CN105364437A - Manufacturing technology for trimming blades - Google Patents
Manufacturing technology for trimming blades Download PDFInfo
- Publication number
- CN105364437A CN105364437A CN201510601836.1A CN201510601836A CN105364437A CN 105364437 A CN105364437 A CN 105364437A CN 201510601836 A CN201510601836 A CN 201510601836A CN 105364437 A CN105364437 A CN 105364437A
- Authority
- CN
- China
- Prior art keywords
- steel
- blade
- temperature
- ingot
- cutting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a manufacturing technology for trimming blades. The manufacturing technology comprises the main steps of steelmaking, external refining, electroslag re-dissolving, ingot casting, forging, annealing, shot blasting, cutting and repairing. The processes of the manufacturing technology are simple, operation is easy, and produced trimming blades are sharp, resistant to abrasion, high in rigidity and tenacity and suitable for trimming and cutting.
Description
Technical field
The present invention relates to blade production technology, particularly relate to a kind of manufacturing process of trimmer blade.
Background technology
Blade comprises the blade part referring to non-hilt; Be contained in the stalloy of shaving in insurance knife rest; Be contained in the sheet cutlery being mechanically used as to cut.Blade is divided into a lot of type, as circular knife and circular shear blade.The circular shape of profile, general circular knife is applied in plant equipment, mainly cuts, the machining functions such as deburring.Circular knife all has interstitial hole usually, and object to make it be fixed in plant equipment, thus reach cutting function.Wherein also have a lot of money circular blade edge to be dentation (flat tooth, pointed tooth, irregular dentation), the edge of a knife put the first edge on a knife or a pair of scissors two-sided, one side, do not put the first edge on a knife or a pair of scissors three kinds.Slitting blade is mainly used in paper, film, gold/silver foil, cutting of the article such as aluminium foil, Copper Foil, tape, and require that blade cut-out resistance is minimum, mar proof is maximum.Sometimes micron accuracies must be reached for the requirement cutlery of commodity precision.Razor blade stock is widely used in pottery, printing machinery, paper industry, carton, forestry, rubber, plastics, food machinery, light textile, electrical equipment, light industry and machinery, aluminium foil, metalized film, tobacco, cigarette machinery, packaging material, film, electronic apparatus, electric wire, cable, shipbuilding, chemical fibre, glass, weaving, feed, paper tube, forestry, woodworking machinery, plastic crushing, banding, middle envelope machinery, bottom-sealing bag-making machine, timber is processed, packaging for foodstuff, papermaking aluminium foil is cut, metallurgical dynamo-electric, medicinal material, the various industry such as rubber.Therefore the development of following blade industry will be very good.
Summary of the invention
The invention provides a kind of manufacturing process of trimmer blade.For realizing object of the present invention, technical scheme of the present invention is as follows:
A manufacturing process for trimmer blade, is characterized in that, its concrete steps are:
(1) make steel
Iron and steel raw material is heated to 1200-1350 DEG C and carries out melting material, melting material duration is 60-120min;
(2) external refining
By the molten steel that just refines at 1600 DEG C and
ppduring CO=1 atmospheric pressure vacuum container in carry out degassed, deoxidation, desulfurization process;
(3) electroslag remelting
Electroslag remelting at high temperature carries out, and temperature is 1900-1700 DEG C, and smelting electric current is 8000-14000A;
(4) ingot casting
Pour in ingot mould by the molten steel of molten state, cooling forms steel ingot;
(5) forge
Carry out pressure punching blade with forging press to steel ingot shaping, punching pressure is 35-50MPa;
(6) anneal
Carry out stress relief annealing process to blade, heating-up temperature is 500-550 DEG C, and temperature retention time is 2-8h;
(7) ball blast
Clear up cast(ing) surface under velocity of shot is 30-50m/s, cleaning duration is 15-20min;
(8) cut
According to the specification size of trimmer blade, foundry goods is carried out cutting process by abrasive wheel cutting machine, abrasive machine rotating speed is 2000-5000r/min;
(9) repair
Sanding and polishing process is carried out to the otch under cutting;
Preferably, what the middle steel ingot cooling means of step (1) adopted is air-cooled.
