CN105314935B - 一种节能环保的建筑内墙隔音保温方法 - Google Patents
一种节能环保的建筑内墙隔音保温方法 Download PDFInfo
- Publication number
- CN105314935B CN105314935B CN201510681742.XA CN201510681742A CN105314935B CN 105314935 B CN105314935 B CN 105314935B CN 201510681742 A CN201510681742 A CN 201510681742A CN 105314935 B CN105314935 B CN 105314935B
- Authority
- CN
- China
- Prior art keywords
- wall
- sound
- cement
- powder
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种节能环保的建筑内墙隔音保温方法，包括墙面找平、上水泥浆、涂隔音保温层、表层处理步骤。所述的涂隔音保温层步骤包括涂基料层和涂主料层；所述的涂主料层中主料的制备方法包括：将水泥、粉砂、水按1:1.5:3.3的质量比例混合均匀，得到稀泥浆。向稀泥浆中依次加入聚氨酯泡沫颗粒、黄麻纤维、橡胶粒子、白炭黑、硫膏粉，加入量分别为稀泥浆质量的7.2%、15.4%、1%、1.6%、3.2%。向搅拌机内的混合物中加入水性丙烯酸乳液、珍珠岩、硅藻粉、岩棉，加入量分别为稀泥浆质量的8%、4.2%、3%、5.1%。采用本发明方法处理的墙壁，声音降低73‑75分贝，导热系数≤0.029W/m.K。
Description
技术领域
本发明涉及一种墙壁隔音、保温方法，具体的说，涉及一种节能环保的建筑内墙隔音保温方法，属于建筑技术领域。
背景技术
随着城镇化的发展，现在，我国楼房居住的居民日益增多，很多以前在农村居住的居民由于生活或者工作的需要，也在城市购买楼房或者租赁住楼房居住。而楼房与平房居住的一个重要区别就是楼房不隔音，很多市民受到这方面的困扰，特别是有病人、孕妇、婴儿等需要安静的家庭。
传统的墙体隔音方法是在墙壁上打轻钢龙骨或木龙骨，龙骨外面安装厚的石膏板或木板，在板间的空腔填充岩棉或玻璃棉等吸音材料，通过墙体的空腔来达到隔音的目的。但是，这种方法的问题在于，造价高，适合KTV等盈利场所，而普通家庭采用的很少；而且，这种方法大大减少了原有的建筑空间，如果是中小户型的房子，这种隔音方法很不实用。
专利CN201410511181.4公开了一种防噪音复合板，包括外层的隔护层、封裹材料和芯部材料，所述的隔护层包括最外层的防护板和内层的纤维布，防护板为内表面具有均匀分布小孔的岩棉板，厚度为5-8mm，其纤维布为玻璃纤维编制成的多轴向布，纤维布的厚度是0.1-0.3mm。该发明虽然解决了隔音的问题，但方法复杂，采用了多种易燃材料，普通家庭应用，不够安全、实用，而且，成本较高。
专利CN201210230356.5公开了一种隔音保温材料、隔音保温层及其制备方法和应用，该发明方虽然有一定的隔音、保温作用，但厚度较厚，且材料不适合普通家庭装修，主要适合应用于机房、车间、车库、歌厅等场所，而且，容易造成一定的室内污染，不够绿色、环保。
