CN104151898A - High-temperature-resistant paint - Google Patents
High-temperature-resistant paint Download PDFInfo
- Publication number
- CN104151898A CN104151898A CN201410358727.7A CN201410358727A CN104151898A CN 104151898 A CN104151898 A CN 104151898A CN 201410358727 A CN201410358727 A CN 201410358727A CN 104151898 A CN104151898 A CN 104151898A
- Authority
- CN
- China
- Prior art keywords
- parts
- silane coupling
- ethyl cellulose
- resistant coating
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a high-temperature-resistant paint which is prepared from the following raw materials in parts by weight: 30-50 parts of epoxy modified organic silicon resin, 10-20 parts of hexachlorocyclotriphosphonitrile, 10-15 parts of ceramic powder, 6-10 parts of mica powder, 9-13 parts of trichloroethylene, 2-5 parts of dispersing and wetting agent, 1-4 parts of silane coupling agent, 4-6 parts of ethyl cellulose and 1-3 parts of n-butanol. The paint has the advantages of favorable high temperature resistance, excellent corrosion resistance, favorable viscosity and high adhesive force, and is widely applied to the industrial fields of metallurgy, petroleum industry, natural gas exploitation, aerospace and the like.
Description
Technical field
The present invention relates to a kind of high-temperature resistant coating.
Background technology
High-temperature resistant coating can be divided into organic high temperature-resistant coating and the large class of refractory inorganic paint two.Phosphoric acid salt lead powder coating is exactly a kind of refractory inorganic paint.It has the feature of heat-resisting, anti-slander, conduction, and raw material is cheap and easy to get, and preparation technology is extremely simple.This coating is commonly used to the pole plate of brushing high-voltage electrostatic dust separator, can extend the work-ing life of electric precipitator and improve operating conditions.Therefore, be subject to cement, the clamor extensive attention of department of the use electric precipitations such as metallurgy, electric industry.Environmental protection, harmless.The general strong adhesion of high-temperature resistant coating, good toughness, is adapted to the application of stainless steel, aluminium, iron phosphide, pottery, bamboo carbon material.Excellent resistance to elevated temperatures, under long term high temperature uses, gloss and colour stable.Excellent scratch resistance and antiseptic property, hardness is high, and wear resistance is good.The excellent ability of not being stained with that continues, can withstand long term exposure boiling water, the edible materials such as salt solution, milk, egg, butter.
Summary of the invention
The deficiency existing for prior art, the technical problem to be solved in the present invention is that a kind of coating is provided, resistance to elevated temperatures is good, antiseptic property is excellent, and have good viscosity, strong adhesion, is widely used in the industrial circles such as metallurgy, petroleum industry, Natural gas extraction, aerospace.
For solving the problems of the technologies described above, technical scheme of the present invention is, a kind of high-temperature resistant coating, and its raw material by following parts by weight is made:
Epoxy modified silicone resin 30-50 part, hexachlorocyclotriphosphazene 10-20 part, ceramics powder 10-15 part, mica powder 6-10 part, trieline 9-13 part, disperses wetting agent 2-5 part, silane coupling agent 1-4 part, ethyl cellulose 4-6 part, propyl carbinol 1-3 part.
Optimisation technique scheme of the present invention is, a kind of high-temperature resistant coating, and its raw material by following parts by weight is made:
40 parts of epoxy modified silicone resins, 15 parts of hexachlorocyclotriphosphazenes, 13 parts of ceramics powders, 8 parts of mica powders, 11 parts of trielines, disperse 4 parts of wetting agents, 2 parts of silane coupling agents, 5 parts of ethyl cellulose, 2 parts of propyl carbinols.
The invention has the beneficial effects as follows, coating resistance to elevated temperatures of the present invention is good, antiseptic property is excellent, and has good viscosity, and strong adhesion, is widely used in the industrial circles such as metallurgy, petroleum industry, Natural gas extraction, aerospace.
Embodiment
embodiment 1
A kind of high-temperature resistant coating, its raw material by following parts by weight is made:
30 parts of epoxy modified silicone resins, 10 parts of hexachlorocyclotriphosphazenes, 10 parts of ceramics powders, 6 parts of mica powders, 9 parts of trielines, disperse 2 parts of wetting agents, 1 part of silane coupling agent, 4 parts of ethyl cellulose, 1 part of propyl carbinol.
embodiment 2
A kind of high-temperature resistant coating, its raw material by following parts by weight is made:
50 parts of epoxy modified silicone resins, 20 parts of hexachlorocyclotriphosphazenes, 15 parts of ceramics powders, 10 parts of mica powders, 13 parts of trielines, disperse 5 parts of wetting agents, 4 parts of silane coupling agents, 6 parts of ethyl cellulose, 3 parts of propyl carbinols.
embodiment 3
A kind of high-temperature resistant coating, its raw material by following parts by weight is made:
40 parts of epoxy modified silicone resins, 15 parts of hexachlorocyclotriphosphazenes, 13 parts of ceramics powders, 8 parts of mica powders, 11 parts of trielines, disperse 4 parts of wetting agents, 2 parts of silane coupling agents, 5 parts of ethyl cellulose, 2 parts of propyl carbinols.
Claims (2)
1. a high-temperature resistant coating, is characterized in that: its raw material by following parts by weight is made:
Epoxy modified silicone resin 30-50 part, hexachlorocyclotriphosphazene 10-20 part, ceramics powder 10-15 part, mica powder 6-10 part, trieline 9-13 part, disperses wetting agent 2-5 part, silane coupling agent 1-4 part, ethyl cellulose 4-6 part, propyl carbinol 1-3 part.
2. high-temperature resistant coating according to claim 1, is characterized in that: its raw material by following parts by weight is made:
40 parts of epoxy modified silicone resins, 15 parts of hexachlorocyclotriphosphazenes, 13 parts of ceramics powders, 8 parts of mica powders, 11 parts of trielines, disperse 4 parts of wetting agents, 2 parts of silane coupling agents, 5 parts of ethyl cellulose, 2 parts of propyl carbinols.