CN105272059A - Dolomite colored coating powder having air-purifying function - Google Patents
Dolomite colored coating powder having air-purifying function Download PDFInfo
- Publication number
- CN105272059A CN105272059A CN201510776636.XA CN201510776636A CN105272059A CN 105272059 A CN105272059 A CN 105272059A CN 201510776636 A CN201510776636 A CN 201510776636A CN 105272059 A CN105272059 A CN 105272059A
- Authority
- CN
- China
- Prior art keywords
- powder
- dolomite
- air purification
- purification function
- acidifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses dolomite colored coating powder having an air-purifying function. According to the technical scheme, the dolomite colored coating powder is characterized in that ingredients include attapulgite pottery clay powder having the air-purifying function, calcined dolomite powder, acidified zeolite particles, colored portland cement, Paris plaster, white carbon black, calcium chloride, aerosil, expanded perlite, nanometer silver-loaded antibacterial powder, nanometer titanium dioxide, sodium pyrophosphate and powder defoaming agents. The ingredients of the dolomite colored coating powder having the air-purifying function are input three times into a stirring machine to be stirred evenly and packaged into the finished product. By the adoption of the colored coating, in indoor wall decoration, an artistic emboss effect of various embossed three-dimensional colored patterns can be achieved through spraying and manufacturing, after spraying, a coating is hard, the porosity is high, the specific surface area is large, adhesion is high, indoor formaldehyde, ammonia nitrogen, benzene and other harmful substances can be adsorbed and decomposed, and the functions of automatic humidification, flame retarding, mould prevention, sterilization, deodorization and air purification are achieved.
Description
Technical field
The present invention relates to coating, be specifically related to a kind of dolomite colo(u)r coating powder with air purification function.
Background technology
Along with the continuous improvement of living condition, the requirement of modern finishing is more and more higher, people's pay attention to day by day makes the indoor environment of environment protection health, good indoor environment is the healthy important leverages of people, beautify indoor environment, the finishing of outstanding characteristics, select the measured artistic texture coating of matter, not only allow your home room individual character show, and do not worry the follow-up bad phenomenon such as coming off, ftracture after fitting up, peeling.
In recent years, people enjoy a lot to adopt with natural nonmetalliferous ore as the various types of coating of main material production, with the environment of adsorption cleaning indoor, but, if the nonmetalliferous ore raw material adopted does not have well to carry out modification, the performance that nonmetalliferous ore raw material is superior can not be given full play to, some coating is in order to increase the specific surface area of nonmetalliferous ore raw material, that often the particle fineness of nonmetalliferous ore raw material is processed is very thin, and the binding agent of the organic or inorganic that compatibility is a large amount of in the raw material of coating, these binding agents are adhesive in the surface of nonmetalliferous ore feed particles, greatly reduce the absorption property of nonmetalliferous ore raw material, directly have influence on the quality of coating.
Dolomite is a kind of deposit carbon Carbonate Rocks, and primarily of rhombspar composition, be often mixed into quartz, feldspar, calcite and clay mineral, in canescence, property is crisp, and hardness is little.
Chinese patent Authorization Notice No. CN101704656B, authorized announcement date: on 09 26th, 2012, name is called " a kind of inner-wall coating composition ", disclose " internal wall finishing material, particularly relate to a kind of by natural material form containing diatomaceous building material composition.Each component and weight percentage thereof are: diatomite: 20-40%, oyster shell whiting: 20-58%, white clouds rock sand: 8-32%, casein food grade: 2-10%, 4A zeolite powder: 5-12%, marine alga rubber powder: 3-8%, flaxen fiber: 0.5-1.5%, titanium dioxide: 2-5% ".
Have employed the nonmetalliferous ore raw materials such as diatomite, oyster shell whiting, white clouds rock sand in the batching of above-mentioned patent, although the diatomite that have employed through calcination process and oyster shell whiting, do not carry out necessary acidification, white cement is not adopted in batching, but adopting marine alga rubber powder, marine alga rubber powder is a kind of thickening material, and film shaped property is good, diatomite micropore can be blocked, reduce the functional of kieselguhr wall material.Dolomite ore deposit main component is calcium carbonate and magnesiumcarbonate, and mohs hardness value is between 3.5 to 4, and this patent adopts 80 ~ 120 object white clouds rock sands, just a kind of framework material.
