CN105293666A - 复合絮凝剂 - Google Patents
复合絮凝剂 Download PDFInfo
- Publication number
- CN105293666A CN105293666A CN201510916725.XA CN201510916725A CN105293666A CN 105293666 A CN105293666 A CN 105293666A CN 201510916725 A CN201510916725 A CN 201510916725A CN 105293666 A CN105293666 A CN 105293666A
- Authority
- CN
- China
- Prior art keywords
- solution
- flocculation agent
- sodium hydroxide
- value
- composite flocculation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种复合絮凝剂，其制备方法包括以下步骤：步骤1、硅酸盐配制成浓度为20-50%的溶液；步骤2、加入20%浓度硫酸和氢氧化钠溶液调节PH将溶液活化，取得聚合硅酸溶液；步骤3、将溶液搅拌，并加入铁盐药剂溶液；步骤4、加入氢氧化钠调节PH值，使金属离子与硅酸共聚，并搅拌均匀；步骤5、熟化后获得成品，新配方的复合絮凝剂降具有处理效果好、处理速度明显提高、废水处理成本低等优势，从而提高水资源的利用率。
Description
技术领域
本发明涉及水处理技术领域，尤其是一种适用于污水系统的复合絮凝剂。
背景技术
随着工业的飞速发展，供水紧张和污水净化成为我国乃至世界各地面临的主要难题之一。我国是个缺水的国家，城市工业用水量大，且排放的工业废水中含有一定量的污染物，使本来有限的水资源又有一部分失去了使用价值。因此，提高水资源利用率是刻不容缓的事情。自1827年人们首次使用硫酸铝(AI2(SO4)3)进行水质澄清净化处理后，絮凝过程一直是水质净化澄清处理工艺过程中不可缺少的技术环节。因此研究开发出处理效果好、废水处理成本低的新型复合絮凝剂具有非常广阔的应用前景。
发明内容
本发明的目的在于提供一种将药剂的使用效果发挥到最佳，同时降低废水处理成本的复合絮凝剂。
为解决上述技术问题，本发明提供一种复合絮凝剂，其制备方法包括以下步骤：
步骤1、硅酸盐配制成浓度为20-50％的溶液；
步骤2、加入20％浓度硫酸和氢氧化钠溶液调节PH将溶液活化，取得聚合硅酸溶液；
步骤3、将溶液搅拌，并加入铁盐药剂溶液；
步骤4、加入氢氧化钠调节PH值，使金属离子与硅酸共聚，并搅拌均匀；
步骤5、熟化后获得成品。
本发明改进有，所述步骤1中硅酸盐配置的浓度为30％。
本发明改进有，所述步骤2中，溶液的PH值调节至5.0，并酸化15min。
本发明改进有，步骤4中硅酸盐与金属离子的比例为1:1。
本发明的有益效果为：新配方的复合絮凝剂降具有处理效果好、处理速度明显提高、废水处理成本低等优势，从而提高水资源的利用率。
具体实施方式
为详细说明本发明的技术内容、构造特征、所实现目的及效果，以下结合实施方式详予说明。
本发明提供一种复合絮凝剂，其制备方法具体包括以下步骤：
步骤1、硅酸盐配制成浓度为20-50％的溶液，优选的，硅酸盐配置的浓度为30％。
步骤2、加入20％浓度硫酸和氢氧化钠溶液调节PH将溶液活化，取得聚合硅酸溶液；
步骤3、将溶液搅拌，并加入铁盐药剂溶液；
步骤4、加入氢氧化钠调节PH值，使金属离子与硅酸共聚，并搅拌均匀；
步骤5、熟化后获得成品。
此种复合絮凝剂降具有处理效果好、废水处理成本低等优势，从而提高水资源的利用率。
下面通过一个实施例详细进一步说明新型复合絮凝剂的制备过程：
1.将配置好一定浓度的硅酸盐用20％硫酸或者氢氧化钠调节PH至5.0，酸化15min左右；
2.在不断搅拌下，在上述酸化的溶液中加入铁盐等其它配置好定量的溶液；
3.在不断搅拌下，加入氢氧化钠调节PH值，使金属离子与硅酸共聚。其硅酸盐与金属离子的比例为1:1。
制备后的复合絮凝剂可以通过实验证明其效果。
1、试验方法：采用COD自动消解回流仪进行煮沸消解，冷却后采用硫酸亚铁铵进行滴定。
2、试验条件：温度：25℃
搅拌速度:由快至慢(搅拌速度从250转/分-20-30转/分逐渐递减，时间约为30min。
废水PH值：8.0-9.5之间(8.5左右效果最佳)
3、试验水源：焦化厂二沉池出水①、焦化厂二沉池出水②
4、试验药剂：复合絮凝剂、PAC(喷雾聚合氯化铝，含量30％)
5、试验结果
焦化厂二沉池出水①COD数值245mg/L
焦化厂二沉池出水①COD数值320mg/L
试验结论：
从以上计算的试验结果可以看出对于同是焦化厂二沉池的排水，当COD数值不同时，复合絮凝剂的去除率始终保持在50％以上，在加药量大的情况下，可达到72％，达到废水排放标准；在相同的水质，相同的试验条件，相同的加药量的条件下，废水的处理效果远远不如使用相同加药量下的复合絮凝剂。充分说明，复合絮凝剂的使用效果比单一的絮凝剂更佳，处理效果也更为理想。
通过这项研究，在焦化废水的处理过程中，处理速度明显提高，处理效果明显加强，同时提高了水资源的在利用率，以减轻对环境的压力。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (4)
1.一种复合絮凝剂，其特征在于，其制备方法包括以下步骤：
步骤1、硅酸盐配制成浓度为20-50%的溶液；
步骤2、加入20%浓度硫酸和氢氧化钠溶液调节PH将溶液活化，取得聚合硅酸溶液；
步骤3、将溶液搅拌，并加入铁盐药剂溶液；
步骤4、加入氢氧化钠调节PH值，使金属离子与硅酸共聚，并搅拌均匀；
步骤5、熟化后获得成品。
2.根据权利要求1所述的复合絮凝剂，其特征在于，所述步骤1中硅酸盐配置的浓度为30%。
3.根据权利要求1所述的复合絮凝剂，其特征在于，所述步骤2中，溶液的PH值调节至5.0，并酸化15min。
4.根据权利要求1所述的复合絮凝剂，其特征在于，步骤4中硅酸盐与金属离子的比例为1:1。