总之，现有技术存在以下缺陷： （1）降音效果不理想；（2）保温效果差；（3）在降音、保温的同时，难以实现较好的防水、防火效果；（4）传统方法使用成本高，消耗能源多，而且容易造成室内甲醛污染。
发明内容
本发明要解决的问题是针对以上不足，提供一种，实现以下发明目的：
（1）提高墙壁的隔音效果，使声音降低73-75分贝；
（2）提高墙壁的保温效果，使导热系数≤0.029W/m.K；
（3）提高墙壁的防水效果；
（4）提高墙壁的防火效果；
（5）降低成本，节约能源，避免甲醛污染。
为实现上述发明目的，采用以下技术方案：
一种节能环保的建筑内墙隔音保温方法，包括墙面找平、上水泥浆、涂隔音保温层、表层处理步骤。
以下是对上述技术方案的进一步改进：
所述的涂隔音保温层步骤包括涂基料层和涂主料层；所述的涂基料层中使用的基料粉料包括以下组分：水泥、醋酸乙烯共聚物、羟丙基甲基纤维素、甲酸钙。
所述基料粉料的组分配比为：水泥：醋酸乙烯共聚物：羟丙基甲基纤维素：甲酸钙=100：3：6.5：2。
所述的涂主料层中主料的制备方法包括：将水泥、粉砂、水按1:1.5:3.3的质量比例混合均匀，得到稀泥浆。
所述的涂主料层中主料的制备方法还包括：向稀泥浆中依次加入聚氨酯泡沫颗粒、黄麻纤维、橡胶粒子、白炭黑、硫膏粉，加入量分别为稀泥浆质量的7.2%、15.4%、1%、1.6%、3.2%。
所述的涂主料层中主料的制备方法还包括：向搅拌机内的混合物中加入水性丙烯酸乳液、珍珠岩、硅藻粉、岩棉，加入量分别为稀泥浆质量的8%、4.2%、3%、5.1%。
所述的醋酸乙烯共聚物：含量为18wt%，密度为0.94g/cm3，熔融指数为1.7g/10min。
所述的聚氨酯泡沫颗粒：颗粒直径大小为0.5-8mm；所述的黄麻纤维：纤维强力≥255N，含杂率＜1.2%，纤维长度为3-10cm。
所述的硅藻粉：Fe2O3含量为1.5%，烧失量≤0.3%，水分含量≤1.2%，比表面积为0.2㎡/g，pH值为7.5。
采用本发明方法处理的墙壁，声音降低73-75分贝，导热系数≤0.029W/m.K。
与现有技术相比，本发明技术方案具有以下有益效果：
（1）本发明方法处理过的墙壁，隔音效果好，可使声音降低73-75分贝；
（2）本发明方法处理过的墙壁，保温效果好，导热系数≤0.029W/m.K，冬季无供暖的情况下，室内外温差为10-16℃；
（3）本发明方法处理过的墙壁，防水效果好，经水72小时浸泡，无渗水、阴湿现象发生；
（4）本发明方法处理过的墙壁，防火效果好，用瓦斯灯火焰对墙面正面燃烧8-10分钟，墙面无任何损坏；
（5）本发明方法处理过的墙壁，耐酸碱腐蚀性能强；
（6）本发明方法采用的原材料均为环保、绿色材料，避免了传统方法的耗能大、室内甲醛污染严重、占用空间大等缺点，具有绿色环保、节约能源、可持续的优点；适合家庭装修应用。
具体实施方式
实施例1 一种节能环保的建筑内墙隔音保温方法
步骤1 墙面找平
将建筑内墙找平，若墙面平整度较差，需用石膏先单独找平，再进行整体墙面的找平；找平后的墙面，平整度小于正负2.5mm。
步骤2 上水泥浆
用水将内墙面喷湿，用水量为2ml/㎡；然后上水泥浆，将水泥浆均匀涂抹在墙面上，涂抹厚度为7mm；表面无需抹平，使表面存有纹理，并凸有部分毛刺；
所述的水泥浆为水泥：细砂：乳胶漆：植物纤维：水按照100：180：4：19：295的质量比混合均匀得到混合物；
