Handle platen screw thread lock pin nitrile rubber step pressuring plate glass pick-up unit
Technical field
The present invention relates to a kind of tempered glass test verification device, classification number: G01N3/32, particularly relate to so a kind of pressing plate surrounding can zoom in or out, and utilize turning worktable to carry out the handle platen screw thread lock pin nitrile rubber step pressuring plate glass pick-up unit of tested glass intensity.
Background technology
Along with expanding economy, glass is more and more extensive in the application of all trades and professions.At present, much important glass component, such as large glass curtain wall and glass zenith, the windshield of aerospace vehicle is all adopt the special glasss such as tempered glass, requires very strict, therefore check the performance of glass just to seem more and more important to glass properties.From 1 day May in 2003, China implements mandatory inspection system to automobile, train, architectural safety glass used, and the safety glass product not obtaining Compulsory Certification of Products certificate and do not apply China Compulsory Product Certification mark must not dispatch from the factory, import and sale.
Fragmentation test is a kind of major way detecting tempered glass quality, according to national standard requirement, fragment after the fragmentation of the tempered glass that 3mm is thick in any 50*50mm should be greater than 30, fragment after the fragmentation of the tempered glass that 4mm ~ 12mm is thick in any 50*50mm should be greater than 40, allowed a small amount of strip fragment, its length is no more than 75mm.The trend of strip fragment and glass edge should be almost parallel, and as not parallel, angle can not more than 45 degree, if having one not up to standard, be substandard product.
Existing tempered glass fragmentation test method is freely lain on testing table by tempered glass sample, and retrain glass periphery by adhesive tape or other modes, or cover thin film on tempered glass, splashes to prevent glass fragment.The position of distance periphery about 20mm on the longest edge center line of sample, be that the pane hammer of 0.2mm scholar 0.05mm or drift impact with tip curvature radius, making sample broken, is that the fragment number in center of circle radius 75mm circle does not conduct a survey within the scope of product edges 20mm and with shock point.The measure retaining fragment pattern should start after 10s after the blow and terminate in 3min after the blow.This method not only operates inconvenience, spended time is longer, and adhesive tape is disposable product, easily cause waste and pollute, and the tape residue on test platen must be removed clean after each test, could remove clean cullet, otherwise residual chopped glass will affect experiment test operation next time.
Simultaneously adhesive tape also has and is burst by tempered glass the possibility that strength collapses out, and causing operating personnel injured, therefore, is very necessary to the improvement of tempered glass fragmentation test device.
Chinese Patent Application No.: 2009203050079, toughened glass falling sphere test bed, for solving tempered glass when testing, glass fragment can be caused everywhere to splash, adopt the way of carriage case, although can effective mobile phone glass fragment, the reading of inconvenient glass fragment, and also the installation effectiveness doing multi-disc tempered glass is continuously lower.
Another number of patent application: the 201420595067.X of China, tempered glass fragmentation status test unit, propose the pressing plate that some brand-new method and measures deal with brittle glass, but cannot accomplish that arbitrary dimension regulates, also cannot accomplish to allow four limit pressing plates all at grade.At least to have in this patent while be cannot contact with experiment work table top.Simultaneously the unsettled barricade 5 that is referred to as in embodiment cannot contact with base 1 together with other three side bumpers wall, has to use catch 4 to make up the space between unsettled barricade 5 and base 1, cause surrounding discontinuity.In addition, catch 4 local width is fixing, polylith can only be adopted to splice, cannot accomplish the consecutive variations of different in width.
