CN105349021A - 一种防腐涂料的制备方法 - Google Patents

一种防腐涂料的制备方法 Download PDF

Info

Publication number
CN105349021A
CN105349021A CN201510892727.XA CN201510892727A CN105349021A CN 105349021 A CN105349021 A CN 105349021A CN 201510892727 A CN201510892727 A CN 201510892727A CN 105349021 A CN105349021 A CN 105349021A
Authority
CN
China
Prior art keywords
preparation
anticorrosive paint
parts
stirring
rotating speed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510892727.XA
Other languages
English (en)
Inventor
陈涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510892727.XA priority Critical patent/CN105349021A/zh
Publication of CN105349021A publication Critical patent/CN105349021A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防腐涂料,一种防腐涂料的制备方法,其中,其制备步骤如下:将环氧树脂、三羟基聚醚、甲苯二异氰酸酯放入反应器内混合,混合转速为55r/min,搅拌时间为20min,搅拌完成后,再将乙醇、玻璃粉、滑石粉、二甲苯依次放入搅拌,搅拌转速为45r/min,搅拌时间为15min即可。本发明一种防腐涂料的制备方法的防腐性能极佳,使用时将其喷涂在型材表面,大大提高型材的防腐性能。可广泛用于工程建筑,机械装配等领域。

Description

一种防腐涂料的制备方法
技术领域
本发明涉及一种防腐涂料的制备方法。
背景技术
随着现代工业的迅速发展,人们对于型材的要求也越来越高。目前,一般型材都没有做很好的防腐措施,其防腐效果往往不佳,难以满足现代人对于新型建材的要求,因此研发出一种能够提高型材防腐性能的涂料越来越受到人们的关注。
发明内容
本发明所要解决的技术问题是针对以上弊端提供一种防腐涂料的制备方法。
一种防腐涂料的制备方法,其中,其制备步骤如下:
将环氧树脂、三羟基聚醚、甲苯二异氰酸酯放入反应器内混合,混合转速为55r/min,搅拌时间为20min,搅拌完成后,再将乙醇、玻璃粉、滑石粉、二甲苯依次放入搅拌,搅拌转速为45r/min,搅拌时间为15min即可。
上述一种防腐涂料的制备方法,其中,所述乙醇为无水乙醇。
本发明的有益效果为:本发明一种防腐涂料的制备方法的的防腐性能极佳,使用时将其喷涂在型材表面,大大提高型材的防腐性能。可广泛用于工程建筑,机械装配等领域。
具体实施方式
以下通过具体实施例对本发明的具体实施方式作进一步详细的说明。
实例一:
一种防腐涂料的制备方法,其中,其制备方法如下:将78份环氧树脂、45份三羟基聚醚、13份甲苯二异氰酸酯放入反应器内混合,混合转速为55r/min,搅拌时间为20min,搅拌完成后,再将11份无水乙醇、13份玻璃粉、7份滑石粉、8份二甲苯依次放入搅拌,搅拌转速为45r/min,搅拌时间为15min。即可。
实例二:
一种防腐涂料的制备方法,其中,其制备方法如下:将125份环氧树脂、55份三羟基聚醚、129份甲苯二异氰酸酯放入反应器内混合,混合转速为55r/min,搅拌时间为20min,搅拌完成后,再将17份无水乙醇、25份玻璃粉、12份滑石粉、15份二甲苯依次放入搅拌,搅拌转速为45r/min,搅拌时间为15min。即可。
实例三:
一种防腐涂料的制备方法,其中,其制备方法如下:将90份环氧树脂、52份三羟基聚醚、23份甲苯二异氰酸酯放入反应器内混合,混合转速为55r/min,搅拌时间为20min,搅拌完成后,再将14份无水乙醇、17份玻璃粉、9份滑石粉、11份二甲苯依次放入搅拌,搅拌转速为45r/min,搅拌时间为15min。即可。
本发明的有益效果为:本发明一种防腐涂料的制备方法的的防腐性能极佳,使用时将其喷涂在型材表面,大大提高型材的防腐性能。户外作业使用防腐时长达10年之久,可广泛用于工程建筑,机械装配等领域。
这里本发明的描述和应用是说明性的,并非想将本发明的范围限制在上述实施例中,因此,本发明不受本实施例的限制,任何采用等效替换取得的技术方案均在本发明保护的范围内。

Claims (2)

1.一种防腐涂料的制备方法,其特征在于,其制备步骤如下:
将环氧树脂、三羟基聚醚、甲苯二异氰酸酯放入反应器内混合,混合转速为55r/min,搅拌时间为20min,搅拌完成后,再将乙醇、玻璃粉、滑石粉、二甲苯依次放入搅拌,搅拌转速为45r/min,搅拌时间为15min即可。
2.如权利要求1所述的一种防腐涂料,其特征在于,所述乙醇为无水乙醇。
CN201510892727.XA 2015-12-08 2015-12-08 一种防腐涂料的制备方法 Pending CN105349021A (zh)