The purposes of this patent be " really accomplish non-volatile, without discharge, pollution-free.Owing to not containing the hydraulic materials such as white cement, the construction open hour are long, and the material be stirred, can use for a long time, convenient construction, avoids waste of material.Pack with Moisture Proof Pager Bag, can standing storage, bring convenience to the producer, can produce in a large number, dealer does not worry material failure problem yet ", the function purified air can not be had.
Summary of the invention
The object of the invention is to overcome weak point in prior art, a kind of dolomite colo(u)r coating powder with air purification function is provided.
The batching with the dolomite colo(u)r coating powder of air purification function is made up of the dolomite rock powder after having the Attapulgite potter's clay powder of air purification function, calcining, zeolite granular, colored portland cement, gesso, white carbon black, calcium chloride, micropowder silica gel, pearlstone, nano silver-supported antibacterial powder, nano titanium oxide, trisodium phosphate and powder defoamer after acidifying.
There is the production method of the dolomite colo(u)r coating powder of air purification function: the batching of the dolomite colo(u)r coating powder with air purification function divided in three input stirrers and stir, after stirring, be packaged as finished product.
Dolomite loses carbonic acid gas when being fired to 700 ~ 900 DEG C, becomes calcium oxide and magnesian mixture, is called causticity dolomite, has pure white, strong clinging power, coagulation force and good fire-resistant, heat-proof quality.
The Attapulgite potter's clay powder with air purification function glues attapulgite clay by height, attapulite constant humidity amendment, natural-minerals adsorptive filter medium, Leafy twigs of Oriental Arborvitae, aluminium silicate fiber peacekeeping polyacrylamide form; there is good cohesiveness, plasticity-, thixotropy, resistivity against fire and thermostability; can the objectionable impurities such as formaldehyde, ammonia and benzene in effective absorbed air, protection of the environment and promote the healthy of people.
Colored portland cement is called colored portland cement by silicate cement heat material and proper amount of gypsum (or white portland cement), blended material and tinting material band the colorful one hydraulic cementing materials that is levigate or that be mixed, colored portland cement primitive colour has redness, yellow, blueness, green, brown and black etc., and quality needs the standard meeting " JC/T870-2012 colored portland cement ".
Zeolite has powerful adsorption function, even if still can active adsorption under low relative humidity, lower concentration, higher temperature conditions, is therefore stable performance, sorbent material that adsorption effect is good, is applicable to off gas treatment and purifying air.
Zeolite after 420 ~ 480 DEG C of roastings, then carries out acidification, and zeolite obtains further activation, forms loose porous cavernous body, and its adsorption effect is in optimum value.The zeolite that the present invention selects has: clinoptilolite, mordenite, euthalite, chabazite, scolecite, heulandite, natrolite, mordenite and stilbite.
Natural dihydrate gypsum is also called plaster stone, and through calcining, levigately obtain gesso, the plaster of Paris has more microvoid structure, makes it the excellent sound insulation of tool, heat insulation and fire resistance.
White carbon black is a kind of ultra tiny inorganic porous property material, because its particle diameter is very little, there is the stability that specific surface area is large, superficial attractive forces is strong, chemical purity is high, dispersing property is good, superior, the performance that reinforcing, thickening property, sticking power and thixotropy etc. are special.
Calcium chloride has outstanding adsorptive power and low desorption temperature to ammonia, has great application prospect in synthetic ammonia fractionation by adsorption.But because calcium chloride not easily forms stable porous material, little with the contact area of gas ammonia, and easily expand in Adsorption and desorption process, lump, therefore make it to be difficult to be put to practical application in this respect.Calcium chloride is supported on high surface area carrier, greatly can improve the contact area of calcium chloride and gas ammonia.
Micropowder silica gel is a kind of inorganic chemical product of white powder, and its physicochemical property is: nontoxic, tasteless, do not fire, not quick-fried, non-volatile, corrosion-free, pore volume is large, surfactivity is strong, stable chemical nature, not with acid, alkali effect, water insoluble.
