CN105295413B - A kind of product of rubber and plastic mechanical property modifying agent - Google Patents
A kind of product of rubber and plastic mechanical property modifying agent Download PDFInfo
- Publication number
- CN105295413B CN105295413B CN201510771910.4A CN201510771910A CN105295413B CN 105295413 B CN105295413 B CN 105295413B CN 201510771910 A CN201510771910 A CN 201510771910A CN 105295413 B CN105295413 B CN 105295413B
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- product
- plastic
- mechanical property
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of product of rubber and plastic mechanical property modifying agent, the defect existed for existing product of rubber and plastic, by resinae, polyethylene, silane coupler, carboxylic acid compound, water reducer, epoxide, phosphite ester, toughener, plasticiser, the preparing raw materials such as anti-wear agent are constituted, the product of rubber and plastic mechanical property modifying agent of the present invention, it is not only nontoxic, good weatherability, with preferable stability, it is applied to and goes obtained finished product that there is preferable fire resistance in product of rubber and plastic, anti-wear performance, tensile resistance and intensity, and it still is able to keep good mechanical performance in hot environment for a long time, it is unlikely to deteriorate impaired, service life is long, with very strong practical value.
Description
Technical field
The present invention relates to a kind of rubber and plastics auxiliaries, more particularly, to a kind of product of rubber and plastic mechanical property modifying agent.
Background technology
In automobile industry, Automobile Plastic Rubber accessory species is various, such as rain brush, seal fitting, damping air spring circle, tooth form
Cutting belt etc., different product is different to the mechanical property requirements of rubber and plastic accessory with the place to use of accessory, and due to automobile
For the long-term lossy product of update cycle length, and many places are all in hot operation state in use, and this is just right
Accessory require it is very high, from the performance such as intensity, fire resistance, low-temperature resistance, stretch-proof, high temperature resistance, wear-resistant for have certain
It is required that, this applied to the mechanical property modifying agent in rubber and plastic accessory also just to having further high standards.
A kind of exploitation dedicated for improving the mechanical property modifying agent of Automobile Plastic Rubber accessory article is worth research.
The content of the invention
Goal of the invention:In order to solve in the presence of prior art the problem of, the present invention, which proposes one kind, effectively to be changed
It is apt to the product of rubber and plastic mechanical property of fire resistance, anti-high and low-temp performance, anti-wear performance, tensile resistance and the intensity of product of rubber and plastic
Modifying agent.
Technical scheme:To achieve these objectives, the present invention takes following technical scheme:
A kind of product of rubber and plastic mechanical property modifying agent, the preparing raw material of following components is included according to weight meter:Resinae 15-
20 parts, 5-10 parts of polyethylene, 3-6 parts of silane coupler, 5-12 parts of carboxylic acid compound, 4-6 parts of water reducer, epoxide 3-
6 parts, 3-7 parts of phosphite ester, 1-5 parts of toughener, 3-6 parts of plasticiser, 2-5 parts of anti-wear agent.
Further, the resinae is the mixture of flame-retardant resin and phenolic resin.
Further, in the resinae content of flame-retardant resin more than 50%.
Further, the epoxide is one kind in expoxy propane, epoxy silicon oil, epoxychloropropane.
Further, the carbon atom number of the carboxylic acid compound is not less than 6.
Further, the toughener is haloflex.
Further, the plasticiser is environment-friendlyplasticizer plasticizer.
Further, silicone oil is not less than 20% in the anti-wear agent.
Beneficial effect:A kind of product of rubber and plastic mechanical property modifying agent that the present invention is provided, exists for existing product of rubber and plastic
Defect, by resinae, polyethylene, silane coupler, carboxylic acid compound, water reducer, epoxide, phosphite ester, increasing
Tough dose, plasticiser, the preparing raw material such as anti-wear agent constitute, product of rubber and plastic mechanical property modifying agent of the invention, it is not only nontoxic,
Good weatherability, with preferable stability, be applied to gone in product of rubber and plastic obtained finished product there is preferable fire resistance, it is wear-resisting
Performance, tensile resistance and intensity, and for a long time in hot environment still be able to keep good mechanical performance, be unlikely to deteriorate by
Damage, service life is long, with very strong practical value.
Embodiment
Embodiment 1:
A kind of product of rubber and plastic mechanical property modifying agent, the preparing raw material of following components is included according to weight meter:Resinae 15
Part, 5 parts of polyethylene, 3 parts of silane coupler, 5 parts of carboxylic acid compound, 4 parts of water reducer, 3 parts of epoxide, phosphite ester 3
Part, 1 part of toughener, 3 parts of plasticiser, 2 parts of anti-wear agent.
