CN105348942A - Corrosion-resistant stamping part fixture and preparation process thereof - Google Patents
Corrosion-resistant stamping part fixture and preparation process thereof Download PDFInfo
- Publication number
- CN105348942A CN105348942A CN201510886352.6A CN201510886352A CN105348942A CN 105348942 A CN105348942 A CN 105348942A CN 201510886352 A CN201510886352 A CN 201510886352A CN 105348942 A CN105348942 A CN 105348942A
- Authority
- CN
- China
- Prior art keywords
- parts
- protective layer
- fixture
- stablizer
- oxidation inhibitor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a corrosion-resistant stamping part fixture and a preparation process thereof. The corrosion-resistant stamping part fixture comprises a fixture body, wherein the surface of the fixture body is coated with a protective layer; the protective layer comprises the following ingredients: 18-22 parts of polyvinyl chloride resin, 15-25 parts of ethylene-tetrafluoroethylene copolymer, 9-13 parts of pigment filler, 3-7 parts of a levelling agent, 3-5 parts of a stabilizer, 6-9 parts of an antioxidant, 18-20 parts of epoxy resin, 38-42 parts of water and 3-9 parts of composite rare earth. According to the invention, the service life of the fixture is prolonged and the working efficiency is improved.
Description
Technical field
The present invention relates to stamping parts field, relate to a kind of corrosion-resistant stamping parts fixture and preparation technology thereof specifically.
Background technology
At present in stamping parts manufacturing processed, generally adopting artificial manual manipulation when picking and placeing stamping parts, under negligence of operation, easily human body being damaged, there is security incident, so utilize the off-line operation of stamping parts fixture, under the overall situation of this humidity of China, ferrous products easily becomes damp corrosion, cause the phenomenon that accessory working life shortens greatly, add cost, reduce working efficiency, now research and develop a kind of corrosion-resistant stamping parts fixture and the preparation technology thereof that can overcome above defect.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of corrosion-resistant stamping parts fixture and preparation technology thereof, and the utilization ratio that corrosion-resistant stamping parts fixture can improve stamping parts fixture reduces learies, improves working efficiency.
For achieving the above object, the invention provides following technical scheme: a kind of corrosion-resistant stamping parts fixture and preparation technology thereof, comprise fixture, chucking surface is coated with layer protective layer, and protective layer comprises following composition:
Polyvinyl chloride (PVC) RESINS 18-22 part
Ethylene-tetrafluoroethylene copolymer 15-25 part
Color stuffing 9-13 part
Flow agent 3-7 part
Stablizer 3-5 part
Oxidation inhibitor 6-9 part
Epoxy resin 18-20 part
Water 38-42 part
Compound rare-earth 3-9 part;
Color stuffing is the mixture of red iron oxide and zinc phosphate; Stablizer is CH
4o
2calcium zinc stabilizer; Oxidation inhibitor is the mixture of antioxidant 1076 and antioxidant 1010; Flow agent is polyacrylic acid or Walocel MT 20.000PV; Compound rare-earth comprises following component by mass percentage: dysprosium: 9-15%, lanthanum: 6-17%, cerium: 19-25%, praseodymium: 6-18%, neodymium: 6-11%, and all the other are lanthanon, and each component sum of above lanthanide rare is 100%.
Aforesaid corrosion-resistant stamping parts fixture and preparation technology thereof, chucking surface is coated with layer protective layer, and protective layer comprises following composition:
Polyvinyl chloride (PVC) RESINS 18 parts
Ethylene-tetrafluoroethylene copolymer 15 parts
Color stuffing 9 parts
Flow agent 3 parts
Stablizer 3 parts
6 parts, oxidation inhibitor
Epoxy resin 18 parts
38 parts, water
Compound rare-earth 3 parts;
Color stuffing is the mixture of red iron oxide and zinc phosphate; Stablizer is CH
4o
2calcium zinc stabilizer; Oxidation inhibitor is the mixture of antioxidant 1076 and antioxidant 1010; Flow agent is polyacrylic acid or Walocel MT 20.000PV; Compound rare-earth comprises following component by mass percentage: dysprosium: 9%, lanthanum: 6%, cerium: 19%, praseodymium: 6%, neodymium: 6%, and all the other are lanthanon, and each component sum of above lanthanide rare is 100%.