Pearlstone has the features such as apparent density is light, thermal conductivity is low, chemical stability is good, and the present invention selects the Task-size Controlling of expanded perlite granule at 0.125 ~ 0.42 millimeter.
Nano silver-supported antibacterial powder has higher heatproof, security, has broad-spectrum long-acting to anti-the killing of bacterium, mould, with existing anti-biotic material ratio, has the advantages such as long-acting, nontoxic.
Nano titanium oxide is under the effect of light, similar photosynthetic light-catalyzed reaction can be produced, produce the extremely strong free hydroxy of oxidation capacity and active oxygen, there is very strong photoredox function, the various organic compound of oxidable decomposition and part inorganics, the cytolemma of bacterium and the protein of solidification virus can be destroyed, can kill bacteria Sum decomposition organic pollutant, organic pollutant is resolved into free of contamination water and carbonic acid gas, thus there is extremely strong sterilization, deodorizing, mildew-resistant, anti-fouling and self-cleaning, air purification function.
Trisodium phosphate is a kind of water white transparency crystallization or white crystalline powder, soluble in water, is used as dispersion agent and emulsifying agent in the present invention.
Powder defoamer is white powdery solids, is a kind of Efficient powder defoamer, have froth breaking fast, press down bubble length, low, the resistance to polyelectrolyte of use cost, strong alkali-acid resistance, resistance to high-shear, the foam of aquosity system can be eliminated.
The present invention is achieved by following technical proposals:
The batching with the dolomite colo(u)r coating powder of air purification function is made up of following component by weight percentage: the Attapulgite potter's clay powder 10 ~ 35% with air purification function, dolomite rock powder 5 ~ 30% after calcining, zeolite granular 2 ~ 25% after acidifying, colored portland cement 5 ~ 30%, gesso 2 ~ 10%, white carbon black 2 ~ 10%, calcium chloride 2 ~ 10%, micropowder silica gel 2 ~ 5%, pearlstone 0.5 ~ 5%, nano silver-supported antibacterial powder 0.5 ~ 3%, nano titanium oxide 0.5 ~ 3%, trisodium phosphate 0.01 ~ 3% and powder defoamer 0.1 ~ 0.8%.
There is the production method of the dolomite colo(u)r coating powder of air purification function: stir in the stirrer first zeolite granular after the acidifying in batching and pearlstone input operated, after stirring, the Attapulgite potter's clay powder of air purification function will be had, colored portland cement, dolomite rock powder after calcining, gesso, calcium chloride, stir in trisodium phosphate and powder defoamer input stirrer, again by micropowder silica gel after stirring, white carbon black, stir in nano silver-supported antibacterial powder and nano titanium oxide input stirrer, the dolomite colo(u)r coating powder with air purification function is packaged as after stirring.
The production method of the dolomite rock powder after calcining: 1. first dolomite is carried out pulverizing and sieving, granularity≤5.0 millimeter of the dolomite particle after screening; 2. calcine in the dolomite particle input rotary kiln after screening, calcining temperature controls at 750 ~ 850 DEG C, and calcination time controls at 60 ~ 120 minutes; 3. the dolomite rock powder after calcining is processed as, granularity≤0.074 millimeter of the dolomite rock powder particle after calcining by the dolomite particle input grinding machine after calcining.
The production method of the zeolite granular after acidifying: 1. first zeolite is carried out pulverizing and first time screening, the Task-size Controlling of the zeolite granular after screening is at 0.149 ~ 0.42 millimeter; 2. by the zeolite granular input revolution roasting in kilns after screening, maturing temperature controls at 420 ~ 480 DEG C, and roasting time controls at 60 ~ 120 minutes; 3. carry out acidification by the zeolite granular input dilute sulphuric acid pond after roasting, the preparation of dilute sulphuric acid comprises following component by weight percentage: the sulfuric acid 6 ~ 10% of concentration 98 ﹪, water 90 ~ 94%, and acidification time controling was at 4 ~ 12 hours; 4. the zeolite granular after acidified process is taken out and drain away the water, the zeolite granular work in-process after for acidifying are dried in input rotary dryer, bake out temperature controls at 150 ~ 250 DEG C, and drying time controls at 30 ~ 60 minutes, and the zeolite granular work in-process water content after acidifying is less than 2.0%; 5. be the zeolite granular after acidifying after the zeolite granular work in-process after acidifying being carried out second time screening, the Task-size Controlling of the zeolite granular after acidifying is at 0.125 ~ 0.42 millimeter.