Summary of the invention
For above prior art Problems existing, the present invention adopts the direct Turnover testing platen of platen handle, being equipped with screw fastening locks solid, in conjunction with surrounding isoplanar slippage wheel Anchor plate kit, opposite side clamp portion carries out the adjustable design in isoplanar, achieve the tempered glass for sizes different size, a kind of verification test device can be shared to do tempered glass fragmentation test, specific as follows:
Handle platen screw thread lock pin nitrile rubber step pressuring plate glass pick-up unit, comprise test platen and plate frame, upper connecting rod after lower link and frame after lower link and frame before upper connecting rod and frame before organic frame between two plate frames, before frame before upper connecting rod and frame after lower link and frame after lower link and frame upper connecting rod two ends be combined with pull-rod nut two plate frames fixed, as improvement:
Described test platen rear end facade has platen handle, and there is platen rotating shaft described test platen both sides, and the platen rotating shaft of both sides is rotatable to be respectively fixed in bearing spider, and bearing spider is fixed on plane on plate frame; There is supporting traverse described position, plate frame upper back, and supporting traverse holds test lower plane both sides, platen rear end;
Stud lock pin external thread matches with lock pin bearing inner hole thread, and lock pin bearing is fixed on plane on plate frame, and the cylinder bulb of the stud lock pin termination of both sides can enter locking positioning in the spiral shell cone column lockhole of test platen both sides;
Plane is fixed wtih isoplanar step Anchor plate kit to described test platen, go back pull bar in before organic frame before frame before upper connecting rod and frame between lower link, in before frame, before pull bar and described frame, after upper connecting rod and described frame, upper connecting rod is fixed wtih cullet returnable jointly;
On described test platen, plane has the nickel-base alloy wearing layer of one deck 1.4 to 1.6 millimeters thick, the material composition of described nickel-base alloy wearing layer is made up of the element of following percentage by weight: Ni:30-32, Cr:12-13, Al:17-18, Mo:4-6, Cu:25-27, Sn:1-2, and surplus is Co and inevitable impurity; The weight percent content of described impurity is: O.05 C is less than, Si is less than 0.20, Mn is less than 0.25, S is less than O.Ol0, P and is less than O.015, and the rockwell superficial hardness number of this nickel-base alloy wearing layer is HRC55.
As further improvement: described test platen has pressing plate fixing threaded hole, in described isoplanar step Anchor plate kit at least one clamp portion pressing plate on plane has pressing plate step through-hole, sunk screw passes through described pressing plate step through-hole and matches with described pressing plate fixing threaded hole.
As further improvement: on every only described plate frame, plane is respectively arranged with two bearing seat screws and two locking pin seat screws, plated frame plate face there is in before lower through-hole after lower through-hole before the front upper through hole of horizontally disposed frame, frame, frame, frame upper through hole after through hole and frame.
As further improvement: described isoplanar step Anchor plate kit is made up of the isoplanar step pressing plate that four physical dimensions are identical, is respectively: on the right of pressing plate deckle, the pressing plate left side, pressing plate opposite side and pressing plate; Every isoplanar step pressing plate comprises clamp portion and slippage part, and pressing plate deckle comprises deckle clamp portion and deckle slippage part; The pressing plate left side comprises left side clamp portion and left side slippage part, and pressing plate opposite side comprises opposite side clamp portion and opposite side slippage part, comprises the right clamp portion and the right slippage part on the right of pressing plate;
Described slippage part is positioned at described clamp portion one end and is overlapped on plane on clamp portion; The lower surface of described slippage part is slippage lower plane, slippage lower plane has step groove, and the upper surface of described clamp portion is plane on pressing plate, and pressing plate plane has step protruding rail; On described slippage lower plane and described pressing plate, plane is in sustained height;
For being slidably matched between step groove in step protruding rail on described deckle clamp portion and described the right slippage part, for being slidably matched between step groove in step protruding rail on described left side clamp portion and described deckle slippage part, for being slidably matched between step groove in step protruding rail on described opposite side clamp portion and described left side slippage part, for being slidably matched between the step groove in the step protruding rail on described the right clamp portion and described opposite side slippage part; Have pressing plate slope inside the clamp portion of every pressing plate, the angle on described pressing plate slope and pressing plate between plane is 54-56 to spend, and pressing plate slope is also adhered fixed rubber compressing tablet;
Described rubber compressing tablet adopts synthesis nitrile rubber, its material composition is: nitrile rubber 43-45%, carbon black 22-24%, zinc paste 2-4%, dibutyl ester 11-13%, stearic acid 0.7-0.9%, paraffin: 5.4-5.6%, promoter 1.1-1.3%, aging resister 1.2-1.4%, and all the other are inserts.