Aforesaid corrosion-resistant stamping parts fixture and preparation technology thereof, chucking surface is coated with layer protective layer, and protective layer comprises following composition:
Polyvinyl chloride (PVC) RESINS 22 parts
Ethylene-tetrafluoroethylene copolymer 25 parts
Color stuffing 13 parts
Flow agent 7 parts
Stablizer 5 parts
9 parts, oxidation inhibitor
Epoxy resin 20 parts
42 parts, water
Compound rare-earth 9 parts;
Described color stuffing is the mixture of red iron oxide and zinc phosphate; Described stablizer is CH
4o
2calcium zinc stabilizer; Described oxidation inhibitor is the mixture of antioxidant 1076 and antioxidant 1010; Described flow agent is polyacrylic acid or Walocel MT 20.000PV; Described compound rare-earth comprises following component by mass percentage: dysprosium: 15%, lanthanum: 17%, cerium: 25%, praseodymium: 18%, neodymium: 11%, and all the other are lanthanon, and each component sum of above lanthanide rare is 100%.
Aforesaid corrosion-resistant stamping parts fixture and preparation technology thereof, concrete preparation method is as follows for the protective layer on this fixture:
(1) polyvinyl chloride (PVC) RESINS, color stuffing, flow agent, oxidation inhibitor are joined in ball grinder by above-mentioned formula and carry out ball milling, its medium speed is 250-300 rev/min, every 40 minutes positive and negative alternates once, ball milling 4-5 hour; Take out and dry in 50 DEG C of baking ovens, then sieve below powder to 300 order;
(2) gained mixture in above-mentioned steps (1) is added in glass-melting furnace at 1300-1500 DEG C of melting 1.5-2h, high temp glass melt after melting is put into rapidly cold water cold quenching and is become glass yarn, ball mill is pulverized, wears into granularity and be less than 200 object powder;
Wherein, described Ball-milling Time is 17-23h;
(3) ethylene-tetrafluoroethylene copolymer, stablizer, epoxy resin, water, compound rare-earth is added by the mixed powder in above-mentioned steps (2); vibrate 40-55min in ultrasonator; room temperature leaves standstill 72h; then be coated in the surface of fixture, under room temperature, dry solidification can obtain this protective layer.
Technical scheme beneficial effect of the present invention is adopted to be: the stamping parts fixture protective layer prepared in the present invention can be unaffected in a humidity environment, adds the life-span of fixture, decrease condemnation factor, improve working efficiency; The stablizer added in the present invention is CH
4o
2calcium zinc stabilizer, this stablizer has goodish stability, the transparency, and good processability; Oxidation inhibitor is the mixture of antioxidant 1076 and antioxidant 1010, and this oxidation inhibitor is nontoxic, and good processability is cheap; Flow agent is polyacrylic acid or Walocel MT 20.000PV, and stability is high, can improve grinding efficiency.