The production method with the Attapulgite potter's clay powder of air purification function is: (1) rear the input in pulverizer of batching mixing with the Attapulgite potter's clay powder of air purification function pulverized, the compound particles fineness after pulverizing is less than 0.5 millimeter; (2) pulverulent mixture is added and soak in old pond that to carry out soaking old process with water be work in-process, soak old time controling at 7 ~ 30 days; (3) inputted in vacuum-extruder by work in-process and be squeezed into cylindrical bar, the diameter control of cylindrical bar is at 2 ~ 10 millimeters; (4) cylindrical bar is input to cement threshing ground and carries out airing, the cylindrical bar water content after airing is less than 15%; (5) be meal by carrying out abrasive dust in the cylindrical bar input grinding machine after airing, the particle fineness of meal is less than 0.074 millimeter.
The Attapulgite potter's clay powder with air purification function adopts to be applied for " having the Attapulgite potter's clay powder of air purification function " on February 25th, 2011 by the present inventor, Chinese patent Authorization Notice No. is: CN102173743B, authorized announcement date: on July 25th, 2012.
High sticky attapulgite clay is the attapulgite clay adopting the complete processing improving viscosity of attapulgite clay to produce, and from the attapulgite clay of mining area exploitation, needs the weathering through 30 ~ 120 days; Modification processing method is: calculate by weight percentage, gets the attapulgite clay after weathering 94 ~ 98%, evenly adds 2 ~ 6% sodium carbonate, and in common input fermentation vat, add clear water and carry out immersion ageing, soak time is 72 ~ 120 hours; Get the attapulgite clay after immersion, stir in input stirrer, and by the attapulgite clay after stirring, be extruded into thin slice through extrusion machine, its gauge control at 0.5 ~ 2 millimeter, by attapulgite clay thin slice, carry out airing, the attapulgite clay thin slice after airing, its water content≤15%; Batching is calculated by weight percentage: the attapulgite clay 94 ~ 98% after airing, High hydrophilous resin 0.5 ~ 5% and Mierocrystalline cellulose 0.5 ~ 3%, above-mentioned batching is stirred, inputs in grinding machine and carry out abrasive dust, particle fineness≤0.074 millimeter after stirring;
Above-mentioned production technique adopts to be applied for " improving the complete processing of viscosity of attapulgite clay " on June 20th, 2005 by the present inventor, and Chinese patent Authorization Notice No. is: CN1317067C, authorized announcement date: on May 23rd, 2007.
The detection method of high sticky attapulgite clay: get 28.0g attapulgite clay powder sample, add in the suspension cup of homogenizer, add 372g water again, suspension cup is placed on homogenizer, stir 20 minutes under the rotating speed of 11000 revs/min, to pour in the beaker of 250mL through high-speed stirring sample suspension again, use the viscosity of NDJ-1 type rotational viscosimeter test suspension liquid, tested viscosity value >=2200mPas is high sticky attapulgite clay.
The vitriol oil per-cent of concentration 98% described in the present invention is weight percentage, and PCm is weight percentage.
Dolomite in the present invention loses carbonic acid gas when being fired to 700 ~ 900 DEG C, becoming calcium oxide and magnesian mixture, be called causticity dolomite, is a kind of gelling material, at the construction field (site), be conducive to increasing the rear setting and harden intensity of dolomite colo(u)r coating powder spraying with air purification function.
Wilkinite after rice hulls after the Attapulgite potter's clay powder with air purification function glues attapulgite clay, quick dissolved sodium silicate, zeolite powder, acidifying by height, the zeolite after acidifying, Concavo-convex excellent stone clay after the acidify, acidifying, the raw material such as diatomite, volcanics, alumine, Leafy twigs of Oriental Arborvitae, aluminium silicate fiber peacekeeping polyacrylamide after acidifying form.
There are a large amount of micropores and gac in the Attapulgite potter's clay powder with air purification function, there is good cohesiveness, plasticity-, thixotropy, resistivity against fire and thermostability, can the objectionable impurities such as formaldehyde, ammonia and benzene in effective absorbed air.
