared with prior art, tool of the present invention has the following advantages and beneficial effect: use inorganic combustion inhibitor, safety non-toxic, can not produce toxic gas; Polynite is a kind of very excellent char-forming agent, can improve Flame Retardancy; MBS auxiliary agent while increase PVC toughness, can not reduce again the resistance toheat of tubing; The use of rare-earth stearate and hydrotalcite, can improve the thermostability of PVC.
Embodiment
Below in conjunction with embodiment, illustrate the present invention further, following embodiment should be understood and be only not used in for illustration of the present invention and limit the scope of the invention.
Embodiment 1
A kind of fire resistant flame retardant pvc pipe, is made up of the raw material of following parts by weight: polyvinyl chloride resin 60 parts, polynite 1 part, lubricant 1 part, inorganic combustion inhibitor 3 parts, thermo-stabilizer 1 part, weighting agent 2 parts, impact modifier 6 parts.
Wherein, polynite is nano imvite; Inorganic combustion inhibitor is one or both combinations in antimonous oxide, magnesium hydroxide and aluminium hydroxide, if two kinds of combinations, mixes according to the ratio of 1:1.5; Thermo-stabilizer is rare-earth stearate and hydrotalcite; Lubricant is stearin; Impact modifier MBS auxiliary agent.
Said components material is taken according to weight part, puts into high-speed mixer, stir 15 minutes at 120 DEG C of temperature, discharging when material is cooled to 35 DEG C; Then twin screw extruder extrusion moulding is fed into.
Embodiment 2
A kind of fire resistant flame retardant pvc pipe, is made up of the raw material of following parts by weight: polyvinyl chloride resin 70 parts, polynite 2 parts, lubricant 1.5 parts, inorganic combustion inhibitor 4 parts, thermo-stabilizer 2 parts, weighting agent 3 parts, impact modifier 8 parts.
Wherein, polynite is nano imvite; Inorganic combustion inhibitor is one or both combinations in antimonous oxide, magnesium hydroxide and aluminium hydroxide, if two kinds of combinations, mixes according to the ratio of 1:1.5; Thermo-stabilizer is rare-earth stearate and hydrotalcite; Lubricant is stearin; Impact modifier MBS auxiliary agent.
Said components material is taken according to weight part, puts into high-speed mixer, stir 15 minutes at 120 DEG C of temperature, discharging when material is cooled to 35 DEG C; Then twin screw extruder extrusion moulding is fed into.
Embodiment 3
A kind of fire resistant flame retardant pvc pipe, is made up of the raw material of following parts by weight: polyvinyl chloride resin 78 parts, polynite 2.5 parts, lubricant 1.8 parts, inorganic combustion inhibitor 4.5 parts, thermo-stabilizer 2.7 parts, weighting agent 3 parts, impact modifier 9 parts.
Wherein, polynite is nano imvite; Inorganic combustion inhibitor is one or both combinations in antimonous oxide, magnesium hydroxide and aluminium hydroxide; Thermo-stabilizer is rare-earth stearate and hydrotalcite; Lubricant is stearin; Impact modifier MBS auxiliary agent.
Said components material is taken according to weight part, puts into high-speed mixer, stir 18 minutes at 120 DEG C of temperature, discharging when material is cooled to 35 DEG C; Then twin screw extruder extrusion moulding is fed into.
Embodiment 4
A kind of fire resistant flame retardant pvc pipe, is made up of the raw material of following parts by weight: polyvinyl chloride resin 80 parts, polynite 3 parts, lubricant 2 parts, inorganic combustion inhibitor 5 parts, thermo-stabilizer 3 parts, weighting agent 4 parts, impact modifier 10 parts.
Wherein, polynite is nano imvite; Inorganic combustion inhibitor is one or both combinations in antimonous oxide, magnesium hydroxide and aluminium hydroxide, if two kinds of combinations, mixes according to the ratio of 1:1.5; Thermo-stabilizer is rare-earth stearate and hydrotalcite; Lubricant is stearin; Impact modifier MBS auxiliary agent.
Said components material is taken according to weight part, puts into high-speed mixer, stir 18 minutes at 120 DEG C of temperature, discharging when material is cooled to 35 DEG C; Then twin screw extruder extrusion moulding is fed into.
Carry out flame retardant resistance test experiments respectively to embodiment 1-4, experimental result is as follows:
Can draw from upper table, prepare pvc pipe flame resistance effect according to material component ratio in embodiment 4 best.
Compare the physicals of the PVC in the physicals of general industry PVC and the present invention, result is as following table:
As can be seen from the above table, the tubing thermotolerance prepared of the present invention is relatively good.
Technique means disclosed in the present invention program is not limited only to the technique means disclosed in above-mentioned technique means, also comprises the technical scheme be made up of above technical characteristic arbitrary combination.
Claims (6)
1. a fire resistant flame retardant pvc pipe, is characterized in that, is made up of the raw material of following parts by weight: polyvinyl chloride resin 60-80 part, polynite 1-3 part, lubricant 1-2 part, inorganic combustion inhibitor 3-5 part, thermo-stabilizer 1-3 part, weighting agent 2-4 part, impact modifier 6-10 part.
2. a kind of fire resistant flame retardant pvc pipe according to claim 1, is characterized in that: described polynite is nano imvite.
3. a kind of fire resistant flame retardant pvc pipe according to claim 1, is characterized in that: described inorganic combustion inhibitor is one or both combinations in antimonous oxide, magnesium hydroxide and aluminium hydroxide.
4. a kind of fire resistant flame retardant pvc pipe according to claim 1, is characterized in that: described thermo-stabilizer is rare-earth stearate and hydrotalcite.
5. a kind of fire resistant flame retardant pvc pipe according to claim 1, is characterized in that: described lubricant is stearin.
6. a kind of fire resistant flame retardant pvc pipe according to claim 1, is characterized in that: described impact modifier is MBS auxiliary agent.