所述的细砂：粒径大于0.15mm的颗粒含量不超过全重的60%；
所述的乳胶漆：为水乳型弹性丙烯酸共聚物；
所述植物纤维：为椰壳纤维，纤维长为3-7cm，其中纤维长为5-7cm的椰壳纤维占纤维总重量的30-45%。
步骤3 涂隔音保温层
进行步骤2的上水泥浆后，晾20分钟，开始涂隔音保温层，隔音保温层包括基料层和主料层。
（1）涂基料层
将基料粉料和水按1:0.4的质量比混合，搅拌均匀，得到基料；先往墙上刷一层基料，使基料的厚度为0.8cm；基料层刷好后，无需抹平毛刺；在表面用铁丝网压制凹槽，铁丝网网眼为4cm×4cm的方形网眼，压制的凹槽深度为3-5mm，凹槽宽度为2-3mm，遍布整个墙体。
所述基料粉料包括水泥、醋酸乙烯共聚物、羟丙基甲基纤维素、甲酸钙，质量配比为水泥：醋酸乙烯共聚物：羟丙基甲基纤维素：甲酸钙=100：3：6.5：2；
所述的醋酸乙烯共聚物：含量为18wt%，密度为0.94g/cm3，熔融指数为1.7g/10min；
所述的羟丙基甲基纤维素：含量为98%，密度为90 g/cm3；
所述的甲酸钙：含量为98%，密度为900 g/cm3。
（2）涂主料层
基料层处理完之后，马上涂抹主料层，主料的涂抹厚度为4cm，涂抹均匀后，刮平表层。
所述主料的制备方法为：
用搅拌机将水泥、粉砂、水按1:1.5:3.3的质量比例混合均匀，得到稀泥浆；
向稀泥浆中依次加入聚氨酯泡沫颗粒、黄麻纤维、橡胶粒子、白炭黑、硫膏粉，加入量分别为稀泥浆质量的7.2%、15.4%、1%、1.6%、3.2%；
打开搅拌，设置80rpm的转速，搅拌均匀；
持续搅拌的同时，依次向搅拌机内的混合物中加入水性丙烯酸乳液、珍珠岩、硅藻粉、岩棉，加入量分别为稀泥浆质量的8%、4.2%、3%、5.1%；
搅拌均匀，制得主料。
所述的聚氨酯泡沫颗粒：颗粒直径大小为0.5-8mm；
所述的黄麻纤维：纤维强力≥255N，含杂率＜1.2%，纤维长度为3-10cm；
所述的硅藻粉：Fe2O3含量为1.5%，烧失量≤0.3%，水分含量≤1.2%，比表面积为0.2㎡/g，pH值为7.5。
步骤4 表层处理
将水泥、粉砂、硼酸铝、水按1：2：0.08：3的质量比例混合均匀，涂于隔音保温层表面。
处理完成后，墙面可实现较好的隔音保温效果；房间使用前可根据需要在表面刮腻子或喷乳胶漆。
实施例2 一种节能环保的建筑内墙隔音保温方法
步骤1 墙面找平
与实施例1的操作方法相同。
步骤2 上水泥浆
用水将内墙面喷湿，用水量为3ml/㎡；然后上水泥浆，将水泥浆均匀涂抹在墙面上，涂抹厚度为6mm；表面无需抹平，使表面存有纹理，并凸有部分毛刺；
所述的水泥浆为水泥：细砂：乳胶漆：植物纤维：水按照100：180：4：19：295的质量比混合均匀得到混合物；
所述的细砂：粒径大于0.15mm的颗粒含量不超过全重的60%；
所述的乳胶漆：为水乳型弹性丙烯酸共聚物；
所述植物纤维：为椰壳纤维，纤维长为3-7cm，其中纤维长为5-7cm的椰壳纤维占纤维总重量的30-45%。
步骤3 涂隔音保温层
进行步骤2的上水泥浆后，晾25分钟，开始涂隔音保温层，隔音保温层包括基料层和主料层。
（1）涂基料层
将基料粉料和水按1:0.5的质量比混合，搅拌均匀，得到基料；先往墙上刷一层基料，使基料的厚度为1cm；基料层刷好后，无需抹平毛刺；在表面用铁丝网压制凹槽，铁丝网网眼为4cm×4cm的方形网眼，压制的凹槽深度为4mm，凹槽宽度为2-3mm，遍布整个墙体。