Adopt the Attapulgite potter's clay powder with air purification function for mainly raw material, produce the dolomite colo(u)r coating powder with air purification function, given full play to the effective efficiency of the Attapulgite potter's clay powder with air purification function.
Although the rice hulls have acidifying in the Attapulgite potter's clay powder batching with air purification function after, zeolite after acidifying, Concavo-convex excellent stone clay after the acidify, the raw materials such as the wilkinite after acidifying and the diatomite after acidifying, owing to having particle fineness≤0.074 millimeter of the Attapulgite potter's clay powder of air purification function, be equivalent to 200 orders, be applicable to produce pottery craft product, in order to ensure air purification function of the present invention, adjustment is needed to have the grain composition of the dolomite colo(u)r coating powder of air purification function, by the Task-size Controlling of the zeolite granular after acidifying at 0.125 ~ 0.42 millimeter, be equivalent to 40 ~ 120 orders, adsorption efficiency and the intensity of the rear wall surface spraying layer of dolomite colo(u)r coating powder spraying with air purification function can be improved.
The production method of the zeolite granular after acidifying adopts to be pulverized, first time screening, roasting, acidifying, drains, dries and technical process that second time is sieved, carries out acidifying, substantially increase the acidifying quality of zeolite, adsorption efficiency and acidification rate after first roasting.
The dolomite colo(u)r coating powder internal particle grating with air purification function is even, granularity maximum in particle is 0.42 millimeter, minimum grain graininess is nano level, at the construction field (site), the dolomite colo(u)r coating powder with air purification function is added in the water in paint can, stir into muddy, spraying machine or spray gun is utilized to carry out spraying application, the dolomite colo(u)r coating powder with air purification function by pressurized air to obtain sizable speed, be mapped to by spray metope by nozzle, just form firmly sprayed coating; The dolomite colo(u)r coating powder with air purification function in delivery hose can smooth and easy, stably pass through, there is not the phenomenon of blocking pipe.
The dolomite colo(u)r coating powder with air purification function has stronger adhesive power, can not produce the segregation of colo(u)r coating, more there will not be layering, and after spraying, setting and harden speed is fast, and sprayed coating shrinking percentage is little, can not produce map cracking and landing phenomenon.
The add-on of adjustment gesso can control the setting rate of the dolomite colo(u)r coating powder with air purification function.
Utilize white carbon black the to have stability that specific surface area is large, superficial attractive forces is strong, chemical purity is high, dispersing property is good, superior, reinforcing good feature, regulates adsorption effect, thickening property, sticking power and the thixotropy with the dolomite colo(u)r coating powder of air purification function.
Calcium chloride and micropowder silica gel support on the topical carrier of dolomite colo(u)r coating powder with air purification function, can increase the performance of the absorption of the dolomite colo(u)r coating powder with air purification function, mildew-resistant and deodorizing.
Production method of the present invention stirs in the stirrer first zeolite granular after the acidifying in batching and pearlstone input operated, after stirring, the Attapulgite potter's clay powder of air purification function will be had, colored portland cement, dolomite rock powder after calcining, gesso, calcium chloride, stir in trisodium phosphate and powder defoamer input stirrer, again by micropowder silica gel after stirring, white carbon black, stir in nano silver-supported antibacterial powder and nano titanium oxide input stirrer, after stirring, micropowder silica gel, white carbon black, nano silver-supported antibacterial powder and nano titanium oxide are easy to the surface disperseing also load to prepare burden at other, solve the agglomeration traits that nano material is difficult to disperse, enhance the sterilization of nano material, deodorizing, mildew-resistant, the result of use of anti-fouling and self-cleaning and air purification function.
The Attapulgite potter's clay powder with air purification function in the present invention's batching has good cohesiveness, plasticity-and thixotropy, do not need to add the heavy viscous materials such as various Mierocrystalline cellulose, redispersible rubber powder, urea-formaldehyde resin, emulsion sizing agent more in addition, improve the absorption property of the dolomite colo(u)r coating powder with air purification function.