As further improvement: on described pressing plate, plane is 21 to 23 millimeters to the distance of described step protruding rail top plane, the width of described transition raised line is 7 to 9 millimeters, the height of described transition raised line is 6 to 8 millimeters, and the described single-ended opening of step protruding rail;
Described slippage lower plane is 21 to 23 millimeters to the distance of described step groove-bottom plane, and the width of described transition groove is 7 to 9 millimeters, and the height of described transition groove is 6 to 8 millimeters, and described step groove both ends open.
Beneficial effect of the present invention is:
(1), test platen rear end facade there is platen handle, the turning vibrational power flow of test platen can be driven, be convenient to remove chunk glass remove, be equipped with cullet returnable, guarantee that chunk glass does not scatter, supporting traverse hold test platen after lower plane, in conjunction with the lock pin crank handle of both sides, match with lock pin bearing inner hole thread by means of stud lock pin, the cylinder bulb of stud lock pin termination is made to enter locking positioning in the spiral shell cone column lockhole of test platen both sides, overcome the defect that the direct Turnover testing platen of platen handle does not have self-locking, make to keep firmly solid in the armourplate glass process of whole test.
(2), container bin gate spring is set respectively between lower draw-bar before the container of bin gate hook and both sides, guarantees that container discharge door can touch container discharge mouth tightly, do not allow chunk glass scatter.
(3), isoplanar step Anchor plate kit is adopted, particularly slippage part is positioned at clamp portion one end and is overlapped on plane on clamp portion, and plane is in sustained height on described slippage lower plane and described pressing plate, guarantee that tested armourplate glass surrounding is in same plane and is fixed, discontinuity.
(4), between the step groove of every limit pressing plate and adjacent step protruding rail for being slidably matched, realize can regulating arbitrarily continuously the armourplate glass of different specification size.
(5) angle on, described pressing plate slope and pressing plate between plane is 54-56 to spend, and described pressing plate slope is bonded with one deck rubber compressing tablet, adjustment width armourplate glass carried out plane spacing while, a downward component can be produced, make tested armourplate glass touch test platen, avoid the uneven generation explosion of armourplate glass local pressure.
(6), achieve detection experiment overall process and save disposable product adhesive tape, not only save test consumables cost, avoid contaminated environment; Also shorten the activity duration, the tape residue on test platen need not be removed clean after each test, only need to remove clean cullet, just can implement experiment test operation next time, make work efficiency improve twice.Priorly thoroughly avoid because adhesive tape is burst by tempered glass the possibility that strength collapses out, the personal safety of operating personnel is more secure.
Accompanying drawing explanation
Fig. 1 unloads in stereoscopic appearance figure, figure of the present invention except isoplanar step Anchor plate kit 500.
Fig. 2 be cylinder bulb 199 and the spiral shell of stud lock pin 189 termination in Fig. 1 bore column lockhole 198 binding site along stud lock pin 189 axial line vertical cross section.
Fig. 3 is that the cylinder bulb 199 of stud lock pin 189 termination in Fig. 2 bores column lockhole 198 disengaged condition with spiral shell.
Fig. 4 is the plate frame 200 stereoscopic appearance figure separately in Fig. 1.
Fig. 5 is the test platen 190 stereoscopic appearance figure separately in Fig. 1.
Fig. 6 is the independent stereoscopic appearance figure of upper connecting rod 179 after lower link 176 after lower link 175 before upper connecting rod 174 before the frame in Fig. 1, frame, frame, the front middle pull bar 177 of frame and frame.
Fig. 7 is cullet returnable in Fig. 1 140 and the stereoscopic appearance figure of container discharge door 146 assembly.
Fig. 8 is that the cullet returnable 140 in Fig. 7 unloads the independent stereoscopic appearance figure after except container discharge door 146.
Isoplanar step Anchor plate kit 500 placed by test platen 190 in Fig. 1 to Fig. 9, and is fixed wtih the duty stereoscopic appearance figure of armourplate glass 600.
Back side stereoscopic appearance figure when Figure 10 is test platen 190 rotation in Fig. 9.
Figure 11 is the vertical view that the isoplanar step Anchor plate kit 500 in Fig. 9 is combinationally using.
Figure 12 is the A-A cut-open view in Figure 11.
Figure 13 is the B-B cut-open view in Figure 11, is placed on test platen 190 after armourplate glass 600 is fixed.
