CN105295472A - High-thermal-conductivity non-stick paint - Google Patents
High-thermal-conductivity non-stick paint Download PDFInfo
- Publication number
- CN105295472A CN105295472A CN201510856346.6A CN201510856346A CN105295472A CN 105295472 A CN105295472 A CN 105295472A CN 201510856346 A CN201510856346 A CN 201510856346A CN 105295472 A CN105295472 A CN 105295472A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermal
- powder
- stick paint
- conductivity non
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A high-thermal-conductivity non-stick paint consists of the following raw materials in parts by weight: 2-3.5 parts of graphene powder, 20-30 parts of silicon dioxide sol, 8-10 parts of polyimide, 5-10 parts of methyl methacrylate, 5-10 parts of acrylic acid, 20-30 parts of methyltrimethoxysilane, 2-3 parts of fluorosilicon oil, 10-15 parts of titanium dioxide pigment, 12-15 parts of aluminium oxide wear resistant powder, 1-3 parts of bentonite, 10-15 parts of deionized water and 4-6 parts of ethylene glycol butyl ether. The high-thermal-conductivity non-stick paint is high in thermal conductivity coefficient and good in ductility, can be tightly combined with a base material, is long in service life, has very high market competitiveness, and can be used for kitchen utensils with ceramic and metal bases.
Description
Technical field
The present invention relates to kitchen tools technical field of coatings, especially relate to one and be applicable to and decoct dish, high heat conduction non-viscous paint of the cookers such as baking tray and preparation method thereof.
Background technology
The non-adhesive coating generally applied on the market at present mainly contains two classes, and a class take tetrafluoroethylene (PTFE) as the fluoro coatings of main film forming matter, as Teflon; Another kind of is exactly the ceramic coating prepared by sol-gel method (sol-gel) with silicon sol and alkoxy silane monomer.Adopt the inorganic nano paint prepared of sol-gel technique to overcome the problem of traditional organic coating temperature tolerance, flame resistivity and difference of hardness, it has thermostability, wear-resisting, anti scuffing and the inorganic body properties of materials such as not to fire.This system coating is mainly solvent with water, and also without the need to adding PFOA additive in its manufacture and production process, construction solidification process VOC quantity discharged is few, so be the coating of a kind of complete environmental protection, nontoxic health.On market, the ceramic coating for cooker aspect of the existing FDA of meeting food safety class requirement has some shortcomings below: 1, cracking easily appears in film, especially particularly evident in light-coloured prods; 2, wear resisting property is not good, affects the lasting use of product.
Summary of the invention
For the problems referred to above that prior art exists, the applicant provides a kind of high heat conduction non-stick pan coating.Coating heat transfer coefficient of the present invention is high, and ductility is good, is combined closely, usage period limit for length, has the very large market competitiveness, can be used for the kitchen utensils of pottery, metal base with base material.
Technical scheme of the present invention is as follows:
A kind of high heat conduction non-stick pan coating, is made up of the raw material of following weight part:
Graphene powder 2-3.5 part; Silica sol 20-30 part; Polyimide 8-10 part; Methyl methacrylate 5-10 part; Vinylformic acid 5-10 part; Methyltrimethoxy silane 20-30 part; Fluorosilicon oil 2-3 part; Titanium white powder pigment 10-15 part; Aluminum oxide abrasion-resistant powder 12-15 part; Wilkinite 1-3 part; Deionized water 10-15 part; Butyl glycol ether 4-6 part.The number of each raw material is weight part above.
The technique effect that the present invention is useful is:
This coating heat transfer coefficient is high, comprehensively have employed silicon oxide, aluminum oxide abrasion-resistant powder and wilkinite, make its hardness and wear resistance have also been obtained guarantee, binding agent adopts the organic materials of environment-protecting asepsis composite, bounding force is strong, makes coating have ductility and the splitting resistance of height.
Embodiment
Below in conjunction with embodiment, the present invention is specifically described.
Embodiment 1
A kind of high heat conduction non-stick pan coating, is made up of the raw material of following weight part:
3.5 parts, Graphene powder; Silica sol 30 parts; Polyimide 10 parts; Methyl methacrylate 10 parts; 10 parts, vinylformic acid; Methyltrimethoxy silane 30 parts; Fluorosilicon oil 3 parts; Titanium white powder pigment 15 parts; Aluminum oxide abrasion-resistant powder 15 parts; Wilkinite 3 parts; Deionized water 15 parts; Butyl glycol ether 6 parts.
Embodiment 2
A kind of high heat conduction non-stick pan coating, is made up of the raw material of following weight part:
2 parts, Graphene powder; Silica sol 20 parts; Polyimide 8 parts; Methyl methacrylate 5 parts; 5 parts, vinylformic acid; Methyltrimethoxy silane 20 parts; Fluorosilicon oil 2 parts; Titanium white powder pigment 10 parts; Aluminum oxide abrasion-resistant powder 12 parts; Wilkinite 1 part; Deionized water 10 parts; Butyl glycol ether 4 parts.
Embodiment 3
A kind of high heat conduction non-stick pan coating, is made up of the raw material of following weight part:
3 parts, Graphene powder; Silica sol 25 parts; Polyimide 9 parts; Methyl methacrylate 8 parts; 7 parts, vinylformic acid; Methyltrimethoxy silane 25 parts; Fluorosilicon oil 2 parts; Titanium white powder pigment 12 parts; Aluminum oxide abrasion-resistant powder 14 parts; Wilkinite 2 parts; Deionized water 12 parts; Butyl glycol ether 5 parts.
The number of each raw material is weight part above.
Claims (1)
1. a high heat conduction non-stick pan coating, is characterized in that being made up of the raw material of following weight part:
Graphene powder 2-3.5 part; Silica sol 20-30 part; Polyimide 8-10 part; Methyl methacrylate 5-10 part; Vinylformic acid 5-10 part; Methyltrimethoxy silane 20-30 part; Fluorosilicon oil 2-3 part; Titanium white powder pigment 10-15 part; Aluminum oxide abrasion-resistant powder 12-15 part; Wilkinite 1-3 part; Deionized water 10-15 part; Butyl glycol ether 4-6 part.