Expanded perlite granule inside is polynuclear plane, frangible higher with water-intake rate, when body of wall temperature variation, pearlstone is because of water-swelling generation bubbling cracking phenomena, the higher heat-insulating property that also can reduce material of water-intake rate, the utilization of lagging material is restricted, after mixing with the Attapulgite potter's clay powder with air purification function, owing to having, viscosity of attapulgite clay in the Attapulgite potter's clay powder of air purification function is high and plasticity-is good, the shortcoming that expanded pearlite rock mass is frangible and water-intake rate is higher can be made up, and it is light to make full use of pearlstone unit weight, thermal conductivity is low, resistivity against fire is strong, sound-proofing properties is good, hole is trickle, the feature that physical and chemical performance is stable.
The dolomite colo(u)r coating powder with air purification function is adopted to carry out indoor wall decoration, can spray and produce the artistic anaglyph of multiple stereo concave-convex chromatic pattern, the grain composition in batching is optimized due to the dolomite colo(u)r coating powder with air purification function, after spraying, coating is hard, porosity is high, specific surface area is large, cohesiveness is strong, can adsorption-decomposition function indoor formaldehyde, ammonia nitrogen, benzene, toluene, the objectionable impurities such as dimethylbenzene and ethylbenzene, also there is automatic humidifying, prevent condensation, fire-retardant, sound insulation, heat insulation, mildew-resistant, sterilization, deodorizing, anti-fouling and self-cleaning, the function purified air.
The dolomite colo(u)r coating powder with air purification function is applicable to indoor wall decoration.
Embodiment
Below in conjunction with embodiment, the invention will be further described:
The batching with the dolomite colo(u)r coating powder of air purification function is made up of following component by weight percentage: the Attapulgite potter's clay powder 28% with air purification function, dolomite rock powder 14% after calcining, zeolite granular 16% after acidifying, colored portland cement 26%, gesso 5%, white carbon black 3%, calcium chloride 2%, micropowder silica gel 2%, pearlstone 2%, nano silver-supported antibacterial powder 0.6%, nano titanium oxide 0.5%, trisodium phosphate 0.5% and powder defoamer 0.4%.
There is the production method of the dolomite colo(u)r coating powder of air purification function: stir in the stirrer first zeolite granular after the acidifying in batching and pearlstone input operated, after stirring, the Attapulgite potter's clay powder of air purification function will be had, colored portland cement, dolomite rock powder after calcining, gesso, calcium chloride, stir in trisodium phosphate and powder defoamer input stirrer, again by micropowder silica gel after stirring, white carbon black, stir in nano silver-supported antibacterial powder and nano titanium oxide input stirrer, the dolomite colo(u)r coating powder with air purification function is packaged as after stirring.
The production method of the dolomite rock powder after calcining: 1. first dolomite is carried out pulverizing and sieving, granularity≤5.0 millimeter of the dolomite particle after screening; 2. calcine in the dolomite particle input rotary kiln after screening, calcining temperature controls at 800 ~ 850 DEG C, and calcination time controls at 100 minutes; 3. the dolomite rock powder after calcining is processed as, granularity≤0.074 millimeter of the dolomite rock powder particle after calcining by the dolomite particle input grinding machine after calcining.
The production method of the zeolite granular after acidifying: 1. first zeolite is carried out pulverizing and first time screening, the Task-size Controlling of the zeolite granular after screening is at 0.149 ~ 0.42 millimeter; 2. by the zeolite granular input revolution roasting in kilns after screening, maturing temperature controls at 450 ~ 480 DEG C, and roasting time controls at 90 minutes; 3. carry out acidification by the zeolite granular input dilute sulphuric acid pond after roasting, the preparation of dilute sulphuric acid comprises following component by weight percentage: the sulfuric acid 8% of concentration 98 ﹪, water 92%, and acidification time controling was at 10 hours; 4. the zeolite granular after acidified process is taken out and drain away the water, the zeolite granular work in-process after for acidifying are dried in input rotary dryer, bake out temperature controls at 200 ~ 220 DEG C, and drying time controls at 60 minutes, and the zeolite granular work in-process water content after acidifying is less than 2.0%; 5. be the zeolite granular after acidifying after the zeolite granular work in-process after acidifying being carried out second time screening, the Task-size Controlling of the zeolite granular after acidifying is at 0.125 ~ 0.42 millimeter.