Embodiment
embodiment 1
The present embodiment provides a kind of corrosion-resistant stamping parts fixture and preparation technology thereof, and comprise fixture, chucking surface is coated with layer protective layer, and protective layer comprises following composition:
Polyvinyl chloride (PVC) RESINS 18 parts
Ethylene-tetrafluoroethylene copolymer 15 parts
Color stuffing 9 parts
Flow agent 3 parts
Stablizer 3 parts
6 parts, oxidation inhibitor
Epoxy resin 18 parts
38 parts, water
Compound rare-earth 3 parts;
Color stuffing is the mixture of red iron oxide and zinc phosphate; Stablizer is CH
4o
2calcium zinc stabilizer; Oxidation inhibitor is the mixture of antioxidant 1076 and antioxidant 1010; Flow agent is polyacrylic acid or Walocel MT 20.000PV; Compound rare-earth comprises following component by mass percentage: dysprosium: 9%, lanthanum: 6%, cerium: 19%, praseodymium: 6%, neodymium: 6%, and all the other are lanthanon, and each component sum of above lanthanide rare is 100%;
Concrete preparation method is as follows for protective layer on above-mentioned fixture:
(1) polyvinyl chloride (PVC) RESINS, color stuffing, flow agent, oxidation inhibitor are joined in ball grinder by above-mentioned formula and carry out ball milling, its medium speed is 250 revs/min, every 40 minutes positive and negative alternates once, ball milling 4 hours; Take out and dry in 50 DEG C of baking ovens, then sieve below powder to 300 order;
(2) add at 1300 DEG C of melting 1.5h in glass-melting furnace by gained mixture in above-mentioned steps (1), the high temp glass melt after melting is put into rapidly cold water cold quenching and is become glass yarn, and ball mill is pulverized, and wears into granularity and is less than 200 object powder;
Wherein, described Ball-milling Time is 17h;
(3) ethylene-tetrafluoroethylene copolymer, stablizer, epoxy resin, water, compound rare-earth is added by the mixed powder in above-mentioned steps (2); vibrate 40min in ultrasonator; room temperature leaves standstill 72h, is then coated in the surface of fixture, and under room temperature, dry solidification can obtain this protective layer.
embodiment 2
The present embodiment provides a kind of corrosion-resistant stamping parts fixture and preparation technology thereof, and comprise fixture, chucking surface is coated with layer protective layer, and protective layer comprises following composition:
Polyvinyl chloride (PVC) RESINS 22 parts
Ethylene-tetrafluoroethylene copolymer 25 parts
Color stuffing 13 parts
Flow agent 7 parts
Stablizer 5 parts
9 parts, oxidation inhibitor
Epoxy resin 20 parts
42 parts, water
Compound rare-earth 9 parts;
Described color stuffing is the mixture of red iron oxide and zinc phosphate; Described stablizer is CH
4o
2calcium zinc stabilizer; Described oxidation inhibitor is the mixture of antioxidant 1076 and antioxidant 1010; Described flow agent is polyacrylic acid or Walocel MT 20.000PV; Described compound rare-earth comprises following component by mass percentage: dysprosium: 15%, lanthanum: 17%, cerium: 25%, praseodymium: 18%, neodymium: 11%, and all the other are lanthanon, and each component sum of above lanthanide rare is 100%;
Concrete preparation method is as follows for protective layer on above-mentioned fixture:
(1) polyvinyl chloride (PVC) RESINS, color stuffing, flow agent, oxidation inhibitor are joined in ball grinder by above-mentioned formula and carry out ball milling, its medium speed is 300 revs/min, every 40 minutes positive and negative alternates once, ball milling 5 hours; Take out and dry in 50 DEG C of baking ovens, then sieve below powder to 300 order;
(2) add at 1500 DEG C of melting 2h in glass-melting furnace by gained mixture in above-mentioned steps (1), the high temp glass melt after melting is put into rapidly cold water cold quenching and is become glass yarn, and ball mill is pulverized, and wears into granularity and is less than 200 object powder;
Wherein, described Ball-milling Time is 23h;
(3) ethylene-tetrafluoroethylene copolymer, stablizer, epoxy resin, water, compound rare-earth is added by the mixed powder in above-mentioned steps (2); vibrate 55min in ultrasonator; room temperature leaves standstill 72h, is then coated in the surface of fixture, and under room temperature, dry solidification can obtain this protective layer.
In addition to the implementation, the present invention can also have other embodiments.All employings are equal to the technical scheme of replacement or equivalent transformation formation, all drop on the protection domain of application claims.
