CN1052882A - Thermally adherent polymer film - Google Patents
Thermally adherent polymer film Download PDFInfo
- Publication number
- CN1052882A CN1052882A CN 89104153 CN89104153A CN1052882A CN 1052882 A CN1052882 A CN 1052882A CN 89104153 CN89104153 CN 89104153 CN 89104153 A CN89104153 A CN 89104153A CN 1052882 A CN1052882 A CN 1052882A
- Authority
- CN
- China
- Prior art keywords
- weight
- film
- synergist
- grams
- film according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention is a kind of thermally adherent polymer film, its raw material consists of, the multipolymer 85-94% (weight) that has polar group, oxidation inhibitor 0.6-1.5% (weight), inorganic Synergist S-421 95 5-10% (weight), pigment dyestuff 0.1-0.8% (weight), static inhibitor 0.1-1.0% (weight), other Synergist S-421 95 0.1-4.0% (weight).This film has good thermal caking performance and heat sealability, is applicable to most of metallic substance and polarity non-metallic material heat posted compoundly, is widely used in the fields such as comprehensive shielded sheath of packing, anticorrosion, electric wire and cable.
Description
The invention belongs to a kind of polymer film, particularly relate to a kind of thermally adherent polymer film.
Present widely used polyethylene, polyvinyl chloride film does not all have the cohesiveness with other material, when needs bondings compound (promptly laminating), generally need film and bonded base material are made corona treatment respectively, make it the surface polarization, and carry out compoiste adhering behind the coated with adhesive again, so cohesiveness is not good enough, and operational path is loaded down with trivial details, the production cost height.
The objective of the invention is in order to solve above-mentioned shortcoming, a kind of film that can directly carry out thermal caking with most of metallic substance and polarity non-metallic material is provided.
The material component proportioning of thermal caking film of the present invention is, the multipolymer 85-94%(weight that has polar group), oxidation inhibitor 0.6-1.5%(weight), inorganic Synergist S-421 95 5-10%(weight), pigment dyestuff 0.1-0.8%(weight), static inhibitor 0.1-4.0%(weight).Other Synergist S-421 95 0.1-4.0%(weight).
The multipolymer that has polar group described in the present invention is general normal to be ethylene/acrylic acid copolymer (EAA), the ethene/acrylic ester multipolymer, also can be ethylene/methacrylic acid (EMMA), ethylene/vinyl acetate multipolymer (EVA) waits other to have the multipolymer of polar group.
Oxidation inhibitor described in the present invention is general normal to be phenolic antioxidant, as 2,6 ditertbutylparacresols.2,2-methylene bis (4-methyl-6 tertiary butyl) phenol, 4, two (the 6-tertiary butyl 3 methyl) phenol of 4-sulfuration, styrenated phenol etc.; Or amine antioxidants, as DNP(nitrogen nitrogen 2-β-benzene naphthalene Ursol D), DTTD(nitrogen ammonia 2 diphenyl-para-phenylene diamines), pyridyl-naphthalidine etc.; Or the ester kind antioxidant, defend at least a in tetrol ester, β-propionic acid octadecanol ester, sulfuration dipropionic acid two lauryls etc. as the four seasons.
Inorganic Synergist S-421 95 described in the present invention is general normal to be calcium carbonate powders, calcium sulphate powders, talcum powder, and SiO 2 powder, titanium dioxide, calcinated argil etc. or its mixture, granularity is advisable with 20-50m μ.
Pigment dyestuff described in the present invention general normal be the titanium cyanines, a kind of in thioindigo, anthraquinone, pyrene tetracid, dioxazines, the acid junket etc.
Static inhibitor described in the present invention general normal be amphoteric substance, as two property tetrahydroglyoxalines etc.
Other Synergist S-421 95 described in the present invention is generally coupling agent; as methyl-silicone oil, vinyltriethoxysilane (A-151); titanic acid ester such as vinyl three (2-methoxyethoxy) silane silane series coupling agents such as (A-172) and isopropyl triisostearoyl titanate are a kind of in the coupling agent; also can be to be total to its properties-correcting agent, as anti copper agent, anti-aging agent, fire retardant, anti UV agent etc.
