CN105348883A - 一种稳定性汽车专用涂层材料 - Google Patents
一种稳定性汽车专用涂层材料 Download PDFInfo
- Publication number
- CN105348883A CN105348883A CN201511013287.2A CN201511013287A CN105348883A CN 105348883 A CN105348883 A CN 105348883A CN 201511013287 A CN201511013287 A CN 201511013287A CN 105348883 A CN105348883 A CN 105348883A
- Authority
- CN
- China
- Prior art keywords
- parts
- polypropylene
- coating material
- automobiles
- stable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种稳定性汽车专用涂层材料,其由以下重量份数的原料制成:甲基丙烯酸甲酯16-24份,二甲基硅氧烷0.4-0.9份,异氰尿酸三缩水甘油酯0.3-1.5份,聚丙烯13-22份,热塑性聚氨酯15-26份,乙烯共聚物弹性体10-20份,二氧化硅粉体4-7份,石灰石12-24份,消泡剂1.2-2.2份,改性丙烯酸树脂30-36份,钛白粉4-8份,溶剂7-13份,聚丙稀4-7份,稳定剂2-4份,分散剂1-3份。本发明的有益效果是,本发明的稳定性汽车专用涂层材料,具有耐老化耐腐蚀的优势,减速制动平稳,涂层性能稳定,保光性、耐酸雨性得到显著的提高,而且成本低。
Description
技术领域
本发明涉及一种稳定性汽车专用涂层材料。
背景技术
随着汽车作为高档消费品进入普通大众的消费视野,汽车及其表面涂料的年产量均以超过百分十的增幅呈现在人们面前,与此同时汽车的外观与使用寿命日益受到重视。汽车涂装的目的是使汽车车身具有优良的外观装饰性、耐候性、舒适性、密封性、耐腐蚀性,以提高其商品价值和延长其使用年限。目前随着汽车工业的发展,对汽车涂层材料的要求越来严格,根据汽车的使用环境条件,涂层不仅要具有很好的耐候性和耐腐蚀性,还需应具有极好的装饰性和稳定性。
发明内容
针对现有技术的不足,本发明要解决的问题是,提供一种稳定性汽车专用涂层材料,具有耐老化耐腐蚀的优势,减速制动平稳,涂层性能稳定,保光性、耐酸雨性得到显著的提高,而且成本低。
为解决上述技术问题,本发明的技术方案是,一种稳定性汽车专用涂层材料,其由以下重量份数的原料制成:
甲基丙烯酸甲酯16-24份,二甲基硅氧烷0.4-0.9份,异氰尿酸三缩水甘油酯0.3-1.5份,聚丙烯13-22份,热塑性聚氨酯15-26份,乙烯共聚物弹性体10-20份,二氧化硅粉体4-7份,石灰石12-24份,消泡剂1.2-2.2份,改性丙烯酸树脂30-36份,钛白粉4-8份,溶剂7-13份,聚丙稀4-7份,稳定剂2-4份,分散剂1-3份。
优化的,一种稳定性汽车专用涂层材料,其由以下重量份数的原料制成:
甲基丙烯酸甲酯20份,二甲基硅氧烷0.6份,异氰尿酸三缩水甘油酯0.8份,聚丙烯18份,热塑性聚氨酯20份,乙烯共聚物弹性体15份,二氧化硅粉体5.5份,石灰石18份,消泡剂1.8份,改性丙烯酸树脂33份,钛白粉6份,溶剂10份,聚丙稀5.5份,稳定剂3份,分散剂2份。
本发明的有益效果是,本发明的稳定性汽车专用涂层材料,具有耐老化耐腐蚀的优势,减速制动平稳,涂层性能稳定,保光性、耐酸雨性得到显著的提高,而且成本低。
具体实施方式
实施例1
名字,其由以下重量份数的原料制成:
甲基丙烯酸甲酯16份,二甲基硅氧烷0.4份,异氰尿酸三缩水甘油酯0.3份,聚丙烯13份,热塑性聚氨酯15份,乙烯共聚物弹性体10份,二氧化硅粉体4份,石灰石12份,消泡剂1.2份,改性丙烯酸树脂30份,钛白粉4份,溶剂7份,聚丙稀4份,稳定剂2份,分散剂1份。
实施例2
名字,其由以下重量份数的原料制成:
甲基丙烯酸甲酯24份,二甲基硅氧烷0.9份,异氰尿酸三缩水甘油酯1.5份,聚丙烯22份,热塑性聚氨酯26份,乙烯共聚物弹性体20份,二氧化硅粉体7份,石灰石24份,消泡剂2.2份,改性丙烯酸树脂36份,钛白粉8份,溶剂13份,聚丙稀7份,稳定剂4份,分散剂3份。
实施例3
一种稳定性汽车专用涂层材料,其由以下重量份数的原料制成:
甲基丙烯酸甲酯20份,二甲基硅氧烷0.6份,异氰尿酸三缩水甘油酯0.8份,聚丙烯18份,热塑性聚氨酯20份,乙烯共聚物弹性体15份,二氧化硅粉体5.5份,石灰石18份,消泡剂1.8份,改性丙烯酸树脂33份,钛白粉6份,溶剂10份,聚丙稀5.5份,稳定剂3份,分散剂2份。
Claims (2)
1.一种稳定性汽车专用涂层材料,其特征在于:其由以下重量份数的原料制成:
甲基丙烯酸甲酯16-24份,二甲基硅氧烷0.4-0.9份,异氰尿酸三缩水甘油酯0.3-1.5份,聚丙烯13-22份,热塑性聚氨酯15-26份,乙烯共聚物弹性体10-20份,二氧化硅粉体4-7份,石灰石12-24份,消泡剂1.2-2.2份,改性丙烯酸树脂30-36份,钛白粉4-8份,溶剂7-13份,聚丙稀4-7份,稳定剂2-4份,分散剂1-3份。
2.根据权利要求1所述的稳定性汽车专用涂层材料,其特征在于:其由以下重量份数的原料制成:
甲基丙烯酸甲酯20份,二甲基硅氧烷0.6份,异氰尿酸三缩水甘油酯0.8份,聚丙烯18份,热塑性聚氨酯20份,乙烯共聚物弹性体15份,二氧化硅粉体5.5份,石灰石18份,消泡剂1.8份,改性丙烯酸树脂33份,钛白粉6份,溶剂10份,聚丙稀5.5份,稳定剂3份,分散剂2份。