CN105297019A - Novel ZG18MNCRMORE steel corrosion solution - Google Patents

Novel ZG18MNCRMORE steel corrosion solution Download PDF

Info

Publication number
CN105297019A
CN105297019A CN201410303246.6A CN201410303246A CN105297019A CN 105297019 A CN105297019 A CN 105297019A CN 201410303246 A CN201410303246 A CN 201410303246A CN 105297019 A CN105297019 A CN 105297019A
Authority
CN
China
Prior art keywords
corrosion
solution
picric acid
novel
steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410303246.6A
Other languages
Chinese (zh)
Inventor
李娜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410303246.6A priority Critical patent/CN105297019A/en
Publication of CN105297019A publication Critical patent/CN105297019A/en
Pending legal-status Critical Current

Abstract

The invention discloses a novel ZG18MNCRMORE steel corrosion solution. Picric acid, copper chloride and ethyl alcohol are added into distilled water to form the corrosion solution, 3% of picric acid, 4.5% of copper chloride, 8.5% of ethyl alcohol and the balance distilled water are used according to the volume percent, and the picric acid, the copper chloride and the ethyl alcohol are added in sequence during preparation. After corrosion through the corrosion solution, the grain boundary and the grains of the ZG18MNCRMORE steel are clearly displayed, the corrosion effect is good, the metallographic sample preparation time is greatly shortened, and the corrosion time is short.

Description

A kind of novel ZG18MNCRMORE steel corrosion solution
technical field:
The present invention relates to a kind of novel ZG18MNCRMORE steel corrosion solution, belong to etchant solution technical field.
background technology:
The metallographic structure of ZG18MNCRMORE steel is difficult to corrosion, even if out it organizes also often show incomplete in corrosion, thus usually all adopt anode overlay film to add polarisation to observe its metallographic, also have some common etchant solutions to corrode it, but effect is not clearly simultaneously.Therefore how the etching pit of ZG18MNCRMORE steel becomes simple and fast is the difficult problem waiting to solve.
summary of the invention:
The technical problem to be solved in the present invention: provide a kind of novel ZG18MNCRMORE steel corrosion solution, it is clear that the crystal boundary of the ZG18MNCRMORE steel after corrosion and crystal grain show, and corrosive effect is good.
Technical scheme of the present invention:
A kind of novel ZG18MNCRMORE steel corrosion solution, in distilled water, add picric acid, cupric chloride, alcohol makes etchant solution, wherein picric acid, cupric chloride, alcohol are respectively 3%, 4.5%, 8.5% with volume fraction, surplus is distilled water, successively adds picric acid, cupric chloride, alcohol during preparation.
Described etchant solution adopts conventional solution preparation method to prepare.
Beneficial effect of the present invention:
Compared with prior art, after etchant solution corrosion of the present invention, it is clear that the crystal boundary of ZG18MNCRMORE steel and crystal grain show, and corrosive effect is better, shorten the metallographic sample preparation time greatly, and etching time is shorter.
accompanying drawing illustrates:
Fig. 1 is the corrosive effect figure of 100 times.。
embodiment:
Embodiment:
A kind of novel ZG18MNCRMORE steel corrosion solution, in 84ml distilled water, add 3mL picric acid, 4.5mL cupric chloride, 8.5mL alcohol makes etchant solution, successively add picric acid, cupric chloride, alcohol during preparation, then stir with glass stick.
Be used for by the etchant solution made through above-mentioned steps corroding ZG18MNCRMORE steel, concrete effect is shown in Fig. 1, and the effect of known etchant solution of the present invention is better, and it is clear that crystal boundary and crystal grain show.

Claims (2)

1. a novel ZG18MNCRMORE steel corrosion solution, it is characterized in that: in distilled water, add picric acid, cupric chloride, alcohol makes etchant solution, wherein picric acid, cupric chloride, alcohol are respectively 3%, 4.5%, 8.5% with volume fraction, surplus is distilled water, successively adds picric acid, cupric chloride, alcohol during preparation.
2. one according to claim 1 novel ZG18MNCRMORE steel corrosion solution, is characterized in that: described etchant solution adopts conventional solution preparation method to prepare.
CN201410303246.6A 2014-06-30 2014-06-30 Novel ZG18MNCRMORE steel corrosion solution Pending CN105297019A (en)