When using the various additive beyond the above-mentioned resin, can directly add, also can be earlier and new LDPE (film grade) or as interpolation again after the mixed with resin granulation of base-material.
Thermal caking film of the present invention is a blown film, earlier various components is mixed by a certain percentage, is blow molded into the film that thickness is 0.05mm through the extrusion-blown modling unit then.
The mechanical property and the adhesiveproperties of thermal caking film of the present invention are as shown in table 1.
Table 1:
Longitudinal fracture intensity (MPa) 26.0-30.0
Cross-breaking strength (MPa) 26.0-30.0
Longitudinal tensile strain rate (%) 400-600
Cross direction elongation (%) 600-700
Stripping strength (N/Cm) 6.00-7.00 behind film and the aluminium foil compound sticking
Heat seal strength (N/Cm) 17.00-26.00
Describe the present invention in detail with embodiment below.
Embodiment 1:
By filling a prescription 1 with oxidation inhibitor, inorganic Synergist S-421 95 and pigment dyestuff adopt general method to be mixed with pellet earlier.
Prescription 1
Oxidation inhibitor pellet oxidation inhibitor 500 grams
EAA 3500 grams
Inorganic Synergist S-421 95 pellet silicon-dioxide 500 grams
EAA 1500 grams
Pigment dyestuff pellet phthalocyanine 270 grams
EAA 730 grams
And then 2 take by weighing various pellet components by prescription, mix after the extrusion-blown modling unit is blow molded into the film that thickness is 0.05mm.
Prescription 2
EAA pellet 8100 grams
Oxidation inhibitor pellet 800 grams
Inorganic Synergist S-421 95 pellet 800 grams
Phthalocyanine pellet 300 grams
Embodiment 2:
Take by weighing various components by prescription 3, mix after the extrusion-blown modling unit is blow molded into the film that thickness is 0.05mm.
Prescription 3
EAA 9200 grams
Two (the 6-tertiary butyl-3 methyl) phenol 60 grams of 4,4 sulfurations
Calcium carbonate powders 500 grams
Phthalocyanine 40 grams
Sulfuration dipropionic acid two lauryls 100 grams
Two property tetrahydroglyoxalines, 50 grams
Isopropyl triisostearoyl titanate 50 grams
Embodiment 3:
Take by weighing various components by prescription 4, mix after the extrusion-blown modling unit is blow molded into the film that thickness is 0.05mm.
Prescription 4
EAA 922 grams
Two (the 6-tertiary butyl-3-methyl) phenol 80 grams of 4,4 sulfurations
Calcium carbonate powders 550 grams
Acidic chromium 100 grams
Two property tetrahydroglyoxalines, 50 grams
Claims (7)
1, a kind of high polymer cemented film, it is characterized in that raw material consists of, the multipolymer 85-94% (weight) that has polar group, oxidation inhibitor 0.6-1.5% (weight), inorganic Synergist S-421 95 5-10% (weight), pigment dyestuff 0.1-0.8% (weight), static inhibitor 0.1-1.0% (weight), other Synergist S-421 95 0.1-4.0% (weight).
2, film according to claim 1, the multipolymer component that it is characterized in that having polar group is ethylene/acrylic acid or its lipin polymer.
3, film according to claim 1 is characterized in that the oxidation inhibitor component is one of phenolic antioxidant, amine antioxidants and ester kind antioxidant at least.
4, film according to claim 1 is characterized in that inorganic Synergist S-421 95 is a calcium carbonate powders, SiO 2 powder, titanium dioxide, calcinated argil, or its mix powder.
5, film according to claim 1 is characterized in that pigment dyestuff is the peptide cyanines, a kind of in thioindigo, anthraquinone, pyrene tetracid, the dioxazines.
6, such as claim 1 the art film, it is characterized in that static inhibitor is an amphoteric substance.
7, such as claim 1 the art film, it is characterized in that other Synergist S-421 95 is a coupling agent.