所述基料粉料包括水泥、醋酸乙烯共聚物、羟丙基甲基纤维素、甲酸钙，质量配比为水泥：醋酸乙烯共聚物：羟丙基甲基纤维素：甲酸钙=100：3：6.5：2；
所述的醋酸乙烯共聚物：含量为18wt%，密度为0.94g/cm3，熔融指数为1.7g/10min；
所述的羟丙基甲基纤维素：含量为98%，密度为90 g/cm3；
所述的甲酸钙：含量为98%，密度为900 g/cm3。
（2）涂主料层
基料层处理完之后，马上涂抹主料层，主料的涂抹厚度为4.3cm，涂抹均匀后，刮平表层。
所述主料的制备方法为：
用搅拌机将水泥、粉砂、水按1:1.5:3.3的质量比例混合均匀，得到稀泥浆；
向稀泥浆中依次加入聚氨酯泡沫颗粒、黄麻纤维、橡胶粒子、白炭黑、硫膏粉，加入量分别为稀泥浆质量的7.6%、15.8%、1.2%、1.7%、1.9%；
打开搅拌，设置80rpm的转速，搅拌均匀；
持续搅拌的同时，依次向搅拌机内的混合物中加入水性丙烯酸乳液、珍珠岩、硅藻粉、岩棉，加入量分别为稀泥浆质量的8.2%、4.4%、2%、3.8%；
搅拌均匀，制得主料。
所述的聚氨酯泡沫颗粒：颗粒直径大小为0.5-8mm；
所述的黄麻纤维：纤维强力≥255N，含杂率＜1.2%，纤维长度为3-10cm；
所述的硅藻粉：Fe2O3含量为1.5%，烧失量≤0.3%，水分含量≤1.2%，比表面积为0.2㎡/g，pH值为7.5。
步骤4 表层处理
与实施例1的操作方法相同。
实施例3 一种节能环保的建筑内墙隔音保温方法
步骤1 墙面找平
与实施例1的操作方法相同。
步骤2 上水泥浆
用水将内墙面喷湿，用水量为3.5ml/㎡；然后上水泥浆，将水泥浆均匀涂抹在墙面上，涂抹厚度为8mm；表面无需抹平，使表面存有纹理，并凸有部分毛刺；
所述的水泥浆为水泥：细砂：乳胶漆：植物纤维：水按照100：180：4：19：295的质量比混合均匀得到混合物；
所述的细砂：粒径大于0.15mm的颗粒含量不超过全重的60%；
所述的乳胶漆：为水乳型弹性丙烯酸共聚物；
所述植物纤维：为椰壳纤维，纤维长为3-7cm，其中纤维长为5-7cm的椰壳纤维占纤维总重量的30-45%。
步骤3 涂隔音保温层
进行步骤2的上水泥浆后，晾40分钟，开始涂隔音保温层，隔音保温层包括基料层和主料层。
（1）涂基料层
将基料粉料和水按1:0.8的质量比混合，搅拌均匀，得到基料；先往墙上刷一层基料，使基料的厚度为1.2cm；基料层刷好后，无需抹平毛刺；在表面用铁丝网压制凹槽，铁丝网网眼为4cm×4cm的方形网眼，压制的凹槽深度为5mm，凹槽宽度为2-3mm，遍布整个墙体。
所述基料粉料包括水泥、醋酸乙烯共聚物、羟丙基甲基纤维素、甲酸钙，质量配比为水泥：醋酸乙烯共聚物：羟丙基甲基纤维素：甲酸钙=100：3：6.5：2；
所述的醋酸乙烯共聚物：含量为18wt%，密度为0.94g/cm3，熔融指数为1.7g/10min；
所述的羟丙基甲基纤维素：含量为98%，密度为90 g/cm3；
所述的甲酸钙：含量为98%，密度为900 g/cm3。
（2）涂主料层
基料层处理完之后，马上涂抹主料层，主料的涂抹厚度为4.5cm，涂抹均匀后，刮平表层。
所述主料的制备方法为：
用搅拌机将水泥、粉砂、水按1:1.5:3.3的质量比例混合均匀，得到稀泥浆；
