CN105348951A - High-wear-resisting non-stick paint and application thereof - Google Patents
High-wear-resisting non-stick paint and application thereof Download PDFInfo
- Publication number
- CN105348951A CN105348951A CN201510864467.5A CN201510864467A CN105348951A CN 105348951 A CN105348951 A CN 105348951A CN 201510864467 A CN201510864467 A CN 201510864467A CN 105348951 A CN105348951 A CN 105348951A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- viscous paint
- application
- high abrasion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
High-wear-resisting non-stick paint is prepared from, by weight, 20-35 parts of monox sol, 40-46 parts of ptfe water-based resin, 6-10 parts of crylic acid, 1-3 parts of silicone oil, 10-15 parts of spherical ceramic micro powder, 10-15 parts of titanium dioxide pigment, 1-3 parts of bentonite, 1-3 parts of silver nitrate, 1-3 parts of aluminum nitrate, 5-10 parts of absolute ethyl alcohol and 5-10 parts of deionized water. The obtained paint system has the advantages of being excellent in crack preventing performance, good in wear resistance, convenient to construct and the like.
Description
Technical field
The present invention relates to kitchen tools technical field of coatings, especially relate to one and be applicable to and decoct dish, high abrasion crack resistence non-viscous paint of the cookers such as baking tray and preparation method thereof.
Background technology
The non-adhesive coating generally applied on the market at present mainly contains two classes, and a class take tetrafluoroethylene (PTFE) as the fluoro coatings of main film forming matter, as Teflon; Another kind of is exactly the ceramic coating prepared by sol-gel method (sol-gel) with silicon sol and alkoxy silane monomer.Adopt the inorganic nano paint prepared of sol-gel technique to overcome the problem of traditional organic coating temperature tolerance, flame resistivity and difference of hardness, it has thermostability, wear-resisting, anti scuffing and the inorganic body properties of materials such as not to fire.This system coating is mainly solvent with water, and also without the need to adding PFOA additive in its manufacture and production process, construction solidification process VOC quantity discharged is few, so be the coating of a kind of complete environmental protection, nontoxic health.On market, the ceramic coating for cooker aspect of the existing FDA of meeting food safety class requirement has some shortcomings below: 1, cracking easily appears in film, especially particularly evident in light-coloured prods; 2, wear resisting property is not good, affects the lasting use of product.
Summary of the invention
For the problems referred to above that prior art exists, the applicant provides a kind of high abrasion non-viscous paint and application thereof.It is excellent that gained coating system of the present invention has crack resistence, and wear resisting property is good, the features such as easy construction.
Technical scheme of the present invention is as follows:
A kind of high abrasion non-viscous paint, is made up of the raw material of following weight part:
Silica sol 20-35 part; Tetrafluoroethylene water-based resin 40-46 part; Vinylformic acid 6-10 part; Silicone oil 1-3 part; Spherical ceramic micro mist 10-15 part; Titanium white powder pigment 10-15 part; Wilkinite 1-3 part; Silver Nitrate 1-3 part; Aluminum nitrate 1-3 part; Dehydrated alcohol 5-10 part; Deionized water 5-10 part.The number of each raw material is weight part above.
Described non-viscous paint is used for the kitchen tackle of coated ceramic, metal base.
The technique effect that the present invention is useful is:
The present invention adopts silica sol and spherical ceramic micro mist, wilkinite, greatly improves the hardness of coating; The application of Silver Nitrate and aluminum nitrate improves toughness and the wear resistance of coating; Binding agent is Environment-friendlynon-toxic non-toxic.Preparation method of the present invention is scientific and reasonable, simple, is convenient to implement, nontoxic to environment; The anti-bacteria ceramic coating of preparation not only has good mechanical property, and intensity is high, and heat resistant and wear resistant is scratch-resistant, diverse in function, can meet the different requirements of human consumer.
Embodiment
Below in conjunction with embodiment, the present invention is specifically described.
Embodiment 1
A kind of high abrasion non-viscous paint, is made up of the raw material of following weight part:
Silica sol 20 parts; Tetrafluoroethylene water-based resin 40 parts; 6 parts, vinylformic acid; Silicone oil 1 part; Spherical ceramic micro mist 10 parts; Titanium white powder pigment 10 parts; Wilkinite 1 part; Silver Nitrate 1 part; Aluminum nitrate 1 part; Dehydrated alcohol 5 parts; Deionized water 5 parts.
Described non-viscous paint is used for the kitchen tackle of coated ceramic, metal base.
Embodiment 2
A kind of high abrasion non-viscous paint, is made up of the raw material of following weight part:
Silica sol 35 parts; Tetrafluoroethylene water-based resin 46 parts; 10 parts, vinylformic acid; Silicone oil 3 parts; Spherical ceramic micro mist 15 parts; Titanium white powder pigment 15 parts; Wilkinite 3 parts; Silver Nitrate 3 parts; Aluminum nitrate 3 parts; Dehydrated alcohol 10 parts; Deionized water 10 parts.
Described non-viscous paint is used for the kitchen tackle of coated ceramic, metal base.
Embodiment 3
A kind of high abrasion non-viscous paint, is made up of the raw material of following weight part:
Silica sol 30 parts; Tetrafluoroethylene water-based resin 42 parts; 8 parts, vinylformic acid; Silicone oil 2 parts; Spherical ceramic micro mist 13 parts; Titanium white powder pigment 12 parts; Wilkinite 2 parts; Silver Nitrate 2 parts; Aluminum nitrate 2 parts; Dehydrated alcohol 8 parts; Deionized water 8 parts.
Described non-viscous paint is used for the kitchen tackle of coated ceramic, metal base.
The number of each raw material is weight part above.
Claims (2)
1. a high abrasion non-viscous paint, is characterized in that being made up of the raw material of following weight part:
Silica sol 20-35 part; Tetrafluoroethylene water-based resin 40-46 part; Vinylformic acid 6-10 part; Silicone oil 1-3 part; Spherical ceramic micro mist 10-15 part; Titanium white powder pigment 10-15 part; Wilkinite 1-3 part; Silver Nitrate 1-3 part; Aluminum nitrate 1-3 part; Dehydrated alcohol 5-10 part; Deionized water 5-10 part.
2. an application for high abrasion non-viscous paint coating according to claim 1, is characterized in that the kitchen tackle of described non-viscous paint for coated ceramic, metal base.