Wherein, the resinae is the mixture of flame-retardant resin and phenolic resin;Flame-retardant resin in the resinae
Content more than 50%;The epoxide is expoxy propane;The carbon atom number of the carboxylic acid compound is not less than 6;
The toughener is haloflex;The plasticiser is environment-friendlyplasticizer plasticizer;Silicone oil is not less than in the anti-wear agent
20%.
Embodiment 2:
A kind of product of rubber and plastic mechanical property modifying agent, the preparing raw material of following components is included according to weight meter:Resinae 20
Part, 10 parts of polyethylene, 6 parts of silane coupler, 12 parts of carboxylic acid compound, 6 parts of water reducer, 6 parts of epoxide, phosphite ester
7 parts, 5 parts of toughener, 6 parts of plasticiser, 5 parts of anti-wear agent.
Wherein, the resinae is the mixture of flame-retardant resin and phenolic resin;Flame-retardant resin in the resinae
Content more than 50%;The epoxide is epoxy silicon oil;The carbon atom number of the carboxylic acid compound is not less than 6;
The toughener is haloflex;The plasticiser is environment-friendlyplasticizer plasticizer;Silicone oil is not less than in the anti-wear agent
20%.
Embodiment 3:
A kind of product of rubber and plastic mechanical property modifying agent, the preparing raw material of following components is included according to weight meter:Resinae 17
Part, 8 parts of polyethylene, 3-6 parts of silane coupler, 8 parts of carboxylic acid compound, 5 parts of water reducer, 5 parts of epoxide, phosphite ester
5 parts, 3 parts of toughener, 5 parts of plasticiser, 4 parts of anti-wear agent.
Wherein, the resinae is the mixture of flame-retardant resin and phenolic resin;Flame-retardant resin in the resinae
Content more than 50%;The epoxide is epoxychloropropane;The carbon atom number of the carboxylic acid compound is not less than
6;The toughener is haloflex;The plasticiser is environment-friendlyplasticizer plasticizer;Silicone oil is not less than in the anti-wear agent
20%.
It will be prepared into after modifying agent and answer according to the preparation method of traditional modifying agent according to above-described embodiment 1-3 composition
Use in product of rubber and plastic, take its finished product to be measured its heatproof air aging performance, the measurement result of shear strength is specific such as
Shown in following table:
Embodiment | Embodiment 1 | Embodiment 2 | Embodiment 3 |
250℃/1h(MPa) | 41.3 | 42.4 | 40.8 |
300℃/1h(MPa) | 81.3 | 80.6 | 82.2 |
Such as data display in upper table, the product of rubber and plastic mechanical property for the embodiment 1-3 being formulated using the present composition is changed
The product of rubber and plastic of property agent has all reached higher level under 250 DEG C/1h and 300 DEG C/1h shear strength test, better than normal
Advise product of rubber and plastic.
Using a kind of above-described embodiment 1-3 product of rubber and plastic mechanical property modifying agent, more traditional product of rubber and plastic is not only nontoxic
Harmless, good weatherability, with preferable stability, is applied to and goes obtained finished product to have preferable anti-flammability in product of rubber and plastic
Energy, anti-wear performance, tensile resistance and intensity, and it still is able to keep good mechanical performance, no in hot environment for a long time
Perishable impaired, service life is long, with very strong practical value.
It should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention,
Some improvement can also be made, these improvement also should be regarded as protection scope of the present invention.
Claims (3)
1. a kind of product of rubber and plastic mechanical property modifying agent, it is characterised in that include the preparing raw material of following components according to weight meter:
15-20 parts of resinae, 5-10 parts of polyethylene, 3-6 parts of silane coupler, 5-12 parts of carboxylic acid compound, 4-6 parts of water reducer, ring
3-6 parts of oxygen compound, 3-7 parts of phosphite ester, 1-5 parts of toughener, 3-6 parts of plasticiser, 2-5 parts of anti-wear agent;The resinae is
The mixture of flame-retardant resin and phenolic resin;The content of flame-retardant resin is more than 50% in the resinae;The epoxy compound
Thing is one kind in expoxy propane, epoxy silicon oil, epoxychloropropane;The toughener is haloflex;The plasticiser is
Environment-friendlyplasticizer plasticizer.
2. product of rubber and plastic mechanical property modifying agent according to claim 1, it is characterised in that:The carboxylic acid compound
Carbon atom number is not less than 6.
3. product of rubber and plastic mechanical property modifying agent according to claim 1, it is characterised in that:Silicone oil contains in the anti-wear agent
Amount is not less than 20%.