Figure 14 is the vertical view of the pressing plate deckle 510 in Figure 11.
Figure 15 is the partial enlarged drawing in Figure 12.
Figure 16 is opposite side slippage part 548 partial enlarged drawing in Figure 15.
Figure 17 is deckle clamp portion 519 partial enlarged drawing in Figure 16.
Figure 18 is the isometric front view of Figure 14.
Figure 19 is the rear isometric view of Figure 14.
Embodiment
The present invention is described in detail below in conjunction with the drawings and specific embodiments:
In Fig. 1, Fig. 2, Fig. 3, Fig. 4, Fig. 5, Fig. 6, Fig. 9, Figure 10 and Figure 11: handle platen screw thread lock pin nitrile rubber step pressuring plate glass pick-up unit, comprise test platen 190 and plate frame 200, upper connecting rod 179 after lower link 176 and frame after lower link 175 and frame before upper connecting rod 174 and frame before organic frame between two plate frames 200, before frame before upper connecting rod 174 and frame after lower link 175 and frame after lower link 176 and frame upper connecting rod 179 two ends be combined with pull-rod nut 178 two plate frames 200 fixed, as improvement:
Described test platen 190 rear end facade has platen handle 155, and there is platen rotating shaft 196 described test platen 190 both sides, and the platen rotating shaft 196 of both sides is rotatable to be respectively fixed in bearing spider 163, and bearing spider 163 is fixed on plane on plate frame 200; There is supporting traverse 717 described position, plate frame 200 upper back, and supporting traverse 717 holds test lower plane both sides, platen 190 rear end;
Stud lock pin 189 external thread matches with lock pin bearing 180 inner hole thread, lock pin bearing 180 is fixed on plane on plate frame 200, and the cylinder bulb 199 of stud lock pin 189 termination of both sides can enter locking positioning in the spiral shell cone column lockhole 198 of test platen 190 both sides;
Plane is fixed wtih isoplanar step Anchor plate kit 500 to described test platen 190, go back pull bar 177 in before organic frame before frame before upper connecting rod 174 and frame between lower link 175, in before frame, before pull bar 177 and described frame, after upper connecting rod 174 and described frame, upper connecting rod 179 is fixed wtih cullet returnable 140 jointly;
On described test platen 190, plane has the nickel-base alloy wearing layer of one deck 1.4 to 1.6 millimeters thick, the material composition of described nickel-base alloy wearing layer is made up of the element of following percentage by weight: Ni:31, Cr:12.5, Al:17.5, Mo:5, Cu:26, Sn:1.5, and surplus is Co and inevitable impurity; The weight percent content of described impurity is: C for O.04, Si is 0.17, Mn is 0.23, S is O.O09, P for O.012, the rockwell superficial hardness number of this nickel-base alloy wearing layer is HRC55.
As further improvement: described test platen 190 has pressing plate fixing threaded hole 197, in described isoplanar step Anchor plate kit 500 at least one clamp portion pressing plate on plane 516 has pressing plate step through-hole 501, sunk screw 195 passes through described pressing plate step through-hole 501 and matches with described pressing plate fixing threaded hole 197.
As further improvement: on every only described plate frame 200, plane is respectively arranged with two bearing seat screws 160 and two locking pin seat screws 186, plate frame 200 plate face there is in before lower through-hole 276 after lower through-hole 275 before the front upper through hole 274 of horizontally disposed frame, frame, frame, frame upper through hole 279 after through hole 277 and frame.
