CN105273675B - A kind of water-based fireproof binding agent - Google Patents
A kind of water-based fireproof binding agent Download PDFInfo
- Publication number
- CN105273675B CN105273675B CN201510767700.8A CN201510767700A CN105273675B CN 105273675 B CN105273675 B CN 105273675B CN 201510767700 A CN201510767700 A CN 201510767700A CN 105273675 B CN105273675 B CN 105273675B
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- binding agent
- nano
- based fireproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of water-based fireproof binding agent, belongs to water-based fireproof binding agent used in transmission & distribution electrical domain, to solve the problems, such as in the polyurethane adhesive water resistance used in transmission & distribution electrical domain, freexing tolerance difference.Water-based fireproof binding agent of the present invention, include the component of following parts by weight:20 30 parts of PEPA, 30 40 parts of PPG, 20 30 parts of isocyanates, 14 parts of 22 dimethylolpropionic acid, 0.5 1 parts of N methyl pyrrolidones, 24 parts of triethylamine, 1 1.5 parts of nano-aluminum hydroxide, 0.5 1 parts of nano-sized magnesium hydroxide, 12 parts of antifreezing agent.Water-based fireproof binding agent of the present invention, there is preferable water resistance, water-tolerant;With preferable resistance to frost, suitable for rugged environment outside transmission & distribution electrical domain room;And with good fire-retardant, fire protecting performance.
Description
Technical field
The present invention relates to a kind of adhesive, specifically, is related to water-based fireproof used in a kind of transmission & distribution electrical domain and bonds
Agent.
Background technology
Aqueous binders are that, using water as solvent or dispersant, substitute has the poisonous of pollution to have to environment using resin as glutinous material
Solvent, and a kind of environmentally friendly adhesive being prepared into.Waterborne polyurethane binders be using water replace organic solvent as
The new polyurethane system of decentralized medium, also referred to as water dispersible polyurethane, aqueous polyurethane or water-based polyurethane.Aqueous polyurethane with
Water is solvent, and pollution-free, safe and reliable, good mechanical performance, compatibility are good, easily modified.But such binding agent water resistance
Difference, freeze-proof binding agent that is poor, and being applied in transmission & distribution electrical domain, because its it is more in outdoor environment using, it is necessary to be subjected to wind
An important factor for rain is beaten and the test of cruel winter severe cold, therefore the water resistance of binding agent and freeze-proof turn into influence binding agent quality.
The content of the invention
To solve the above problems, the present invention provides a kind of water-tolerant, freeze-proof good water-based fireproof binding agent.
Water-based fireproof binding agent of the present invention, include the component of following parts by weight:PEPA 20-30 parts, gather
Ethoxylated polyhydric alcohol 30-40 parts, isocyanates 20-30 parts, 2-2- dimethylolpropionic acid 1-4 parts, 1-METHYLPYRROLIDONE 0.5-1 parts,
Triethylamine 2-4 parts, nano-aluminum hydroxide 1-1.5 parts, nano-sized magnesium hydroxide 0.5-1 parts, propane diols 1-2 parts.
Preferably, water-based fireproof binding agent of the present invention includes the component of following parts by weight:20 parts of PEPA,
30 parts of PPG, 20 parts of isocyanates, 2 parts of 2-2- dimethylolpropionic acids, 0.5 part of 1-METHYLPYRROLIDONE, triethylamine 2
Part, 1.5 parts of nano-aluminum hydroxide, 0.5 part of nano-sized magnesium hydroxide, 2 parts of propane diols.
Preferably, the PEPA is prepared by adipic acid and BDO, molecular weight 2500, degree of functionality
For 2.
Preferably, the PPG molecular weight is 1000, degree of functionality 2.
Preferably, the isocyanates is methyl diphenylene diisocyanate;Its isocyanate index (NCO/OH mol ratio
Value) it is 1.2.
Preferably, the mass ratio of the nano-aluminum hydroxide and nano-sized magnesium hydroxide is 3:2.
Compared with prior art, the beneficial effects of the invention are as follows:Water-based fireproof binding agent of the present invention, have preferable
Water resistance, water-tolerant;Containing antifreeze component propane diols, obtained water-based fireproof binding agent has preferably antifreeze
Performance, suitable for rugged environment outside transmission & distribution electrical domain room;Because containing nano-sized magnesium hydroxide and nano-aluminum hydroxide flame retardant composition,
Obtained water-based fireproof binding agent has good fire-retardant, fire protecting performance.
Embodiment
The present invention is further explained with reference to embodiment.
