CN105317132A - Anti-termite heat-insulation sound-isolation and high-temperature-resistant composite plate combining pottery glass boards and stalk board - Google Patents
Anti-termite heat-insulation sound-isolation and high-temperature-resistant composite plate combining pottery glass boards and stalk board Download PDFInfo
- Publication number
- CN105317132A CN105317132A CN201410392337.1A CN201410392337A CN105317132A CN 105317132 A CN105317132 A CN 105317132A CN 201410392337 A CN201410392337 A CN 201410392337A CN 105317132 A CN105317132 A CN 105317132A
- Authority
- CN
- China
- Prior art keywords
- glass plate
- pottery
- stalk
- potter
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A conventional stainless steel composite board is filled with foam plastics, and has the defects of inflammability and insufficient strength. The foam plastics combust in the flame, and a stainless steel board wrapped by the foam plastics can be damaged by generated gas. A composite plate combining pottery glass boards and a stalk board is made of the pottery glass boards and the noninflammable stalk board; water glass is used as a high-temperature-resistant flame retardant, so that stalks are noninflammable at high temperature of 1000 DEG C; the noninflammable stalk board is alkalescent, so that an anti-termite effect is achieved, and fungus growth is avoided; the noninflammable stalk board is provided with a great number of hollow holes, and has good heat-insulation and sound-isolation performance; the stalk board is hardened by the water glass; after the stalk board is dried, the texture is hard like wood, and hardness and durability are realized; and the pottery glass boards do not rust. Therefore, the service life of the composite plate exceeds a hundred years. Carbon molecules in the stalk board and silicon molecules in the water glass take a chemical reaction in the flame to generate silicon carbide. The silicon carbide is a hard substance capable of resisting high temperature of 1000 DEG C, so that when a fire hazard occurs, the rigidity change of the composite plate is not great, and the fire hazard expansion can be prevented. Therefore, the composite plate is the best building material for building factory buildings and temporary buildings.
Description
Cornstalk or sorghum stalk easily burn; Present stainless steel clad plate, fills with foamed plastics, and it exists inflammable and shortcoming that is insufficient strength, its foamed plastics burning in flame, and the corrosion resistant plate of parcel can destroy by the gas of generation; Market has no pottery glass plate compound stalk plate.
The worm ant that this technology proposes does not eat the pottery glass plate compound stalk plate that heat preservation and soundproof thousand degree does not fire, and is called for short pottery glass plate compound stalk plate, can helps the shortcoming overcoming above-mentioned existence.
Pottery glass plate compound stalk plate, its beneficial effect is, thousand degree do not fire, and ant does not eat worm, and fungi does not grow, heat preservation and soundproof, hard durable, and the life-span is super century-old.
Worm ant does not eat the pottery glass plate compound stalk plate that heat preservation and soundproof thousand degree does not fire, and the technical scheme that its technical solution problem adopts is, with pottery glass plate, does not fire stalk plate, water glass and high-temperature-resistant adhesive composition; Its technique is: high-temperature-resistant adhesive makes, and makes with water glass and heating starch; Pottery glass plate basin makes, and one or more pyroceram screen cloth is starched by potter's clay, and potter's clay slurry can add adhesive, removes unnecessary potter's clay slurry, obtains potter's clay slurry parcel glass web fabric swatch; Potter's clay slurry parcel glass web fabric swatch can be made shallow basin, three limits of shallow basin can exceed another side, and become 90 degree of angular distortions in basin, obtain the shallow basin of potter's clay slurry parcel glass web fabric swatch; Glass web fabric swatch, the potter's clay slurry of potter's clay slurry parcel send kiln to fire after wrapping up the shallow basin drying of glass web fabric swatch, obtain pottery glass plate (1), pottery glass plate basin (1); Pottery glass plate hollow body makes, and can make hollow body with potter's clay slurry parcel glass web fabric swatch again, hollow body is flat, three side seals, and potter's clay slurry parcel glass web fabric swatch hollow body, send kiln to fire, obtain pottery glass plate hollow body (1) after drying; Stalk slab (2) do not fire after can be coated with high-temperature-resistant adhesive, put in pottery glass plate basin, get suitable pottery glass plate, advance pottery glass plate basin from the low limit of pottery glass plate basin, stalk slab will not be fired and cover parcel closely, obtain pottery glass plate compound stalk plate (3), or, after not firing the available high-temperature-resistant adhesive painting of stalk slab (2), advance pottery glass plate hollow body by flat hollow body side, get suitable pottery glass plate and be sealed side, obtain pottery glass plate compound stalk plate (3); Thus pottery glass plate compound stalk plate that heat preservation and soundproof thousand degree do not fire is run to make worm ant not eat.As Fig. 1
Existing combination principle introduction pottery glass plate compound stalk plate:
Pottery glass plate is explained: make pottery as the pottery of pottery.