As further improvement: in Fig. 1, Fig. 7, Fig. 8: described cullet returnable 140 comprises end swash plate 141, container header board 143, container biside plate 142 after container, and after container, end swash plate 141 has container discharge mouth 147 between being connected with container header board 143, after container, end swash plate 141 highest point has upper hook 184 after container, and after container, upper hook 184 fixedly hangs over casing tube of tension rod 171 position after frame on upper connecting rod 179, container header board 143 highest point has the front upper hook 148 of container, and the front upper hook 148 of container fixedly hangs over casing tube of tension rod 171 position before frame on upper connecting rod 174, container header board 143 is lower draw-bar 149 before there is container the both sides being positioned at container discharge mouth 147 coboundary position, container discharge door 146 is had between lower draw-bar 149 before the container of both sides, container discharge door 146 there is bin gate link up with 245, before the container of bin gate hook 245 and both sides, lower draw-bar 149 is on coaxial cable, container bin gate spring 145 is had respectively between lower draw-bar 149 before the container of bin gate hook 245 and both sides, casing tube of tension rod 171 in before frame on pull bar 177 runs through lower draw-bar 149 and container bin gate spring 145 and bin gate hook 245 before described container, before the frame that in before frame, on pull bar 177, the pull rod stud 172 at two ends passes through on biside plate open frame 200 respectively after mesopore 277, it is fastening that pull rod stud 172 is furnished with pull-rod nut 178.
As further improvement: Fig. 9, Figure 10, Figure 11, Figure 12, Figure 13, Figure 14, Figure 15, Figure 16, Figure 17, Figure 18 are with in Figure 19: described isoplanar step Anchor plate kit 500 is made up of the isoplanar step pressing plate that four physical dimensions are identical, is respectively: on the right of pressing plate deckle 510, the pressing plate left side 520, pressing plate opposite side 530 and pressing plate 540; Every isoplanar step pressing plate comprises clamp portion and slippage part, and pressing plate deckle 510 comprises deckle clamp portion 519 and deckle slippage part 518; The pressing plate left side 520 comprises left side clamp portion 529 and left side slippage part 528, and pressing plate opposite side 530 comprises opposite side clamp portion 539 and opposite side slippage part 538, and on the right of pressing plate, 540 comprise the right clamp portion 549 and the right slippage part 548;
Described slippage part is positioned at described clamp portion one end and is overlapped on plane on clamp portion; The lower surface of described slippage part is slippage lower plane 561, slippage lower plane 561 has step groove 541, and the upper surface of described clamp portion is plane 516 on pressing plate, and plane 516 has step protruding rail 514 with pressing plate; Described slippage lower plane 561 is in sustained height with plane 516 on described pressing plate;
For being slidably matched between step groove 541 in step protruding rail 514 on described deckle clamp portion 519 and described the right slippage part 548, for being slidably matched between step groove 541 in step protruding rail 514 on described left side clamp portion 529 and described deckle slippage part 518, for being slidably matched between step groove 541 in step protruding rail 514 on described opposite side clamp portion 539 and described left side slippage part 528, for being slidably matched between step groove 541 in step protruding rail 514 on described the right clamp portion 549 and described opposite side slippage part 538, have pressing plate slope 515 inside the clamp portion of every pressing plate, the angle on described pressing plate slope 515 and pressing plate between plane 516 is 54-56 to spend, and pressing plate slope 515 is also adhered fixed rubber compressing tablet 551,
Described rubber compressing tablet 551 adopts synthesis nitrile rubber, its material composition is: nitrile rubber 44%, carbon black 23%, zinc paste 3%, dibutyl ester 12%, stearic acid 0.8%, paraffin: 5.5%, promoter 1.2%, aging resister 1.3%, all the other are inserts.
As further improvement: the distance that on described pressing plate, plane 516 pushes up plane to described step protruding rail 514 is 21 to 23 millimeters, the width of described transition raised line 571 is 7 to 9 millimeters, the height of described transition raised line 571 is 6 to 8 millimeters, and the described single-ended opening of step protruding rail 514;
Described slippage lower plane 561 is 21 to 23 millimeters to the distance of described step groove 541 baseplane, the width of described transition groove 574 is 7 to 9 millimeters, the height of described transition groove 574 is 6 to 8 millimeters, and described step groove 541 both ends open;
Be clearance fit between transition groove 574 in transition raised line 571 on described the right clamp portion 549 and opposite side slippage part 538, for being slidably matched between transition groove 574 in transition raised line 571 on described left side clamp portion 529 and deckle slippage part 518, for being slidably matched between transition groove 574 in transition raised line 571 on described deckle clamp portion 519 and the right slippage part 548, for being slidably matched between the transition groove 574 in the transition raised line 571 on described opposite side clamp portion 539 and left side slippage part 528.