向稀泥浆中依次加入聚氨酯泡沫颗粒、黄麻纤维、橡胶粒子、白炭黑、硫膏粉，加入量分别为稀泥浆质量的7.8%、16.4%、1.5%、1.2%、2.3%；
打开搅拌，设置80rpm的转速，搅拌均匀；
持续搅拌的同时，依次向搅拌机内的混合物中加入水性丙烯酸乳液、珍珠岩、硅藻粉、岩棉，加入量分别为稀泥浆质量的9%、5.2%、3.6%、2.1%；
搅拌均匀，制得主料。
所述的聚氨酯泡沫颗粒：颗粒直径大小为0.5-8mm；
所述的黄麻纤维：纤维强力≥255N，含杂率＜1.2%，纤维长度为3-10cm；
所述的硅藻粉：Fe2O3含量为1.5%，烧失量≤0.3%，水分含量≤1.2%，比表面积为0.2㎡/g，pH值为7.5。
步骤4 表层处理
与实施例1的操作方法相同。
实验结果：
（1）按照实施例1-3的方法分别处理3个完全相同的房间的四面墙壁，进行隔音实验，实验方法：在房间内用发生器发出100分贝的声音，在房间外1m距离内检测声音高度，检测结果见表1；
表1
由表1可见，本发明方法的隔音效果好，可使声音降低73-75分贝。
（2）经试验，本发明方法处理过的墙壁，保温效果好，导热系数≤0.029W/m.K，冬季无供暖的情况下，室内外温差为10-16℃。
（3）经试验，本发明方法处理过的墙壁，防水效果好，经水72小时浸泡，无渗水、阴湿现象发生。
（4）经试验，本发明方法处理过的墙壁，防火效果好，用瓦斯灯火焰对墙面正面燃烧8-10分钟，墙面无任何损坏。
（5）经试验，本发明方法处理过的墙壁，耐酸碱性能强，分别采用pH为3的酸溶液和pH为11的碱溶液浸湿墙面60分钟，墙面均未发生任何损坏。
另外，本发明方法采用的原材料均为环保、绿色材料，避免了传统方法的耗能大、室内甲醛污染严重、占用空间大等缺点，具有绿色环保、节约能源、可持续的优点；适合家庭装修应用。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (2)
1.一种节能环保的建筑内墙隔音保温方法，其特征在于：包括墙面找平、上水泥浆、涂隔音保温层、表层处理步骤；
所述的涂隔音保温层步骤包括涂基料层和涂主料层；所述的涂基料层中使用的基料粉料包括以下组分：水泥、醋酸乙烯共聚物、羟丙基甲基纤维素、甲酸钙；
所述基料粉料的组分配比为：水泥：醋酸乙烯共聚物：羟丙基甲基纤维素：甲酸钙=100：3：6.5：2；
所述的涂主料层中主料的制备方法为：
将水泥、粉砂、水按1:1.5:3.3的质量比例混合均匀，得到稀泥浆；
向稀泥浆中依次加入聚氨酯泡沫颗粒、黄麻纤维、橡胶粒子、白炭黑、硫膏粉，加入量分别为稀泥浆质量的7.2%、15.4%、1%、1.6%、3.2%；
向搅拌机内的混合物中加入水性丙烯酸乳液、珍珠岩、硅藻粉、岩棉，加入量分别为稀泥浆质量的8%、4.2%、3%、5.1%；
所述的硅藻粉：Fe2O3含量为1.5%，烧失量≤0.3%，水分含量≤1.2%，比表面积为0.2㎡/g，pH值为7.5；
所述的醋酸乙烯共聚物：含量为18wt%，密度为0.94g/cm3，熔融指数为1.7g/10min；
所述的聚氨酯泡沫颗粒：颗粒直径大小为0.5-8mm；所述的黄麻纤维：纤维强力≥255N，含杂率＜1.2%，纤维长度为3-10cm。
2.根据权利要求1所述的一种节能环保的建筑内墙隔音保温方法，其特征在于：处理后的墙壁，声音降低73-75分贝，导热系数≤0.029W/m.K。