Claims (2)
1. one kind has the dolomite colo(u)r coating powder of air purification function, it is characterized in that, the batching with the dolomite colo(u)r coating powder of air purification function is made up of following component by weight percentage: the Attapulgite potter's clay powder 10 ~ 35% with air purification function, dolomite rock powder 5 ~ 30% after calcining, zeolite granular 2 ~ 25% after acidifying, colored portland cement 5 ~ 30%, gesso 2 ~ 10%, white carbon black 2 ~ 10%, calcium chloride 2 ~ 10%, micropowder silica gel 2 ~ 5%, pearlstone 0.5 ~ 5%, nano silver-supported antibacterial powder 0.5 ~ 3%, nano titanium oxide 0.5 ~ 3%, trisodium phosphate 0.01 ~ 3% and powder defoamer 0.1 ~ 0.8%,
The described production method with the Attapulgite potter's clay powder of air purification function is: (1) rear the input in pulverizer of batching mixing with the Attapulgite potter's clay powder of air purification function pulverized, the compound particles fineness after pulverizing is less than 0.5 millimeter; (2) pulverulent mixture is added and soak in old pond that to carry out soaking old process with water be work in-process, soak old time controling at 7 ~ 30 days; (3) inputted in vacuum-extruder by work in-process and be squeezed into cylindrical bar, the diameter control of cylindrical bar is at 2 ~ 10 millimeters; (4) cylindrical bar is input to cement threshing ground and carries out airing, the cylindrical bar water content after airing is less than 15%; (5) be meal by carrying out abrasive dust in the cylindrical bar input grinding machine after airing, the particle fineness of meal is less than 0.074 millimeter;
The production method of the dolomite rock powder after described calcining: 1. first dolomite is carried out pulverizing and sieving, granularity≤5.0 millimeter of the dolomite particle after screening; 2. calcine in the dolomite particle input rotary kiln after screening, calcining temperature controls at 750 ~ 850 DEG C, and calcination time controls at 60 ~ 120 minutes; 3. the dolomite rock powder after calcining is processed as, granularity≤0.074 millimeter of the dolomite rock powder particle after calcining by the dolomite particle input grinding machine after calcining;
The production method of the zeolite granular after described acidifying: 1. first zeolite is carried out pulverizing and first time screening, the Task-size Controlling of the zeolite granular after screening is at 0.149 ~ 0.42 millimeter; 2. by the zeolite granular input revolution roasting in kilns after screening, maturing temperature controls at 420 ~ 480 DEG C, and roasting time controls at 60 ~ 120 minutes; 3. carry out acidification by the zeolite granular input dilute sulphuric acid pond after roasting, the preparation of dilute sulphuric acid comprises following component by weight percentage: the sulfuric acid 6 ~ 10% of concentration 98 ﹪, water 90 ~ 94%, and acidification time controling was at 4 ~ 12 hours; 4. the zeolite granular after acidified process is taken out and drain away the water, the zeolite granular work in-process after for acidifying are dried in input rotary dryer, bake out temperature controls at 150 ~ 250 DEG C, and drying time controls at 30 ~ 60 minutes, and the zeolite granular work in-process water content after acidifying is less than 2.0%; 5. be the zeolite granular after acidifying after the zeolite granular work in-process after acidifying being carried out second time screening, the Task-size Controlling of the zeolite granular after acidifying is at 0.125 ~ 0.42 millimeter;
The Task-size Controlling of described expanded perlite granule is at 0.125 ~ 0.42 millimeter.
2. the dolomite colo(u)r coating powder with air purification function according to claim 1, it is characterized in that, there is the production method of the dolomite colo(u)r coating powder of air purification function: stir in the stirrer first zeolite granular after the acidifying in batching and pearlstone input operated, after stirring, the Attapulgite potter's clay powder of air purification function will be had, colored portland cement, dolomite rock powder after calcining, gesso, calcium chloride, stir in trisodium phosphate and powder defoamer input stirrer, again by micropowder silica gel after stirring, white carbon black, stir in nano silver-supported antibacterial powder and nano titanium oxide input stirrer, the dolomite colo(u)r coating powder with air purification function is packaged as after stirring.