As further improvement: have return pulley forked standard 124 respectively before and after bottom described plate frame 200, mobile return pulley 400 is had in the middle of return pulley forked standard 124, being rotatable clearance fit between mobile return pulley 400 center pit and return pulley pivot pin 122 cylindrical, is interference fit between the through hole on return pulley pivot pin 122 two ends and return pulley forked standard 124.
In embodiment, described test platen 190 there are 4 pressing plate fixing threaded holes 197, in described isoplanar step Anchor plate kit 500 at least deckle clamp portion 519 pressing plate on plane 516 has 4 pressing plate step through-holes 501,4 sunk screws 195 pass through described pressing plate step through-hole 501 successively and match with described pressing plate fixing threaded hole 197, are fixed on described test platen 190 by described isoplanar step Anchor plate kit 500.
Before frame before upper connecting rod 174, frame after lower link 175, frame after lower link 176, frame before upper connecting rod 179 and frame in pull bar 177 geomery all the same, be all made up of the pull rod stud 172 at casing tube of tension rod 171 and two ends.
Device assembling process:
The pull rod stud 172 at the two ends before frame before upper connecting rod 174, frame after lower link 175, frame after lower link 176 and frame on upper connecting rod 179 to pass through after lower through-hole 275 before the front upper through hole 274 of frame of both sides, frame, frame upper through hole 279 after lower through-hole 276 and frame respectively, and each pull rod stud 172 outer end has pull-rod nut 178 immovable fitting fastening.
The platen rotating shaft 196 of described test platen 190 both sides coordinates with bearing spider 163 endoporus is rotatable, and the bearing spider 163 of both sides is fixed on bearing seat screw 160 by four bearing seat screws respectively.
Stud lock pin 189 external thread matches with lock pin bearing 180 inner hole thread, the lock pin bearing 180 of both sides is fixed on locking pin seat screw 186 by four locking pin seat screws respectively, and the cylinder bulb 199 of stud lock pin 189 termination of both sides can enter locking positioning in the spiral shell cone column lockhole 198 of test platen 190 both sides.
When one, will do fragmentation test to tempered glass, step is as follows:
(1), the platen handle 155 grasped on test platen 190 rear end facade exerts oneself downwards, and make test platen 190 rear end lower plane push down supporting traverse 717, test platen 190 presents horizontality.Stud lock pin 189 on the lock pin crank handle 187 of the hand both sides of difference, makes stud lock pin 189 enter locking positioning in the spiral shell cone column lockhole 198 of test platen 190 both sides.
(2), by pressing plate deckle 510 identical for four physical dimensions, the pressing plate left side 520, on the right of pressing plate opposite side 530 and pressing plate, 540 are placed on above test platen 190, for being slidably matched between step groove 514 in step protruding rail 514 on deckle clamp portion 519 and the right slippage part 548, the right clamp portion 549 on step protruding rail 514 and the step groove 514 in opposite side slippage part 538 between for being slidably matched, for being slidably matched between step groove 514 in step protruding rail 514 on left side clamp portion 529 and deckle slippage part 518, for being slidably matched between step groove 514 in step protruding rail 514 on opposite side clamp portion 539 and left side slippage part 528, make the pressing plate deckle 510 that four physical dimensions are identical, the pressing plate left side 520, the surrounding ambient in besieged city between 540 on the right of pressing plate opposite side 530 and pressing plate,
(3), above-mentioned surrounding ambient size is greater than the physical dimension of the armourplate glass 600 wanting tested, armourplate glass 600 that will be tested is placed on above the test platen 190 in above-mentioned surrounding ambient, on the right of the pressing plate deckle 510 that mobile four physical dimensions are identical successively, the pressing plate left side 520, pressing plate opposite side 530 and pressing plate 540, the rubber compressing tablet 551 on every pressing plate is made to touch four limit outer rims of the armourplate glass 600 wanting tested;
(4) after, wanting tested armourplate glass 600 to be fixed, exert a force on assigned address according to testing standard pane hammer, tested armourplate glass 600 is destroyed, requires to detect according to national standard, complete the fragmentation status test of tempered glass;
(5), remove the isoplanar step pressing plate on 1 to 2 limit, the stud lock pin 189 on the lock pin crank handle 187 of hand both sides in the other direction, makes stud lock pin 189 exit the spiral shell cone column lockhole 198 of test platen 190 both sides, removes locking positioning.