Burn till the temperature about 1,000 degree of pottery with potter's clay, the resistance to temperature of order pottery glass screen cloth reduces and cost-saving.
Do not fire stalk plate to make, corn or sorghum stalk removal of impurities are arranged, soaks into corn or sorghum stalk with water glass, dry after removing unnecessary water glass, obtain and do not fire stalk plate; With high-temperature-resistant adhesive polylith do not fired stalk plate be bonded into slab after dry, during bonding, each layer does not fire stalk plate and can stagger alternately in length and breadth, obtains and does not fire stalk slab.
Water glass is heat-resistant fireproof agent, and corn or sorghum stalk thousand degree are not fired; Water glass makes the stalk plate matter after dry doing hard like wood; Water glass is alkalescent material, and it makes stalk plate containing alkalescence, makes that worm ant can not eat, fungi can not grow, and the order pottery glass plate compound stalk plate life-span is super century-old; Pottery glass plate is made basin or hollow body, is to make pottery glass plate pin not firing stalk slab tightly, producing pottery glass plate and tightly wrapping up the effect of not firing stalk slab, making the better effects if of pottery glass plate compound stalk plate; Each layer does not fire stalk plate and staggers in length and breadth alternately, can strengthen the bending resistance of pottery glass plate compound stalk plate; Do not fire stalk slab and have a lot of hollow hole, heat preservation and soundproof is functional; Pottery glass plate compound stalk plate, based on corn or sorghum stalk, do not fire stalk plate thickness and can surpass tens centimeters, pottery glass plate thickness does not surpass two millimeters, only plays the waterproof action as not firing stalk plate; Potter's clay only uses as adhesive glass screen cloth, and its consumption is few, so pottery glass plate, is actually glass web fabric swatch; Potter's clay slurry adds adhesive, and potter's clay can be made to be not easy to depart from glass web; , in flame, there is chemical reaction Formed SiClx in the carbon molecule of stalk plate and the silicon molecule of water glass.Carborundum is the hard material of resistance to thousand several years high temperature, so when fire occurs, the variation in rigidity of pottery glass plate compound stalk plate is little, and fire can be stoped to expand.
In sum, glass plate compound of making pottery stalk plate is the best constructional materials building factory building, lightly constructed and simply equipped building.
Figure of description illustrates:
Fig. 1: worm ant does not eat the pottery glass plate compound stalk plate that heat preservation and soundproof thousand degree does not fire
1, pottery glass plate, pottery glass plate basin, pottery glass plate hollow body, 2 do not fire stalk slab, 3 pottery glass plate compound stalk plates.
Claims (1)
1. worm ant does not eat the pottery glass plate compound stalk plate that heat preservation and soundproof thousand degree does not fire, and it is characterized in that, with pottery glass plate, does not fire stalk plate, water glass and high-temperature-resistant adhesive composition; Its technique is: high-temperature-resistant adhesive makes, and makes with water glass and heating starch; Pottery glass plate basin makes, and one or more pyroceram screen cloth is starched by potter's clay, and potter's clay slurry can add adhesive, removes unnecessary potter's clay slurry, obtains potter's clay slurry parcel glass web fabric swatch; Potter's clay slurry parcel glass web fabric swatch can be made shallow basin, three limits of shallow basin can exceed another side, and become 90 degree of angular distortions in basin, obtain the shallow basin of potter's clay slurry parcel glass web fabric swatch; Glass web fabric swatch, the potter's clay slurry of potter's clay slurry parcel send kiln to fire after wrapping up the shallow basin drying of glass web fabric swatch, obtain pottery glass plate, pottery glass plate basin; Pottery glass plate hollow body makes, and can make hollow body with potter's clay slurry parcel glass web fabric swatch again, hollow body is flat, three side seals, and potter's clay slurry parcel glass web fabric swatch hollow body, send kiln to fire, obtain pottery glass plate hollow body after drying; Stalk slab do not fire after can be coated with high-temperature-resistant adhesive, put in pottery glass plate basin, get suitable pottery glass plate, advance pottery glass plate basin from the low limit of pottery glass plate basin, stalk slab will not be fired and cover parcel closely, obtain pottery glass plate compound stalk plate, or not firing stalk slab with after high-temperature-resistant adhesive painting, can advance pottery glass plate hollow body by flat hollow body side, get suitable pottery glass plate and be sealed side, obtain pottery glass plate compound stalk plate; Thus pottery glass plate compound stalk plate that heat preservation and soundproof thousand degree do not fire is run to make worm ant not eat.