CN105349823A - 新型锰合金模具材料 - Google Patents
新型锰合金模具材料 Download PDFInfo
- Publication number
- CN105349823A CN105349823A CN201510775140.0A CN201510775140A CN105349823A CN 105349823 A CN105349823 A CN 105349823A CN 201510775140 A CN201510775140 A CN 201510775140A CN 105349823 A CN105349823 A CN 105349823A
- Authority
- CN
- China
- Prior art keywords
- alloy
- mould material
- novel manganese
- resistance
- alloy mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型锰合金模具材料,包括以下重量百分比的成分:Al:13.0%-16.0%、Fe:2.0%-4.0%、Mn:0.8%-1.0%、Re:0.01%-0.5%、Ti:0.1%-1.2%、Co:0.6%-2.0%,余量为Cu,总量为100%。本发明提供的新型锰合金模具材料,添加适量稀土改善了合金的铸造性能,提高了合金熔融液的流动性,减少了铸造缩孔、气孔、偏析及裂纹的倾向,同时稀土对金属表面具有改性作用,明显提高了合金的抗氧化性、抗氢脆、抗磨损、抗腐蚀性能,延长了合金的使用寿命。
Description
技术领域
本发明涉及一种合金材料,具体涉及一种新型锰合金模具材料。
背景技术
锰及锰合金具有高的导热、导电、耐腐蚀性能,以及良好的制造加工性能,因而广泛的应用于电力、电工、机械、航天等许多领域。但随着这些高新技术对材料性能的要求日益苛刻,传统锰合金材料在部分领域已不能满足使用要求,尤其是需要同时满足高强度、高导电性、抗氧化耐热腐蚀性等综合性能场合,如机械制造行业的管材、线材、板材、坯锭等连铸模具结晶器;高强度引线框架锰合金带材;高速铁路用高强度高导电锰合金接触线材;冶金矿热炉电极瓦板、接线板、汇流排、把持器等锰合金材料。虽然,目前在锰合金材料方面做了很多研究,但所研制的高强高导锰合金性能仍无法满足要求。
发明内容
本发明的目的在于,提供一种新型锰合金模具材料,添加适量稀土改善合金的铸造性能,提高合金熔融液的流动性,减少铸造缩孔、气孔、偏析及裂纹的倾向,同时稀土对金属表面具有改性作用,可明显提高合金的抗氧化性、抗氢脆、抗磨损、抗腐蚀性能,延长合金的使用寿命。
所述新型锰合金模具材料,包括以下重量百分比的成分:
Al:13.0%-16.0%、Fe:2.0%-4.0%、Mn:0.8%-1.0%、Re:0.01%-0.5%、Ti:0.1%-1.2%、Co:0.6%-2.0%,余量为Cu,总量为100%。
本发明提供的新型锰合金模具材料,其有益效果在于,添加适量稀土改善了合金的铸造性能,提高了合金熔融液的流动性,减少了铸造缩孔、气孔、偏析及裂纹的倾向,同时稀土对金属表面具有改性作用,明显提高了合金的抗氧化性、抗氢脆、抗磨损、抗腐蚀性能,延长了合金的使用寿命。
具体实施方式
下面结合一个实施例,对本发明提供的新型锰合金模具材料进行详细的说明。
实施例
所述新型锰合金模具材料,包括以下重量百分比的成分:
Al:13.0%-16.0%、Fe:2.0%-4.0%、Mn:0.8%-1.0%、Re:0.01%-0.5%、Ti:0.1%-1.2%、Co:0.6%-2.0%,余量为Cu,总量为100%。
Claims (1)
1.一种新型锰合金模具材料,其特征在于:它包括以下重量百分比的成分:Al:13.0%-16.0%、Fe:2.0%-4.0%、Mn:0.8%-1.0%、Re:0.01%-0.5%、Ti:0.1%-1.2%、Co:0.6%-2.0%,余量为Cu,总量为100%。