CN105332142A - Garment fabric adding with metal materials - Google Patents

Garment fabric adding with metal materials Download PDF

Info

Publication number
CN105332142A
CN105332142A CN201510878165.3A CN201510878165A CN105332142A CN 105332142 A CN105332142 A CN 105332142A CN 201510878165 A CN201510878165 A CN 201510878165A CN 105332142 A CN105332142 A CN 105332142A
Authority
CN
China
Prior art keywords
fibre
warp thread
fabric
fiber
weight ratio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510878165.3A
Other languages
Chinese (zh)
Inventor
沈雪球
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang Shengdanrong Clothing Co Ltd
Original Assignee
Taicang Shengdanrong Clothing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang Shengdanrong Clothing Co Ltd filed Critical Taicang Shengdanrong Clothing Co Ltd
Priority to CN201510878165.3A priority Critical patent/CN105332142A/en
Publication of CN105332142A publication Critical patent/CN105332142A/en
Pending legal-status Critical Current

Abstract

The invention discloses garment fabric adding with metal materials. The garment fabric adding with the metal materials is a fabric body formed by weaving warp and weft, the warp is formed by blending pineapple fiber and thermosensitive color-changing fiber, and the weft is formed by blending metal filaments and milk fiber. The garment fabric adding with the metal materials has the advantages of being simple in structure, exquisite in design and high in heat retention property.