Claims (4)
1. corrosion-resistant stamping parts fixture and a preparation technology thereof, comprise fixture, it is characterized in that: described chucking surface is coated with layer protective layer, described protective layer comprises following composition:
Polyvinyl chloride (PVC) RESINS 18-22 part
Ethylene-tetrafluoroethylene copolymer 15-25 part
Color stuffing 9-13 part
Flow agent 3-7 part
Stablizer 3-5 part
Oxidation inhibitor 6-9 part
Epoxy resin 18-20 part
Water 38-42 part
Compound rare-earth 3-9 part;
Described color stuffing is the mixture of red iron oxide and zinc phosphate; Described stablizer is CH
4o
2calcium zinc stabilizer; Described oxidation inhibitor is the mixture of antioxidant 1076 and antioxidant 1010; Described flow agent is polyacrylic acid or Walocel MT 20.000PV; Described compound rare-earth comprises following component by mass percentage: dysprosium: 9-15%, lanthanum: 6-17%, cerium: 19-25%, praseodymium: 6-18%, neodymium: 6-11%, and all the other are lanthanon, and each component sum of above lanthanide rare is 100%.
2. corrosion-resistant stamping parts fixture according to claim 1 and preparation technology thereof, it is characterized in that: described chucking surface is coated with layer protective layer, described protective layer comprises following composition:
Polyvinyl chloride (PVC) RESINS 18 parts
Ethylene-tetrafluoroethylene copolymer 15 parts
Color stuffing 9 parts
Flow agent 3 parts
Stablizer 3 parts
6 parts, oxidation inhibitor
Epoxy resin 18 parts
38 parts, water
Compound rare-earth 3 parts;
Described color stuffing is the mixture of red iron oxide and zinc phosphate; Described stablizer is CH
4o
2calcium zinc stabilizer; Described oxidation inhibitor is the mixture of antioxidant 1076 and antioxidant 1010; Described flow agent is polyacrylic acid or Walocel MT 20.000PV; Described compound rare-earth comprises following component by mass percentage: dysprosium: 9%, lanthanum: 6%, cerium: 19%, praseodymium: 6%, neodymium: 6%, and all the other are lanthanon, and each component sum of above lanthanide rare is 100%.
3. corrosion-resistant stamping parts fixture according to claim 1 and preparation technology thereof, it is characterized in that: described chucking surface is coated with layer protective layer, described protective layer comprises following composition:
Polyvinyl chloride (PVC) RESINS 22 parts
Ethylene-tetrafluoroethylene copolymer 25 parts
Color stuffing 13 parts
Flow agent 7 parts
Stablizer 5 parts
9 parts, oxidation inhibitor
Epoxy resin 20 parts
42 parts, water
Compound rare-earth 9 parts;
Described color stuffing is the mixture of red iron oxide and zinc phosphate; Described stablizer is CH
4o
2calcium zinc stabilizer; Described oxidation inhibitor is the mixture of antioxidant 1076 and antioxidant 1010; Described flow agent is polyacrylic acid or Walocel MT 20.000PV; Described compound rare-earth comprises following component by mass percentage: dysprosium: 15%, lanthanum: 17%, cerium: 25%, praseodymium: 18%, neodymium: 11%, and all the other are lanthanon, and each component sum of above lanthanide rare is 100%.
4. the corrosion-resistant stamping parts fixture according to claim arbitrary in claim 1-3 and preparation technology thereof, is characterized in that, concrete preparation method is as follows for the protective layer on this fixture:
(1) polyvinyl chloride (PVC) RESINS, color stuffing, flow agent, oxidation inhibitor are joined in ball grinder by above-mentioned formula and carry out ball milling, its medium speed is 250-300 rev/min, every 40 minutes positive and negative alternates once, ball milling 4-5 hour; Take out and dry in 50 DEG C of baking ovens, then sieve below powder to 300 order;
(2) gained mixture in above-mentioned steps (1) is added in glass-melting furnace at 1300-1500 DEG C of melting 1.5-2h, high temp glass melt after melting is put into rapidly cold water cold quenching and is become glass yarn, ball mill is pulverized, wears into granularity and be less than 200 object powder;
Wherein, described Ball-milling Time is 17-23h;
(3) ethylene-tetrafluoroethylene copolymer, stablizer, epoxy resin, water, compound rare-earth is added by the mixed powder in above-mentioned steps (2); vibrate 40-55min in ultrasonator; room temperature leaves standstill 72h; then be coated in the surface of fixture, under room temperature, dry solidification can obtain this protective layer.