The platen handle 155 grasped on the facade of test platen 190 rear end is upwards exerted oneself, and test platen 190 rear end promotes, and test platen 190 rear end lower plane is away from supporting traverse 717.After being spent by inclination 10 to 20 by test platen 190, dispose tempered glass fragment and call among cullet returnable 140.
(6), the platen handle 155 grasped on test platen 190 rear end facade exerts oneself downwards, and test platen 190 presents horizontality again.Stud lock pin 189 on the lock pin crank handle 187 of respectively hand both sides again, makes stud lock pin 189 enter locking positioning in the spiral shell cone column lockhole 198 of test platen 190 both sides, as long as prepare for next tested armourplate glass 600;
(7), when the chunk glass in cullet returnable 140 is many to when will rafting, to rafting car is placed on below container discharge mouth 147, with the bin gate handle 246 pulled out on container discharge door 146, rafting the chunk glass in cullet returnable 140.Unclamp bin gate handle 246, under the accumulation of energy counter-force effect of container bin gate spring 145, container discharge door 146 can touch container discharge mouth 147 tightly, does not allow chunk glass scatter.
Two, the above-mentioned outstanding substantive distinguishing features of the present invention, guarantees to bring following significant progressive effect:
(1), test platen 190 rear end facade there is platen handle 155, the turning vibrational power flow of test platen 190 can be driven, be convenient to remove chunk glass remove, be equipped with cullet returnable 140, guarantee that chunk glass does not scatter, supporting traverse 717 holds the rear lower plane of test platen 190, in conjunction with the lock pin crank handle 187 of both sides, match with lock pin bearing 180 inner hole thread by means of stud lock pin 189, the cylinder bulb 199 of stud lock pin 189 termination is made to enter locking positioning in the spiral shell cone column lockhole 198 of test platen 190 both sides, overcome the defect that the direct Turnover testing platen of platen handle does not have self-locking, make to keep firmly solid in armourplate glass 600 process of whole test.
(2), container bin gate spring 145 is set respectively between lower draw-bar 149 before the container of bin gate hook 245 and both sides, guarantees that container discharge door 146 can touch container discharge mouth 147 tightly, do not allow chunk glass scatter.
(3), isoplanar step Anchor plate kit 500 is adopted, particularly slippage part is positioned at clamp portion one end and is overlapped on plane on clamp portion, and described slippage lower plane 561 is in sustained height with plane 516 on described pressing plate, guarantee that tested armourplate glass 600 surrounding is in same plane and is fixed, discontinuity.
(4), between the step groove 514 of every limit pressing plate and adjacent step protruding rail 514 for being slidably matched, realize can regulating arbitrarily continuously the armourplate glass 600 of different specification size.
(5) angle on, described pressing plate slope 515 and pressing plate between plane 516 is 54-56 to spend, and described pressing plate slope 515 is bonded with the rubber compressing tablet 551 of one deck 2.1-2.3 millimeters thick, adjustment width armourplate glass 600 carried out plane spacing while, a downward component can be produced, make tested armourplate glass 600 touch test platen 190, avoid the uneven generation explosion of armourplate glass 600 local pressure.
(6), achieve detection experiment overall process and save disposable product adhesive tape, not only save test consumables cost, avoid contaminated environment; Also shorten the activity duration, the tape residue on test platen 190 need not be removed clean after each test, only need to remove clean cullet, just can implement experiment test operation next time, make work efficiency improve twice.Priorly thoroughly avoid because adhesive tape is burst by tempered glass the possibility that strength collapses out, the personal safety of operating personnel is more secure.
Three, table 1 present invention employs isoplanar step Anchor plate kit to compare with the data using disposable product adhesive tape conventionally test to do.
The data of (table 1) operating efficiency operating efficiency compare
As can be drawn from Table 1: the rubber compressing tablet 551 adopting synthesis nitrile rubber, its specific material composition physical characteristics that formula has, guarantees to go through hundred experiment test operations without breakage, and test platen 190 base Alloy Coating On 45 alloy wear-resisting layer is intact.