Description

A kind of garment material adding metal material
Technical field
The present invention relates to a kind of garment material adding metal material.
Background technology
In clothes big world, the fabric of clothes is multifarious, makes rapid progress.But generally, high-quality, high-grade fabric, mostly have the feature of several aspects such as wear is comfortable, absorbing sweat is breathed freely, it is well-pressed to dangle, vision is noble, sense of touch is soft and graceful.Be produced on the clothes of formal social life institute wear, cotton textiles, pure wool, pure silk, pure gunny products should be selected.With the clothes that these four kinds of pure natural quality fabrics make, mostly class is higher.Sometimes, the clothes of the pure leatherwork of wear are also allow.Kind (1) shuttle-woven fabric, also claims woven fabric, is the fabric that mutual vertical to warp thread and weft yarn weave in is formed.It is the ABC that each designers needs to be grasped that Correct Analysis identification fabric performance also applies to costume design reasonably and accurately, otherwise fabric identification error may cause the design of whole money clothes, makes, and the links such as dress or washing go wrong.The identification of garment material comprises the raw material identification of garment material, external appearance characteristic identification and presentation quality identification etc.Observe and identify that fabric is not only by vision, and with the sense of hearing, sense of touch is sense of smell even.As used the gloss light and shade of the visual effect viewing fabric of eyes, staining conditions, surface thickness and tissue, the external appearance characteristic of lines and fiber, such as pure cotton cloth gloss is common, outward appearance is not carefully clean, coarse even have cotton junction impurity, and woollen goods gloss of wool and blend polyester is brighter, has flash sense, body bone slightly removes the softness of mistake firmly, and obviously gives prominence to the increase of terylene content.Lack soft soft and moist sense, fabric is well-pressed.Smooth, smooth; Use the haptic effect of hand can feel the soft or hard of fabric and fiber, smooth, thickness, elasticity, changes in temperature etc., can also measure intensity and the elongation of yarn in fiber with hand.
Different fabrics has different gas permeabilities, hygroscopicity, the performances such as warmth retention property, and such as COTTON FABRIC has good gas permeability and hygroscopicity, comfortable and easy to wear, and warmth retention property is good, is optimal children's garment fabric.Select will confirm the gas permeability of fabric, heat insulating ability, hygroscopicity, the performance characteristics such as static behaviour during fabric, then for the stiffness of fabric, weight sense, soft durometer and drapability consider that it is applicable to doing which type of moulding, do which type of style etc.
Summary of the invention
The object of the present invention is to provide a kind of garment material adding metal material, there is structure simple, design ingenious, the advantage that warmth retention property is strong.
Technical scheme of the present invention is: a kind of garment material adding metal material, the garment material of described interpolation metal material forms fabric main body by warp thread and weft yarns, described warp thread is formed by pina fibre and polychromatic fibre blending, described weft yarn is formed by wire and blended by milk fibre, described wire is filamentary silver, the density of described warp thread is 100D/48F, the density of described weft yarn is 300D/96F, the weight ratio that described pina fibre accounts for described warp thread is 50%-55%, and the weight ratio that described polychromatic fibre accounts for described warp thread is 45%-50%.
In a preferred embodiment of the present invention, the weight ratio that described pina fibre accounts for described warp thread is 54%, and the weight ratio that described polychromatic fibre accounts for described warp thread is 46%.
In a preferred embodiment of the present invention, in described weft yarn, the part by weight of wire and milk fibre is 1:2.
A kind of garment material adding metal material of the present invention, has structure simple, designs ingenious, the advantage that warmth retention property is strong.
Detailed description of the invention
Be described in detail below in conjunction with to preferred embodiment of the present invention, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
A kind of garment material adding metal material of the present invention, the garment material of described interpolation metal material forms fabric main body by warp thread and weft yarns, described warp thread is formed by pina fibre and polychromatic fibre blending, described weft yarn is formed by wire and blended by milk fibre, described wire is filamentary silver, the density of described warp thread is 100D/48F, the density of described weft yarn is 300D/96F, the weight ratio that described pina fibre accounts for described warp thread is 50%-55%, the weight ratio that described polychromatic fibre accounts for described warp thread is 45%-50%, the weight ratio that described pina fibre accounts for described warp thread is 54%, the weight ratio that described polychromatic fibre accounts for described warp thread is 46%, in described weft yarn, the part by weight of wire and milk fibre is 1:2.
Further illustrate, pina fibre and arghan, also known as pina, be the fiber extracted from pineapple leaf, belong to blade bast-fibre.Pina fibre is combined closely by many fibre bundles and is formed, and each fibre bundle is made up of 10 ~ 20 individual fiber cells set again.Fiber surface is coarse, has longitudinal slot and hole, laterally has minor matters, without natural distortion.Individual fiber cells is cylindrical, and two ends point, smooth surface, has wire lumen.Pina fibre white appearance, soft and smooth property, feel as silk, therefore has again the appellation of pineapple silk.Pina fibre after deep processing process, white appearance, soft and smooth property, can with natural fabric or synthetic fiber blending, knit system fabric easily print and dye, absorbing sweat is breathed freely, well-pressed wrinkle resistant, comfortable and easy to wear.Pina fibre and cotton blending can produce denim, and drapability is similar to cotton denim; Pina fibre and silk blending can be made into senior ceremonial dress face fabric; Make weft yarn with the pure pina fibre yarn that Revolving cup spinning is produced, make warp thread with cotton or other blended yarn, various drapery and UPHOLSTERY FABRIC can be produced; Western-style clothes and coat fabric can be produced with wool spinning equipment spinning wool and pina fibre blended yarn; The pina fibre that jute equipment is produced, silk/cotton blended yarn can knit Curtains Fabrics processed, sheet, UPHOLSTERY FABRIC, towel, carpet etc.; Can be used for producing knitting women coat, socks etc. with flax device fabrication terylene, acrylic fibers, pina fibre blended yarn.
Further illustrating, milk fibre had both been different from the natural fabrics such as cotton, fiber crops, silk, hair, and different with chemical fibres such as polyamide fibre, acrylic fibers, terylene and polypropylene fibre again, therefore its performance is between natural fabric and synthetic fiber.Its physical and chemical indexes detected value is as follows: dry fracture strength >=2.5cn/dtex; The dry ultimate strength coefficient of variation≤14%; Dry elongation at break 16.0% ~ 25.0%; The dry elongation at break coefficient of variation≤12%; Line density deviation ratio ± 4.0%; The line density coefficient of variation≤3.5%; Dye uniformity (ash card) >=3 ~ 4 grades; Regain 4% ~ 6%; Fiber bacteriostasis rate >=80%.Do not use formaldehyde azo auxiliary agent or raw material, fiber content of formaldehyde is zero; Be rich in ten eight seed amino acids useful to human body, can metabolism of human cell be promoted, prevent skin senescence, itch, nutrition skin; Have natural moisturizing factor, therefore can keep skin moisture content, make skin soft and moist smooth, reduce wrinkle, have broad-spectrum antibacterial function, persistence is strong, and natural bacteriostatic function reaches more than 99%, and antibiotic rate reaches more than 80%.Have the feel as cashmere, its filament number is thin, light specific gravity, elongation at break, Curl, crimp recovery closest to cashmere and wool, jewelry, expensive clothing and other valuables that fiber is bulk, sense of touch is soft, comfortable as cashmere, cunning is glutinous; Fiber is pale, has the natural gloss of silkiness, and outward appearance is graceful, and Sun-proof fastness, anti-perspiration fastness reach 4 ~ 3 grades.Milk protein fiber section is irregular round, space is covered with in section, longitudinally there are many grooves, protein molecule is distributed in the surface of fiber, containing native protein NMF and a large amount of hydrophilic radical, human sweat can be absorbed rapidly, be imported in air fast by groove and distribute, make the skin of people remain dry condition, anti-fluffing, pilling tendency reach 3 ~ 4 grades.The invention provides a kind of fabric of waterproof, there is structure simple, design ingenious, the advantage that warmth retention property is strong.
The specific embodiment of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the technical scope disclosed by the present invention, and the change can expected without creative work or replacement, all should be encompassed within protection scope of the present invention.Therefore, the protection domain that protection scope of the present invention should limit with claims is as the criterion.

Claims (3)

1. one kind is added the garment material of metal material, it is characterized in that: the garment material of described interpolation metal material forms fabric main body by warp thread and weft yarns, described warp thread is formed by pina fibre and polychromatic fibre blending, described weft yarn is formed by wire and blended by milk fibre, described wire is filamentary silver, the density of described warp thread is 100D/48F, the density of described weft yarn is 300D/96F, the weight ratio that described pina fibre accounts for described warp thread is 50%-55%, and the weight ratio that described polychromatic fibre accounts for described warp thread is 45%-50%.
2. the garment material of interpolation metal material according to claim 1, is characterized in that: the weight ratio that described pina fibre accounts for described warp thread is 54%, and the weight ratio that described polychromatic fibre accounts for described warp thread is 46%.
3. the garment material of interpolation metal material according to claim 1, is characterized in that: in described weft yarn, the part by weight of wire and milk fibre is 1:2.
CN201510878165.3A 2015-12-04 2015-12-04 Garment fabric adding with metal materials Pending CN105332142A (en)