Embodiment 1
A kind of water-based fireproof binding agent, include the component of following parts by weight:20 parts of PEPA, PPG 30
Part, 20 parts of methyl diphenylene diisocyanate, 2 parts of 2-2- dimethylolpropionic acids, 0.5 part of 1-METHYLPYRROLIDONE, triethylamine 2
Part, 1.5 parts of nano-aluminum hydroxide, 0.5 part of nano-sized magnesium hydroxide, 2 parts of propane diols.
The PEPA is prepared by adipic acid and BDO, molecular weight 2500, degree of functionality 2;Institute
It is 1000 to state PPG molecular weight, degree of functionality 2.
Preparation method is as follows:
(1) PEPA, PPG are heated, vacuum dehydration;
(2) isocyanates is added in step (1), prepolymerization reaction is carried out under catalyst;
(3) 2-2- dimethylolpropionic acids and 1-METHYLPYRROLIDONE are added, continues to react obtained base polyurethane prepolymer for use as;
(4) triethylamine deionized water solution is added into base polyurethane prepolymer for use as, mixed at high speed is uniform;
(5) nano-sized magnesium hydroxide and nano-aluminum hydroxide, propane diols are continuously added into step (4), mixed at high speed is uniform;
(6) triethylamine is added, modified aqueous polyurethane is made.
The mass ratio of triethylamine is 20 in step (4) and step (6):1.
Embodiment 2
The present embodiment is same as Example 1 in addition to following characteristics:
A kind of water-based fireproof binding agent, include the component of following parts by weight:30 parts of PEPA, PPG 40
Part, 25 parts of isocyanates, 1 part of 2-2- dimethylolpropionic acids, 0.6 part of 1-METHYLPYRROLIDONE, triethylamine 3 part, nanometer hydroxide
1.5 parts of aluminium, 0.9 part of nano-sized magnesium hydroxide, 1.5 parts of propane diols.
Embodiment 3
The present embodiment is same as Example 1 in addition to following characteristics:
A kind of water-based fireproof binding agent, include the component of following parts by weight:26 parts of PEPA, PPG 34
Part, 27 parts of isocyanates, 3 parts of 2-2- dimethylolpropionic acids, 0.7 part of 1-METHYLPYRROLIDONE, triethylamine 2.3 part, nanometer hydrogen-oxygen
Change 1.4 parts of aluminium, 0.6 part of nano-sized magnesium hydroxide, 1 part of propane diols.
Performance test is carried out to the water-based fireproof binding agent obtained by three embodiments, data are as shown in table 1.
The water-based fireproof Binder Properties data of table 1
Claims (4)
1. a kind of water-based fireproof binding agent, it is characterised in that be made up of the material component of following parts by weight:
PEPA 20-30 parts;
PPG 30-40 parts;
Isocyanates 20-30 parts;
2-2- dimethylolpropionic acid 1-4 parts;
1-METHYLPYRROLIDONE 0.5-1 parts;
Triethylamine 2-4 parts;
Nano-aluminum hydroxide 1-1.5 parts;
Nano-sized magnesium hydroxide 0.5-1 parts;
Propane diols 1-2 parts;
The PEPA is prepared by adipic acid and BDO, molecular weight 2500, degree of functionality 2;
The PPG molecular weight is 1000, degree of functionality 2;
The preparation process of the water-based fireproof binding agent is as follows:
(1) PEPA, PPG are heated, vacuum dehydration;
(2) isocyanates is added in step (1), prepolymerization reaction is carried out under catalyst;
(3) 2-2- dimethylolpropionic acids and 1-METHYLPYRROLIDONE are added, continues to react obtained base polyurethane prepolymer for use as;
(4) triethylamine deionized water solution is added into base polyurethane prepolymer for use as, mixed at high speed is uniform;
(5) nano-sized magnesium hydroxide and nano-aluminum hydroxide, propane diols are continuously added into step (4), mixed at high speed is uniform;
(6) triethylamine is added, modified aqueous polyurethane is made;
The mass ratio of triethylamine is 20 in step (4) and step (6):1.
2. water-based fireproof binding agent according to claim 1, it is characterised in that by the material component group of following parts by weight
Into:20 parts of PEPA, 30 parts of PPG, 20 parts of isocyanates, 2 parts of 2-2- dimethylolpropionic acids, N- methylpyrroles
0.5 part of alkanone, 2 parts of triethylamine, 1.5 parts of nano-aluminum hydroxide, 0.5 part of nano-sized magnesium hydroxide, 2 parts of propane diols.
3. water-based fireproof binding agent according to claim 1 or 2, it is characterised in that the isocyanates is diphenylmethyl
Alkane diisocyanate;Its isocyanate index is 1.2.
4. water-based fireproof binding agent according to claim 1, it is characterised in that the nano-aluminum hydroxide and nanometer hydrogen-oxygen
The mass ratio for changing magnesium is 3:2.