Preferably, the forge hot that in step (5), forging adopts, hot forging temperature is 850 DEG C.
Beneficial effect: the invention provides a kind of trimmer blade Forging Technology, its key step comprises steel-making-external refining-electroslag remelting-ingot casting-forging-annealing-ball blast-cutting-repairing, this production process is simple to operation, the trimmer blade produced, sharp wear-resisting, good rigidly toughness is large, is applicable to prune cutting and uses.
Detailed description of the invention
The technological means realized for making the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with detailed description of the invention, setting forth the present invention further.
A manufacturing process for trimmer blade, is characterized in that, its concrete steps are:
(1) make steel
Iron and steel raw material is heated to 1200 DEG C and carries out melting material, melting material duration is 120min;
(2) external refining
By the molten steel that just refines at 1600 DEG C and
ppduring CO=1 atmospheric pressure vacuum container in carry out degassed, deoxidation, desulfurization process;
(3) electroslag remelting
Electroslag remelting at high temperature carries out, and temperature is 1900 DEG C, and smelting electric current is 10000A;
(4) ingot casting
Pour in ingot mould by the molten steel of molten state, cooling forms steel ingot;
(5) forge
Carry out pressure punching blade with forging press to steel ingot shaping, punching pressure is 50MPa;
(6) anneal
Carry out stress relief annealing process to blade, heating-up temperature is 550 DEG C, and temperature retention time is 6h;
(7) ball blast
Clear up cast(ing) surface under velocity of shot is 45m/s, cleaning duration is 15min;
(8) cut
According to the specification size of trimmer blade, foundry goods is carried out cutting process by abrasive wheel cutting machine, abrasive machine rotating speed is 2000r/min;
(9) repair
Sanding and polishing process is carried out to the otch under cutting;
Wherein, what in step (1), steel ingot cooling means adopted is air-cooled, and the forge hot that in step (5), forging adopts, hot forging temperature is 850 DEG C.
The invention provides a kind of manufacturing process of trimmer blade, its key step comprises steel-making-external refining-electroslag remelting-ingot casting-forging-annealing-ball blast-cutting-repairing, and the trimmer blade produced is sharp wear-resisting, and good rigidly toughness is large, is applicable to prune cutting and uses.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. a manufacturing process for trimmer blade, is characterized in that, its concrete steps are:
(1) make steel
Iron and steel raw material is heated to 1200-1350 DEG C and carries out melting material, melting material duration is 60-120min;
(2) external refining
By the molten steel that just refines at 1600 DEG C and
ppduring CO=1 atmospheric pressure vacuum container in carry out degassed, deoxidation, desulfurization process;
(3) electroslag remelting
Electroslag remelting at high temperature carries out, and temperature is 1900-1700 DEG C, and smelting electric current is 8000-14000A;
(4) ingot casting
Pour in ingot mould by the molten steel of molten state, cooling forms steel ingot;
(5) forge
Carry out pressure punching blade with forging press to steel ingot shaping, punching pressure is 35-50MPa;
(6) anneal
Carry out stress relief annealing process to blade, heating-up temperature is 500-550 DEG C, and temperature retention time is 2-8h;
(7) ball blast
Clear up cast(ing) surface under velocity of shot is 30-50m/s, cleaning duration is 15-20min;
(8) cut
According to the specification size of trimmer blade, foundry goods is carried out cutting process by abrasive wheel cutting machine, abrasive machine rotating speed is 2000-5000r/min;
(9) repair
Sanding and polishing process is carried out to the otch under cutting.
2. the manufacturing process of a kind of trimmer blade according to claim 1, is characterized in that, what in step (1), steel ingot cooling means adopted is air-cooled.
3. the manufacturing process of a kind of trimmer blade according to claim 1, is characterized in that, the forge hot that in step (5), forging adopts, hot forging temperature is 850 DEG C.